CN113416351A - 一种用于管道补强修复的高强复合缠绕带生产配方 - Google Patents
一种用于管道补强修复的高强复合缠绕带生产配方 Download PDFInfo
- Publication number
- CN113416351A CN113416351A CN202110597567.1A CN202110597567A CN113416351A CN 113416351 A CN113416351 A CN 113416351A CN 202110597567 A CN202110597567 A CN 202110597567A CN 113416351 A CN113416351 A CN 113416351A
- Authority
- CN
- China
- Prior art keywords
- parts
- mixture
- production formula
- winding belt
- strength composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用于管道补强修复的高强复合缠绕带生产配方，包括以下重量份成分：基础载体：30～60份、金属混合物：12～24份、玻璃纤维混合物：24～48份、涂胶混合物：24～48份。通过添加金属混合物增加基础载体的强度，通过添加玻璃纤维混合物增加基础载体的耐磨性，然后通过涂胶混合物制作而成用于与管道进行连接的涂胶层，通过向涂胶层内添加纳米二氧化硅等材料，增加涂胶层的稳定性和粘度，保证本缠绕带在对管道完成修补后具有更高的稳定性。
Description
技术领域
本发明涉及管道修复技术领域，具体为一种用于管道补强修复的高强复合缠绕带生产配方。
背景技术
管道在使用的过程中，由于自身或外界的因素，会造成管道的侧壁发生渗漏或破损，为了不影响管道的使用，减少对管道的损害，需要对管道进行抢修，为了抢修的快速，需要使用到缠绕带对其管道的侧壁进行缠绕封闭，完成对管道的修补。但是，现有的缠绕带在使用的过程中强度较低，而且耐磨性较差，在修补完成后还容易受到外界的影响，从而造成再次渗漏或破损，从而导致影响管道的正常使用。为此，我们提出一种用于管道补强修复的高强复合缠绕带生产配方。
发明内容
本发明的目的在于提供一种用于管道补强修复的高强复合缠绕带生产配方，以解决上述背景技术中提出的问题。
一种用于管道补强修复的高强复合缠绕带生产配方，包括以下重量份成分：基础载体：30～60份、金属混合物：12～24份、玻璃纤维混合物：24～48份、涂胶混合物：24～48份。
优选的，包括以下重量份成分：基础载体：64份、金属混合物：16份、玻璃纤维混合物：32份、涂胶混合物：32份。
优选的，所述基础载体包括以下重量份成分：天然橡胶：20～30份、PU和EP聚合物：15～25份、分散剂：1～10份、偶联剂：1～3份、固化剂：2～10份、消泡剂：0.3～0.5份、蒸馏水:10～15份。
优选的，所述基础载体包括以下重量份成分：天然橡胶：25份、PU和EP聚合物：20份、分散剂：7份、偶联剂：2份、固化剂：4份、消泡剂：0.5份、蒸馏水:13份。
优选的，所述PU和EP聚合物中PU的含量为20%。
优选的，所述金属混合物包括：柔性石墨粉末和不锈钢金属粉末，所述柔性石墨粉末和不锈钢金属粉末按质量比例1：0.8进行混合。
优选的，所述玻璃纤维混合物包括：玻璃纤维和超高分子聚乙烯，所述玻璃纤维和超高分子聚乙烯按质量比例1：1进行混合。
优选的，所述涂胶混合物包括以下重量份成分：环氧树脂：20～30份、润湿剂：5～10份、纳米二氧化硅：2～4份、固化剂：5～10份、偶联剂：10～15份。
与现有技术相比，本发明的有益效果是：一种用于管道补强修复的高强复合缠绕带生产配方，通过设置基础载体形成制作缠绕带的主体，然后向基础载体内添加金属混合物和玻璃纤维混合物，通过添加金属混合物增加基础载体的强度，通过添加玻璃纤维混合物增加基础载体的耐磨性，然后通过涂胶混合物制作而成用于与管道进行连接的涂胶层，通过向涂胶层内添加纳米二氧化硅等材料，增加涂胶层的稳定性和粘度，保证本缠绕带在对管道完成修补后具有更高的稳定性。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明提供一种技术方案：一种用于管道补强修复的高强复合缠绕带生产配方，包括以下重量份成分：基础载体：30～60份、金属混合物：12～24份、玻璃纤维混合物：24～48份、涂胶混合物：24～48份，通过在基础载体内添加金属混合物和玻璃纤维混合物增强缠绕带在对管道补强修复后的强度和缠绕带的抗腐蚀性能，涂胶混合物形成涂胶层用于与管道的管壁进行粘接，其中各组分的重量占比最优如下：基础载体：64份、金属混合物：16份、玻璃纤维混合物：32份、涂胶混合物：32份。
