CN112704594A - 一种快速止血防水敷料贴及其制备方法和应用 - Google Patents
一种快速止血防水敷料贴及其制备方法和应用 Download PDFInfo
- Publication number
- CN112704594A CN112704594A CN202011535541.6A CN202011535541A CN112704594A CN 112704594 A CN112704594 A CN 112704594A CN 202011535541 A CN202011535541 A CN 202011535541A CN 112704594 A CN112704594 A CN 112704594A
- Authority
- CN
- China
- Prior art keywords
- layer
- fiber
- waterproof
- hemostatic
- rapid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种快速止血防水敷料贴及其制备方法和应用，快速止血防水敷料贴包括外层为拒水保护层，防止伤口被水浸渍，保证良好的机械性能；中间层为吸液层，减少血液流失、封闭出血点、防止二次污染；里层为功能层，包括一定配比的蒲公英纤维与竹纤维制得，蒲公英纤维具有消炎杀菌、止血的功效，竹纤维具有天然抗菌、透气的作用，并且由纤维直接制得功能层，不会发生泄漏，三层结构相互配合，使得敷料贴能够同时具有良好的防水、杀菌、以及快速止血的综合效果，可广泛应用于制备快速止血制品中。
Description
技术领域
本发明涉及止血敷料技术领域，更具体地，涉及一种快速止血防水敷料贴及其制备方法和应用。
背景技术
传统敷料一般由棉、软麻布和亚麻布加工而成，传统敷料贴的止血功效多依靠物理止血，止血效率较低，也不具有杀菌消炎的功效。中国专利CN200410073871.2(公开日2009.03.04)公开了一种抗菌敷料，包含三层结构，外层为高弹透气无纺布层，中层为高粘纤维层，且含有抗菌消炎、止血微米级超细药粉，内层为漏斗形多孔流延膜，虽然该敷料可以通过中间层的超细药粉消炎杀菌，高粘纤维层吸水后会膨胀，吸收大量分泌液，同时封闭出血点，但是这种敷料主要依靠超细药粉来达到消炎杀菌、止血的效果，而这种超细药粉容易泄露，导致消炎杀菌、止血效果下降。
发明内容
本发明要解决的技术问题是克服现有止血敷料的消炎杀菌、止血效果不够好的缺陷和不足，提供一种快速止血防水敷料贴，具有优异的消炎杀菌、快速止血的效果，并且还具有较好的机械性能。
本发明的又一目的是提供一种快速止血防水敷料贴的制备方法。
本发明的另一目的是提供一种快速止血防水敷料贴的应用。
本发明上述目的通过以下技术方案实现：
一种快速止血防水敷料贴，包括外层、中间层和里层，其中外层为拒水保护层，外层材料为涤纶、锦纶或丙纶中的一种或几种；中间层为吸液层，中间层材料为粘胶纤维、莱塞尔纤维和醋酯纤维中的一种或几种；里层为功能层，里层材料为蒲公英纤维与竹纤维。
本发明利用蒲公英纤维和竹纤维制得功能层，第一，蒲公英纤维携带的大量负离子，能够迅速结合或者粘附血小板、红血球，释放出凝血因子止血，实现快速止血；蒲公英纤维中的黄酮类物质激活凝血因子，启动体内凝血系统，在凝血酶的作用下，加固形成不溶性纤维蛋白多聚体，发挥强大稳定的止血功效；而竹纤维具有良好的透气性，瞬间吸水性及天然抗菌的功能，二者可以发挥协同增效作用，更好的发挥消炎杀菌、快速止血的作用；第二，以上两种都属于天然植物纤维，易于降解，安全环保，且成本较低，第三，本发明直接利用具有消炎抗菌、止血作用的纤维作为功能层，可以很好的固定在快速止血防水敷料贴中，更为可靠，不会发生泄漏，更好地发挥消炎抗菌、止血的作用；而外层为拒水保护层，在提供一定机械强度的同时具有拒水功能，防止伤口被水浸渍；中间的吸液层，遇血后吸附血液中的水分，血液粘度和稠度变大，血液流速减慢，血液流失减少，且可吸取伤口处的组织液、水分，防止伤口的二次污染；纤维吸水后会膨胀，膨胀后会覆盖创面，能够封闭出血点，达到止血的目的，具有较高的吸液能力。
