CN112897979A - 一种以硅藻土为填料的强效防霉墙面装饰材料 - Google Patents
一种以硅藻土为填料的强效防霉墙面装饰材料 Download PDFInfo
- Publication number
- CN112897979A CN112897979A CN202110162069.4A CN202110162069A CN112897979A CN 112897979 A CN112897979 A CN 112897979A CN 202110162069 A CN202110162069 A CN 202110162069A CN 112897979 A CN112897979 A CN 112897979A
- Authority
- CN
- China
- Prior art keywords
- parts
- diatomite
- proof wall
- wall decoration
- sepiolite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种以硅藻土为填料的强效防霉墙面装饰材料，按照重量份的原料包括：硅藻土50‑600份、凹凸棒土50‑250份、海泡石50‑250份、石膏粉50‑250份、滑石粉30‑250份、氢氧化镁30‑150份、羟乙基纤维素3‑30份、二氧化硅气溶胶30‑250份、吡啶硫酮锌5‑120份、无机颜料10‑100份。本发明调节室内湿度、隔音隔热、吸附甲醛、芳香烃、二氯甲烷等室内有毒气体，阻燃、消烟、防滴，装饰材料具有物理化学性质稳定、不掉色、不褪色、无腐蚀、环保、抗菌防霉的特点。本发明采用的材料都是天然环保的，成本降低，生产工序简单，颜色自然，不刺眼，环保性能更高，弱碱不刺激皮肤。
Description
技术领域
本发明涉及室内装饰材料技术领域，具体是一种以硅藻土为填料的强效防霉墙面装饰材料。
背景技术
硅藻泥涂料是近年来发展起来的一类新型功能性墙面装饰环保材料，其主要成分是硅藻土，利用硅藻土多孔的结构来吸附空气中的有害气体，添加光触媒利用光触媒的光催化作用来分解空气中的甲醛等有害物质，利用灰钙粉的耐水和杀菌防霉等优点来做为辅助材料，在添加白水泥来做为胶凝材料来粘接材料上墙。
但是现有的硅藻泥由于无机材料之间的粘合力差，涂料在建筑墙面施工后存在易掉粉、易脱落的技术问题，为了解决这个问题，往往在涂料中添加有机胶类物质，由于这类物质残存溶剂气味大，易堵塞硅藻土孔隙，在较大程度上降低了硅藻泥涂料的环保功能，随着时间的推移此类有机胶类聚合物生物降解速度加快，导致涂料耐久性差。此外，这种壁材不具备分解甲醛等有害气体的功能，从硅藻泥涂料的发展趋势上看，开发多功能、粘接强度大、耐久性好的硅藻泥涂料，将是建筑装饰涂料行业未来的发展方向。
发明内容
本发明的目的在于提供一种颜色自然、环保性能更高、弱碱不刺激皮肤的以硅藻土为填料的强效防霉墙面装饰材料，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：
一种以硅藻土为填料的强效防霉墙面装饰材料，按照重量份的原料包括：硅藻土50-600份、凹凸棒土50-250份、海泡石50-250份、石膏粉50-250份、滑石粉30-250份、氢氧化镁30-150份、羟乙基纤维素3-30份、二氧化硅气溶胶30-250份、吡啶硫酮锌5-120份、无机颜料10-100份。
