CN112745662A - Creep-resistant ultraviolet-proof wood-plastic material - Google Patents
Creep-resistant ultraviolet-proof wood-plastic material Download PDFInfo
- Publication number
- CN112745662A CN112745662A CN202110056966.7A CN202110056966A CN112745662A CN 112745662 A CN112745662 A CN 112745662A CN 202110056966 A CN202110056966 A CN 202110056966A CN 112745662 A CN112745662 A CN 112745662A
- Authority
- CN
- China
- Prior art keywords
- parts
- creep
- resistant
- ultraviolet
- plastic material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of wood-plastic materials, and particularly relates to a creep-resistant ultraviolet-proof wood-plastic material. The creep-resistant ultraviolet-proof wood-plastic material comprises the following raw materials: 10-20 parts of creep-resistant polyamide, 1.5-3.5 parts of aggregate, 1-5 parts of zinc stearate, 0.1-2 parts of ultraviolet absorbent, 1-5 parts of oil, 1-3 parts of sodium methyl silicate, 0.5-1.5 parts of propylene oxide, 0.1-1.5 parts of antioxidant, 5-10 parts of polypropylene and 5-10 parts of straw. The invention has simple and easily obtained raw materials and can be conveniently produced in batch.
Description
Technical Field
The invention belongs to the field of wood-plastic materials, and particularly relates to a creep-resistant ultraviolet-proof wood-plastic material.
Background
The plastic-wood material, also called wood-plastic composite material, can be understood as a plate or a section bar produced by mainly using plastics (recycled waste plastics such as polypropylene (PP), Polyethylene (PE), polyvinyl chloride (PVC) and the like) as raw materials, mixing the waste plant fibers such as wood flour, rice hull, straw and the like into a new wood material, and then carrying out plastic processing technologies such as extrusion, mould pressing, injection molding and the like. The method is mainly used in industries such as building materials, furniture, logistics packaging and the like.
The board is made by mixing plastic and wood powder according to a certain proportion and then performing hot extrusion molding, and is called as an extruded wood-plastic composite board.
The plastic-wood composite material is a novel environment-friendly building material which appears in recent years, and is just started abroad. The raw materials used by the wood-plastic product can use waste plastics, waste wood, agricultural and forestry straws and other plant fibers as base materials, and do not contain any additional harmful components.
But also can be recycled, so that the product is a novel product which is environment-friendly, energy-saving and resource recycling in the true sense. With the improvement of the attention degree of people to environmental resources, a circular economic development mode taking waste material recovery and resource comprehensive utilization as the core becomes the trend of the world economic development. The resource recycling technology is vigorously developed, and the method has a profound influence on national economic development and environmental sustainable development. The production of wood-plastic composite products by using waste plastics and wood fibers is a good project meeting the requirement.
As the domestic market is still in the beginning stage, the plastic-wood products are not popularized in a large scale in the domestic market. Compared with the North America market, the growth of the wood-plastic composite material and the finished product has a considerable space, the yield of the domestic wood-plastic composite material market is expected to exceed million tons in recent years, the yield exceeds 10 million yuan, and a novel wood-plastic composite product system is formed.
Disclosure of Invention
The invention aims to provide a creep-resistant ultraviolet-proof wood-plastic material.
In order to achieve the purpose, the invention provides a creep-resistant ultraviolet-proof wood-plastic material which comprises the following raw materials:
10-20 parts of creep-resistant polyamide, 1.5-3.5 parts of aggregate, 1-5 parts of zinc stearate, 0.1-2 parts of ultraviolet absorbent, 1-5 parts of oil, 1-3 parts of sodium methyl silicate, 0.5-1.5 parts of propylene oxide, 0.1-1.5 parts of antioxidant, 5-10 parts of polypropylene and 5-10 parts of straw.
