CN113425913B - 一种用于胸外科的功能器具 - Google Patents

一种用于胸外科的功能器具 Download PDF

Info

Publication number
CN113425913B
CN113425913B CN202110689469.0A CN202110689469A CN113425913B CN 113425913 B CN113425913 B CN 113425913B CN 202110689469 A CN202110689469 A CN 202110689469A CN 113425913 B CN113425913 B CN 113425913B
Authority
CN
China
Prior art keywords
ceramic powder
nano titanium
titanium oxynitride
oxynitride ceramic
macroporous alumina
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN202110689469.0A
Other languages
English (en)
Other versions
CN113425913A (zh
Inventor
虞桂平
黄斌
陆红艳
单一波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangyin Peoples Hospital
Original Assignee
Jiangyin Peoples Hospital
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangyin Peoples Hospital filed Critical Jiangyin Peoples Hospital
Priority to CN202110689469.0A priority Critical patent/CN113425913B/zh
Publication of CN113425913A publication Critical patent/CN113425913A/zh
Application granted granted Critical
Publication of CN113425913B publication Critical patent/CN113425913B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种用于胸外科的功能器具，其原料组成质量百分比为：褐藻淀粉硫酸酯为1～5％，负载纳米氮氧化钛陶瓷粉的高纯大孔氧化为1～5％，聚乳酸为余量；负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝的原料为纳米氮氧化钛陶瓷粉，山梨醇以及高纯大孔氧化铝。本发明的优点在于：其主要的聚乳酸材料经注塑组成，聚乳酸可降解，且对人体无害，在手术中不会产生次生感染，保证手术的有效进行和病人的身体安全。

