CN113443875A - 一种种植型预留大空隙混凝土及其制备方法和应用 - Google Patents
一种种植型预留大空隙混凝土及其制备方法和应用 Download PDFInfo
- Publication number
- CN113443875A CN113443875A CN202110774919.6A CN202110774919A CN113443875A CN 113443875 A CN113443875 A CN 113443875A CN 202110774919 A CN202110774919 A CN 202110774919A CN 113443875 A CN113443875 A CN 113443875A
- Authority
- CN
- China
- Prior art keywords
- concrete
- parts
- gap
- planting type
- type reserved
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及混凝土技术领域，具体涉及种植型预留大空隙混凝土及其制备方法和应用。种植型预留大空隙混凝土，由如下重量份数的原料制成：碎石80～85份；硅酸盐水泥15～20份；添加剂0.5～1份；发酵椰子皮5～10份；水5～10份。本发明采用发酵椰子皮制得种植型预留大空隙混凝土，混凝土能够吸附城市污染物粉尘，减少扬尘污染，还能够根据环境及功能需要设计图案、颜色，充分与周围环境相结合，以及在城市树池防护及绿化，高速公路、城际铁路、尾矿坝等边坡绿化防护。提供绿色、健康、舒适的城市道路，还能与自然环境亲和，做到建筑与环境的和谐共处、永续发展。
Description
技术领域
本发明涉及混凝土技术领域，具体涉及一种种植型预留大空隙混凝土及 其制备方法和应用。
背景技术
为了降低环境负荷、改善生态环境，多年来国内外对多孔混凝土开展了大 量的实验研究，多孔混凝土就是采用特殊工艺制备的具有特殊孔结构与表面特 性的生态混凝土，再生粗骨料制备的多孔生态混凝土不仅具有一定的强度、良 好的透水性，还能够缓解建筑垃圾占用大量土地资源的压力，具有良好的生态 效益和经济效益；利用其制备的多孔植被混凝土可以应用于边坡防护、路面铺 装、屋顶花园等建设中，产生了良好的防冲刷、防洪害、恢复生态作用，具备 净化水质、改善景观的优越性。
虽然现有技术中已经存在了种类多样的多孔混凝土，但是目前的植被混 凝土仍然存在有缺陷，例如，混凝土中无植物存活所需营养成分，空隙率较 小、不规则、不利于绿植的种植，这些原因均导致了植物种植周期长且绿植 死亡后不便更换的技术缺陷。
发明内容
针对上述存在的技术不足，本发明提供了一种种植型预留大空隙混凝土 及其制备方法和应用，本发明通过采用发酵椰子皮制得了种植型预留大空隙 混凝土，此混凝土能够应用于湿地绿化、河堤加固、小区绿化、高速公路和 城际铁路边坡绿化防护等项目，旨在解决普通多孔混凝土应用过程中存在的 难扎根、存活难、植物种植周期长的问题。
为实现上述目的，本发明的技术方案如下：
一种种植型预留大空隙混凝土，由如下重量份数的原料制成：碎石80～85 份；硅酸盐水泥15～20份；添加剂0.5～1份；发酵椰子皮5～10份；水5～10 份。
优选的，所述添加剂由1～1.5份混凝土表面增强剂、3.1份羧酸盐、0.3～0.8 份硫酸钠、1～4份硫酸铁混合而成。
优选的，所述发酵椰子皮按照如下步骤制备：
将椰子皮粉碎后装袋并加水，于密封状态下室温发酵30-40d；
其中，椰子皮与水的质量比为1:0.5～0.7。
本发明还保护了种植型预留大空隙混凝土的制备方法，包括如下步骤：
(1)称量：按照如下重量份数称取原料：碎石80～85份；硅酸盐水泥 15～20份；添加剂0.5～1份；发酵椰子皮5～10份；水5～10份，备用；
(2)将碎石、硅酸盐水泥、添加剂、发酵椰子皮和水共同搅拌均匀，然 后入模成型，得到成型混凝土，将成型混凝土再经养护，得到种植型预留大 空隙混凝土。
优选的，所述养护的方法为：将成型混凝土表面覆盖塑料薄膜，终凝后， 保持18～22℃、相对湿度大于95％的条件下养护4～7d，脱模并进行二次养护。
