CN112795320A - Waterproof lining material, waterproof fabric and waterproof treatment method of fabric - Google Patents
Waterproof lining material, waterproof fabric and waterproof treatment method of fabric Download PDFInfo
- Publication number
- CN112795320A CN112795320A CN202011115141.XA CN202011115141A CN112795320A CN 112795320 A CN112795320 A CN 112795320A CN 202011115141 A CN202011115141 A CN 202011115141A CN 112795320 A CN112795320 A CN 112795320A
- Authority
- CN
- China
- Prior art keywords
- waterproof
- fabric
- lining material
- melt adhesive
- hot melt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a waterproof lining material, which comprises waterproof cloth, wherein a hot melt adhesive layer is attached to the outer side surface of the waterproof cloth, and the hot melt adhesive film is microPunching to form micropores with density of 7-12 ten thousand/M2And the outer side surface of the hot melt adhesive film is covered with a paper pasting layer. The invention also discloses a waterproof fabric, and the waterproof lining material is attached to the inner side of the outer fabric after the paper-attached layer is uncovered, and is pressed and bonded to form the waterproof fabric. The invention also discloses a waterproof treatment method of the fabric. The waterproof lining material can be directly attached and ironed on the inner side of the fabric on the outer side after the paper layer is uncovered, various fabrics can obtain excellent waterproof effects only by adopting a simpler and more convenient method, and the waterproof lining material has excellent air permeability while having the waterproof effect.
Description
Technical Field
The invention relates to the field of fabric waterproof treatment, in particular to a waterproof lining material which can be used for clothes fabrics or shoe fabrics and is mainly used for shoe fabrics. The invention also relates to a waterproof fabric made of the waterproof lining material. The invention also relates to a waterproof treatment method of the fabric.
Background
The traditional waterproof fabric for the shoes comprises an outer woven fabric layer and an inner woven fabric layer, wherein the outer woven fabric layer and the inner woven fabric layer are connected into a whole through knot yarns, one of the outer woven fabric layer and the inner woven fabric layer is woven by high-elasticity silk yarns, the other one of the outer woven fabric layer and the inner woven fabric layer is woven by low-elasticity and low-ductility silk yarns, and the silk yarns forming the outer woven fabric layer and the inner woven fabric layer are adhered with a waterproof material layer. The waterproof fabric for the shoes can be directly used as a shoe fabric, other surface layers do not need to be attached, but the waterproof fabric also has the problem that the application range of the waterproof technology has certain limitation, and the waterproof fabric is complex in processing method and inconvenient to use at any time.
Disclosure of Invention
The invention aims to provide a waterproof lining material which can be directly adhered and ironed on various fabrics to form waterproof fabrics. The technical problem to be solved by the invention also comprises providing a waterproof fabric made of the waterproof lining material. The technical problem to be solved by the invention also comprises providing a waterproof treatment method of the fabric.
Therefore, the waterproof lining material provided by the invention comprises waterproof cloth, wherein the hot melt adhesive layer is attached to the outer side surface of the waterproof cloth, the hot melt adhesive film is subjected to minimally invasive punching, and the density of formed micropores is 7-12 ten thousand/M2And the outer side surface of the hot melt adhesive film is covered with a paper pasting layer.
Preferably, the yarns forming the waterproof cloth adopt 10-15% of spandex and 85-90% of terylene by mass.
Preferably, spandex is adopted as the yarn in the high elasticity direction of the waterproof cloth, and terylene is adopted as the yarn in the low elasticity direction of the waterproof cloth.
Preferably, the thickness of the hot melt adhesive film is 0.05mm-0.09 mm.
According to the waterproof fabric provided by the invention, the waterproof lining material is attached to the inner side of the outer fabric after the paper pasting layer is uncovered, and is pressed and bonded.
The invention provides a waterproof treatment method of fabric, which comprises the following steps:
A. adding a penetrant into warm water at the temperature of 30-40 ℃, uniformly stirring, adding 2-3 g of penetrant into each kilogram of warm water according to the mass, placing the fabric layer into the warm water, cleaning and drying;
B. adding a cross-linking agent, a waterproof agent and glacial acetic acid into warm water at the temperature of 35-50 ℃, uniformly stirring, wherein the cross-linking agent and the waterproof agent are added firstly, the glacial acetic acid is added finally, the mixing amount of the cross-linking agent, the waterproof agent and the glacial acetic acid is that 8-15 g of the cross-linking agent, 80-120 g of the waterproof agent and 3-5 g of the glacial acetic acid are added into warm water per kilogram according to the mass, placing the fabric into a solution for soaking and dewatering, drying at 105 ℃ and 130 ℃ for 120 min, and drying at 170 ℃ and 190 ℃ for 30-60 s.
Preferably, in the step B: and (3) placing the fabric into a solution for soaking and dewatering, and ensuring that the solution accounting for 25-35% of the fabric mass remains on the fabric.
Preferably, the facing comprises a waterproof inner facing and/or an outer facing.
The invention provides the following technical effects:
the waterproof lining material can be directly attached and ironed on the inner side of the fabric on the outer side after the paper layer is uncovered, various fabrics can obtain excellent waterproof effects only by adopting a simpler and more convenient method, and the waterproof lining material has excellent air permeability while having the waterproof effect.
Detailed Description
The present invention will be described in further detail with reference to examples.
