CN112812613A - 一种耐水的室内面层腻子及其制备方法 - Google Patents
一种耐水的室内面层腻子及其制备方法 Download PDFInfo
- Publication number
- CN112812613A CN112812613A CN202011380671.7A CN202011380671A CN112812613A CN 112812613 A CN112812613 A CN 112812613A CN 202011380671 A CN202011380671 A CN 202011380671A CN 112812613 A CN112812613 A CN 112812613A
- Authority
- CN
- China
- Prior art keywords
- sludge
- putty
- water
- surface layer
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种耐水的室内面层腻子,包括以下组分:活化处理的淤泥5‑20%;白水泥0‑30%;重钙40‑60%;膨润土0‑5%;灰钙0‑20%;聚乙烯醇0.2‑1%;纤维素醚0.2‑1%;防腐剂0.1‑0.5%。其中,活化处理的淤泥通过以下方式制备:1)过滤淤泥,取第三次过滤的淤泥水洗中性,备用。2)烘干过滤淤泥。3)焙烧淤泥。4)微波养护处理得活化处理的淤泥。本发明通过了过滤、烘干、焙烧和微波养护处理淤泥,显著增强腻子表面的耐水性能;通过活化处理的淤泥和聚乙烯醇复掺技术,有效提高了腻子与基层的粘结性能,防止腻子产生从基层脱落剥离现象。
Description
技术领域
本发明属于建筑材料技术领域,具体涉及一种耐水的室内面层腻子及其制备方法。
背景技术
腻子经常做为墙面找平材料应用在建筑装饰装修工程中,现有的内墙腻子粉的组分可谓是大同小异,性能基本参照标准JG/T298-2010《建筑室内用腻子》。内墙腻子在正常的墙面涂覆后,使用年限有限,一般为几年。腻子寿命主要是受环境变化影响较大,温湿度的变化会引起腻子脱层,脱落等,甚至开裂,鼓包等现象。常用的室内腻子遇水或处于潮湿环境时经常产生霉斑和长菌的现象,不但影响腻子的质量和美观,还降低腻子的使用寿命。尽管有文献CN 108707362 A 采用灰钙、双飞粉、羟丙基甲基纤维素、聚乙烯醇、可再分散胶粉和淀粉醚制备了耐水腻子。文献CN 111607280A通过白水泥、淀粉醚、PVA、灰钙、重钙、HPMC、杀菌防腐剂、分散剂、纳米纤维、玻璃纤维和滑石粉制备了底层耐水腻子粉。上述文献采用常规材料制备腻子,均未提到采用固体废弃物来制备腻子,而固体废弃物的利用也是建筑材料中的一大方向。
随着建筑材料的不断发展,各砂浆企业或相关科研院所均配备大量的实验室,以研发和满足不同场所建材的应用。在研发和试验的过程中会产生大量的湿淤泥,这些废弃料中含有丰富的资源,具有一定的利用价值,但颗粒分布比较宽,从微米尺寸颗粒的细粉到毫米级的砂子。当这些淤泥处理不当时,一方面造成管道堵塞,另一方面可能会污染地下水,解决这些问题迫在眉睫。
针对这些问题,耐水腻子应运而生,耐水腻子具有更好的粘接强度和抗潮湿环境的能力,还能实现利用固体废弃物解决环境污染的问题。
发明内容
针对现有技术中存在的问题,本发明设计的目的在于提供一种环境污染少,变废为宝的耐水的室内面层腻子及其制备方法。
本发明通过以下技术方案加以实现:
所述的一种耐水的室内面层腻子,其特征在于由以下重量份的组分组成,活化处理的淤泥5-20%,白水泥0-30%,重钙40-60%,膨润土0-5%,灰钙0-20%,聚乙烯醇0.1-1%,纤维素醚0.1-1%,防腐剂0.1-0.5%。
所述的一种耐水的室内面层腻子,其特征在于所述活化处理的淤泥采用以下方法制备:
1)淤泥过滤:将砂浆厂实验室产生的淤泥进行三级过滤,取第三次过滤的淤泥进行水洗,直至所洗出来的水为中性为止,得到水洗后的淤泥;
2)淤泥烘干:将步骤1)水洗后的淤泥进行烘干,温度为80-105℃,烘干至恒重,然后磨细成粉状,并全部通过0.315mm的方孔筛,得到三级淤泥;
3)淤泥焙烧:将步骤2)制得的三级淤泥在一定的温度下进行焙烧,并进行保温,然后急冷处理,使其具有一定的活性,得到焙烧淤泥粉末;
4)淤泥养护:将步骤3)制得的焙烧淤泥粉末进行微波养护处理,即得活化处理的淤泥。
所述的一种耐水的室内面层腻子,其特征在于水泥为32.5等级、42.5等级的白色硅酸盐水泥中的一种;所述重钙为300-800目的重钙;所述膨润土为钠基膨润土;所述灰钙为325-425目的灰钙。
所述的一种耐水的室内面层腻子,其特征在于所述聚乙烯醇为醇解度80%,分子量6000-8000的聚乙烯醇。
所述的一种耐水的室内面层腻子,其特征在于所述纤维素醚为黏度40000-75000mPa.s的羟乙基甲基纤维素、羟丙基甲基纤维素中的一种。
所述的一种耐水的室内面层腻子,其特征在于所述防腐剂为无机粉末防腐剂。
所述的一种耐水的室内面层腻子,其特征在于步骤3)中焙烧温度为650-700℃,保温时间为2-4h。
所述的一种耐水的室内面层腻子,其特征在于步骤4)中微波功率为560-700W,微波处理时间为5-10min。
所述的一种耐水的室内面层腻子的制备方法,其特征在于制备方法如下:首先将配方量白水泥、重钙、膨润土、灰钙、纤维素醚和防腐剂先进行高速搅拌,使其均匀混合,然后加入配方量的活化处理的淤泥进行低速搅拌混合,即可得到粉料;将聚乙烯醇加入到适量的水,在20-25℃的温度条件下低速搅拌,持续3-5min,然后静置排气1-2h,进行二次低速搅拌,持续搅拌3-5min,使其充分溶解,放置1-2h,最后加入粉料和剩余的水一起搅拌均匀即可使用。
所述的一种室内面层腻子的制备方法,其特征在于聚乙烯醇与水的质量比为1:30-100,所述粉料与剩余水的比例为1:0.4-0.7。
与现有技术相比,本发明具有以下有益效果:
1)本发明配方合理,制定工艺简单,通过焙烧和微波养护处理淤泥,制备活化处理的淤泥,减少了环境污染,充分利用固体废弃物,优化了环境;
2)通过活化处理的淤泥和聚乙烯醇复掺技术,改善腻子的耐水性能,使耐水腻子的拉伸粘结强度高,体积稳定性好,耐水效果好,浸水后无气泡脱落现象;
3)添加了防腐剂,使耐水腻子在潮湿环境下不宜长霉斑,延长了腻子的使用寿命。
具体实施方式
为了更好地理解本发明,下面通过实施例对本发明作进一步说明,实施例只用于解释本发明,不会对本发明构成任何的限定。本发明有效调节各组分的用量及制备工艺,制得的耐水的室内面层腻子。
实施例1
一种耐水的室内面层腻子,以重量份计,包括以下组分:
活化处理的淤泥5%;32.5白水泥10%;800目重钙60%;纳基膨润土4%;325目的灰钙20%;PVA聚乙烯醇0.5%;75000mPa.s羟丙基甲基纤维素0.4%;防腐剂0.1%。