优选地，所述蒲公英纤维与竹纤维的质量比为3～5：1。竹纤维还能够提供一定的支撑强度。
更优选地，所述蒲公英纤维与竹纤维的质量比为3：1。
优选地，所述外层材料为涤纶和/或锦纶。
优选地，所述中间层材料为粘胶纤维和/或醋酯纤维。
优选地，所述中间层的网面密度为80～170g/m2。
优选地，所述外层的网面密度为50～80g/m2。
优选地，所述中间层材料的细度为1.0～6.0D，长度为35～75mm。
优选地，所述外层材料的细度为1.5～15D，长度为32～76mm。
本发明还保护上述快速止血防水敷料贴的制备方法，包括如下步骤：
将外层材料、中间层材料和里层材料分别梳理后，然后将三层梳理后的材料经水刺加固制得快速止血防水敷料贴。
本发明采用多层水刺加固工艺，不使用任何化学制剂，对环境无污染，所制得的快速止血防水敷料贴更加安全环保。
优选地，所述梳理前还包括纤维开松的步骤。
优选地，所述梳理的喂棉罗拉速度为0.5～1.2m/m2，锡林速度为360～500m/m2，道夫速度为8～20m/m2，杂乱辊速度为8～20m/m2。
优选地，所述水刺包括预水刺和后续四道水刺，其中预水刺压力为20～30bar，后续四道水刺压力分别为40～50bar、60～75bar、90～110bar、90～110bar。
本发明还保护上述快速止血防水敷料贴在止血制品中的应用。
与现有技术相比，本发明的有益效果是：
本发明的快速止血防水敷料贴包括外层为拒水保护层，防止伤口被水浸渍，保证快速止血防水敷料贴更好的机械性能；中间层为吸液层，减少血液流失、封闭出血点、防止二次污染；里层为功能层，包括一定配比的蒲公英纤维与竹纤维制得，蒲公英纤维具有消炎杀菌、止血的功效，竹纤维具有天然抗菌、透气的作用，并且由纤维直接制得功能层，不会发生泄漏，本发明的快速止血防水敷料贴，可以更好的发挥快速止血、消炎杀菌的功效，可广泛应用于制备快速止血制品中。
附图说明
图1为本发明实施例1制得的快速止血防水敷料贴的断面结构。
具体实施方式
下面结合具体实施方式对本发明作进一步的说明，但实施例并不对本发明做任何形式的限定。除非另有说明，本发明实施例采用的原料试剂为常规购买的原料试剂。
各实施例和对比例中的原料：
涤纶纤维：非织造型6D*50mm，仪征市东南化纤原料有限公司；
粘胶纤维：ReVisco 4D*40mm，唐山三友集团化纤有限公司；
蒲公英纤维：WXtm 6D*30mm；山东永信；
竹纤维：1.5D*38mm，绍兴久久隆纺织有限公司；
医用纱布敷料：A型，120g/m2，5cm*7cm，江西中赣医疗器械有限公司。
实施例1
一种快速止血防水敷料贴，包括外层、中间层和里层三层结构，其中外层为拒水保护层，外层材料为涤纶；中间层为吸液层，中间层材料为粘胶纤维；里层为功能层，里层材料为蒲公英纤维与竹纤维，所述蒲公英纤维与竹纤维的质量比为3：1。
上述快速止血防水敷料贴的制备方法，包括如下步骤：
S1.纤维开松准备：涤纶纤维，细度为6.4D，长度为50mm；粘胶纤维，细度为3.6D，长度为40mm；按照所需纤网面密度称取相应质量的纤维，对各层纤维分别进行开松；
S2.直铺梳理：将S1得到的各层所需纤维分别喂入梳理机，采用直铺法进行梳理，梳理后，所得纤维皆沿机器方向(MD)方向排列；所述梳理工艺为喂棉罗拉速度为0.8m/m2，锡林速度为400m/m2，道夫速度为10m/m2，杂乱辊速度为10m/m2；
