CN113149563A - 硅基纳米墙体翻新防水材料 - Google Patents
硅基纳米墙体翻新防水材料 Download PDFInfo
- Publication number
- CN113149563A CN113149563A CN202110473769.5A CN202110473769A CN113149563A CN 113149563 A CN113149563 A CN 113149563A CN 202110473769 A CN202110473769 A CN 202110473769A CN 113149563 A CN113149563 A CN 113149563A
- Authority
- CN
- China
- Prior art keywords
- silicon
- based nano
- agent
- waterproof material
- waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于墙面翻新领域，具体涉及硅基纳米墙体翻新防水材料，本发明公开了硅基纳米墙体翻新防水材料。包括以下组分：基料、助留剂、阻燃剂、防水剂、流变改性剂、粘合剂、低级醇、偶联剂、除菌剂和水。本发明中基材吸附连接其他成分以形成一种多效硅基纳米墙体翻新防水材料，其中防水剂在墙漆的表面排列成规则的分子结构防水层，并与墙漆中的金属离子形成不溶性憎水盐填充在墙面的微小孔隙中；镁盐与金刚烷羧酸盐使得本发明形成良好的流动、流平性能；改性二氧化钛凝胶加强隔热效果的同时净化墙体界面以延长墙体寿命。
Description
技术领域
本发明属于墙面翻新领域，具体涉及硅基纳米墙体翻新防水材料。
背景技术
墙面涂料是指用于建筑墙面的装饰和保护，使建筑墙面美观整洁，同时也能够起到保护建筑墙面，延长其使用寿命的作用。长期使用后，墙面涂料的稳定性往往会变差，墙面开裂、起鼓、起皮并脱落都会严重影响墙面。于是，墙体在使用一段时间后，需要进行翻新。
早期的翻新漆含有大量的甲醛，污染环境，对人体健康造成危害，之后出现的改进翻新漆虽然甲醛含量低，但是漆膜偏薄、耐磨性较差，同时不容易挂壁、不容易晒干、防水性不好。
发明内容
本发明所要解决的技术问题是：一种多效硅基纳米墙体翻新防水材料。
为了解决上述第一个技术问题，本发明采用的技术方案为：包括以下组分：
基料、助留剂、阻燃剂、防水剂、流变改性剂、粘合剂、低级醇、偶联剂、除菌剂；
所述基料包括碳酸钙与煅烧高岭土，所述煅烧高岭土比表面积较大，可吸附连接其他成分，而煅烧高岭土与碳酸钙相互配合使用，使本申请在涂覆于墙体表面时，形成哑光效果；
所述防水剂包括三乙醇胺、脂肪酸与吐温-80，该防水剂能够在墙漆的表面排列成规则的分子结构防水层，并与墙漆中的金属离子形成不溶性憎水盐填充在墙面的微小孔隙中；
所述低级醇的碳原子数小于等于4。
进一步地，所述组分的重量份数为：
基料70～90
助留剂0.05～0.2
阻燃剂0.1～0.8
防水剂1～5
流变改性剂0.8～2.7
粘合剂0.3～2
低级醇12～18
偶联剂4～6
除菌剂4～13
水3～18。
进一步地，所述基料包括水泥、煤灰、粗沙、细沙。
进一步地，所述助留剂为聚二烯丙基二甲基氯化铵、聚乙烯亚胺、阳离子聚丙烯酰胺中的至少一种。
进一步地，所述阻燃剂为氢氧化镁，该阻燃剂具有分解产物无毒性、烟雾小等优点。
进一步地，所述碳酸钙与煅烧高岭土的质量比为(3～7)：(6～15)。
进一步地，所述流变改性剂为镁盐与金刚烷羧酸盐的混合改性剂，其具有优异的耐碱性、耐玷污性、抗腐蚀性和耐擦洗性，有助于墙漆形成良好的流动、流平性能，提高本申请的提刷性能并使其具有较好的遮盖效果。
进一步地，所述镁盐与金刚烷羧酸盐的质量比为(1～10)：(2～15)。
进一步地，所述粘合剂为羟丙基甲基纤维素醚、羟乙基纤维素醚和甲基纤维素醚中的至少一种。
进一步地，所述低级醇为异丙醇、甲醇或乙醇中的至少一种。
进一步地，所述偶联剂为有机羧酸偶联剂、多异氰酸酯偶联剂、钛酸酯偶联剂、有机硅偶联剂中的一种。
进一步地，所述除菌剂为改性二氧化钛凝胶，优选地，所述改性二氧化钛凝胶为二氧化钛/二氧化硅气凝胶。其受到光照后能够生成杀菌粒子，这些杀菌粒子长时间对污渍、细菌和霉菌进行高效地分解和清洁，以达到净化空气、消除有害微生物和延长墙体寿命的功效。此外，纳米气凝胶的隔热性能确保本发明涂层具有隔热效果。