Description

一种用于胸外科的功能器具
【技术领域】
本发明涉及胸外科器具技术领域，具体地说，是一种用于胸外科的功能器具。
【背景技术】
近年来我国胸外科领域获得了快速的发展，胸外科相关基础研究、理论以及先进理念不断取得突破，相关的组织工程和以3D为代表的新材料、新防护器具、新技术在临床上得到了广泛的应用，在规范化治疗方面得到了普遍的使用，获得了良好的手术效果，大大的提高了术后病人的成活率，并减轻了病人的痛苦，促进了患者的康复。
其中，用于胸外科的功能器具、材料等新应用起到了重要的保护作用，取得了良好的使用效果，获得了医生、患者的一致好评。
中国专利(申请号：201621233526.5)公开了一种用于胸外科的功能器具，其结构包括夹器、夹柄、轴器，所述夹器连接有夹柄，所述轴器活动连接有夹柄，所述夹器包括夹口、夹交位、衔接固定体、衔接辅助体，所述夹口设有夹交位。现有的用于胸外科的功能器具无法有效做到使用时更加灵活省力。
中国专利(申请号：201520744173.4)设计了一种用于胸外科的功能器具，刀柄内的前端设有LED灯，末端设有电池组及图像传输信号装置，刀体的刀尖上端设有微型探头，微型探头通过导线与电路板相连接，LED灯通过导线与电路板相连，图像传输信号装置通过导线与电路板相连接，刀柄上设有LED开关和微型探头开关，LED开关和微型探头开关分别设置在LED灯及微型探头与电路板连接的导线上，刀体靠近刀尖的上方设有吸血血囊，吸血血囊通过吸血管依次连接着吸血泵和血袋，吸血管穿过所述刀柄，吸血管上设有单向阀，单向阀固定安装在所述刀柄的上端前侧；本实用新型在进行胸外科手术时方便安全，操作起来方便，省时省力，极大的减轻了医务人员的工作难度。
当前，胸外科功能器具更是向着具有良好的生物相容性，对人体无任何伤害，可降解，在手术中不会产生次生感染，保证手术的有效进行和病人的身体安全等方向发展。
【发明内容】
本发明的目的在于克服现有技术的不足，提供一种用于胸外科的功能器具。
本发明的目的是通过以下技术方案来实现的：
一种用于胸外科的功能器具，其原料组成质量百分比为：
褐藻淀粉硫酸酯 1～5％
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝 1～5％
聚乳酸 余量
褐藻淀粉硫酸酯在功能器具中的质量分数为2～4％。
褐藻淀粉硫酸酯在功能器具中的质量分数为3％。
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝在功能器具中的质量分数为2～4％。
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝在功能器具中的质量分数为3％。
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝的原料为纳米氮氧化钛陶瓷粉，山梨醇以及高纯大孔氧化铝。
纳米氮氧化钛陶瓷粉在负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝中的质量分数为20～30％，优选为25％。
山梨醇在负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝中的质量分数为1～3％，优选为2％。山梨醇主要是在湿法研磨中起到相容剂的功效。
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝的制备方法，将纳米氮氧化钛陶瓷粉，山梨醇以及高纯大孔氧化铝通过湿法研磨的工艺制备。
一种用于胸外科的功能器具，将各种原料混合后注塑制备出所需的手上器具。
本申请的纳米TiON具有很强的光催化杀菌作用。在受到可见光照射下，TiON将水分解成自由基，自由基进入细菌的细胞壁内，破坏细胞壁，降解细胞内组织结构，进而杀死细胞，起抗菌杀菌作用。
本申请的高纯大孔氧化铝由于具有较大的比表面积，比表面积在350g/m2，比较适合作为抗菌剂的载体，同时由于氧化铝的铝元素也存在人体中，与人体的相容性较好，这也是我们选择高纯大孔氧化铝作为载体的原因。
本申请的褐藻淀粉硫酸酯能有效地降低血脂和血液凝固性，抗血小板凝集，改善血液流变学指标，提高血中高密度脂蛋白水平，从多方面起着预防冠心病及心肌梗塞的作用。专家们研究发现，褐藻淀粉硫酸酯能显著降低血脂，并且有提高高密度脂蛋白的作用。
与现有技术相比，本发明的积极效果是：
本发明的聚乳酸具有良好的生物相容性，同时对人体无任何伤害的作用。
一种用于胸外科的功能器具，可以为一次性腔内探针等其它手上器具，其主要的聚乳酸材料经注塑组成，聚乳酸可降解，且对人体无害，在手术中不会产生次生感染，保证手术的有效进行和病人的身体安全。
【具体实施方式】
以下提供本发明一种用于胸外科的功能器具的具体实施方式。
实施例1
一种用于胸外科的功能器具，其原料组成质量百分比为：
褐藻淀粉硫酸酯 1％
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝 1％
聚乳酸 98％
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝的原料为纳米氮氧化钛陶瓷粉，山梨醇以及高纯大孔氧化铝。
纳米氮氧化钛陶瓷粉在负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝中的质量分数为20％。
山梨醇在负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝中的质量分数为1％。山梨醇主要是在湿法研磨中起到相容剂的功效。
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝的制备方法，将纳米氮氧化钛陶瓷粉，山梨醇以及高纯大孔氧化铝通过湿法研磨的工艺制备。
一种用于胸外科的功能器具，将各种原料混合后注塑制备出所需的手上器具。
本申请的纳米TiON具有很强的光催化杀菌作用。在受到可见光照射下，TiON将水分解成自由基，自由基进入细菌的细胞壁内，破坏细胞壁，降解细胞内组织结构，进而杀死细胞，起抗菌杀菌作用。
本申请的高纯大孔氧化铝由于具有较大的比表面积，比表面积在350g/m2，比较适合作为抗菌剂的载体，同时由于氧化铝的铝元素也存在人体中，与人体的相容性较好，这也是我们选择高纯大孔氧化铝作为载体的原因。
本申请的褐藻淀粉硫酸酯能有效地降低血脂和血液凝固性，抗血小板凝集，改善血液流变学指标，提高血中高密度脂蛋白水平，从多方面起着预防冠心病及心肌梗塞的作用。专家们研究发现，褐藻淀粉硫酸酯能显著降低血脂，并且有提高高密度脂蛋白的作用。
实施例2
一种用于胸外科的功能器具，其原料组成质量百分比为：
褐藻淀粉硫酸酯 2％
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝 2％
聚乳酸 96％
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝的原料为纳米氮氧化钛陶瓷粉，山梨醇以及高纯大孔氧化铝。
纳米氮氧化钛陶瓷粉在负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝中的质量分数为22％。
山梨醇在负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝中的质量分数为1.5％。山梨醇主要是在湿法研磨中起到相容剂的功效。
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝的制备方法，将纳米氮氧化钛陶瓷粉，山梨醇以及高纯大孔氧化铝通过湿法研磨的工艺制备。
一种用于胸外科的功能器具，将各种原料混合后注塑制备出所需的手上器具。
实施例3
一种用于胸外科的功能器具，其原料组成质量百分比为：
褐藻淀粉硫酸酯 3％
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝 3％
聚乳酸 94％
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝的原料为纳米氮氧化钛陶瓷粉，山梨醇以及高纯大孔氧化铝。
纳米氮氧化钛陶瓷粉在负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝中的质量分数为25％。
山梨醇在负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝中的质量分数为2％。山梨醇主要是在湿法研磨中起到相容剂的功效。
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝的制备方法，将纳米氮氧化钛陶瓷粉，山梨醇以及高纯大孔氧化铝通过湿法研磨的工艺制备。
一种用于胸外科的功能器具，将各种原料混合后注塑制备出所需的手上器具。
实施例4
一种用于胸外科的功能器具，其原料组成质量百分比为：
褐藻淀粉硫酸酯 4％
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝 4％
聚乳酸 92％
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝的原料为纳米氮氧化钛陶瓷粉，山梨醇以及高纯大孔氧化铝。
纳米氮氧化钛陶瓷粉在负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝中的质量分数为27％。
山梨醇在负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝中的质量分数为2.5％。山梨醇主要是在湿法研磨中起到相容剂的功效。
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝的制备方法，将纳米氮氧化钛陶瓷粉，山梨醇以及高纯大孔氧化铝通过湿法研磨的工艺制备。
一种用于胸外科的功能器具，将各种原料混合后注塑制备出所需的手上器具。
实施例5
一种用于胸外科的功能器具，其原料组成质量百分比为：
褐藻淀粉硫酸酯 5％
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝 5％
聚乳酸 90％
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝的原料为纳米氮氧化钛陶瓷粉，山梨醇以及高纯大孔氧化铝。
纳米氮氧化钛陶瓷粉在负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝中的质量分数为30％。
山梨醇在负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝中的质量分数为3％。山梨醇主要是在湿法研磨中起到相容剂的功效。
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝的制备方法，将纳米氮氧化钛陶瓷粉，山梨醇以及高纯大孔氧化铝通过湿法研磨的工艺制备。
一种用于胸外科的功能器具，将各种原料混合后注塑制备出所需的手上器具。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员，在不脱离本发明构思的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围内。