优选的，所述二次养护的方法为：在混凝土的大空隙中置入营养土，浇 水至营养土浸湿，养护7-10d。
本发明还保护了种植型预留大空隙混凝土在制备生态植被型混凝土中的 应用。
优选的，所述应用的方法为：
(1)调节种植型预留大空隙混凝土pH至6.0～7.5；
(2)向种植型预留大空隙混凝土的空隙内加入营养物；
(3)将育好的绿植种苗移植于种植型预留大空隙混凝土的大空隙中并室 内养护；
(4)将养护的绿植种苗14-20d后移栽，再进行常规培育。
与现有技术相比，本发明的有益效果：
1、本发明加入发酵椰子皮，发酵椰子皮能够改善生态混凝土对绿植提供 营养物的途径和数量；通过发酵椰子皮提供的大空隙能够改善生态混凝土中 对绿植根系的约束，继而降低植物种植过程中难扎根、存活难的技术缺陷； 发酵椰子皮提供了大空隙，使得混凝土便于对种植育好的绿植苗直接进行养 护，改善了原本需要种子种植的方法，缩短了种植时间；本发明还能够通过 调整孔径、间距等条件，继而适应不同绿植对于种植环境的需求。
2、本发明还进行了二次养护，二次养护的目的在于：进一步保证混凝土 强度、防止混凝土表面干燥产生的裂缝，并使得营养土中的营养成分渗入到 生态空隙中。
3、本发明制得了种植型预留大空隙混凝土，混凝土能够吸附城市污染物 粉尘，减少扬尘污染，还能够根据环境及功能需要设计图案、颜色，充分与 周围环境相结合，以及在城市树池防护及绿化，高速公路、城际铁路、尾矿 坝等边坡绿化防护。提供了一种绿色、健康、舒适的城市道路，还能与自然 环境亲和，做到建筑与环境的和谐共处、永续发展。
3、本发明对椰子皮进行了发酵处理，若椰子皮未发酵，椰子皮会在土壤 内发酵并产生热量，继而产生烧根的技术缺陷；添加剂同时用于中和水泥的 碱性。
附图说明
图1为规则孔洞型模具结构示意图；
图2为模具中加入透水混凝土和植生基液的结构示意图；
图3为在生态混凝土试块中植入植被的结构示意图；
图4为本发明实施例1制得的种植型预留大空隙混凝土的实物图。
具体实施方式
下面对本发明的具体实施方式进行详细描述，但应当理解本发明的保护 范围并不受具体实施方式的限制。基于本发明中的实施例，本领域普通技术 人员在没有做出创造性劳动的前提下所获得的所有其他实施例，都属于本发 明保护的范围。本发明各实施例中所述实验方法，如无特殊说明，均为常规 方法。
实施例1
一种种植型预留大空隙混凝土的制备方法，包括如下步骤：
(1)发酵椰子皮的制备：
将椰子皮粉碎后装袋并加水，椰子皮与水的质量比为1:0.5，于密封状态 下室温发酵40d，得到发酵椰子皮；
(2)称量：按照如下重量份数称取原料：碎石80份；硅酸盐水泥20份； 添加剂0.5份；发酵椰子皮10份；水5份，备用；
添加剂由1份混凝土表面增强剂、3.1份羧酸盐、0.8份硫酸钠、1份硫酸 铁混合而成；
(3)将碎石、硅酸盐水泥、添加剂、发酵椰子皮和水共同搅拌均匀，然 后入模成型，得到成型混凝土，将成型混凝土再经养护，得到种植型预留大 空隙混凝土；
(4)养护的方法为：将成型混凝土表面覆盖塑料薄膜，终凝后，保持18℃、 相对湿度大于95％的条件下养护5d，脱模并进行二次养护；
(5)二次养护的方法为：在混凝土的大空隙中置入营养土，浇水至营养 土浸湿，养护7d。
实施例2
一种种植型预留大空隙混凝土的制备方法，包括如下步骤：
(1)发酵椰子皮的制备：
将椰子皮粉碎后装袋并加水，椰子皮与水的质量比为1:0.6，于密封状态 下室温发酵35d，得到发酵椰子皮；
(2)称量：按照如下重量份数称取原料：碎石82份；硅酸盐水泥18份； 添加剂0.7份；发酵椰子皮9份；水8份，备用；
添加剂由1.3份混凝土表面增强剂、3.1份羧酸盐、0.5份硫酸钠、2份硫 酸铁混合而成；
(3)将碎石、硅酸盐水泥、添加剂、发酵椰子皮和水共同搅拌均匀，然 后入模成型，得到成型混凝土，将成型混凝土再经养护，得到种植型预留大 空隙混凝土；
(4)养护的方法为：将成型混凝土表面覆盖塑料薄膜，终凝后，保持20℃、 相对湿度大于95％的条件下养护7d，脱模并进行二次养护；