作为本发明进一步的方案：所述以硅藻土为填料的强效防霉墙面装饰材料，按照重量份的原料包括：硅藻土80-550份、凹凸棒土80-220份、海泡石80-220份、石膏粉80-220份、滑石粉40-220份、氢氧化镁40-120份、羟乙基纤维素4-25份、二氧化硅气溶胶40-220份、吡啶硫酮锌8-110份、无机颜料15-90份。
作为本发明进一步的方案：所述以硅藻土为填料的强效防霉墙面装饰材料，按照重量份的原料包括：硅藻土100-500份、凹凸棒土100-200份、海泡石100-200份、石膏粉100-200份、滑石粉50-200份、氢氧化镁50-100份、羟乙基纤维素5-20份、二氧化硅气溶胶50-200份、吡啶硫酮锌10-100份、无机颜料20-80份。
作为本发明进一步的方案：所述硅藻土、凹凸棒土、海泡石粒度为20-100目。
作为本发明进一步的方案：所述无机颜料为氧化铁红、铝酸钴蓝、铋黄中的任意一种或两种。
作为本发明进一步的方案：所述羟乙基纤维素的粘度为100000。
与现有技术相比，本发明的有益效果是：
本发明中硅藻土具有比表面积大、孔隙率高、重量轻的特点，可起到调节室内湿度、隔音隔热、吸附甲醛、芳香烃、二氯甲烷等室内有毒气体的作用。羟乙基纤维素可起到增稠、保护氢氧化铝水合物胶体、强化粘合能力、提高浆料的涂抹性的作用。氢氧化镁是一种新型环保绿色无机阻燃剂，具有阻燃、消烟、防滴、填充等多重功能。无机颜料无毒、无害、环保，可使装饰材料具有物理化学性质稳定、不掉色、不褪色、无腐蚀、环保的特点。吡啶硫酮锌可起到极佳的抗菌防霉。本发明采用的材料都是天然环保的，成本降低，生产工序简单，颜色自然，不刺眼，环保性能更高，弱碱不刺激皮肤。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
本发明实施例中，一种以硅藻土为填料的强效防霉墙面装饰材料，按照重量份的原料包括：硅藻土50份、凹凸棒土50份、海泡石50份、石膏粉50份、滑石粉30份、氢氧化镁30份、羟乙基纤维素3份、二氧化硅气溶胶30份、吡啶硫酮锌5份、无机颜料10份。所述硅藻土、凹凸棒土、海泡石粒度为20目。所述无机颜料为氧化铁红。所述羟乙基纤维素的粘度为100000。
所以硅藻土为填料的强效防霉墙面装饰材料的制备过程，是将硅藻土、凹凸棒土、海泡石、石膏粉、滑石粉、氢氧化镁、羟乙基纤维素、二氧化硅气溶胶、吡啶硫酮锌、无机颜料混合搅拌均匀即得。
实施例2
本发明实施例中，一种以硅藻土为填料的强效防霉墙面装饰材料，按照重量份的原料包括：硅藻土600份、凹凸棒土250份、海泡石250份、石膏粉250份、滑石粉250份、氢氧化镁150份、羟乙基纤维素30份、二氧化硅气溶胶250份、吡啶硫酮锌120份、无机颜料100份。所述硅藻土、凹凸棒土、海泡石粒度为100目。所述无机颜料为铝酸钴蓝。所述羟乙基纤维素的粘度为100000。
所以硅藻土为填料的强效防霉墙面装饰材料的制备过程，是将硅藻土、凹凸棒土、海泡石、石膏粉、滑石粉、氢氧化镁、羟乙基纤维素、二氧化硅气溶胶、吡啶硫酮锌、无机颜料混合搅拌均匀即得。
实施例3
本发明实施例中，一种以硅藻土为填料的强效防霉墙面装饰材料，按照重量份的原料包括：硅藻土80份、凹凸棒土80份、海泡石80份、石膏粉80份、滑石粉40份、氢氧化镁40份、羟乙基纤维素4份、二氧化硅气溶胶40份、吡啶硫酮锌8份、无机颜料15份。所述硅藻土、凹凸棒土、海泡石粒度为40目。所述无机颜料为铋黄。所述羟乙基纤维素的粘度为100000。
