CN112900766A - Processing method for generating chromatic aberration on surface of putty wall - Google Patents
Processing method for generating chromatic aberration on surface of putty wall Download PDFInfo
- Publication number
- CN112900766A CN112900766A CN202110070244.7A CN202110070244A CN112900766A CN 112900766 A CN112900766 A CN 112900766A CN 202110070244 A CN202110070244 A CN 202110070244A CN 112900766 A CN112900766 A CN 112900766A
- Authority
- CN
- China
- Prior art keywords
- putty
- wall
- wall surface
- primer
- rolling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a treatment method for generating chromatic aberration on the surface of a putty wall, which comprises the following steps of removing a release agent and other grease components attached to the wall surface by using an oil removing cleaning agent, then using putty paste and bottom layer putty to paint a putty base material layer on the wall surface obtained after the treatment in the step one, then using putty powder to paint a putty surface material layer, then using abrasive paper to polish the wall surface obtained after the putty is painted for two times in sequence, then rolling the wall surface obtained after polishing with a primer of the same batch, and then rolling the surface paint of the same batch for two times in sequence after the primer is rolled and brushed. The putty wall surface processing method can process the putty wall surface, and reduce the occurrence of the phenomenon of wall surface color difference, thereby improving the integrity and the aesthetic property of the wall surface.
Description
Technical Field
The invention mainly relates to the technical field of wall construction, in particular to a processing method for generating chromatic aberration on the surface of a putty wall.
Background
After the construction of the main frame and the wall surface of the building is finished, the construction of the outer wall surface and the inner wall surface of the building is generally finished by smearing materials with certain thickness, such as cement, lime and the like.
According to the construction method of the combined building wall surface provided by the patent document with the application number of CN201210251328.1, the method adopts the wallboard with a sheet structure, and the edge of the main body of the wallboard is provided with a concave fixing notch; and attaching the wall board to the wall surface, smearing and connecting concrete or cement paste at the butt joint of the wall board, and filling the fixed notch with the concrete or cement paste. The construction method of the combined building wall surface is simple, convenient and quick, any cutting combination of the prefabricated wall boards can be carried out according to the size of the building wall body, secondary leveling operation is not needed, meanwhile, the wall boards can also be produced industrially, the wall surface construction cost is reduced, and the construction efficiency is improved.
However, the wall surface construction method has defects, for example, although the wall surface treatment method does not need to perform secondary leveling operation, the putty powder is a semi-finished product, and since the quality of the mineral powder mined in a mining area is different due to different areas, the color difference phenomenon often occurs, and the occurrence of the color difference phenomenon often affects the coordination of wall surface construction and reduces the construction quality.
Disclosure of Invention
The invention mainly provides a method for processing the color difference generated on the surface skin of a putty wall surface, which is used for solving the technical problems in the background technology.
The technical scheme adopted by the invention for solving the technical problems is as follows:
a processing method for generating color difference on the surface skin of a putty wall surface comprises the following steps:
removing oil from the wall surface, namely removing a release agent and other oil components attached to the wall surface by using an oil removing cleaning agent;
secondly, coating putty fabric, namely coating a putty base material layer on the wall surface obtained after the treatment in the first step by using putty paste and bottom putty, and then coating a putty fabric layer by using putty powder;
step three, wall surface polishing, namely sequentially polishing the wall surface treated in the step two twice by using abrasive paper;
and step four, rolling and brushing a paint film, namely rolling and brushing the same batch of primer on the wall surface obtained in the step three, and sequentially rolling and brushing the same batch of finish paint twice after the rolling and brushing of the primer is finished.
Further, the thickness of the putty base material layer and the putty surface material layer in the second step is 1.5-2.5 cm.
Further, the putty paste and the bottom layer putty in the second step are both waterproof putty.
Further, a thermometer is used for measuring the temperature in the second step, when the temperature exceeds 35 ℃, lacquer polyethylene glue is added into the raw materials used for the putty-coated fabric, and the raw materials are uniformly stirred by a stirrer.
And further, adding sand grains into the bottom putty layer raw material in the second step.
Further, 280-300 meshes of waterproof abrasive paper is used for polishing during the first polishing in the third step, and 360-400 meshes of waterproof abrasive paper is used for polishing for the second time during the second polishing.
Furthermore, the thickness of the primer fabric and the finish fabric in the fourth step is 2-2.5 mm.
Further, stirring the raw material of the face paint in the fourth step by using a stirrer, wherein the stirring time is 15-25 min, and the stirring speed is 500-800 r/min.
And further, after finishing rolling brushing of the primer in the fourth step, naturally drying for two days by using a temperature detector when the temperature exceeds 25 ℃, and naturally drying for five days when the temperature does not exceed 25 ℃, and then rolling brushing of the finish paint.