本发明的有益效果在于：本发明中基材吸附连接其他成分以形成一种多效硅基纳米墙体翻新防水材料，其中所述防水剂在墙漆的表面排列成规则的分子结构防水层，并与墙漆中的金属离子形成不溶性憎水盐填充在墙面的微小孔隙中；镁盐与金刚烷羧酸盐等流变改性剂使得本发明形成良好的流动、流平性能；改性二氧化钛凝胶等除菌剂能够实现加强隔热效果的同时净化墙体界面以延长墙体寿命。
具体实施方式
为详细说明本发明的技术内容、所实现目的及效果，以下结合实施方式予以说明。
实施例1
硅基纳米墙体翻新防水材料，其组分如表1：
表1
| 序号 | 组分 | 含量 |
| 1 | 基料 | 70g |
| 2 | 助留剂 | 0.1g |
| 3 | 阻燃剂 | 0.8 |
| 4 | 防水剂 | 4 |
| 5 | 流变改性剂 | 0.8 |
| 6 | 粘合剂 | 0.3 |
| 7 | 低级醇 | 12 |
| 8 | 偶联剂 | 6 |
| 9 | 除菌剂 | 10 |
| 10 | 水 | 10 |
所述基料为16g的42.5R水泥、7g煤灰、15g粒径为0.7mm的粗沙、10g粒径为0.125mm的细沙、2g碳酸钙与20g煅烧高岭土。
所述助留剂为0.1g聚二烯丙基二甲基氯化铵。
所述阻燃剂为0.8g氢氧化镁。
所述防水剂为1.2g三乙醇胺、1.4g脂肪酸与1.4g吐温-80。
所述流变改性剂为0.4g镁盐与0.4g金刚烷羧酸盐。
所述粘合剂为0.1g羟丙基甲基纤维素醚和0.2g甲基纤维素醚。
所述低级醇为2g异丙醇、10g乙醇。
所述偶联剂为3g乙酸、2g多亚甲基多苯基多异氰酸酯和1g甲基苯基硅树脂。
实施例2
硅基纳米墙体翻新防水材料，其组分如表2：
表2
| 序号 | 组分 | 含量 |
| 1 | 基料 | 70g |
| 2 | 助留剂 | 0.05g |
| 3 | 阻燃剂 | 0.1 |
| 4 | 防水剂 | 1 |
| 5 | 流变改性剂 | 0.8 |
| 6 | 粘合剂 | 0.3 |
| 7 | 低级醇 | 12 |
| 8 | 偶联剂 | 4 |
| 9 | 除菌剂 | 4 |
| 10 | 水 | 10 |
所述基料为16g的42.5R水泥、7g煤灰、15g粒径为0.7mm的粗沙、10g粒径为0.125mm的细沙、2g碳酸钙与20g煅烧高岭土。
所述助留剂为0.05g聚二烯丙基二甲基氯化铵。
所述阻燃剂为0.1g氢氧化镁。
所述防水剂为0.2g三乙醇胺、0.4g脂肪酸与0.4g吐温-80。
所述流变改性剂为0.4g镁盐与0.4g金刚烷羧酸盐。
所述粘合剂为0.1g羟丙基甲基纤维素醚和0.2g甲基纤维素醚。
所述低级醇为2g异丙醇、10g乙醇。
所述偶联剂为2g乙酸、1g多亚甲基多苯基多异氰酸酯和1g甲基苯基硅树脂。
实施例3
硅基纳米墙体翻新防水材料，其组分如表3：
表3
| 序号 | 组分 | 含量 |
| 1 | 基料 | 70g |
| 2 | 助留剂 | 0.15g |
| 3 | 阻燃剂 | 0.5 |
| 4 | 防水剂 | 3 |
| 5 | 流变改性剂 | 2 |
| 6 | 粘合剂 | 0.3 |
| 7 | 低级醇 | 12 |
| 8 | 偶联剂 | 5 |
| 9 | 除菌剂 | 8 |
| 10 | 水 | 10 |
所述基料为16g的42.5R水泥、7g煤灰、15g粒径为0.7mm的粗沙、10g粒径为0.125mm的细沙、2g碳酸钙与20g煅烧高岭土。
所述助留剂为0.15g聚二烯丙基二甲基氯化铵。
所述阻燃剂为0.5g氢氧化镁。
所述防水剂为0.2g三乙醇胺、0.4g脂肪酸与1.4g吐温-80。
所述流变改性剂为1g镁盐与1g金刚烷羧酸盐。
所述粘合剂为0.1g羟丙基甲基纤维素醚和0.2g甲基纤维素醚。
所述低级醇为2g异丙醇、10g乙醇。
所述偶联剂为3g乙酸、1g多亚甲基多苯基多异氰酸酯和1g甲基苯基硅树脂。
实施例4
硅基纳米墙体翻新防水材料，其组分如表4：
表4
| 序号 | 组分 | 含量 |
| 1 | 基料 | 70g |
| 2 | 助留剂 | 0.2g |
| 3 | 阻燃剂 | 0.7 |
