CN1130412C - 聚合物泡沫体中层离颗粒的分散 - Google Patents

聚合物泡沫体中层离颗粒的分散 Download PDF

Info

Publication number
CN1130412C
CN1130412C CN97192487A CN97192487A CN1130412C CN 1130412 C CN1130412 C CN 1130412C CN 97192487 A CN97192487 A CN 97192487A CN 97192487 A CN97192487 A CN 97192487A CN 1130412 C CN1130412 C CN 1130412C
Authority
CN
China
Prior art keywords
polymer
polymer foam
melt
polymkeric substance
ethylene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN97192487A
Other languages
English (en)
Other versions
CN1212001A (zh
Inventor
S·V·卡兰德
C－J·仇
J·H·索尔科
K·W·苏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dow Global Technologies LLC
Original Assignee
Dow Global Technologies LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dow Global Technologies LLC filed Critical Dow Global Technologies LLC
Publication of CN1212001A publication Critical patent/CN1212001A/zh
Application granted granted Critical
Publication of CN1130412C publication Critical patent/CN1130412C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及一种按如下方法制备的聚合物泡沫体：将亲有机的多层化材料分散到含具有极性官能度的链烯或苯乙烯类聚合物的熔体中以便至少一产分聚合物插到各层颗粒之间；在该条件下用发泡剂将聚合物膨胀形成聚合物泡沫。亲有机的多层化材料也可分散到链烯或苯乙烯类单体中，该单体然后可在发泡步骤前或与之同时聚合形成聚合物熔体。

Description

聚合物泡沫体中层离颗粒的分散
本发明涉及由其中已分散有层离或分层的亲有机多层化颗粒的树脂制备的聚合物泡沫体。
毫微复合材料，为含有分散于连续的聚合物基质中的单个层如硅酸盐层(1-100nm厚)的组合物，使得聚合物物理性能的增强比常规加工的玻璃或矿物增强的聚合物中陶瓷含量要低得多。这些毫微复合材料可用两步法合成，第一步是多层颗粒的改性，通常是通过钠或钾离子(以天然的云母型硅酸盐形式存在)与有机阳离子(例如：硅酸烷基铵或适当地官能化的有机硅烷)进行离子交换。此改性步骤通常使得亲水性云母型硅酸盐变为亲有机性。在第二步中，使可熔融加工的聚合物(或就地聚合的单体)和夹带的颗粒相容形成物理性能增强的聚合物。
毫微复合材料记载于U.S.专利4,739,007、4,618,528、4,528,235、4,874,728、4,889,885、4,810,734和5,385,776及WO/93/11190中。
本发明论述了需要通过提供一种由如下方法制备的聚合物泡沫来提高聚合物泡沫体的物理性能，该方法包括如下步骤：a)将亲有机的多层化颗粒分散到含有具有极性官能度的链烯或苯乙烯类聚合物的熔体中以便至少一部分聚合物插在各层颗粒之间；b)在该条件下将聚合物用发泡剂膨胀形成聚合物泡沫体。
