CN112760660A - Cleaning agent for holographic nickel plate and preparation method thereof - Google Patents
Cleaning agent for holographic nickel plate and preparation method thereof Download PDFInfo
- Publication number
- CN112760660A CN112760660A CN202011560497.4A CN202011560497A CN112760660A CN 112760660 A CN112760660 A CN 112760660A CN 202011560497 A CN202011560497 A CN 202011560497A CN 112760660 A CN112760660 A CN 112760660A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- water
- nickel plate
- oxygen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a cleaning agent for a holographic nickel plate, which comprises the following components: 20-50 parts by weight of white water, 5-10 parts by weight of glass water, 5-15 parts by weight of butter oil, 10-20 parts by weight of oxygen-containing mineral water, 2-5 parts by weight of detergent, 5-30 parts by weight of bleaching water, 10-20 parts by weight of hydrochloric acid, 30-70 parts by weight of alcohol and 80-170 parts by weight of diluent; the invention has the advantages that: the cleaning solution prepared by taking the margarine, the oxygen-containing mineral water, the cleaning agent, the bleaching water and the hydrochloric acid as main raw materials can effectively clean residual paint on the nickel plate, the aim of quick drying can be achieved when the cleaning solution is cleaned due to the addition of the ethanol in the mixture, the cleaning solution has high-temperature resistance due to the glass water, and the problems of high temperature resistance, extremely quick volatilization and effective cleaning are effectively solved.
Description
Technical Field
The invention relates to the technical field of cleaning fluid, and particularly relates to a cleaning agent for a holographic nickel plate and a preparation method thereof.
Background
The existing double-pressure seamless transfer film product process is characterized in that a used raw material laser metal nickel plate (working plate) is attached to a plate roller of a molding press by using high-temperature-resistant glue, a precoating film and the nickel plate are laminated, a high-temperature operation laser layer process is carried out, information layer paint on the precoating film is separated out along with the accumulation of the running time of a machine, after the imprinting of a certain meter number, the paint is transferred to the nickel plate to cause the nickel plate to be plugged and blocked, the laser luster is gradually weakened, darkened, laser whitening or blackening and other irregular phenomena are generated, the nickel plate cannot be continuously used, the nickel plate needs to be replaced again, the cost of each nickel plate is about 500 yuan, the working time of 4 hours needs to be consumed under the condition that the nickel plate is successfully completed when the nickel plate is replaced, if abnormal time is generated midway, the consumed time is longer, and the cost is increased more.
Disclosure of Invention
The invention aims to provide the cleaning agent for the holographic nickel plate, which can effectively clean residual paint on the nickel plate, thereby prolonging the service life of the nickel plate and reducing the production cost.
In order to solve the technical problems, the invention is realized by the following technical scheme: a cleaning agent for a holographic nickel plate comprises the following components: 20-50 parts of white water, 5-10 parts of glass water, 5-15 parts of butter oil, 10-20 parts of oxygen-containing mineral water, 2-5 parts of a cleaning agent, 5-30 parts of bleaching water, 10-20 parts of hydrochloric acid, 30-70 parts of alcohol and 80-170 parts of a diluent.
Preferably, the composition comprises the following components: 20 parts by weight of white water, 5 parts by weight of glass water, 5 parts by weight of margarine, 10 parts by weight of oxygen-containing mineral water, 2 parts by weight of detergent, 5 parts by weight of bleaching water, 10 parts by weight of hydrochloric acid, 30 parts by weight of alcohol and 170 parts by weight of diluent.
Preferably, the composition comprises the following components: 50 parts by weight of white water, 10 parts by weight of glass water, 15 parts by weight of margarine, 20 parts by weight of oxygen-containing mineral water, 5 parts by weight of detergent, 30 parts by weight of bleaching water, 20 parts by weight of hydrochloric acid, 70 parts by weight of alcohol and 80 parts by weight of diluent.
Preferably, the composition comprises the following components: 35.73 parts by weight of white water, 7.52 parts by weight of glass water, 10.31 parts by weight of margarine, 15.57 parts by weight of oxygen-containing mineral water, 3.58 parts by weight of detergent, 20.12 parts by weight of bleaching water, 15.74 parts by weight of hydrochloric acid, 44.61 parts by weight of alcohol and 125.95 parts by weight of diluent.
