CN109315861A - A kind of flame-retardant garment plus material and preparation method thereof - Google Patents
A kind of flame-retardant garment plus material and preparation method thereof Download PDFInfo
- Publication number
- CN109315861A CN109315861A CN201811409289.7A CN201811409289A CN109315861A CN 109315861 A CN109315861 A CN 109315861A CN 201811409289 A CN201811409289 A CN 201811409289A CN 109315861 A CN109315861 A CN 109315861A
- Authority
- CN
- China
- Prior art keywords
- parts
- flame
- retardant
- plus material
- garment plus
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of flame-retardant garment plus material and preparation method thereof, which is made of the raw material of following composition by weight ratio；30-40 parts of flame-retardant acrylic fibre, 20-30 parts of latex, 10-20 parts of polyester resin, 5-15 parts of cumyl peroxide, 2-5 parts of nano antibacterial agent, 2-6 parts of surfactant, 1-3 parts of flame-retardant additive and 3-7 parts of hydroxypropyl PASELLI EASYGEL.Flame-retardant garment plus material of the invention has flame retardant property good, and antibacterial functions power is strong, it is not easy to lead to bacteria breed, comfort is good, the beneficial effect of simple process and low cost.
Description
Technical field
The present invention relates to a kind of dress materials, especially a kind of flame-retardant garment plus material and preparation method thereof.
Background technique
Currently, with people's lives level be continuously improved, clothes be also it is miscellaneous, clothes with fabric production and
At fabric is exactly the material for making clothes.As one of clothes three elements, fabric can not only annotate clothes style and
Characteristic, and directly control the expression effect of the color of clothes, moulding.The noble quality for showing itself is perfect, soft.But
It is to be easy in existing garment material, poor flame retardant properties are easy to be ruined in use, and antibacterial functions power is weak
Lead to bacteria breed, comfort is poor.In view of the above problems, my company develops a kind of flame-retardant garment plus material and preparation method thereof.
Summary of the invention
The object of the present invention is to provide a kind of flame-retardant garment plus materials and preparation method thereof.Flame-resistant garment face of the invention
Material has flame retardant property good, and antibacterial functions power is strong, it is not easy to lead to bacteria breed, comfort is good, the effect of simple process and low cost
Fruit.
Technical solution of the present invention: a kind of flame-retardant garment plus material, the original of the following composition by weight ratio of the flame-retardant garment plus material
Material is made；30-40 parts of flame-retardant acrylic fibre, 20-30 parts of latex, 10-20 parts of polyester resin, 5-15 parts of cumyl peroxide, nanometer
2-5 parts of antibacterial agent, 2-6 parts of surfactant, 1-3 parts of flame-retardant additive and 3-7 parts of hydroxypropyl PASELLI EASYGEL.
In flame-retardant garment plus material above-mentioned, which is made of the raw material of following composition by weight ratio；Fire-retardant nitrile
30-35 parts of synthetic fibre, 25-30 parts of latex, 15-20 parts of polyester resin, 10-15 parts of cumyl peroxide, 4-5 parts of nano antibacterial agent,
2-4 parts of surfactant, 2-3 parts of flame-retardant additive and 3-5 parts of hydroxypropyl PASELLI EASYGEL.
In flame-retardant garment plus material above-mentioned, which is made of the raw material of following composition by weight ratio；Fire-retardant nitrile
33 parts of synthetic fibre, 28 parts of latex, 18 parts of polyester resin, 13 parts of cumyl peroxide, 4 parts of nano antibacterial agent, 3 parts of surfactant,
2 parts and 4 parts of hydroxypropyl PASELLI EASYGEL of flame-retardant additive.
In the preparation method of flame-retardant garment plus material above-mentioned, the preparation method of the flame-retardant garment plus material includes following step
It is rapid:
A, flame-retardant acrylic fibre, latex, polyester resin are carried out heating to be uniformly mixed, obtains A product；
B, cumyl peroxide, nano antibacterial agent, surfactant, flame-retardant additive and hydroxypropyl two will be added in A product to form sediment
Powder phosphate is stirred in high-speed stirring mixer, obtains B product；
C, put product B is put in melt spinning machine, spinning is carried out at 200-250 DEG C, obtains finished product.
In the preparation method of flame-retardant garment plus material above-mentioned, in the step a, the temperature of heating is 80-120 DEG C, mixing
30-50min is stirred using high-speed stirring mixer.
In the preparation method of flame-retardant garment plus material above-mentioned, in the step b, it is stirred 40-60min.
Compared with prior art, flame-retardant garment plus material of the invention has flame retardant property good, and antibacterial functions power is strong, it is not easy to
Lead to bacteria breed, comfort is good, the beneficial effect of simple process and low cost.
Specific embodiment
Below with reference to embodiment, the present invention is further illustrated, but is not intended as the foundation limited the present invention.
The embodiment of the present invention 1: a kind of flame-retardant garment plus material, the raw material of the following composition by weight ratio of the flame-retardant garment plus material
It is made；Flame-retardant acrylic fibre 30kg, latex 20kg, polyester resin 10kg, cumyl peroxide 5kg, nano antibacterial agent 2kg, surface
Activating agent 2kg, flame-retardant additive 1kg and hydroxypropyl PASELLI EASYGEL 3kg.
The preparation method of the flame-retardant garment plus material includes following steps:
A, flame-retardant acrylic fibre, latex, polyester resin are carried out heating to be uniformly mixed, the temperature of heating is 80 DEG C, using high-speed stirred
Mixing machine is stirred 30min, obtains A product；
B, cumyl peroxide, nano antibacterial agent, surfactant, flame-retardant additive and hydroxypropyl two will be added in A product to form sediment
Powder phosphate is stirred 40min in high-speed stirring mixer, obtains B product；
C, put product B is put in melt spinning machine, spinning is carried out at 200 DEG C, obtains finished product.