另一方面，本发明为由如下方法制备的聚合物泡沫体，该方法包括如下步骤：a)将亲有机的多层化颗粒分散于具有极性官能度的可聚合链烯或苯乙烯类单体中以便至少一部分单体插到各层颗粒之间；b)由单体形成聚合物熔体；c)在该条件下用发泡剂将聚合物熔体膨胀形成聚合物泡沫体。
本发明的聚合物泡沫体显示出改善了的缓冲性能和增强了弹性回复性能。另外，与不是由插在亲有机多层化材料层之间的适当官能化的聚合物膨胀制备的泡沫体相比，可以得到提高了的绝缘性和耐火性、优良的抗液体和气体扩散性和提高了的冲击强度。
本发明的聚合物泡沫体可由以下步骤制备：
将亲有机的多层化颗粒分散到含有具有极性官能度的链烯或苯乙烯类聚合物的熔体中以便至少一部分聚合物插到各层颗粒之间；在该条件下用发泡剂将聚合物膨胀形成聚合物泡沫体。另外，亲有机的多层化颗粒可被分散到链烯或苯乙烯类单体或预聚体或其混合物中，然后单体或预聚体可在起泡步骤之前或与其同时就地聚合形成聚合物泡沫体。
适合制备聚合物泡沫体的亲有机多层化颗粒可以通过本领域已知的方法由亲水性页硅酸盐进行制备。该类材料的例子是近晶状粘土矿物质如：蒙脱石、囊脱石、贝得石、铬岭石、水辉石、滑石粉、硅铝锌铅石、magadiite、kenyaite和蛭石。其它有用的多层化颗粒包括伊利石矿物质如ledikite和伊利石与上述粘土矿物质的混合物。其它有用的多层化颗粒，特别是用于阴离子聚合物，为分层的双氢氧化物诸如Mg6Al3.4(OH)18.8(CO3)1.7H2O(见W.T.Reichle.J.Catal〔催化剂杂志〕，94卷第547页(1985))，它具有带正电的层和在层间空隙有可交换的阴离子。层上几乎没有或没有电荷的其它多层化颗粒也可用于本发明，条件是它们可以借助使其层间空隙膨胀的溶胀剂而被插入。该类材料包括氯化物例如ReCl3和FeOCl；硫属化物例如TiS2、MoS2和MoS3；氰化物例如Ni(CN)2和氧化物如H2Si2O5、V5O13、HTiNbO5、Cr0.5V0.5S2、W0.2V2.8O7、Cr3O8、MoO3(OH)2、VOPO4-2H2O、CaPO44CH3-H2O、MnHAsO4-H2O和Ag6Mo10O33。
亲水性多层化颗粒通过钠、钾或钙阳离子与适当的材料例如水溶性聚合物、季铵盐、两性的表面活性剂和胆碱化合物或类似物进行交换可变为亲有机性的。可交换的水溶性聚合物的参考例子包括水溶性的乙烯醇聚合物(如聚乙烯醇)、聚亚烷基二醇例如聚乙二醇、水溶性纤维素聚合物例如甲基纤维素和羧甲基纤维素、烯属不饱和羧酸聚合物例如聚丙烯酸及其盐和聚乙烯基吡咯烷酮。
可用于本发明的季铵盐(阳离子表面活性剂)的参考例子包括具有十八烷基、十六烷基、十四烷基或十二烷基的季铵盐，优选的季铵盐包括二甲基二氢化牛脂铵盐、十八烷基三甲基铵盐、双十八烷基二甲基铵盐、十六烷基三甲基铵盐、双十六烷基二甲基铵盐、十四烷基三甲基铵盐和双十四基二甲基铵盐。
优选那些通过季铵阳离子进行离子交换制备的亲有机性多层化颗粒。更优选的亲有机性多层化物质是用季铵盐处理过的蒙脱石粘土、最优选二甲基二氢化牛脂铵盐，商业上有售，称作CLAYTONETMHY(南部粘土产品公司的商标)。
也可以通过钠、钾或钙阳离子与无机材料、由水解可聚合的金属醇盐如Si(OR)4、Al(OR)3、Ge(OR)4、Si(OC2H5)4、Si(OCH3)4、Ge(OC3H7)或者Ge(OC2H5)4单独或任意混合而得到的聚合物质进行交换制备亲有机性多层化颗粒。另外，无机材料可以是胶态的无机化合物。可以使用的参考性胶态无机化合物包括SiO2、Sb2O3、Fe2O3、Al2O3、TiO2、ZrO2和SnO2，单独或任意混合。
如WO 93/11190.PP.9-21所公开，亲有机性的多层化材料也可通过官能化的有机硅烷化合物交换来制备。
聚合物中所夹带的多层化颗粒浓度取决于其应用，但优选不小于0.1％重量，更优选不小于0.5％重量，最优选不小于1％重量，以聚合物总重为基准；优选不大于40％重量，更优选不大于20％重量，最优选不大于10％重量，以聚合物总重为基准。