其中,活化处理的淤泥采用以下方法制备:1)淤泥过滤:首先将砂浆厂实验室产生的淤泥进行三级过滤,取第三次过滤的淤泥进行水洗,直至中性为止,得到水洗后的淤泥;2)过滤淤泥烘干:将水洗后的淤泥进行烘干,温度为105℃,烘干至恒重,然后磨细成粉状,并全部通过0.315mm的方孔筛,即可得到三级淤泥;3)淤泥焙烧:将三级淤泥在650℃下进行焙烧,并保温2h,然后急冷处理,使其具有一定的活性,得到焙烧淤泥;4)微波养护处理得活化处理的淤泥:将焙烧淤泥粉末进行微波养护处理,微波功率为700W,微波养护5min,即得活化处理的淤泥。
该耐水的室内面层腻子的制备方法为:首先将白水泥、重钙、膨润土、灰钙、纤维素醚和防腐剂先进行高速搅拌,使其均匀混合,然后加入活化处理的淤泥进行低速搅拌混合,即可得到粉料。将聚乙烯醇加入到适量的水,在20-25℃低速搅拌,持续3-5min,然后静置排气1-2h,进行二次低速搅拌,持续搅拌3-5min,使其充分溶解,放置1-2h,最后加入粉料和剩余的水一起搅拌均匀即可使用。
实施例2
一种耐水的室内面层腻子,以重量份计,包括以下组分:
活化处理的淤泥15%;32.5白水泥10%;800目重钙50%;纳基膨润土4%;325目的灰钙20%;PVA聚乙烯醇0.5%;75000mPa.s羟丙基甲基纤维素0.4%;防腐剂0.1%。
其中,活化处理的淤泥采用以下方法制备:1)淤泥过滤:首先将砂浆厂实验室产生的淤泥进行三级过滤,取第三次过滤的淤泥进行水洗,直至中性为止,得到水洗后的淤泥;2)过滤淤泥烘干:将水洗后的淤泥进行烘干,温度为105℃,烘干至恒重,然后磨细成粉状,并全部通过0.315mm的方孔筛,即可得到三级淤泥;3)淤泥焙烧:将三级淤泥在650℃下进行焙烧,并保温2h,然后急冷处理,使其具有一定的活性,得到焙烧淤泥;4)微波养护处理得活化处理的淤泥:将焙烧淤泥粉末进行微波养护处理,微波功率为700W,微波养护5min,即得活化处理的淤泥。
该耐水的室内面层腻子的制备方法同实施例1。
实施例3
一种耐水的室内面层腻子,以重量份计,包括以下组分:
活化处理的淤泥15%;32.5白水泥10%;800目重钙50%;纳基膨润土4.4%;325目的灰钙20%;PVA聚乙烯醇0.3%;75000mPa.s羟丙基甲基纤维素0.2%;防腐剂0.1%。
其中,所述活化处理的淤泥采用以下方法制备:1)淤泥过滤:首先将砂浆厂实验室产生的淤泥进行三级过滤,取第三次过滤的淤泥进行水洗,直至中性为止,得到水洗后的淤泥;2)过滤淤泥烘干:将水洗后的淤泥进行烘干,温度为105℃,烘干至恒重,然后磨细成粉状,并全部通过0.315mm的方孔筛,即可得到三级淤泥;3)淤泥焙烧:将三级淤泥在650℃下进行焙烧,并保温2h,然后急冷处理,使其具有一定的活性,得到焙烧淤泥;4)微波养护处理得活化处理的淤泥:将焙烧淤泥粉末进行微波养护处理,微波功率为700W,微波养护5min,即得活化处理的淤泥。
该耐水的室内面层腻子的制备方法同实施例1。
实施例4
一种耐水的室内面层腻子,以重量份计,包括以下组分:
活化处理的淤泥20%;32.5的白水泥15%;800目重钙60%;纳基膨润土4.4%;PVA聚乙烯醇0.10%;75000mPa.s羟丙基甲基纤维素0.4%;防腐剂0.1%。
其中,所述活化处理的淤泥采用以下方法制备:1)淤泥过滤:首先将砂浆厂实验室产生的淤泥进行三级过滤,取第三次过滤的淤泥进行水洗,直至中性为止,得到水洗后的淤泥;2)过滤淤泥烘干:将水洗后的淤泥进行烘干,温度为105℃,烘干至恒重,然后磨细成粉状,并全部通过0.315mm的方孔筛,即可得到三级淤泥;3)淤泥焙烧:将三级淤泥在650℃下进行焙烧,并保温2h,然后急冷处理,使其具有一定的活性,得到焙烧淤泥;4)微波养护处理得活化处理的淤泥:将焙烧淤泥粉末进行微波养护处理,微波功率为700W,微波养护5min,即得活化处理的淤泥。