Preferably, the diluent comprises the following components: 50-100 parts of printing ink, 10-20 parts of oxygen-containing mineral water, 10-20 parts of sodium carbonate and 10-30 parts of degreasing agent.
The invention also provides a preparation method of the cleaning agent for the holographic nickel plate, which is used for preparing the cleaning solution for washing the nickel plate, and the preparation method sequentially comprises the following steps:
the method comprises the following steps: putting the white water, the glass water, the margarine, the oxygen-containing mineral water, the cleaning agent, the bleaching water, the hydrochloric acid and the alcohol into a first stirring barrel for stirring for 10-20 min;
step two: putting the printing ink, oxygen-containing mineral water, sodium carbonate and a degreasing agent into a second stirring barrel for stirring for 7-15 min;
step three: and (3) adding the mixture mixed in the step one into the mixture mixed in the step two, and stirring for 10-20 min.
In conclusion, the invention has the advantages that: the cleaning solution is prepared by mixing white water, glass water, margarine, oxygen-containing mineral water, a cleaning agent, bleaching water, hydrochloric acid, alcohol and a diluent, because the main components of the coating remained on the nickel plate are resin, an auxiliary agent and various volatile solvents, the cleaning solution prepared by taking the margarine, the oxygen-containing mineral water, the cleaning agent, the bleaching water and the hydrochloric acid as main raw materials can effectively clean the residual coating on the nickel plate, because the mixture is added with ethanol, the aim of quick drying can be achieved when the cleaning solution is cleaned, in addition, because the ethanol is volatilized at a high speed to cause the ethanol to remain, the white water is added into the mixture, the volatilization speed can be reduced, the slow drying effect is achieved, the glass water is added, the cleaning solution has high temperature resistance, and therefore, the cleaning solution prepared by the invention effectively solves the problems of high temperature resistance and high speed volatilization, effective clear problem, thereby great improvement production efficiency, can directly realize the washing of nickel version on the board through the cleaning solution, it is long to have solved current plate change time, the problem that production efficiency is low, for the cost of current change, can practice thrift the replacement cost that is not less than 200W and the use cost of nickel version every month, great reduction manufacturing cost, and nickel version after the washing can mould 10 ~ 20 ten thousand meters, can only press 4.4 ten thousand meters for current nickel version, the life of nickel version is greatly improved, and finally, the setting of diluent, the realization once dilution after enabling the mixture, make the solidification volume of cleaning solution reduce to below 80 ~ 90%, consequently can realize skin direct contact when wasing, do not produce the operation injury, thereby the security performance when wasing has been improved.
Detailed Description
Example one
A cleaning agent for a holographic nickel plate comprises the following components: 20 parts by weight of white water, 5 parts by weight of glass water, 5 parts by weight of margarine, 10 parts by weight of oxygen-containing mineral water, 2 parts by weight of detergent, 5 parts by weight of bleaching water, 10 parts by weight of hydrochloric acid, 30 parts by weight of alcohol and 170 parts by weight of diluent, wherein the diluent comprises the following components: 100 parts of printing ink, 20 parts of oxygen-containing mineral water, 20 parts of sodium carbonate and 30 parts of degreasing agent.
The cleaning solution is prepared by mixing white water, glass water, margarine, oxygen-containing mineral water, a cleaning agent, bleaching water, hydrochloric acid, alcohol and a diluent, because the main components of the coating remained on the nickel plate are resin, an auxiliary agent and various volatile solvents, the cleaning solution prepared by taking the margarine, the oxygen-containing mineral water, the cleaning agent, the bleaching water and the hydrochloric acid as main raw materials can effectively clean the residual coating on the nickel plate, because the mixture is added with ethanol, the aim of quick drying can be achieved when the cleaning solution is cleaned, in addition, because the ethanol is volatilized at a high speed to cause the ethanol to remain, the white water is added into the mixture, the volatilization speed can be reduced, the slow drying effect is achieved, the glass water is added, the cleaning solution has high temperature resistance, and therefore, the cleaning solution prepared by the invention effectively solves the problems of high temperature resistance and high speed volatilization, effective clear problem, thereby great improvement production efficiency, can directly realize the washing of nickel version on the board through the cleaning solution, it is long to have solved current plate change time, the problem that production efficiency is low, for the cost of current change, can practice thrift the replacement cost that is not less than 200W and the use cost of nickel version every month, great reduction manufacturing cost, and nickel version after the washing can mould 10 ~ 20 ten thousand meters, can only press 4.4 ten thousand meters for current nickel version, the life of nickel version is greatly improved, and finally, the setting of diluent, the realization once dilution after enabling the mixture, make the solidification volume of cleaning solution reduce to below 80 ~ 90%, consequently can realize skin direct contact when wasing, do not produce the operation injury, thereby the security performance when wasing has been improved.