至少部分聚合物泡沫体由具有极性官能度的链烯或苯乙烯类聚合物制备。如在此所用，术语“极性官能度”指的是含具有偶极矩的一个基团或多个基团例如酐、羧酸、羟基、硅烷、氯、溴或酯官能度或其混合物的聚合物。例如含有极性官能度的聚合物可以通过以下方法制备：通过聚合含有极性官能度的可聚合单体、将含有极性官能度的可聚合单体与另一种可聚合单体共聚、或者将极性官能度接枝到聚合物主链上。也可以由具有极性官能度的聚合物与不合极性官能度的聚合物共混来制备发泡分散体，即熔体中还可以包括不含极性官能度的链烯或苯乙烯基化合物的聚合物。
用马来酐或乙烯基硅烷接枝的苯乙烯或链烯聚合物、或与马来酐或乙烯基硅烷共聚的苯乙烯或链烯单体特别适合；因为马来酐基团或甲硅烷基团还可用来防止片状颗粒重新凝聚。优选的乙烯基硅烷包括乙烯基Si(OR)3，其中每个R独立为甲基、乙基或丙基，更优选甲基或乙基，最优选甲基。
那些衍生自苯乙烯、α-甲基苯乙烯、乙基苯乙烯、乙烯基甲苯、氯苯乙烯和溴苯乙烯及其混合物的苯乙烯类聚合物也是适合的。这些苯乙烯单体可与其它烯属不饱和化合物例如：丙烯酸、甲基丙烯酸、乙基丙烯酸、马来酐、马来酸、衣康酸、丙烯酸甲酯、甲基丙烯酸甲酯、丙烯酸丁酯、甲基丙烯酸丁酯、丙烯腈、乙烯醇、酰胺和丁二烯共聚。
链烯聚合物包括聚丙烯、聚乙烯及其共聚物和共混物，以及乙烯-丙烯-二烯三元共聚物。产生泡沫结构优选的链烯聚合物包括聚丙烯、线性高密度聚乙烯(HDPE)、不均匀支化的线性低密度聚乙烯(LLDPE)如DOWLEXTM聚乙烯树脂(DOW化学公司的一个商标)、不均匀支化的线性超低密度聚乙烯(ULDPE)如ATTANETMULDPE(DOW化学公司的一个商标)、均匀支化的线性乙烯/α-烯烃共聚物如TAFMERTM(Mitsui石油化学有限公司的一个商标)和EXACTM(Exxon化学公司的一个商标)，可用如US专利3,645,922中所述进行制备；均匀支化的大体上线性的乙烯/α-烯烃聚合物如AFFINITYTM聚烯烃塑性体(DOW化学公司的一个商标)和ENGAGETM聚烯烃弹性体(DuPont DOW弹性体有限公司的一个商标)，可用如US专利5,272,236和5,278,272中所公开的方法制备，和高压、自由基聚合的乙烯聚合物和共聚物如低密度聚乙烯(LDPE)。更优选的链烯聚合物为均匀支化的线性和大体线性的乙烯共聚物，其密度(根据ASTM D-792测定)为0.85g/cm3-0.965g/cm3，优选0.86g/cm3-0.92g/cm3，更优选0.86g/cm3-0.90g/cm3，最优选0.86g/cm3-0.88g/cm3，重均分子量与数均分子量的比率(Mw/Mn)为1.5-3.0，测得的熔体指数(根据ASTM D-1238(190/2.16)测定)为0.1g/10分-100g/10分，熔体流率(I10/I2)为6-20(根据ASTM D-1238(190/10)测定)。
优选的用极性基团官能化的链烯聚合物包括均匀支化的线性和大体线性的用极性官能度接枝的乙烯共聚物、乙烯-丙烯酸(EAA)共聚物例如PRIMACORTM(DOW化学公司的一个商标)、乙烯-甲基丙烯酸(EMAA)共聚物、和乙烯-乙酸乙烯酯(EVA)共聚物如ESCORENETM聚合物(Exxon化学公司的一个商标)和ELVAXTM(E.I.杜邦de Nemours & Co.的一个商标)。更优选用极性基团官能化的链烯聚合物包括大体线性的用马来酐或乙烯基三甲氧基硅烷接枝的乙烯-1-C4-C8链烯烃共聚物(其制备公开于U.S专利5,346,963中)。最优选用马来酐或乙烯基三甲氧基硅烷接枝的乙烯-1-辛烯共聚物，密度为0.86g/cm3-0.88g/cm3。
优选由含极性官能度的链烯聚合物和未官能化的链烯聚合物的混合物制备泡沫。非常优选不均匀支化的大体线性的未用极性基团官能化的乙烯-1-辛烯共聚物和不均匀支化的大体线性的用马来酐或乙烯基三甲氧基硅烷接枝的乙烯-1-辛烯共聚物的混合物。更优选非官能化链烯聚合物与含极性官能度的链烯聚合物的重量比不大于10∶1，最优选不大于5∶1，更优选不小于1∶1，最优选不小于3∶1。
