CN1130663A - 一种云彩涂料及其制备工艺 - Google Patents
一种云彩涂料及其制备工艺 Download PDFInfo
- Publication number
- CN1130663A CN1130663A CN 95118812 CN95118812A CN1130663A CN 1130663 A CN1130663 A CN 1130663A CN 95118812 CN95118812 CN 95118812 CN 95118812 A CN95118812 A CN 95118812A CN 1130663 A CN1130663 A CN 1130663A
- Authority
- CN
- China
- Prior art keywords
- emulsion
- paint
- water
- cloud
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种云彩涂料由合成乳液、颜料填料、助剂及水等组成，它由底、中、面三层涂层复合组成。其制备工艺是将颜料填料、水、助剂按配比投入搅拌缸内搅拌均匀，再送入胶体磨或砂磨机分散研磨，之后倒入合成乳液及助剂搅拌均匀，加入剩余助剂、水性色浆及香料进行搅拌，并调节pH值至7.0-8.5，然后进行过滤，最后经计量装入包装桶内。本发明的云彩涂料装饰效果豪华典雅、富丽堂皇，具有无毒、不燃、不污染环境的优点，其耐候性、耐水性、耐碱性、耐擦洗性好、耐沾污性强，适用于建筑物室内外各种基面的装饰，是一种健康安全型“绿色”涂料。
Description
本发明涉及涂料，尤其是一种云彩涂料及其制备工艺。
近年来，继多彩花纹涂料之后，出现了一种新颖的建筑装饰涂料——云彩涂料。最初云彩涂料是从意大利进口及引进意大利设备和技术生产的，它们的装饰效果豪华典雅、富丽堂皇、如梦如幻，倍受人们的青睐，又被称作梦幻涂料或幻彩涂料，但是因进口或引进产品价格昂贵(进口产品200元/公斤、引进产品80—100元/公斤，施工造价达50—100元/m2)，要大面积推广使用，消费者难以承受。国内也纷纷开发这种涂料，但装饰效果与引进产品相比，还略差一筹。
本发明的目的就是提供一种成本低、装饰效果好、性能稳定的云彩涂料。
本发明目的由以下技术方案来实现：
本发明的云彩涂料由底、中、面三层涂料组成，各层的配方如下(按重量百分比计)：
1.云彩涂料底涂层配方：
合成乳液 25—50 助剂 0—5
水 45—70
底涂层是保证云彩涂料饰面质量的十分重要的涂层，它耐水性、耐碱性、防霉性能优良，能渗透入墙面，增强墙面基层的坚实程度，减少墙面对中面层涂料的吸收，增强附着力。合成乳液可以选用氯偏乳液、醋丙乳液、苯丙乳液、纯丙乳液。助剂可以用消泡剂、成膜助剂、抗冻剂、防霉杀菌剂。
2.云彩涂料中涂层配方：
合成乳液 25—45 颜料填料 10—40
助剂 4—10 水 25—40
水性色浆 1—3
中涂层是使整个装饰面有一个色泽均匀的基面，中涂层色彩的变化可以衬托面涂层，形成色彩交相辉映的光学效果。合成乳液选用醋丙乳液、苯丙乳液和纯丙乳液。中涂层一般以白色和浅色为主，颜料以钛白粉为主，并辅以一定的填料，如轻质碳酸钙、硅灰石粉、滑石粉、瓷土、白炭黑，膨润土、云母粉，超细硅酸铝等。助剂可以选用分散剂、消泡剂、增稠剂、成膜助剂、防冻剂、中和剂、防霉杀菌剂等。中涂层具有优良的耐水性、耐碱性和耐擦洗性，遮盖力很强。
3.云彩涂料的面涂层配方：
合成乳液35—60 颜料填料 3—18
助剂 4—16 香料 0—2
水 25—40 水性色浆 0.2—2
所述的合成乳液选用纯丙乳液、苯丙乳液、醋丙乳液、苯乙烯-丙烯腈-丙烯酸酯共聚乳液(AAS乳液)。所述的颜料填料选用钛白粉、立德粉、云母钛珠光粉、滑石粉、云母粉、瓷土、膨润土、轻质碳酸钙、白炭黑、超细硅酸铝，硅灰石粉等中的一种或多种混合。所述的助剂选用分散剂、清泡剂、流平剂、保湿剂、增稠剂、防冻剂，成膜助剂、防霉杀菌剂、中和剂。所述的香料是食用香精或日化香精或微胶囊缓释香料。香型可以根据人们喜爱选择，也可不加。所述的水可以是蒸馏水或去离子水，也可使用清洁的城市自来水。
