CN113019271A - 一种除甲醛水凝胶及其制备方法 - Google Patents
一种除甲醛水凝胶及其制备方法 Download PDFInfo
- Publication number
- CN113019271A CN113019271A CN202110224081.3A CN202110224081A CN113019271A CN 113019271 A CN113019271 A CN 113019271A CN 202110224081 A CN202110224081 A CN 202110224081A CN 113019271 A CN113019271 A CN 113019271A
- Authority
- CN
- China
- Prior art keywords
- parts
- formaldehyde
- solution
- dihydrogen phosphate
- deionized water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本申请公开了一种除甲醛水凝胶，所述水凝胶按重量份计包括：10‑15份高分子活性聚合物、1‑5份山梨醇、1‑3份甘油、10‑20份活性物质、1‑5份柠檬酸、0.1‑1份磷酸二氢钾、0.1‑1份磷酸二氢钠以及50‑80份去离子水。本申请的除甲醛水凝胶的甲醛去除率高达92％以上，结构稳定，作用时间长，成本低廉实用方便。
Description
技术领域
本申请涉及甲醛消除领域，特别是涉及一种除甲醛水凝胶及其制备方法。
背景技术
随着广大人民对健康要求的越来越高，人们对各自居住环境及用车环境的要求也越来越高，尤其对自用新房及二次装修住房中的甲醛污染问题越来越重视。对于甲醛的危害，主要表现在以下方面：第一，刺激性。包括对皮肤黏膜和呼吸道的刺激，导致流泪咽痛、咳嗽、气短、呼吸困难等症状。第二，致敏性。皮肤接触一定剂量甲醛可引起过敏性皮炎；呼吸道吸入一定剂量甲醛可能诱发支气管哮喘等。第三，致畸性。特别是对孕妇，长期吸入可能导致胎儿畸形，甚至死亡，男子长期吸入可导致男子精子畸形、死亡等。第四，致癌性。甲醛是一种基因毒性物质，可能导致多种肿瘤发病率提升，如白血病。
对于甲醛的来源，主要来源于胶合板(室内装饰，家私，地板等)，腻子/胶水粘合剂(腻子，木工胶水，墙纸粘合剂，地板胶等)，家具(沙发，床垫，窗帘等)，石膏预制件(天花预制件，墙体装饰件，吊顶等)，水性涂料以及其他材料。同样对于车内空气甲醛污染，其主要来源于车内内饰材料，聚氨酯发泡材料(包括座椅，仪表盘等)，车内粘结材料等。而且最关键的是这些材料中的甲醛往往需要3-15年的时间才能完全挥发干净。
目前，市场上有很多专业的除甲醛机构，虽然快速有效，但往往不能彻底根除，治标不治本。所以，使用后还需要采购大量的固体吸附材料来巩固清除的效果。这些吸附材料需要经常更换，导致成本高，效果不好。同时，还会造成二次释放污染。
发明内容
本发明的目的在于提供一种除甲醛水凝胶及其制备方法，以克服现有技术中的不足。
为实现上述目的，本发明提供如下技术方案：一种除甲醛水凝胶，所述水凝胶按重量份计包括：10-15份高分子活性聚合物、1-5份山梨醇、1-3份甘油、10-20份活性物质、1-5份柠檬酸、0.1-1份磷酸二氢钾、0.1-1份磷酸二氢钠以及50-80份去离子水。
在该技术方案中，活性物质可以为三聚氰胺，尿素，2-咪唑啉酮，己二酸二乙酰肼、高分子聚丙烯酸。
优选的，所述水凝胶重量份计包括：12份高分子活性聚合物、2份山梨醇、1份甘油、15份活性物质、2份柠檬酸、0.5份磷酸二氢钾、0.5份磷酸二氢钠以及50-80份去离子水。
在该技术方案中，重量份可以计量为克，1份相当于1克。
优选的，所述高分子活性聚合物为有丙烯酸、甲基丙烯酸和丙烯酰胺聚合而成。
为实现本发明的另一目的，本发明提供如下技术方案：一种除甲醛水凝胶的制备方法，包括：S1:将0.01-0.3份的引发剂加入10-80份的去离子水中，充分溶解后得到溶解液A；S2：在反应釜中加入50-80份去离子水以及2-5份的溶解液A，并加热至80-100℃；S3：将40-80份的聚合物单体匀速泵入反应釜中，保温1小时，保温温度为80-100℃；S4:按顺序将0-50份山梨醇、1-3份甘油、10-20份活性物质加入反应釜中，搅拌至完全溶解得到溶解液B；S5：将pH调节剂加入反应釜中的溶解液B中，将所述溶解液B的pH值调节至6-7；S6：将会所述步骤S5中的溶液降至室温后进行造粒。