优选聚合物上极性官能团的浓度不小于0.1％重量，更优选不小于0.5％重量，最优选不小于1％重量，以苯乙烯或链烯单体和极性官能团的总重量为基准。优选极性官能团的浓度不大于20％重量，更优选不大于15％重量，更优选不大于10％重量，最优选不大于5％重量，以聚合物和极性官能团的总重为基准。
本发明实践中所用的可硫化热塑性橡胶的变化很广泛。该类橡胶的例子有溴化丁基橡胶、氯化聚烯烃如氯化聚乙烯和氯化丁基橡胶、含氟弹性体、丁二烯/丙烯腈弹性体、硅氧烷弹性体、聚丁二烯、聚异丁烯、磺化乙烯-丙烯-二烯三元共聚物、聚氯丁二烯、聚(2，3-二甲基丁二烯)、聚(丁二烯-戊二烯)、氯磺化聚烯烃例如氯磺化聚乙烯和多硫化物弹性体。
亲有机的多层化颗粒可用本领域已知方法如WO 93/11190.PP26-28所公开的方法分散到就地聚合的单体或预聚体中。
混合物可包括各种任选的组分，是通常与聚合物一起使用的添加剂。该任选组分包括成核剂、填料、增塑剂、冲击改性剂、链增长剂、着色剂、脱模润滑剂、抗静电剂、染料和阻燃剂。这些任选组分及适当的用量对本领域普通技术人员来说是熟知的。
分散的预形成的聚合物熔体或就地制备的聚合物可通过适当的途径，如本领域所知的那些方法制成泡沫体。化学发泡剂如偶氮二酰胺、4、4′-氧基双(苯磺酰肼)，或二亚硝基戊四胺，或者物理发泡剂如二氧化碳、CFC和轻质烃可与聚合物熔体或含有夹带的多层化颗粒的反应中间体相接触形成能发泡的凝胶，该凝胶接着可通过模口挤出形成泡沫产品。发泡剂可通过任何适当的方式如挤出、混合或共混加入到聚合物熔体或反应中间体中。优选将发泡剂在足够将其基本均匀分散于其中的高压下与熔融的聚合物或反应中间体混合。已令人惊奇地发现分散的颗粒的存在可以减慢泡沫体中加入的气体损失的速度，从而提供了保持泡沫体完整性的途径。
其它形成泡沫体的方法记载于U.S专利5,340,840，从第13栏49行至第14栏1-35行，以及U.S.专利4,323,528、4,379,859和4,464,484中的相关论述。另外参见K.W.Suh和D.D.Webb在“多孔材料”(CellularMaterials”)所述，摘自“聚合物科学与工程百科全书”第3卷，第2版1-59页(1985)(Encyclopedia of polymer Science and Engineering，Vol.3.Second Edition，pp 1-59(1985))和C.P.Park在“聚烯烃泡沫”(“polyolefin Foams”)中所述，摘自”聚合物泡沫体及发泡技术手册，Hanser出版社，纽约，第187-242页，(1991)”(Handbook of PolymericFoams and Foam Technology，Hanser Publishers，New York，pp 187-242(1991))。
与不含分散的分层材料的泡沫体相比，本发明的泡沫体显示出有用的性能，例如，甚至在暴露于极性介质如水或甲醇中时也有增强的屈服强度和拉伸模量，增强的耐热性和增强的冲击强度。纵使使用少量的分层材料也能使这些性能得以改善。还令人惊奇地发现通过将少量(少于5％份)离子交换的有机粘土加到用极性取代基如马来酐或乙烯基三甲氧基硅烷接枝的密度为0.87g/cm3的树脂中，可得到A Sker C硬度的密度为0.885g/cm3的聚烯烃弹性体树脂(40-45)而基本上不损害密度为0.87g/cm3的树脂的回弹性和滞变。因此，通过将离子交换的有机粘土材料加到低密度发泡的含极性官能度的聚烯烃材料中，可以实现通常理想的高硬度、低滞变和高回弹性的结合。
下列实施例仅作说明的目的，并不意味着限制发明范围。
实施例1、VTMS接枝的含蒙脱石有机粘土的聚烯烃弹性体泡沫体胶块