Further, the primer brushed in the fourth step is an alkali-resistant primer.
Compared with the prior art, the invention has the beneficial effects that:
the putty wall surface is processed, so that the occurrence of the wall surface color difference phenomenon is reduced, the integrity and the attractiveness of the wall surface are improved, and the putty wall surface processing method specifically comprises the following steps: the method comprises the steps of removing release agent and other grease components attached to the wall surface through an oil removing cleaning agent, so as to improve the flatness of the wall surface and the firmness of putty fabric, using waterproof putty as putty paste and bottom putty to enhance the waterproof performance of the putty paste and the bottom putty, using paint polyethylene glue to prevent the water in the putty paste and the bottom putty from evaporating too fast, so that the alkaline components of the putty paste and the bottom putty using alkaline waterproof putty as raw materials are continuously expanded on the paint surface, and long-time sunshine is added to cause the wall surface color change phenomenon, and using waterproof abrasive paper with different meshes to polish the wall surface in batches, so as to improve the flatness of the wall surface, prevent the wall surface from being uneven, prevent the phenomena of cracking, peeling and the like caused by uneven paint film rolled on the wall surface when the paint film is rolled and brushed on the next step, influence the integrity of the wall surface, and brushing the primer and the finish paint in the same batch, therefore, the integrity of the wall surface color is improved, the firmness of the finish paint is improved through the use of the primer, and the saturation of the finish paint is enhanced.
The present invention will be explained in detail below with reference to specific examples.
Detailed Description
While the present invention will be described more fully hereinafter for purposes of facilitating an understanding thereof, the present invention may be embodied in many different forms and is not limited to the embodiments described herein, but rather, these embodiments are provided so that this disclosure will be thorough and complete.
It will be understood that when an element is referred to as being "secured to" another element, it can be directly on the other element or intervening elements may be present, and when an element is referred to as being "connected" to another element, it can be directly connected to the other element or intervening elements may also be present, as the terms "vertical", "horizontal", "left", "right" and the like are used herein for descriptive purposes only.
Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs, and the knowledge of the terms used herein in the specification of the present invention is for the purpose of describing particular embodiments and is not intended to limit the present invention, and the term "and/or" as used herein includes any and all combinations of one or more of the associated listed items.
The embodiment provides a processing method for generating chromatic aberration on the surface of a putty wall, which comprises the following steps:
removing oil from the wall surface, namely removing a release agent and other oil components attached to the wall surface by using an oil removing cleaning agent;
secondly, coating putty fabric, namely coating a putty base material layer on the wall surface obtained after the treatment in the first step by using putty paste and bottom putty, and then coating a putty fabric layer by using putty powder;
step three, wall surface polishing, namely sequentially polishing the wall surface treated in the step two twice by using abrasive paper;
and step four, rolling and brushing a paint film, namely rolling and brushing the same batch of primer on the wall surface obtained in the step three, and sequentially rolling and brushing the same batch of finish paint twice after the rolling and brushing of the primer is finished.
And the thickness of the putty base material layer and the putty surface material layer in the second step is 1.5-2.5 cm, so that the influence on the integrity of the wall due to the cracking of the wall caused by the continuous evaporation of water in the wall due to the too thick putty base material layer and the putty surface material layer is prevented.
Putty cream and bottom putty in the step two are water proof putty to reinforcing putty cream and bottom putty's water resistance can use thermometer measurement temperature in the step two, when the temperature surpassed 35 ℃, add lacquer polyethylene glue in to the raw materials that the putty surface fabric of drapeing over one's shoulders used, and use the even stirring of mixer, thereby utilize lacquer polyethylene glue to prevent that water evaporation is too fast in putty cream and the bottom putty, make use putty cream and the bottom putty alkaline component that is alkaline water proof putty as the raw materials constantly to enlarge on the lacquer painting, in addition long-time sunshine, wall discoloration appears.
And D, adding sand grains into the raw material of the bottom putty layer in the second step, so that the sand grains are utilized to assist the bottom putty layer in leveling, and the sand grains are utilized to increase the hardness, strength and water permeability of the bottom putty layer, thereby preventing the adhesion of the bottom putty layer from being reduced due to insufficient hardness, causing the paint film to tear skin and influencing the integrity of the wall surface.
Use 280 ~ 300 mesh water sand paper to polish when polishing for the first time in the third step, use 360 ~ 400 mesh water sand paper to polish for the second time when polishing for the second time to the water sand paper that utilizes different mesh numbers polishes in batches the wall, thereby has improved the planarization of wall, prevents the wall unevenness, makes the phenomenon such as the fracture and the peeling that the rolling brush leads to the paint film unevenness on the wall when rolling brush the paint film on next step, influences the integrality of wall.