The embodiment of the present invention 2: a kind of flame-retardant garment plus material, the raw material of the following composition by weight ratio of the flame-retardant garment plus material
It is made；Flame-retardant acrylic fibre 35kg, latex 25kg, polyester resin 15kg, cumyl peroxide 10kg, nano antibacterial agent 3kg, surface
Activating agent 4kg, flame-retardant additive 2kg and hydroxypropyl PASELLI EASYGEL 4kg.
The preparation method of the flame-retardant garment plus material includes following steps:
A, flame-retardant acrylic fibre, latex, polyester resin are carried out heating to be uniformly mixed, the temperature of heating is 100 DEG C, using high-speed stirred
Mixing machine is stirred 40min, obtains A product；
B, cumyl peroxide, nano antibacterial agent, surfactant, flame-retardant additive and hydroxypropyl two will be added in A product to form sediment
Powder phosphate is stirred 50min in high-speed stirring mixer, obtains B product；
C, put product B is put in melt spinning machine, spinning is carried out at 220 DEG C, obtains finished product.
The embodiment of the present invention 3: a kind of flame-retardant garment plus material, the raw material of the following composition by weight ratio of the flame-retardant garment plus material
It is made；Flame-retardant acrylic fibre 33kg, latex 28kg, polyester resin 18kg, cumyl peroxide 13kg, nano antibacterial agent 4kg, surface
Activating agent 3kg, flame-retardant additive 2kg and hydroxypropyl PASELLI EASYGEL 4kg.
The preparation method of the flame-retardant garment plus material includes following steps:
A, flame-retardant acrylic fibre, latex, polyester resin are carried out heating to be uniformly mixed, the temperature of heating is 110 DEG C, using high-speed stirred
Mixing machine is stirred 40min, obtains A product；
B, cumyl peroxide, nano antibacterial agent, surfactant, flame-retardant additive and hydroxypropyl two will be added in A product to form sediment
Powder phosphate is stirred 55min in high-speed stirring mixer, obtains B product；
C, put product B is put in melt spinning machine, spinning is carried out at 240 DEG C, obtains finished product.
The embodiment of the present invention 4: a kind of flame-retardant garment plus material, the raw material of the following composition by weight ratio of the flame-retardant garment plus material
It is made；Flame-retardant acrylic fibre 40kg, latex 30kg, polyester resin 20kg, cumyl peroxide 15kg, nano antibacterial agent 5kg, surface
Activating agent 6kg, flame-retardant additive 3kg and hydroxypropyl PASELLI EASYGEL 7kg.
The preparation method of the flame-retardant garment plus material includes following steps:
A, flame-retardant acrylic fibre, latex, polyester resin are carried out heating to be uniformly mixed, the temperature of heating is 120 DEG C, using high-speed stirred
Mixing machine is stirred 50min, obtains A product；
B, cumyl peroxide, nano antibacterial agent, surfactant, flame-retardant additive and hydroxypropyl two will be added in A product to form sediment
Powder phosphate is stirred 60min in high-speed stirring mixer, obtains B product；
C, put product B is put in melt spinning machine, spinning is carried out at 250 DEG C, obtains finished product.
Claims (6)
1. a kind of flame-retardant garment plus material, it is characterised in that: the flame-retardant garment plus material is made of the raw material of following composition by weight ratio；Resistance
Fire acrylic fibers 30-40 parts, 20-30 parts of latex, 10-20 parts of polyester resin, 5-15 parts of cumyl peroxide, nano antibacterial agent 2-5
Part, 2-6 parts of surfactant, 1-3 parts of flame-retardant additive and 3-7 parts of hydroxypropyl PASELLI EASYGEL.
2. flame-retardant garment plus material according to claim 1, it is characterised in that: the following composition by weight of the flame-retardant garment plus material
The raw material of ratio is made；30-35 parts of flame-retardant acrylic fibre, 25-30 parts of latex, 15-20 parts of polyester resin, cumyl peroxide 10-15
Part, 4-5 parts of nano antibacterial agent, 2-4 parts of surfactant, 2-3 parts of flame-retardant additive and 3-5 parts of hydroxypropyl PASELLI EASYGEL.
3. flame-retardant garment plus material according to claim 2, it is characterised in that: the following composition by weight of the flame-retardant garment plus material
The raw material of ratio is made；33 parts of flame-retardant acrylic fibre, 28 parts of latex, 18 parts of polyester resin, 13 parts of cumyl peroxide, nano antibacterial agent
4 parts, 3 parts of surfactant, 2 parts of flame-retardant additive and 4 parts of hydroxypropyl PASELLI EASYGEL.
4. a kind of preparation method of the flame-retardant garment plus material as described in any one of claim 1-3, it is characterised in that: the resistance
The preparation method for firing garment material includes following steps:
A, flame-retardant acrylic fibre, latex, polyester resin are carried out heating to be uniformly mixed, obtains A product；
B, cumyl peroxide, nano antibacterial agent, surfactant, flame-retardant additive and hydroxypropyl two will be added in A product to form sediment
Powder phosphate is stirred in high-speed stirring mixer, obtains B product；
C, put product B is put in melt spinning machine, spinning is carried out at 200-250 DEG C, obtains finished product.
5. the preparation method of flame-retardant garment plus material as claimed in claim 4, it is characterised in that: in the step a, the temperature of heating
Degree is 80-120 DEG C, and mixing is stirred 30-50min using high-speed stirring mixer.
6. the preparation method of flame-retardant garment plus material as claimed in claim 4, it is characterised in that: in the step b, be stirred
40-60min。