将乙烯基三甲氧基硅烷(1.5％重量)、AFFINITYTMEG8200树脂(98.425％重量)和过氧化二枯基(0.075％重量)转动共混30分钟。然后将混合物在按表1所设的条件下操作的韦尔纳-普福莱德勒(Werner-Pfleiderer)ZSK-30共旋转的双螺杆挤出机上进行混合。(AFFINITYTMEG8200树脂是一种大体线性的乙烯-1-辛烯共聚物，其熔体指数为5g/10分钟，密度为0.870g/cm3，I10/I2为7，Mw/Mn为2)。1-5区指的是挤出机加热器各区。
          表1
#1区(℃) 130
#2区(℃) 172
#3区(℃) 185
#4区(℃) 211
#5区(℃) 209
模口温度(℃) 197
熔体温度(℃) 225
挤出机扭矩 70
挤出机转/分 100
模口压力(psi/kPa) 390/2690
水浴温度(℃) 15
所得聚合物(AFFINITY EG 8200.g.VTMS)用于制备如表II所设的胶块配方。CLAYTONETMHY(南部粘土产品公司的商标)是用二甲基二氢化牛油铵处理过的蒙脱石粘土。活性助剂为SARTOMERTM350单体，一种三(甲基丙烯酸)三羟甲基丙烷酯交联活性助剂(Sartomer公司的商标)。在密炼器型丁二烯橡胶密闭式分批混合器中在95-110℃下将各组分混合4-5分钟来制备该配方。然后将混合物在一台加热到80℃的轧制机上压成1/4英寸(0.6cm)-1/2英寸(1.3cm)厚的片材。将大约200g上述配料放入一开口为5英寸×5英寸×0.5英寸(12.7cm×12.7cm×1.3cm)的形镂中。将该材料放入一四面体MTP-8压缩机中在1吨压力(0.56mPa)下在120℃压制20分钟，然后立即在一Carver自动液压机(3895型)中在175℃和25吨压力(14MPa)压制7-8分钟。然后让材料在150-160℃，25吨压力(14MPa)下发泡大约45分钟。先将泡沫体切割成1.5英寸×1.5平方英寸(3.8cm2×3.8cm2)来测定泡沫体密度。然后去掉泡沫体表皮并用霍巴特(Hobart)切片机将厚度调整到0.5英寸(1.3cm)。用测径器测定方块尺寸。然后将样品称重，由质量除以体积测得密度。通过用测径器测量样品初始厚度来测得静态压缩。然后如ASTM D-395方法B所述用0.25英寸(0.63cm)的间隔在一静态压缩变形夹具中将样品压缩50％。泡沫体密度为0.14g/cm3±0.01；静态压缩为62％±4；由Asker C硬度计测定的AkserC硬度为43±2；回弹性为59％±1，按照ASTM D-3574-86测定；滞变为10.8％±0.1.
                      表II
组分 用量(份/100份树脂)
AFFINITYTMEG 8200.g.VTMS树脂 100
偶氮二酰胺 3.0
硬脂酸锌 0.5
氧化锌 1.0
IRGANOXTM1010抗氧剂 0.1
过氧化二枯基(40％活性) 1.0
活性助剂 1.25
二月桂酸二丁锡 0.01
TiO2 3.0
CLAYTONETMHY 4.5
实施例2.VTMS接枝的含蒙脱石有机粘土的聚烯烃弹性体泡沫体胶块
本实施例采用实施例1所述的形成泡沫体胶块的步骤。配方见表III。
                    表III
组分 用量(份/100份树脂)
AFFINITYTMEG8200.g.VTMS树脂 100
偶氮二酰胺 3
氧化锌 1
过氧化二枯基 0.8
活性助剂 2.5
TiO2 3
CLAYTONETMHY 3
压缩变形为65.5％±2.0％，Asker C硬度为51，回弹性为58。
实施例3.MAH接枝的含蒙脱石有机粘土的聚烯烃弹性体泡沫体胶块
由DOW化学公司得到接枝于大体线性的乙烯-1-辛烯共聚物上的马来酐(MAH)。(制备此材料的步骤公开于U.S.专利5,346,963中)此接枝材料(AFFINITYTMEG8200.g.MAH)含有98.12％AFFINITYTMEG8200，1.4％MAH、0.12％二特丁基过氧化物和0.36％矿物油。用AFFINITYTMEG8200.g.MAH和AFFINITYTMEG8200制备泡沫体胶块配方。配方见表IV。(1RGANOXTM是Ciba-Geigy的商标)。