Example two
A cleaning agent for a holographic nickel plate comprises the following components: 50 parts by weight of white water, 10 parts by weight of glass water, 15 parts by weight of margarine, 20 parts by weight of oxygen-containing mineral water, 5 parts by weight of detergent, 30 parts by weight of bleaching water, 20 parts by weight of hydrochloric acid, 70 parts by weight of alcohol and 80 parts by weight of diluent, wherein the diluent comprises the following components: 50 parts of printing ink, 10 parts of oxygen-containing mineral water, 10 parts of sodium carbonate and 10 parts of degreasing agent.
The cleaning solution is prepared by mixing white water, glass water, margarine, oxygen-containing mineral water, a cleaning agent, bleaching water, hydrochloric acid, alcohol and a diluent, because the main components of the coating remained on the nickel plate are resin, an auxiliary agent and various volatile solvents, the cleaning solution prepared by taking the margarine, the oxygen-containing mineral water, the cleaning agent, the bleaching water and the hydrochloric acid as main raw materials can effectively clean the residual coating on the nickel plate, because the mixture is added with ethanol, the aim of quick drying can be achieved when the cleaning solution is cleaned, in addition, because the ethanol is volatilized at a high speed to cause the ethanol to remain, the white water is added into the mixture, the volatilization speed can be reduced, the slow drying effect is achieved, the glass water is added, the cleaning solution has high temperature resistance, and therefore, the cleaning solution prepared by the invention effectively solves the problems of high temperature resistance and high speed volatilization, effective clear problem, thereby great improvement production efficiency, can directly realize the washing of nickel version on the board through the cleaning solution, it is long to have solved current plate change time, the problem that production efficiency is low, for the cost of current change, can practice thrift the replacement cost that is not less than 200W and the use cost of nickel version every month, great reduction manufacturing cost, and nickel version after the washing can mould 10 ~ 20 ten thousand meters, can only press 4.4 ten thousand meters for current nickel version, the life of nickel version is greatly improved, and finally, the setting of diluent, the realization once dilution after enabling the mixture, make the solidification volume of cleaning solution reduce to below 80 ~ 90%, consequently can realize skin direct contact when wasing, do not produce the operation injury, thereby the security performance when wasing has been improved.
EXAMPLE III
A cleaning agent for a holographic nickel plate comprises the following components: 35.73 parts by weight of white water, 7.52 parts by weight of glass water, 10.31 parts by weight of margarine, 15.57 parts by weight of oxygen-containing mineral water, 3.58 parts by weight of detergent, 20.12 parts by weight of bleaching water, 15.74 parts by weight of hydrochloric acid, 44.61 parts by weight of alcohol and 125.95 parts by weight of diluent, wherein the diluent comprises the following components: 75.12 parts of ink, 16.24 parts of oxygen-containing mineral water, 15.38 parts of sodium carbonate and 19.21 parts of degreasing agent.
The cleaning solution is prepared by mixing white water, glass water, margarine, oxygen-containing mineral water, a cleaning agent, bleaching water, hydrochloric acid, alcohol and a diluent, because the main components of the coating remained on the nickel plate are resin, an auxiliary agent and various volatile solvents, the cleaning solution prepared by taking the margarine, the oxygen-containing mineral water, the cleaning agent, the bleaching water and the hydrochloric acid as main raw materials can effectively clean the residual coating on the nickel plate, because the mixture is added with ethanol, the aim of quick drying can be achieved when the cleaning solution is cleaned, in addition, because the ethanol is volatilized at a high speed to cause the ethanol to remain, the white water is added into the mixture, the volatilization speed can be reduced, the slow drying effect is achieved, the glass water is added, the cleaning solution has high temperature resistance, and therefore, the cleaning solution prepared by the invention effectively solves the problems of high temperature resistance and high speed volatilization, effective clear problem, thereby great improvement production efficiency, can directly realize the washing of nickel version on the board through the cleaning solution, it is long to have solved current plate change time, the problem that production efficiency is low, for the cost of current change, can practice thrift the replacement cost that is not less than 200W and the use cost of nickel version every month, great reduction manufacturing cost, and nickel version after the washing can mould 10 ~ 20 ten thousand meters, can only press 4.4 ten thousand meters for current nickel version, the life of nickel version is greatly improved, and finally, the setting of diluent, the realization once dilution after enabling the mixture, make the solidification volume of cleaning solution reduce to below 80 ~ 90%, consequently can realize skin direct contact when wasing, do not produce the operation injury, thereby the security performance when wasing has been improved.