所以硅藻土为填料的强效防霉墙面装饰材料的制备过程，是将硅藻土、凹凸棒土、海泡石、石膏粉、滑石粉、氢氧化镁、羟乙基纤维素、二氧化硅气溶胶、吡啶硫酮锌、无机颜料混合搅拌均匀即得。
实施例4
本发明实施例中，一种以硅藻土为填料的强效防霉墙面装饰材料，按照重量份的原料包括：硅藻土550份、凹凸棒土220份、海泡石220份、石膏粉220份、滑石粉220份、氢氧化镁120份、羟乙基纤维素25份、二氧化硅气溶胶220份、吡啶硫酮锌110份、无机颜料90份。所述硅藻土、凹凸棒土、海泡石粒度为60目。所述无机颜料为氧化铁红、铝酸钴蓝。所述羟乙基纤维素的粘度为100000。
所以硅藻土为填料的强效防霉墙面装饰材料的制备过程，是将硅藻土、凹凸棒土、海泡石、石膏粉、滑石粉、氢氧化镁、羟乙基纤维素、二氧化硅气溶胶、吡啶硫酮锌、无机颜料混合搅拌均匀即得。
实施例5
本发明实施例中，一种以硅藻土为填料的强效防霉墙面装饰材料，按照重量份的原料包括：硅藻土100份、凹凸棒土100份、海泡石100份、石膏粉100份、滑石粉50份、氢氧化镁50份、羟乙基纤维素5份、二氧化硅气溶胶50份、吡啶硫酮锌10份、无机颜料20份。所述硅藻土、凹凸棒土、海泡石粒度为80目。所述无机颜料为铝酸钴蓝、铋黄。所述羟乙基纤维素的粘度为100000。
所以硅藻土为填料的强效防霉墙面装饰材料的制备过程，是将硅藻土、凹凸棒土、海泡石、石膏粉、滑石粉、氢氧化镁、羟乙基纤维素、二氧化硅气溶胶、吡啶硫酮锌、无机颜料混合搅拌均匀即得。
实施例6
本发明实施例中，一种以硅藻土为填料的强效防霉墙面装饰材料，按照重量份的原料包括：硅藻土500份、凹凸棒土200份、海泡石200份、石膏粉200份、滑石粉200份、氢氧化镁100份、羟乙基纤维素20份、二氧化硅气溶胶200份、吡啶硫酮锌100份、无机颜料80份。所述硅藻土、凹凸棒土、海泡石粒度为50目。所述无机颜料为氧化铁红、铋黄。所述羟乙基纤维素的粘度为100000。
所以硅藻土为填料的强效防霉墙面装饰材料的制备过程，是将硅藻土、凹凸棒土、海泡石、石膏粉、滑石粉、氢氧化镁、羟乙基纤维素、二氧化硅气溶胶、吡啶硫酮锌、无机颜料混合搅拌均匀即得。
实施例7
本发明实施例中，一种以硅藻土为填料的强效防霉墙面装饰材料，按照重量份的原料包括：硅藻土200份、凹凸棒土120份、海泡石120份、石膏粉120份、滑石粉80份、氢氧化镁60份、羟乙基纤维素10份、二氧化硅气溶胶80份、吡啶硫酮锌20份、无机颜料30份。所述硅藻土、凹凸棒土、海泡石粒度为80目。所述无机颜料为铝酸钴蓝、铋黄。所述羟乙基纤维素的粘度为100000。
所以硅藻土为填料的强效防霉墙面装饰材料的制备过程，是将硅藻土、凹凸棒土、海泡石、石膏粉、滑石粉、氢氧化镁、羟乙基纤维素、二氧化硅气溶胶、吡啶硫酮锌、无机颜料混合搅拌均匀即得。
实施例8
本发明实施例中，一种以硅藻土为填料的强效防霉墙面装饰材料，按照重量份的原料包括：硅藻土400份、凹凸棒土180份、海泡石180份、石膏粉180份、滑石粉180份、氢氧化镁90份、羟乙基纤维素15份、二氧化硅气溶胶180份、吡啶硫酮锌90份、无机颜料70份。所述硅藻土、凹凸棒土、海泡石粒度为50目。所述无机颜料为氧化铁红、铋黄。所述羟乙基纤维素的粘度为100000。
所以硅藻土为填料的强效防霉墙面装饰材料的制备过程，是将硅藻土、凹凸棒土、海泡石、石膏粉、滑石粉、氢氧化镁、羟乙基纤维素、二氧化硅气溶胶、吡啶硫酮锌、无机颜料混合搅拌均匀即得。
实施例9