| 4 | 防水剂 | 2 |
| 5 | 流变改性剂 | 2 |
| 6 | 粘合剂 | 0.3 |
| 7 | 低级醇 | 12 |
| 8 | 偶联剂 | 5 |
| 9 | 除菌剂 | 9 |
| 10 | 水 | 10 |
所述基料为16g的42.5R水泥、7g煤灰、15g粒径为0.7mm的粗沙、10g粒径为0.125mm的细沙、2g碳酸钙与20g煅烧高岭土。
所述助留剂为0.2g聚二烯丙基二甲基氯化铵。
所述阻燃剂为0.7g氢氧化镁。
所述防水剂为0.7g三乙醇胺、0.9g脂肪酸与1.4g吐温-80。
所述流变改性剂为1g镁盐与1g金刚烷羧酸盐。
所述粘合剂为0.1g羟丙基甲基纤维素醚和0.2g甲基纤维素醚。
所述低级醇为2g异丙醇、10g乙醇。
所述偶联剂为3g乙酸、1g多亚甲基多苯基多异氰酸酯和1g甲基苯基硅树脂。
对比例1
根据硅基纳米墙体翻新防水材料的组分配方，不加入防水剂，其余组分含量同实施例1。
对比例2
根据硅基纳米墙体翻新防水材料的组分配方，不加入流变改性剂，其余组分含量同实施例1。
对比例3
根据硅基纳米墙体翻新防水材料的组分配方，不加入除菌剂，其余组分含量同实施例1。
对比例4
一种墙漆配方,按质量份数取以下组分:35份纯丙烯酸酯乳液、3份聚丙烯酸铵分散剂、20份钛白粉、15份电气石、3份甘油、1份除泡剂、20份水、3份聚丙烯酸增稠剂。
对比例5
一种外墙漆,按重量份数包括如下组分:聚丙烯纤维素1份、硫酸钡100份、高岭土30份、疏水剂40份、金红石钛白粉50份、乙二醇8份、防腐剂0.5份、防霉剂2.8份、纯丙烯酸乳液250份、水性丙烯酸乳液20份、增稠剂2份、去离子水200份。
为了进一步证实本发明所采用的特定组分的效果，将实施例1-4以及对比例1-5制备得的材料分别进行测试：
在需要翻新的旧墙面上拆下多份1m*1m*0.5m，铲去表面旧墙漆，然后分别刷上上述材料,静放7天,然后放入烘箱内50℃烘2h,取出后放置3小时,再放置于室内空间中,该室内空间根据实验需要模拟外部环境,按相关标准进行测试，结果见表5：
表5
从表得，本发明各项指标都达标，本发明具有良好的防水性、耐碱性、贮藏稳定性、抗菌性、耐擦洗性，而且粘结强度高，表干速度快，不易产生空鼓。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等同变换，或直接或间接运用在相关的技术领域，均同理包括在本发明的专利保护范围内。
Claims (10)
1.硅基纳米墙体翻新防水材料，其特征在于：包括以下组分：
基料、助留剂、阻燃剂、防水剂、流变改性剂、粘合剂、低级醇、偶联剂、除菌剂；
所述基料包括碳酸钙与煅烧高岭土；
所述防水剂包括三乙醇胺、脂肪酸与吐温-80；
所述低级醇的碳原子数小于等于4。
2.根据权利要求1所述的硅基纳米墙体翻新防水材料，其特征在于：所述组分的重量份数为：
基料70～90
助留剂0.05～0.2
阻燃剂0.1～0.8
防水剂1～5
流变改性剂0.8～2.7
粘合剂0.3～2
低级醇12～18
偶联剂4～6
除菌剂4～13。
3.根据权利要求1所述的硅基纳米墙体翻新防水材料，其特征在于：
所述基料包括水泥、煤灰、粗沙、细沙。
4.根据权利要求1所述的硅基纳米墙体翻新防水材料，其特征在于：
所述助留剂为聚二烯丙基二甲基氯化铵、聚乙烯亚胺、阳离子聚丙烯酰胺中的至少一种。
5.根据权利要求1所述的硅基纳米墙体翻新防水材料，其特征在于：
所述碳酸钙与煅烧高岭土的质量比为(3～7)：(6～15)。
6.根据权利要求1所述的硅基纳米墙体翻新防水材料，其特征在于：
所述流变改性剂为镁盐与金刚烷羧酸盐的混合改性剂。
7.根据权利要求6所述的硅基纳米墙体翻新防水材料，其特征在于：
所述镁盐与金刚烷羧酸盐的质量比为(1～10)：(2～15)。
8.根据权利要求1所述的硅基纳米墙体翻新防水材料，其特征在于：
所述粘合剂为羟丙基甲基纤维素醚、羟乙基纤维素醚和甲基纤维素醚中的至少一种。
9.根据权利要求1所述的硅基纳米墙体翻新防水材料，其特征在于：
所述偶联剂为有机羧酸偶联剂、多异氰酸酯偶联剂、钛酸酯偶联剂、有机硅偶联剂中的至少一种。
10.根据权利要求1所述的硅基纳米墙体翻新防水材料，其特征在于：
所述除菌剂为改性二氧化钛凝胶。