基础载体包括以下重量份成分：天然橡胶：20～30份、PU和EP聚合物：15份～25份、分散剂：1～10份、偶联剂：1～3份、固化剂：2～10份、消泡剂：0.3～0.5份、蒸馏水:10～15份，基础载体为形成缠绕带的基体，其中各成分的最优重量份如下：基础载体包括以下重量份成分：天然橡胶：25份、PU和EP聚合物：20份、分散剂：7份、偶联剂：2份、固化剂：4份、消泡剂：0.5份、蒸馏水:13份，在基础载体内的偶联剂为A-151硅烷偶联剂，分散剂为OP-10乳化剂，固化剂为D-230固化剂，消泡剂为异辛醇，PU和EP聚合物中PU的含量为20%，当PU和EP聚合物中PU的含量为20%时，提高PU和EP聚合物的抗拉强度、断裂伸长率和冲击韧性。
金属混合物包括：柔性石墨粉末和不锈钢金属粉末，柔性石墨粉末和不锈钢金属粉末按质量比例1：0.8进行混合，通过添加金属混合物提高基础载体的耐温性和耐磨性，柔性石墨粉末采用天然石墨为原材料，经过插层、水洗、干燥、高温膨化等处理后得到一种疏松多孔的物质，具有较低的密度，并且具有较好的耐温性和耐腐蚀性。
玻璃纤维混合物包括：玻璃纤维和超高分子聚乙烯，玻璃纤维和超高分子聚乙烯按质量比例1：1进行混合，通过添加玻璃纤维和超高分子聚乙烯形成耐磨层位于基础载体的表面，增加缠绕带整体的耐磨性。
涂胶混合物包括以下重量份成分：环氧树脂：25份、润湿剂：7份、纳米二氧化硅：3份、固化剂：7份、偶联剂：12份，在涂胶混合物内的，在涂胶混合物内的润湿剂为十二烷基硫酸钠，固化剂为651固化剂，具有更好的粘接性、柔韧性和耐化学稳定性，偶联剂为有机硅烷，通过偶联剂提高环氧树脂的稳定性。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。
Claims (8)
1.一种用于管道补强修复的高强复合缠绕带生产配方，其特征在于，包括以下重量份成分：基础载体：30～60份、金属混合物：12～24份、玻璃纤维混合物：24～48份、涂胶混合物：24～48份。
2.根据权利要求1所述的一种用于管道补强修复的高强复合缠绕带生产配方，其特征在于：包括以下重量份成分：基础载体：64份、金属混合物：16份、玻璃纤维混合物：32份、涂胶混合物：32份。
3.根据权利要求1所述的一种用于管道补强修复的高强复合缠绕带生产配方，其特征在于：所述基础载体包括以下重量份成分：天然橡胶：20～30份、PU和EP聚合物：15～25份、分散剂：1～10份、偶联剂：1～3份、固化剂：2～10份、消泡剂：0.3～0.5份、蒸馏水:10～15份。
4.根据权利要求3所述的一种用于管道补强修复的高强复合缠绕带生产配方，其特征在于：所述基础载体包括以下重量份成分：天然橡胶：25份、PU和EP聚合物：20份、分散剂：7份、偶联剂：2份、固化剂：4份、消泡剂：0.5份、蒸馏水:13份。
5.根据权利要求4所述的一种用于管道补强修复的高强复合缠绕带生产配方的，其特征在于：所述PU和EP聚合物中PU的含量为20%。
6.根据权利要求1所述的一种用于管道补强修复的高强复合缠绕带生产配方的，其特征在于：所述金属混合物包括：柔性石墨粉末和不锈钢金属粉末，所述柔性石墨粉末和不锈钢金属粉末按质量比例1：0.8进行混合。
7.根据权利要求1所述的一种用于管道补强修复的高强复合缠绕带生产配方的，其特征在于：所述玻璃纤维混合物包括：玻璃纤维和超高分子聚乙烯，所述玻璃纤维和超高分子聚乙烯按质量比例1：1进行混合。
8.根据权利要求1所述的一种用于管道补强修复的高强复合缠绕带生产配方的，其特征在于：所述涂胶混合物包括以下重量份成分：环氧树脂：20～30份、润湿剂：5～10份、纳米二氧化硅：2～4份、固化剂：5～10份、偶联剂：10～15份。