优选的，所述pH调节剂按重量份计包括：1-5份柠檬酸，0.1-1份磷酸二氢钾和0.1-1份磷酸二氢钠。
优选的，所述引发剂由过硫酸钠和过硫酸铵中的一种或者两者混合而成。
优选的，所述聚合物单体为丙烯酸，甲基丙烯酸和丙烯酰胺。
与现有技术相比，本申请至少具有以下有益效果：
1、本发明的除甲醛水凝胶为高效的球形水凝胶甲醛清除剂，各活性成分之间能够互相作用，协同增效，大大提高了甲醛的消除效率；
2、本发明的除甲醛水凝胶的结构稳定且作用时间持久，可持续有效达三个月以上；
3、本发明的除甲醛水凝胶使用方便，无需过多维护，使用方便且成本低；可以有效去除室内及车内的甲醛，去除率达到92％以上；
4、本发明的除甲醛水凝胶无毒无害，不会造成二次污染。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行详细的描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动的前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
S1:将0.2克过硫酸钠荣誉10克去离子水，该溶液为A；
S2：将50克去离子水加入250ml四口烧瓶中，并升温至85℃；
S3:将0.5克溶液A加入250ml四口烧瓶中，开启搅拌；
S4:将60克丙烯酸及9.5克溶解A匀速滴入四口烧瓶中，保持温度在90-100℃之间；2小时内滴加结束。
S5:结束滴加后并保持温度在90-100℃,保温时间1小时左右；加48％氢氧化钠溶液，调节pH至6-7之间。
S6:保温结束后，将30克山梨醇、2克甘油、20克活性物质，按顺序加入至反应釜中，搅拌至完全溶解；
S7:将1克柠檬酸，0.5克磷酸二氢钾，0.5克磷酸二氢钠加入至反应釜中，调整pH至6-7之间。
S8：将至室温，并造粒。
经检测，本实施例的除甲醛水凝胶24小时甲醛去除率达到92％。
需要说明的是，在本文中，诸如第一和第二等之类的关系术语仅仅用来将一个实体或者操作与另一个实体或操作区分开来，而不一定要求或者暗示这些实体或操作之间存在任何这种实际的关系或者顺序。而且，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。在没有更多限制的情况下，由语句“包括一个……”限定的要素，并不排除在包括要素的过程、方法、物品或者设备中还存在另外的相同要素。
以上仅是本申请的具体实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本申请原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本申请的保护范围。
Claims (7)
1.一种除甲醛水凝胶，其特征在于：所述水凝胶按重量份计包括：10-15份高分子活性聚合物、1-5份山梨醇、1-3份甘油、10-20份活性物质、1-5份柠檬酸、0.1-1份磷酸二氢钾、0.1-1份磷酸二氢钠以及50-80份去离子水。
2.根据权利要求1所述的一种除甲醛水凝胶，其特征在于：所述水凝胶重量份计包括：12份高分子活性聚合物、2份山梨醇、1份甘油、15份活性物质、2份柠檬酸、0.5份磷酸二氢钾、0.5份磷酸二氢钠以及50-80份去离子水。
3.根据权利要求1-2任一所述的一种除甲醛水凝胶，其特征在于：所述高分子活性聚合物为有丙烯酸、甲基丙烯酸和丙烯酰胺聚合而成；所述活性物质为高分子聚丙烯酸。
4.根据权利要求1-3任一所述的一种除甲醛水凝胶的制备方法，其特征在于:包括：S1:将0.01-0.3份的引发剂加入10-80份的去离子水中，充分溶解后得到溶解液A；S2：在反应釜中加入50-80份去离子水以及2-5份的溶解液A，并加热至80-100℃；S3：将40-80份的聚合物单体匀速泵入反应釜中，保温1小时，保温温度为80-100℃；S4:按顺序将0-50份山梨醇、1-3份甘油、10-20份活性物质加入反应釜中，搅拌至完全溶解得到溶解液B；S5：将pH调节剂加入反应釜中的溶解液B中，将所述溶解液B的pH值调节至6-7；S6：将会所述步骤S5中的溶液降至室温后进行造粒。
5.根据权利要求4所述的一种除甲醛水凝胶的制备方法，其特征在于:所述pH调节剂按重量份计包括：1-5份柠檬酸，0.1-1份磷酸二氢钾和0.1-1份磷酸二氢钠。
6.根据权利要求4所述的一种除甲醛水凝胶的制备方法，其特征在于:所述引发剂由过硫酸钠和过硫酸铵中的一种或者两者混合而成。
7.根据权利要求4所述的一种除甲醛水凝胶的制备方法，其特征在于:所述聚合物单体为丙烯酸，甲基丙烯酸和丙烯酰胺。