Preferably, the creep-resistant ultraviolet-proof wood-plastic material comprises the following raw materials:
12-18 parts of creep-resistant polyamide, 2.0-3.0 parts of aggregate, 1.5-4 parts of zinc stearate, 0.5-1.5 parts of ultraviolet absorbent, 2-4 parts of oil, 1.5-2.5 parts of sodium methyl silicate, 0.8-1.2 parts of propylene oxide, 0.4-1.2 parts of antioxidant, 6-8 parts of polypropylene and 6-8 parts of straw.
Preferably, the weight ratio of the zinc stearate to the sodium methyl silicate is 1.5-4: 2.
preferably, the weight ratio of the aggregate to the oil is 1.5-3.5: 2.5.
preferably, the oil is corn oil.
Preferably, the oil is soybean oil.
Preferably, the antioxidant is antioxidant 1010.
Preferably, the ultraviolet light absorber is UV-P.
Preferably, the aggregate is calcium carbonate.
Preferably, the creep-resistant polyamide is a Suwei IXEF material Ixef 1524 creep-resistant PARA material.
The invention has the beneficial effects that:
the invention has simple and easily obtained raw materials and can be conveniently produced in batch.
Additional features and advantages of the invention will be set forth in the detailed description which follows.
Detailed Description
Preferred embodiments of the present invention will be described in more detail below. While the following describes preferred embodiments of the present invention, it should be understood that the present invention may be embodied in various forms and should not be limited by the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art.
The invention provides a creep-resistant ultraviolet-proof wood-plastic material which comprises the following raw materials:
10-20 parts of creep-resistant polyamide, 1.5-3.5 parts of aggregate, 1-5 parts of zinc stearate, 0.1-2 parts of ultraviolet absorbent, 1-5 parts of oil, 1-3 parts of sodium methyl silicate, 0.5-1.5 parts of propylene oxide, 0.1-1.5 parts of antioxidant, 5-10 parts of polypropylene and 5-10 parts of straw.
According to the invention, in a specific embodiment, the raw material composition of the creep-resistant ultraviolet-proof wood-plastic material comprises the following components:
12-18 parts of creep-resistant polyamide, 2.0-3.0 parts of aggregate, 1.5-4 parts of zinc stearate, 0.5-1.5 parts of ultraviolet absorbent, 2-4 parts of oil, 1.5-2.5 parts of sodium methyl silicate, 0.8-1.2 parts of propylene oxide, 0.4-1.2 parts of antioxidant, 6-8 parts of polypropylene and 6-8 parts of straw.
In a particular embodiment, the weight ratio of zinc stearate to sodium methyl silicate is from 1.5 to 4: 2.
in a particular embodiment, the weight ratio of the aggregate to the oil is 1.5 to 3.5: 2.5.
in a specific embodiment, the oil is corn oil according to the present invention.
In a particular embodiment, according to the present invention, the oil is soybean oil.
In a particular embodiment, according to the present invention, the antioxidant is antioxidant 1010.
In a particular embodiment, according to the present invention, the ultraviolet absorber UV-P.
In a particular embodiment, according to the invention, the aggregate is calcium carbonate.
In a particular embodiment, according to the present invention, the creep resistant polyamide is a threeway IXEF material IXEF 1524 creep resistant PARA material.
Example 1
The embodiment provides a creep-resistant ultraviolet-proof wood-plastic material.
The creep-resistant ultraviolet-proof wood-plastic material comprises the following raw materials:
15 parts of creep-resistant polyamide, 1.5 parts of aggregate, 5 parts of zinc stearate, 0.1 part of ultraviolet absorber, 5 parts of oil, 1 part of sodium methyl silicate, 1.5 parts of propylene oxide, 0.1 part of antioxidant, 10 parts of polypropylene and 5 parts of straw.
Wherein the oil is corn oil; the antioxidant is antioxidant 1010; the ultraviolet absorbent is UV-P; the aggregate is calcium carbonate, and the creep-resistant polyamide is Suwei IXEF material Ixef 1524 creep-resistant PARA material.
Example 2
The embodiment provides a creep-resistant ultraviolet-proof wood-plastic material.