                    表IV
组分 用量(份/100份树脂)
AFFINITYTMEG8200树脂 80
AFFINITYTMEG8200.g.MAH树脂 20
偶氮二酰胺 2.75
硬脂酸锌 0.5
氧化锌 1.0
IRGANOXTM1010抗氧剂 0.1
过氧化二枯基(40％活性) 1.5
活性助剂 1.75
TiO2 3
CLAYTONETMHY 4.5
由此配方按实施例1所述制备泡沫体。泡沫体密度为0.14g/cm3±0.01，Asker C硬度为45±2，回弹性为54％±1，静态压缩变形为80。

Claims (14)

1.一种聚合物泡沫体，由其中已分散有层离或分层的亲有机多层化颗粒的树脂构成并通过包括如下步骤的方法制备：
a)将亲有机的多层化材料分散到含有具有极性官能度的链烯或苯乙烯基化合物的聚合物的熔体中以便至少一部分聚合物插入到各颗粒层之间；b)用发泡剂在该条件下膨胀该聚合物形成聚合物泡沫体。
2.如权利要求1的聚合物泡沫体，其中具有极性官能度的链烯或苯乙烯基化合物的聚合物包括酐、羧酸、羟基、硅烷、氯、溴或酯官能度。
3.如权利要求1的聚合物泡沫体，其中具有极性官能度的链烯或苯乙烯基化合物的聚合物是含有马来酐基团或乙烯基-Si(OR)3基团接枝于其上的链烯聚合物或苯乙烯基化合物的聚合物，其中每个R独立地为甲基、乙基或丙基，其中链烯聚合物为聚丙烯、低密度聚乙烯、线性高密度聚乙烯、不均匀支化的线性低密度聚乙烯、乙烯-丙烯-二烯三元共聚物、不均匀支化的超低密度线性聚乙烯、均匀支化的线性乙烯/α-烯烃共聚物、均匀支化的大体线性的乙烯/α-烯烃聚合物、聚苯乙烯或聚α-甲基苯乙烯。
4.如权利要求1-3任一项的聚合物泡沫体，其中亲有机的多层化材料为用季铵盐处理的蒙脱石粘土。
5.如权利要求4的聚合物泡沫体，其中季铵盐为二甲基二氢化牛脂铵盐、十八烷基三甲基铵盐、双十八烷基二甲基铵盐、十六烷基三甲基铵盐、双十六烷基二甲基铵盐、十四烷基三甲基铵盐或双十四烷基二甲基铵盐。
6.如权利要求1的聚合物泡沫体，其中熔体还包括不含极性官能度的链烯或苯乙烯基化合物的聚合物。
7.如权利要求6的聚合物泡沫体，其中不含极性官能度的链烯聚合物为均匀支化的线性乙烯/α-烯烃共聚物和均匀支化的大体线性的乙烯/α-烯烃聚合物，其密度为0.85g/cm3-0.965g/cm3，Mw/Mn为1.5-3.0，熔体指数为0.1-100g/10分，I10/I2为6-20。
8.如权利要求1的聚合物泡沫体，其中亲有机的多层化颗粒含有1-10％重量的聚合物熔体，以树脂重量为基准。
9.如权利要求8的聚合物泡沫体，其中聚合物熔体含有由如下物质组成的混合物：不均匀支化的大体线性的未用极性基团官能化的乙烯-1-辛烯共聚物和不均匀支化的大体线性的用马来酐或乙烯基三甲氧基硅烷接枝的乙烯-1-辛烯共聚物。
10.如权利要求9的聚合物泡沫体，其中聚合物熔体密度为0.86g/cm3-0.88g/cm3。
11.如权利要求10的聚合物泡沫体，其中未官能化的共聚物与接枝共聚物的重量比范围为1∶1-10∶1。
12.如权利要求11的聚合物泡沫体，其中未官能化的共聚物与接枝共聚物的重量比范围为3∶1-5∶1。
13.如权利要求1的聚合物泡沫体，其中熔体含有一种用极性基团官能化的链烯聚合物，它是乙烯-丙烯酸共聚物、乙烯-乙酸乙烯酯共聚物或乙烯-甲基丙烯酸共聚物。
14.一种聚合物泡沫体，由其中分散有层离或分层的亲有机多层化颗粒的树脂构成并通过含以下步骤的方法制备：a)将亲有机的多层化颗粒分散到具有极性官能度的可聚合链烯或苯乙烯基化合物单体中以便至少一部分单体插入到各层颗粒之间；b)由单体形成聚合物熔体；c)在该条件下用发泡剂将聚合物膨胀形成聚合物泡沫。
CN97192487A 1996-02-23 1997-02-20 聚合物泡沫体中层离颗粒的分散 Expired - Fee Related CN1130412C (zh)