CN112779793A - Preparation method of polyester coating mesh fabric - Google Patents
Preparation method of polyester coating mesh fabric Download PDFInfo
- Publication number
- CN112779793A CN112779793A CN202011592531.6A CN202011592531A CN112779793A CN 112779793 A CN112779793 A CN 112779793A CN 202011592531 A CN202011592531 A CN 202011592531A CN 112779793 A CN112779793 A CN 112779793A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyester
- glass fiber
- cloth
- raw materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of polyester coating mesh cloth, which comprises the following steps: step one, selecting polyester yarn raw materials: the raw materials are selected from the following components in parts by weight: 5-9 parts of ammonium polyphosphate, 12-13 parts of alkali lignin, 6-9 parts of an adhesive, 7-10 parts of polybutene and 5-9 parts of tea polyphenol; step two, introducing the selected raw materials in the step one into a stirring mechanism, injecting polyester molten liquid, and uniformly mixing to obtain mixed molten liquid; selecting glass fiber yarns as base materials to weave glass fiber gridding cloth; and step four, putting the glass fiber mesh cloth obtained in the step three into a glue dipping barrel, and coating the mixed molten liquid to finish glue dipping.
Description
Technical Field
The invention relates to the field of grid cloth related products, in particular to a preparation method of polyester coating grid cloth.
Background
The mesh fabric, as the name implies, is a fabric with a mesh structure, and is widely applied to the fields of reinforcing materials, fabrics, cushions and the like, for example, when the mesh fabric is used in the field of fabrics, due to the structural characteristics of the fabrics, the fabrics which are not processed by special processes are easy to break, have low ignition points, and are easy to cause dangerous situations such as fire and the like, and when the mesh fabric is used in the field of reinforcing materials, the mesh fabric is required to have physical properties such as stronger tensile strength and breaking strength.
Disclosure of Invention
The invention aims to provide a preparation method of polyester coating mesh fabric, which aims to solve the problems of insufficient strength and difficult quality control in the background technology.
In order to achieve the purpose, the invention provides the following technical scheme: a preparation method of polyester coating mesh cloth comprises the following steps:
step one, selecting polyester yarn raw materials: the raw materials are selected from the following components in parts by weight: 5-9 parts of ammonium polyphosphate, 12-13 parts of alkali lignin, 6-9 parts of an adhesive, 7-10 parts of polybutene and 5-9 parts of tea polyphenol;
step two, introducing the selected raw materials in the step one into a stirring mechanism, injecting polyester molten liquid, and uniformly mixing to obtain mixed molten liquid;
selecting glass fiber yarns as base materials to weave glass fiber gridding cloth;
step four, putting the glass fiber mesh cloth obtained in the step three into a glue dipping barrel, and coating the mixed molten liquid to finish glue dipping;
step five, guiding the cloth after gum dipping into a drying box for drying;
and step six, finishing and packaging the dried cloth.
Preferably, in the first step, 5 parts of ammonium polyphosphate, 12 parts of alkali lignin, 6 parts of adhesive, 7 parts of polybutene and 5 parts of tea polyphenol are used.
Preferably, in the second step, the mixing temperature is 80-90 ℃.
Preferably, the drying temperature in the sixth step is preferably 140-150 ℃.
Compared with the prior art, the invention has the beneficial effects that:
according to the preparation method of the polyester coating mesh fabric, the tea polyphenol has strong oxidation resistance and flame retardance, the flame retardance is further improved, the polybutylene enables the ammonium polyphosphate and the polyester melt to be fully and uniformly mixed, the common use of the alkali lignin and the adhesive is beneficial to improving the fracture resistance of the polyester, the sealing performance is strong, the glass fiber is selected as a base material, the high-temperature resistance is excellent, and the good temperature resistance and impact resistance are realized.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments.
The embodiment provided by the invention comprises the following steps: a preparation method of polyester coating mesh cloth comprises the following steps:
step one, selecting polyester yarn raw materials: the raw materials are selected from the following components in parts by weight: 5-9 parts of ammonium polyphosphate, 12-13 parts of alkali lignin, 6-9 parts of an adhesive, 7-10 parts of polybutene and 5-9 parts of tea polyphenol;
step two, introducing the selected raw materials in the step one into a stirring mechanism, injecting polyester molten liquid, and uniformly mixing to obtain mixed molten liquid;
selecting glass fiber yarns as base materials to weave glass fiber gridding cloth;
step four, putting the glass fiber mesh cloth obtained in the step three into a glue dipping barrel, and coating the mixed molten liquid to finish glue dipping;
step five, guiding the cloth after gum dipping into a drying box for drying;
and step six, finishing and packaging the dried cloth.
Further, in the first step, 5 parts of ammonium polyphosphate, 12 parts of alkali lignin, 6 parts of adhesive, 7 parts of polybutene and 5 parts of tea polyphenol.
Further, in the second step, the mixing temperature is 80-90 ℃.
Further, the drying temperature in the sixth step is preferably 140-.
In this embodiment: the tea polyphenol has strong oxidation resistance and flame retardance, the flame retardance is further improved, the polybutylene enables the ammonium polyphosphate and the polyester melt to be fully and uniformly mixed, the common use of the alkali lignin and the adhesive is beneficial to improving the fracture strength of the polyester, the sealing performance is strong, the glass fiber is selected as the base material, the high-temperature resistance is excellent, and the good temperature resistance and impact resistance are realized.
It will be evident to those skilled in the art that the invention is not limited to the details of the foregoing illustrative embodiments, and that the present invention may be embodied in other specific forms without departing from the spirit or essential attributes thereof. The present embodiments are therefore to be considered in all respects as illustrative and not restrictive, the scope of the invention being indicated by the appended claims rather than by the foregoing description, and all changes which come within the meaning and range of equivalency of the claims are therefore intended to be embraced therein.
Claims (4)
1. A preparation method of polyester coating mesh cloth is characterized in that: the method comprises the following steps:
step one, selecting polyester yarn raw materials: the raw materials are selected from the following components in parts by weight: 5-9 parts of ammonium polyphosphate, 12-13 parts of alkali lignin, 6-9 parts of an adhesive, 7-10 parts of polybutene and 5-9 parts of tea polyphenol;
step two, introducing the selected raw materials in the step one into a stirring mechanism, injecting polyester molten liquid, and uniformly mixing to obtain mixed molten liquid;
selecting glass fiber yarns as base materials to weave glass fiber gridding cloth;
step four, putting the glass fiber mesh cloth obtained in the step three into a glue dipping barrel, and coating the mixed molten liquid to finish glue dipping;
step five, guiding the cloth after gum dipping into a drying box for drying;
and step six, finishing and packaging the dried cloth.
2. The method for preparing a polyester coated mesh fabric as claimed in claim 1, wherein: 5 parts of ammonium polyphosphate, 12 parts of alkali lignin, 6 parts of adhesive, 7 parts of polybutene and 5 parts of tea polyphenol in the first step.
3. The method for preparing a polyester coated mesh fabric as claimed in claim 1, wherein: in the second step, the mixing temperature is 80-90 ℃.
4. The method for preparing a polyester coated mesh fabric as claimed in claim 1, wherein: the drying temperature in the sixth step is preferably 140-150 ℃.