S3.将得到的三层纤维网进行平行复合得到复合纤网，三层纤维网排列方向相同；外层的网面密度为60g/m2；中间层的面密度100g/m2；里层的蒲公英纤维与竹纤混合的纤网面密度为60g/m2；
S4.对所得的复合纤网进行水刺加固，将复合纤网置于水刺机输网帘上，所述的复合纤网的喂入方向与排列方向相同，保证纤网内纤维在加固后仍沿MD方向排列，设定合理的输网帘速度和水刺压力，所述水刺工艺为预水刺压力为20bar，主水刺时采用两个水刺头正反水刺，水刺压力分别为40bar、60bar、100bar、100bar；所述的水刺加固，两种纤维在临界处互相穿插、缠结，然后在烘箱内烘干、卷绕得到快速止血防水敷料贴。
本实施例制得的快速止血防水敷料贴的断面结构如图1所示，其中1为外层-拒水保护层；2为中间层-吸液层；3为里层-功能层。
实施例2
本实施例的快速止血防水敷料贴与实施例1相同，区别在于，将涤纶纤维规格替换为细度为8D，长度为64mm，外层网面密度替换为80g/m2；粘胶纤维规格替换细度为4D，长度为40mm；中间层面密度170g/m2；里层的纤网面密度替换为55g/m2。
上述快速止血防水敷料贴的制备方法与实施例1相同，区别在于，步骤S2梳理工艺的参数替换为喂棉罗拉速度为0.5m/m2，锡林速度为360m/m2，道夫速度为8m/m2，杂乱辊速度为8m/m2；主水刺的水刺压力替换为50bar、60bar、90bar、100bar。
实施例3
本实施例的快速止血防水敷料贴与实施例1相同，区别在于，将涤纶纤维规格替换为细度为7D，长度为40mm；外层的纤网面密度为50g/m2，粘胶纤维规格替换细度为2.6D，长度为70mm；里层的纤网面密度替换为80g/m2。
上述快速止血防水敷料贴的制备方法与实施例1相同，区别在于，步骤S2梳理工艺的参数替换为喂棉罗拉速度为1.2m/m2，锡林速度为400m/m2，道夫速度为18m/m2，杂乱辊速度为18m/m2；步骤S4预水刺压力替换为26bar，主水刺压力替换为40bar、75bar、110bar、100bar。
实施例4
本实施例的快速止血防水敷料贴及其制备方法与实施例1相同，区别在于，里层的蒲公英纤维与竹纤维混合的纤网面密度为60g/m2，将蒲公英纤维与竹纤维的质量比替换为5：1。
实施例5
本实施例的快速止血防水敷料贴及其制备方法与实施例1相同，区别在于，外层的网面密度为50g/m2；中间层的面密度170g/m2。
实施例6
本实施例的快速止血防水敷料贴与实施例1相同，区别在于，将外层的涤纶替换为锦纶。
实施例7
本实施例的快速止血防水敷料贴及其制备方法与实施例1相同，区别在于，将粘胶纤维替换为醋酯纤维。
实施例8
本实施例的快速止血防水敷料贴及其制备方法与实施例1相同，区别在于，将蒲公英纤维与竹纤维的质量比替换为4：1。
对比例1
本对比例的敷料贴，与实施例1相比，不加入涤纶，敷料最终为无拒水保护层无纺布。
对比例2
本对比例的敷料贴，与实施例1相比，不加入粘胶纤维，敷料最终为无吸液层无纺布。
对比例3
本对比例的敷料贴，与实施例1相比，不加入竹纤维和蒲公英纤维，敷料最终为无功能层无纺布。
对比例4
本对比例的敷料贴为市售医用纱布敷料，脱脂棉质，A型，克重120g/m2，尺寸5cm*7cm。
性能测试
1、测试方法
(1)织物厚度：按照标准GB/T24218.2-2009测试，仪器：YG141N(宁波纺织仪器厂)型数字式织物厚度仪，压脚面积为2500±20mm2；加压压力为200cN；加压时间为10±1s，每个样品测量10次求均值。
(2)横向断裂强力测试按照标准FZ/T 60005测试。