(5)二次养护的方法为：在混凝土的大空隙中置入营养土，浇水至营养 土浸湿，养护9d。
实施例3
一种种植型预留大空隙混凝土的制备方法，包括如下步骤：
(1)发酵椰子皮的制备：
将椰子皮粉碎后装袋并加水，椰子皮与水的质量比为1:0.7，于密封状态 下室温发酵30d，得到发酵椰子皮；
(2)称量：按照如下重量份数称取原料：碎石85份；硅酸盐水泥15份； 添加剂1份；发酵椰子皮5份；水10份，备用；
添加剂由1.5份混凝土表面增强剂、3.1份羧酸盐、0.3份硫酸钠、4份硫 酸铁混合而成；
(3)将碎石、硅酸盐水泥、添加剂、发酵椰子皮和水共同搅拌均匀，然 后入模成型，得到成型混凝土，将成型混凝土再经养护，得到种植型预留大 空隙混凝土；
(4)养护的方法为：将成型混凝土表面覆盖塑料薄膜，终凝后，保持22℃、 相对湿度大于95％的条件下养护4d，脱模并进行二次养护；
(5)二次养护的方法为：在混凝土的大空隙中置入营养土，浇水至营养 土浸湿，养护10d。
本发明实施例1-实施例3均制得易扎根、易存活、植物种植周期短的种 植型预留大空隙混凝土，且效果平行，下面以实施例2为例，进行混凝土的 应用，具体如下：
(1)根据拟安装防护目标的要求，包括地块大小、是否是坡面、拟种植 何种绿植、有无颜色要求、有无整体拼装后的图案要求等，确定生态混凝土 模具形状和大空隙的直径、间距、排布形式；
(2)根据以上确定的信息，制作生态混凝土预制浇筑模具；
(3)依据混凝土配合比拌制生态混凝土；
(4)将拌制好的生态混凝土注入模具，并覆盖保水膜养护，终凝后间隔 洒水养护；
(5)达到脱模条件后，脱模；
(6)脱模后在预留大空隙中置入营养土，继续洒水养护，保证强度和防 止干裂，由于预留大空隙的存在，能够将育好的绿植苗直接种入大空隙，而 且在绿植死亡后及时方便更换苗体，使得绿植种植周期缩短、成活率提高；
(7)根据要求种植绿植，洒水保墒，等到绿植完全适应新种植环境后， 运至现场安装。
显然，本领域的技术人员可以对本发明进行各种改动和变型而不脱离本 发明的精神和范围。这样，倘若本发明的这些修改和变型属于本发明权利要 求及其等同技术的范围之内，则本发明也意图包含这些改动和变型在内。
Claims (8)
1.一种种植型预留大空隙混凝土，其特征在于，由如下重量份数的原料制成：碎石80～85份；硅酸盐水泥15～20份；添加剂0.5～1份；发酵椰子皮5～10份；水5～10份。
2.根据权利要求1所述的一种种植型预留大空隙混凝土，其特征在于，所述添加剂由1～1.5份混凝土表面增强剂、3.1份羧酸盐、0.3～0.8份硫酸钠、1～4份硫酸铁混合而成。
3.根据权利要求1所述的一种种植型预留大空隙混凝土，其特征在于，所述发酵椰子皮按照如下步骤制备：
将椰子皮粉碎后装袋并加水，于密封状态下室温发酵30-40d；
其中，椰子皮与水的质量比为1:0.5～0.7。
4.一种权利要求1所述的种植型预留大空隙混凝土的制备方法，其特征在于，包括如下步骤：
(1)称量：按照如下重量份数称取原料：碎石80～85份；硅酸盐水泥15～20份；添加剂0.5～1份；发酵椰子皮5～10份；水5～10份，备用；
(2)将碎石、硅酸盐水泥、添加剂、发酵椰子皮和水共同搅拌均匀，然后入模成型，得到成型混凝土，将成型混凝土再经养护，得到种植型预留大空隙混凝土。
5.根据权利要求4所述的种植型预留大空隙混凝土的制备方法，其特征在于，所述养护的方法为：将成型混凝土表面覆盖塑料薄膜，终凝后，保持18～22℃、相对湿度大于95％的条件下养护4～7d，脱模并进行二次养护。
6.根据权利要求5所述的种植型预留大空隙混凝土的制备方法，其特征在于，所述二次养护的方法为：在混凝土的大空隙中置入营养土，浇水至营养土浸湿，养护7-10d。
7.一种根据权利要求1所述的种植型预留大空隙混凝土在制备生态植被型混凝土中的应用。
8.根据权利要求7所述的应用，其特征在于，所述应用的方法为：
(1)调节种植型预留大空隙混凝土pH至6.0～7.5；
(2)向种植型预留大空隙混凝土的空隙内加入营养物；
(3)将育好的绿植种苗移植于种植型预留大空隙混凝土的大空隙中并室内养护；
(4)将养护的绿植种苗14-20d后移栽，再进行常规培育。