该耐水的室内面层腻子的制备方法同实施例1。
对比例1
腻子中不添加活化处理的淤泥,其余条件和实施例4相同。
对比例2
腻子中添加简单过滤筛分后的淤泥,且不进行活化处理,其余条件和实施例4相同。
下面对本发明制得的一种耐水的室内面层腻子进行性能测试,测试结果如表1所示。
表1
从表1测试结果可以看出,本发明制得的耐水的室内面层腻子无泌水现象,拉伸粘结强度高,尤其是浸水粘结强度高,耐磨性和施工性良好,保水性优异。而对比例1样品的浸水后拉伸粘结强度偏低,尤其是对比例2中采用的淤泥仅做了简单的过滤筛分,未作活化处理,使腻子的浸水拉伸黏接强度较低,不足0.3MPa。
以上所述,仅为本发明较佳的具体实施方式,但本发明的保护范围并不局限于此。任何熟悉本技术领域的技术人员在本发明揭示的技术范围内,根据本发明的技术方案及其发明构思加以等同替换或改变,都应涵盖在本发明的保护范围之内。
Claims (10)
1.一种耐水的室内面层腻子,其特征在于由以下重量份的组分组成,活化处理的淤泥5-20%,白水泥0-30%,重钙40-60%,膨润土0-5%,灰钙0-20%,聚乙烯醇0.1-1%,纤维素醚0.1-1%,防腐剂0.1-0.5%。
2.如权利要求1所述的一种耐水的室内面层腻子,其特征在于所述活化处理的淤泥采用以下方法制备:
1)淤泥过滤:将砂浆厂实验室产生的淤泥进行三级过滤,取第三次过滤的淤泥进行水洗,直至所洗出来的水为中性为止,得到水洗后的淤泥;
2)淤泥烘干:将步骤1)水洗后的淤泥进行烘干,温度为80-105℃,烘干至恒重,然后磨细成粉状,并全部通过0.315mm的方孔筛,得到三级淤泥;
3)淤泥焙烧:将步骤2)制得的三级淤泥在一定的温度下进行焙烧,并进行保温,然后急冷处理,使其具有一定的活性,得到焙烧淤泥粉末;
4)淤泥养护:将步骤3)制得的焙烧淤泥粉末进行微波养护处理,即得活化处理的淤泥。
3.如权利要求1所述的一种耐水的室内面层腻子,其特征在于水泥为32.5等级、42.5等级的白色硅酸盐水泥中的一种;所述重钙为300-800目的重钙;所述膨润土为钠基膨润土;所述灰钙为325-425目的灰钙。
4.如权利要求1所述的一种耐水的室内面层腻子,其特征在于所述聚乙烯醇为醇解度80%,分子量6000-8000的聚乙烯醇。
5.如权利要求1所述的一种耐水的室内面层腻子,其特征在于所述纤维素醚为黏度40000-75000mPa.s的羟乙基甲基纤维素、羟丙基甲基纤维素中的一种。
6.如权利要求1所述的一种耐水的室内面层腻子,其特征在于所述防腐剂为无机粉末防腐剂。
7.如权利要求2所述的一种耐水的室内面层腻子,其特征在于步骤3)中焙烧温度为650-700℃,保温时间为2-4h。
8.如权利要求2所述的一种耐水的室内面层腻子,其特征在于步骤4)中微波功率为560-700W,微波处理时间为5-10min。
9.一种耐水的室内面层腻子的制备方法,其特征在于制备方法如下:首先将配方量白水泥、重钙、膨润土、灰钙、纤维素醚和防腐剂先进行高速搅拌,使其均匀混合,然后加入配方量的活化处理的淤泥进行低速搅拌混合,即可得到粉料;将聚乙烯醇加入到适量的水,在20-25℃的温度条件下低速搅拌,持续3-5min,然后静置排气1-2h,进行二次低速搅拌,持续搅拌3-5min,使其充分溶解,放置1-2h,最后加入粉料和剩余的水一起搅拌均匀即可使用。
10.如权利要求9所述的一种室内面层腻子的制备方法,其特征在于聚乙烯醇与水的质量比为1:30-100,所述粉料与剩余水的比例为1:0.4-0.7。