本发明实施例中，一种以硅藻土为填料的强效防霉墙面装饰材料，按照重量份的原料包括：硅藻土300份、凹凸棒土140份、海泡石140份、石膏粉160份、滑石粉100份、氢氧化镁70份、羟乙基纤维素10份、二氧化硅气溶胶100份、吡啶硫酮锌50份、无机颜料40份。所述硅藻土、凹凸棒土、海泡石粒度为40目。所述无机颜料为铝酸钴蓝、铋黄。所述羟乙基纤维素的粘度为100000。
所以硅藻土为填料的强效防霉墙面装饰材料的制备过程，是将硅藻土、凹凸棒土、海泡石、石膏粉、滑石粉、氢氧化镁、羟乙基纤维素、二氧化硅气溶胶、吡啶硫酮锌、无机颜料混合搅拌均匀即得。
实施例10
本发明实施例中，一种以硅藻土为填料的强效防霉墙面装饰材料，按照重量份的原料包括：硅藻土400份、凹凸棒土160份、海泡石160份、石膏粉140份、滑石粉150份、氢氧化镁80份、羟乙基纤维素15份、二氧化硅气溶胶150份、吡啶硫酮锌70份、无机颜料60份。所述硅藻土、凹凸棒土、海泡石粒度为80目。所述无机颜料为氧化铁红、铋黄。所述羟乙基纤维素的粘度为100000。
所以硅藻土为填料的强效防霉墙面装饰材料的制备过程，是将硅藻土、凹凸棒土、海泡石、石膏粉、滑石粉、氢氧化镁、羟乙基纤维素、二氧化硅气溶胶、吡啶硫酮锌、无机颜料混合搅拌均匀即得。
将本发明实施例1-10制备的墙面装饰材料进行甲醛吸附试验，结果如表1所示：
表1
| 组别 | 甲醛吸附率(％) |
| 实施例1 | 75 |
| 实施例2 | 78 |
| 实施例3 | 79 |
| 实施例4 | 80 |
| 实施例5 | 79 |
| 实施例6 | 80 |
| 实施例7 | 81 |
| 实施例8 | 81 |
| 实施例9 | 82 |
| 实施例10 | 83 |
| 市售硅藻泥 | 68 |
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。
Claims (6)
1.一种以硅藻土为填料的强效防霉墙面装饰材料，其特征在于，按照重量份的原料包括：硅藻土50-600份、凹凸棒土50-250份、海泡石50-250份、石膏粉50-250份、滑石粉30-250份、氢氧化镁30-150份、羟乙基纤维素3-30份、二氧化硅气溶胶30-250份、吡啶硫酮锌5-120份、无机颜料10-100份。
2.根据权利要求1所述的以硅藻土为填料的强效防霉墙面装饰材料，其特征在于，按照重量份的原料包括：硅藻土80-550份、凹凸棒土80-220份、海泡石80-220份、石膏粉80-220份、滑石粉40-220份、氢氧化镁40-120份、羟乙基纤维素4-25份、二氧化硅气溶胶40-220份、吡啶硫酮锌8-110份、无机颜料15-90份。
3.根据权利要求1所述的以硅藻土为填料的强效防霉墙面装饰材料，其特征在于，按照重量份的原料包括：硅藻土100-500份、凹凸棒土100-200份、海泡石100-200份、石膏粉100-200份、滑石粉50-200份、氢氧化镁50-100份、羟乙基纤维素5-20份、二氧化硅气溶胶50-200份、吡啶硫酮锌10-100份、无机颜料20-80份。
4.根据权利要求1-3任一所述的以硅藻土为填料的强效防霉墙面装饰材料，其特征在于，所述硅藻土、凹凸棒土、海泡石粒度为20-100目。
5.根据权利要求1-3任一所述的以硅藻土为填料的强效防霉墙面装饰材料，其特征在于，所述无机颜料为氧化铁红、铝酸钴蓝、铋黄中的任意一种或两种。
6.根据权利要求1-3任一所述的以硅藻土为填料的强效防霉墙面装饰材料，其特征在于，所述羟乙基纤维素的粘度为100000。