Example four
A preparation method of a cleaning agent for holographic nickel plates is used for preparing the cleaning solution for washing the nickel plates in the first, second and third embodiments, and the preparation method sequentially comprises the following steps:
the method comprises the following steps: putting the white water, the glass water, the margarine, the oxygen-containing mineral water, the cleaning agent, the bleaching water, the hydrochloric acid and the alcohol into a first stirring barrel for stirring for 10-20 min;
step two: putting the printing ink, oxygen-containing mineral water, sodium carbonate and a degreasing agent into a second stirring barrel for stirring for 7-15 min;
step three: and (3) adding the mixture mixed in the step one into the mixture mixed in the step two, and stirring for 10-20 min.
Other embodiments of the present invention than the preferred embodiments described above will be apparent to those skilled in the art from the present invention, and various changes and modifications can be made therein without departing from the spirit of the present invention as defined in the appended claims.
Claims (6)
1. The cleaning agent for the holographic nickel plate is characterized by comprising the following components in parts by weight: comprises the following components: 20-50 parts of white water, 5-10 parts of glass water, 5-15 parts of butter oil, 10-20 parts of oxygen-containing mineral water, 2-5 parts of a cleaning agent, 5-30 parts of bleaching water, 10-20 parts of hydrochloric acid, 30-70 parts of alcohol and 80-170 parts of a diluent.
2. The cleaning agent for the holographic nickel plate as claimed in claim 1, wherein: comprises the following components: 20 parts by weight of white water, 5 parts by weight of glass water, 5 parts by weight of margarine, 10 parts by weight of oxygen-containing mineral water, 2 parts by weight of detergent, 5 parts by weight of bleaching water, 10 parts by weight of hydrochloric acid, 30 parts by weight of alcohol and 170 parts by weight of diluent.
3. The cleaning agent for the holographic nickel plate as claimed in claim 1, wherein: comprises the following components: 50 parts by weight of white water, 10 parts by weight of glass water, 15 parts by weight of margarine, 20 parts by weight of oxygen-containing mineral water, 5 parts by weight of detergent, 30 parts by weight of bleaching water, 20 parts by weight of hydrochloric acid, 70 parts by weight of alcohol and 80 parts by weight of diluent.
4. The cleaning agent for the holographic nickel plate as claimed in claim 1, wherein: comprises the following components: 35.73 parts by weight of white water, 7.52 parts by weight of glass water, 10.31 parts by weight of margarine, 15.57 parts by weight of oxygen-containing mineral water, 3.58 parts by weight of detergent, 20.12 parts by weight of bleaching water, 15.74 parts by weight of hydrochloric acid, 44.61 parts by weight of alcohol and 125.95 parts by weight of diluent.
5. The cleaning agent for holographic nickel plate as claimed in any of claims 1 to 4, wherein: the diluent comprises the following components: 50-100 parts of printing ink, 10-20 parts of oxygen-containing mineral water, 10-20 parts of sodium carbonate and 10-30 parts of degreasing agent.
6. A preparation method of a cleaning agent for a holographic nickel plate is characterized by comprising the following steps: the cleaning solution for nickel plate washing of claim 5, which is prepared by the following steps in sequence:
the method comprises the following steps: putting the white water, the glass water, the margarine, the oxygen-containing mineral water, the cleaning agent, the bleaching water, the hydrochloric acid and the alcohol into a first stirring barrel for stirring for 10-20 min;
step two: putting the printing ink, oxygen-containing mineral water, sodium carbonate and a degreasing agent into a second stirring barrel for stirring for 7-15 min;
step three: and (3) adding the mixture mixed in the step one into the mixture mixed in the step two, and stirring for 10-20 min.