The waterproof lining material provided by the invention comprises waterproof cloth, a hot melt adhesive layer is attached to the outer side surface of the waterproof cloth,the hot melt adhesive film is subjected to minimally invasive punching, the thickness of the hot melt adhesive film is 0.05mm-0.09mm, most of the hot melt adhesive films are selected to be 0.05mm or 0.07mm in actual operation, and the density of formed micropores is 7-12 ten thousand/M2And the outer side surface of the hot melt adhesive film is covered with a paper pasting layer. The yarn for forming the waterproof cloth adopts 10-15% of spandex and 85-90% of polyester fiber by mass, the configuration modes comprise 12% of spandex and 88% of polyester fiber or 13.5% of spandex and 86.5% of polyester fiber, the spandex is adopted as the yarn in the high elasticity direction of the waterproof cloth, and the polyester fiber is adopted as the yarn in the low elasticity direction of the waterproof cloth.
The invention also provides a waterproof fabric, and the waterproof lining material is attached to the inner side of the outer fabric after the paper-attached layer is uncovered, and is pressed and bonded to form the waterproof fabric.
The invention provides a waterproof treatment method of a fabric, the fabric suitable for the waterproof treatment method comprises a waterproof lining material and/or an outer side fabric, and the method comprises the following steps:
A. adding a penetrant into warm water at the temperature of 30-40 ℃ (30 or 35 ℃ is mostly selected in actual operation), uniformly stirring, adding 2-3 g of penetrant into each kilogram of warm water according to the mass, adding 2.5 g or 2.3 g into the warm water when no kilogram exists in actual operation, and putting the fabric layer into the warm water for cleaning and drying;
B. adding a cross-linking agent, a waterproof agent and glacial acetic acid into warm water at the temperature of 35-50 ℃ (40 or 45 ℃ is mostly selected in actual operation) and uniformly stirring, wherein the cross-linking agent and the waterproof agent are added firstly, the glacial acetic acid is added finally, the mixing amount of the cross-linking agent, the waterproof agent and the glacial acetic acid is calculated according to the mass by adding 8-15 g of the cross-linking agent, 80-120 g of the waterproof agent and 3-5 g of the glacial acetic acid into each kilogram of the warm water, 9 g or 13 g of the cross-linking agent, 92 g or 103 g of the waterproof agent and 3.2 g or 4.5 g of the glacial acetic acid into each kilogram of the warm water in actual operation, placing the fabric into a solution for soaking and dehydration, ensuring that the solution with the mass of 25-35% of the fabric is remained on the fabric, then drying at 105 ℃ and 130 ℃ for 240 minutes, and finally drying at 170 ℃ and 190 ℃ for 30-60 seconds, the temperature treatment in actual operation may be: drying at 110 or 120 ℃ for 125 or 210 minutes, and finally at 178 and 182 ℃ for 37 or 48 seconds.
The above description is only a preferred embodiment of the present invention, and the protection scope of the present invention is not limited to the above embodiments, and all technical solutions belonging to the idea of the present invention belong to the protection scope of the present invention. It should be noted that modifications and embellishments within the scope of the invention may occur to those skilled in the art without departing from the principle of the invention, and are considered to be within the scope of the invention.
Claims (8)
1. The waterproof lining material is characterized in that: comprises a waterproof cloth, a hot melt adhesive layer is attached to the outer side surface of the waterproof cloth, the hot melt adhesive film is subjected to minimally invasive punching, and the density of formed micropores is 7-12 ten thousand/M2And the outer side surface of the hot melt adhesive film is covered with a paper pasting layer.
2. The waterproof lining material of claim 1, wherein: the yarns for forming the waterproof cloth adopt 10-15% of spandex and 85-90% of terylene by mass.
3. The waterproof lining material of claim 2, wherein: the high elasticity direction of the waterproof cloth adopts spandex as yarn, and the low elasticity direction of the waterproof cloth adopts terylene as yarn.
4. The waterproof lining material of claim 1, 2 or 3, wherein: the thickness of the hot melt adhesive film is 0.05mm-0.09 mm.
5. A waterproof fabric is characterized in that: the waterproof lining material is attached to the inner side of the outer fabric after the paper pasting layer is uncovered, and is pressed and bonded in a hot pressing mode.
6. A waterproof treatment method of fabric is characterized by comprising the following steps: the method comprises the following steps:
A. adding a penetrant into warm water at the temperature of 30-40 ℃, uniformly stirring, adding 2-3 g of penetrant into each kilogram of warm water according to the mass, placing the fabric layer into the warm water, cleaning and drying;
B. adding a cross-linking agent, a waterproof agent and glacial acetic acid into warm water at the temperature of 35-50 ℃, uniformly stirring, wherein the cross-linking agent and the waterproof agent are added firstly, the glacial acetic acid is added finally, the mixing amount of the cross-linking agent, the waterproof agent and the glacial acetic acid is that 8-15 g of the cross-linking agent, 80-120 g of the waterproof agent and 3-5 g of the glacial acetic acid are added into warm water per kilogram according to the mass, placing the fabric into a solution for soaking and dewatering, drying at 105 ℃ and 130 ℃ for 120 min, and drying at 170 ℃ and 190 ℃ for 30-60 s.
7. The waterproof treatment method of the waterproof fabric according to claim 6, characterized in that: in the step B: and (3) placing the fabric into a solution for soaking and dewatering, and ensuring that the solution accounting for 25-35% of the fabric mass remains on the fabric.
8. The waterproof treatment method of the waterproof fabric according to claim 6 or 7, characterized in that: the fabric comprises a waterproof lining material and/or an outer side fabric.