Claims (9)

1.一种用于胸外科的功能器具，其特征在于，其原料组成质量百分比为：
褐藻淀粉硫酸酯 1～5％
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝 1～5％
聚乳酸 余量
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝的原料为纳米氮氧化钛陶瓷粉，山梨醇以及高纯大孔氧化铝；
负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝的制备方法，将纳米氮氧化钛陶瓷粉，山梨醇以及高纯大孔氧化铝通过湿法研磨的工艺制备。
2.如权利要求1所述的一种用于胸外科的功能器具，其特征在于，褐藻淀粉硫酸酯在功能器具中的质量分数为2～4％。
3.如权利要求1所述的一种用于胸外科的功能器具，其特征在于，褐藻淀粉硫酸酯在功能器具中的质量分数为3％。
4.如权利要求1所述的一种用于胸外科的功能器具，其特征在于，负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝在功能器具中的质量分数为2～4％。
5.如权利要求1所述的一种用于胸外科的功能器具，其特征在于，负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝在功能器具中的质量分数为3％。
6.如权利要求1所述的一种用于胸外科的功能器具，其特征在于，纳米氮氧化钛陶瓷粉在负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝中的质量分数为20～30％。
7.如权利要求1所述的一种用于胸外科的功能器具，其特征在于，纳米氮氧化钛陶瓷粉在负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝中的质量分数为25％。
8.如权利要求1所述的一种用于胸外科的功能器具，其特征在于，山梨醇在负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝中的质量分数为1～3％。
9.如权利要求1所述的一种用于胸外科的功能器具，其特征在于，山梨醇在负载纳米氮氧化钛陶瓷粉的高纯大孔氧化铝中的质量分数为2％。
CN202110689469.0A 2021-06-17 2021-06-17 一种用于胸外科的功能器具 Active CN113425913B (zh)