(3)杀菌性能：实验方法按照2002年第四版《消毒技术规范》，在体外对临床常见菌株进行5分钟杀菌实验，包括金黄色葡萄球菌(ATCC 6538)、大肠杆菌(8099)、绿脓杆菌)综合菌种。
(4)敷料的湿传递性：按照标准YY/T0471.1-2004、YY/T0471.2-2004，结合国标GB/T24218.6采用合成渗液实施导湿性试验，测试水刺非织造敷料基布在指定时间内的最大芯吸髙度。
(5)防水效果：直接用水淋敷料贴外层，观察有无渗入；渗透记NG，不渗透记录OK。
2、测试结果
表1各实施例和对比例的性能测试结果
敷料对模拟伤口渗液湿传递性良好是指在大量伤口渗液情况下，敷料具备将伤口区域渗液迅速吸收并沿敷料厚度方向传导的能力，湿传递性优良的敷料，能快速清创，减小伤口区渗液积聚和敷料内部渗液回渗的几率；可减小潮湿型伤口的湿度，减小皮肤被渗液浸渍的危害，说明敷料具有快速止血的能力。从以上表1的结果可以看出，与对比例4的主要成分为棉的商用敷料相比，由于本发明采用的粘胶纤维的结晶度低于棉，而且非织结构形成的孔隙较棉纱布小，因此湿传递性明显高于商用敷料，说明本发明的敷料贴可快速的将水分导走，水分导走后及时封闭出血点，并提供合适湿度的创口环境，更容易使伤口愈合达到快速止血目的。
另外，从表1结果还可以看出，本发明实施例的敷料贴的厚度在1.8～2.0mm左右，强力在40N左右，与市售商用敷料相当，机械性能良好，但杀菌效果相对有显著提升，得益于外层功能层防水效果改善，加上里层的竹纤维和蒲公英纤维功能层和中间粘胶纤维层，实施例的吸液改善效果是对比例4的1.5倍左右；从实施例4可以看出，提高一部分蒲公英纤维的比例，可进一步改善吸液量，进而改善止血效果。同时结合对比例1～3看出，去掉相应各个层，都不能达到同时具有防水效果、杀菌性、良好湿传递性以及快速止血的综合效果。
显然，本发明的上述实施例仅是为清楚地说明本发明所作的举例，而并非是对本发明的实施方式的限定。对于所属领域的普通技术人员来说，在上述说明的基础上还可以做出其它不同形式的变化或变动。这里无需也无法对所有的实施方式予以穷举。凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明权利要求的保护范围之内。
Claims (10)
1.一种快速止血防水敷料贴，其特征在于，包括外层、中间层和里层，其中外层为拒水保护层，外层材料为涤纶、锦纶或丙纶中的一种或几种；中间层为吸液层，中间层材料为粘胶纤维、莱塞尔纤维和醋酯纤维中的一种或几种；里层为功能层，里层材料为蒲公英纤维与竹纤维。
2.根据权利要求1所述快速止血防水敷料贴，其特征在于，所述蒲公英纤维与竹纤维的质量比为3～5：1。
3.根据权利要求1或2所述快速止血防水敷料贴，其特征在于，所述外层材料为涤纶和/或锦纶。
4.根据权利要求1所述快速止血防水敷料贴，其特征在于，所述中间层材料为粘胶纤维和/或醋酯纤维。
5.根据权利要求1所述快速止血防水敷料贴，其特征在于，所述中间层的纤网面密度为80～170g/m2。
6.根据权利要求1所述快速止血防水敷料贴，其特征在于，所述外层的纤网面密度为50～80g/m2。
7.根据权利要求1所述快速止血防水敷料贴，其特征在于，所述中间层材料的细度为1.0～6.0D，长度为35～75mm。
8.根据权利要求1所述快速止血防水敷料贴，其特征在于，所述外层材料的细度为1.5～15D，长度为32～76mm。
9.权利要求1～8任一项所述快速止血防水敷料贴的制备方法，其特征在于，包括如下步骤：
将外层材料、中间层材料和里层材料分别梳理后，然后将三层梳理后的材料经水刺加固制得快速止血防水敷料贴。
10.权利要求1～8任一项所述快速止血防水敷料贴在止血制品用敷料贴中的应用。