The creep-resistant ultraviolet-proof wood-plastic material comprises the following raw materials:
12 parts of creep-resistant polyamide, 1.5 parts of aggregate, 5 parts of zinc stearate, 0.1 part of ultraviolet absorber, 5 parts of oil, 1 part of sodium methyl silicate, 1.5 parts of propylene oxide, 0.1 part of antioxidant, 10 parts of polypropylene and 5 parts of straw.
Wherein the oil is corn oil; the antioxidant is antioxidant 1010; the ultraviolet absorbent is UV-P; the aggregate is calcium carbonate, and the creep-resistant polyamide is Suwei IXEF material Ixef 1524 creep-resistant PARA material.
Example 3
The embodiment provides a creep-resistant ultraviolet-proof wood-plastic material.
The creep-resistant ultraviolet-proof wood-plastic material comprises the following raw materials:
18 parts of creep-resistant polyamide, 2 parts of aggregate, 5 parts of zinc stearate, 0.1 part of ultraviolet absorber, 5 parts of oil, 1 part of sodium methyl silicate, 1.5 parts of propylene oxide, 0.1 part of antioxidant, 10 parts of polypropylene and 4 parts of straw.
Wherein the oil is soybean oil; the antioxidant is antioxidant 1010; the ultraviolet absorbent is UV-P; the aggregate is calcium carbonate, and the creep-resistant polyamide is Suwei IXEF material Ixef 1524 creep-resistant PARA material.
Having described embodiments of the present invention, the foregoing description is intended to be exemplary, not exhaustive, and not limited to the embodiments disclosed. Many modifications and variations will be apparent to those of ordinary skill in the art without departing from the scope and spirit of the described embodiments.
Claims (10)
1. The creep-resistant ultraviolet-proof wood-plastic material is characterized by comprising the following raw materials:
10-20 parts of creep-resistant polyamide, 1.5-3.5 parts of aggregate, 1-5 parts of zinc stearate, 0.1-2 parts of ultraviolet absorbent, 1-5 parts of oil, 1-3 parts of sodium methyl silicate, 0.5-1.5 parts of propylene oxide, 0.1-1.5 parts of antioxidant, 5-10 parts of polypropylene and 5-10 parts of straw.
2. The creep-resistant ultraviolet-proof wood-plastic material according to claim 1, wherein the raw material composition of the creep-resistant ultraviolet-proof wood-plastic material comprises:
12-18 parts of creep-resistant polyamide, 2.0-3.0 parts of aggregate, 1.5-4 parts of zinc stearate, 0.5-1.5 parts of ultraviolet absorbent, 2-4 parts of oil, 1.5-2.5 parts of sodium methyl silicate, 0.8-1.2 parts of propylene oxide, 0.4-1.2 parts of antioxidant, 6-8 parts of polypropylene and 6-8 parts of straw.
3. The creep-resistant ultraviolet-proof wood-plastic material as claimed in claim 1, wherein the weight ratio of the zinc stearate to the sodium methyl silicate is 1.5-4: 2.
4. the creep-resistant ultraviolet-proof wood-plastic material as claimed in claim 1, wherein the weight ratio of the aggregate to the oil is 1.5-3.5: 2.5.
5. the creep-resistant UV-resistant wood-plastic material according to claim 1, wherein the oil is corn oil.
6. The creep-resistant ultraviolet-proof wood-plastic material according to claim 1, wherein the oil is soybean oil.
7. The creep-resistant ultraviolet-proof wood-plastic material according to claim 1, wherein the antioxidant is antioxidant 1010.
8. The creep-resistant ultraviolet-proof wood-plastic material according to claim 1, wherein the ultraviolet absorber UV-P.
9. The creep-resistant ultraviolet-proof wood-plastic material according to claim 1, wherein the aggregate is calcium carbonate.
10. The creep-resistant UV-resistant wood-plastic material according to claim 1, wherein the creep-resistant polyamide is a Suwei IXEF material Ixef 1524 creep-resistant PARA material.