本发明的云彩涂料制备工艺是：将水，颜料填料、部分助剂按配比投入搅抖缸内搅拌均匀，再送入胶体磨或砂磨机分散研磨，之后倒入合成乳液及助剂搅拌均匀，加入剩余助剂.水性色浆及香料进行搅拌，并调节PH值至7.0—8.5，然后进行过滤，最后经计量装入包装桶内。
本发明的云彩涂料是一种水性涂料，装饰效果豪华典雅、富丽堂皇，具有无毒、不燃、不污染环境的优点，其耐候性、耐水性、耐碱性、耐擦洗性好，回粘性小，耐玷污性强，适用于建筑物室内外各种基面的装饰。该涂料还具有制造工艺简单，设备投资小的优点，是一种健康安全型“绿色”涂料。
下面结合实施例对本发明作详细说明。
实施例1：(珠光幻彩型)
底涂层配方：氯偏乳液45千克、助剂3千克、水52千克。
中涂层配方：醋丙乳液30千克、钛白粉16千克、云母粉14千克、助剂5千克、水34千克、水性色浆1千克。
面涂层配方：
纯丙乳液 53千克 珠光粉 4千克
分散剂 0.3千克 消泡剂 0.1千克
流平剂 0.6千克 保湿剂 3千克
成膜助剂 2千克 增稠剂 2千克
防霉杀菌剂 0.6千克 中和剂 0.3千克
水性色浆 0.3千克 香料 1千克
防冻剂 0.8千克 水 32千克
面涂层涂料的制备工艺是：将水、分散剂、消泡剂投入搅拌缸内搅匀，投入珠光粉、流平剂、保湿剂、增稠剂、成膜助剂、防霉杀菌剂、防冻剂，边搅边加，然后加入纯丙乳液继续搅拌均匀，再加入水性色浆进行配色，并调节PH值至2.0，之后加入香料搅匀，再过滤最后计量包装。因珠光粉不宜进胶体磨或砂磨机分散研磨，可省去此工序。
实施例2：(悦光彩色型)
底涂层配方：纯丙乳液35千克、助剂5千克、水60千克。
中涂层配方：苯丙乳液25千克、钛白粉25千克、硅灰石粉10千克、助剂9千克、水30千克、水性色浆1千克。
面涂层配方：
苯丙乳液 45千克 钛白粉 5千克
滑石粉 2千克 瓷土 1.5千克
云母粉 1.5千克 膨润土 2千克
分散剂 0.4千克 消泡剂 0.1千克
流平剂 0.6千克 保湿剂 5千克
增稠剂 4千克 防霉杀菌剂 0.6千克
水性色浆 1千克 中和剂 0.3千克
香料 1千克 水 30千克
面涂层涂料的制备工艺：将水、分散剂、消泡剂、增稠剂、防霉杀菌剂先投入搅拌缸内搅匀，再将钛白粉、滑石粉、瓷土、云母粉、膨润土投入搅拌缸内搅拌混合均匀后，送入胶体磨进行分散研磨5遍，再送回搅拌缸内，加入流平剂，保湿剂，成膜助剂搅拌，搅拌均匀后，加入苯丙乳液搅匀后进行配色，并调节PH值至8.0，最后加入香料，过滤后计量包装入桶。
Claims (6)
1、一种云彩涂料由合成乳液、颜料、填料、助剂、水等组成，它是由底、中、面三层涂层复合组成，其特征在于：
(1)云彩涂料底涂层配方：(按重量百分比计)
合成乳液 25—50 助剂 0—5
水 45—70
(2)云彩涂料中涂层配方：(按重量百分比计)
合成乳液 25—45 颜料填料 10—40
助剂 4—10 水 25—40
水性色浆 1—3
(3)云彩涂料面涂层配方：(按重量百分比计)
合成乳液35—60 颜料填料 3—18
助剂 4—16 香料 0—2
水 25—40 水性色浆 0.2—2
2.根据权利要求1所述的云彩涂料，其特征在于：所述的合成乳液是纯丙乳液、苯丙乳液、醋丙乳液、苯乙烯-丙烯腈-丙烯酸酯共聚乳液(AAS乳液)的一种或多种混合，底涂层还可以选用氯偏乳液。
3、根据权利要求1所述的云彩涂料，其特征在于：所述的颜料填料选用钛白粉、立德粉、云母钛珠光粉、滑石粉、云母粉、瓷土、膨润土、轻质碳酸钙、白炭黑、超细硅酸、铝硅灰石粉的一种或多种混合。
4、根据权利要求1所述的云彩涂料，其特征在于：所述的助剂选用分散剂、消泡剂、流平剂、保温剂、增稠剂、防冻剂、成膜助剂、防霉杀菌剂、中和剂的一种或多种。
5、根据权利要求1所述的云彩涂料，其特征在于：所述的香料是食用香精或日化香精或微胶囊缓释香料。
6.根据权利要求1所述的云彩涂料，其制备工艺是：将水、颜料填料、部分助剂按配比投入搅抖缸内搅拌均匀，再送入胶体磨或砂磨机分散研磨，之后倒入合成乳液及助剂搅拌均匀，加入剩余助剂、水性色浆及香料进行搅拌，并调节PH值至7.0—8.5，然后进行过滤，最后经计量装入包装桶内。