In the fourth step, the thickness of the primer plus finish plus fabric is 2-2.5 mm, so that the phenomenon that a paint film blocks and peels off due to the fact that the thickness of the primer plus finish plus fabric is too thick is avoided.
And C, stirring the finish raw materials in the fourth step by using a stirrer, wherein the stirring time is 15-25 min, and the stirring speed is 500-800 r/min, so that the finish raw materials are fully stirred, and color difference caused by different colors of the finish raw materials is prevented.
And D, after finishing rolling brushing of the primer in the fourth step, using a temperature detector, naturally drying for two days when the temperature exceeds 25 ℃, naturally drying for five days when the temperature does not exceed 25 ℃, and then performing rolling brushing of the finish paint, so that the primer brushed to the wall surface by rolling brushing is fully dried, and the phenomenon that the paint film is peeled off due to the separation of the paint film from the wall surface due to moisture is prevented.
The primer brushed in the fourth step is alkali-resistant primer,
the specific operation mode of the invention is as follows:
removing a release agent and other grease components attached to the wall surface by using an oil removing cleaning agent, using putty paste and bottom layer putty to scrape a putty base material layer on the wall surface obtained after the treatment in the step one, then using putty powder to scrape a putty surface material layer, measuring the temperature by using a thermometer in the process, adding paint polyethylene glue into the raw materials used for scraping the putty surface material when the temperature exceeds 35 ℃, uniformly stirring by using a stirring machine, then using abrasive paper to polish the wall surface obtained after the putty is scraped for two times in sequence, then rolling and brushing the same batch of primer on the wall surface obtained after polishing, and rolling and brushing the same batch of finish paint for two times in sequence after the primer is rolled and brushed.
It is to be understood that the invention is not limited to the specific embodiments described above, but is intended to cover such insubstantial modifications of the inventive process concepts and solutions, or their direct application to other applications without such modifications, without departing from the scope of the invention.
Claims (10)
1. A processing method for generating color difference on the surface of a putty wall is characterized by comprising the following steps:
removing oil from the wall surface, namely removing a release agent and other oil components attached to the wall surface by using an oil removing cleaning agent;
secondly, coating putty fabric, namely coating a putty base material layer on the wall surface obtained after the treatment in the first step by using putty paste and bottom putty, and then coating a putty fabric layer by using putty powder;
step three, wall surface polishing, namely sequentially polishing the wall surface treated in the step two twice by using abrasive paper;
and step four, rolling and brushing a paint film, namely rolling and brushing the same batch of primer on the wall surface obtained in the step three, and sequentially rolling and brushing the same batch of finish paint twice after the rolling and brushing of the primer is finished.
2. The processing method for generating color difference on the surface of the putty wall surface as claimed in claim 1, wherein the thickness of the putty base material layer and the putty surface material layer in the second step is 1.5-2.5 cm.
3. The method for treating the chromatic aberration generated on the surface of the putty wall as claimed in claim 1, wherein the putty paste and the bottom layer putty in the second step are both water-resistant putty.
4. The method for treating the color difference of the surface skin of the putty wall as claimed in claim 1, wherein in the second step, a thermometer is used to measure the temperature, when the temperature exceeds 35 ℃, lacquer polyethylene glue is added to the raw material used for the putty-coated fabric, and the mixture is stirred uniformly by a stirrer.
5. The method for treating the color difference of the surface of the putty wall as defined in claim 1, wherein sand grains are added to the raw material of the bottom putty layer in the second step.
6. The method for processing the color difference of the surface of the putty wall as defined in claim 1, wherein 280-300 mesh waterproof abrasive paper is used for polishing in the first polishing in the third step, and 360-400 mesh waterproof abrasive paper is used for polishing in the second polishing.
7. The processing method for generating color difference on the surface of the putty wall as defined in claim 1, wherein the thickness of the primer plus the finish plus in the fourth step is 2-2.5 mm.
8. The method for treating the color difference of the surface skin of the putty wall as claimed in claim 1, wherein a stirrer is used for stirring the raw material of the surface paint in the fourth step, the stirring time is 15-25 min, and the stirring speed is 500-800 r/min.
9. The method for treating the color difference of the surface skin of the putty wall as claimed in claim 1, wherein a temperature detector is used after the rolling brushing of the primer in the fourth step, when the temperature exceeds 25 ℃, the surface paint is naturally dried for two days, and when the temperature does not exceed 25 ℃, the surface paint is naturally dried for five days, and then the rolling brushing of the surface paint is carried out.
10. The method as claimed in claim 1, wherein the primer applied in step four is an alkali-resistant primer.