CN112679089A - Decorative glass flake flashing material and preparation method thereof - Google Patents
Decorative glass flake flashing material and preparation method thereof Download PDFInfo
- Publication number
- CN112679089A CN112679089A CN202110158423.6A CN202110158423A CN112679089A CN 112679089 A CN112679089 A CN 112679089A CN 202110158423 A CN202110158423 A CN 202110158423A CN 112679089 A CN112679089 A CN 112679089A
- Authority
- CN
- China
- Prior art keywords
- glass
- colorant
- soda
- antioxidant
- hollow microspheres
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a decorative glass flake flashing material, which comprises the following raw materials: 40% of glass, 5-20% of hollow microspheres, 10-20% of soda ash, 10% of opacifier, 1-10% of antioxidant, 1-10% of light stabilizer, 1-10% of colorant and 1-10% of fluorescent powder coating, wherein the percentages are mass percentages. According to the invention, the hollow microspheres and the emulsion are added into the raw materials, so that the mechanical strength and the chemical thermal stability of the used material are improved; and the soda ash is utilized, so that bubbles generated in the melting and forming processes of the glass are effectively prevented, and the attractiveness of the formed material is improved; the light stability and the antioxidant improve the coloring effect of the colorant, and the fluorescent powder coating absorbs and stores light energy, so that the attractive effect is further improved at night; can process the preparation to glass, conveniently carry out flash of light material and promote, compare in traditional manufacturing approach, greatly reduced manufacturing cost.
Description
Technical Field
The invention relates to the technical field of decorative materials, in particular to a decorative glass flake flashing material and a preparation method thereof.
Background
The glittering material is mainly an important ornament applied to industries such as cosmetics, glittering decorations, building material decorations, artware, coating, paint and the like, and is used for improving the functionality and the aesthetic property of products and enabling the products to have glittering effect.
Disclosure of Invention
The invention aims to solve the defects in the prior art and provides a decorative glass flake flashing material and a preparation method thereof.
In order to achieve the purpose, the invention adopts the following technical scheme:
a decorative glass flake flashing material comprises the following raw materials: 40% of glass, 5-20% of hollow microspheres, 10-20% of soda ash, 10% of opacifier, 1-10% of antioxidant, 1-10% of light stabilizer, 1-10% of colorant and 1-10% of fluorescent powder coating, wherein the percentages are mass percentages.
Preferably, the colorant comprises MnO2、CoO、Co2O3、FeO、CdS、Fe2O3、Sb2S3And Cu2O。
Preferably, the decorative glass flake glittering material comprises the following raw materials: 40% of glass, 20% of hollow microspheres, 15% of soda ash, 10% of opacifier, 3% of antioxidant, 3% of light stabilizer, 4% of colorant and 5% of fluorescent powder coating.
Preferably, the decorative glass flake glittering material comprises the following raw materials: 40% of glass, 5% of hollow microspheres, 20% of soda ash, 10% of opacifier, 3% of antioxidant, 10% of light stabilizer, 10% of colorant and 2% of fluorescent powder coating.
Preferably, the decorative glass flake glittering material comprises the following raw materials: 40% of glass, 20% of hollow microspheres, 5% of soda ash, 10% of opacifier, 10% of antioxidant, 5% of light stabilizer, 5% of colorant and 10% of fluorescent powder coating.
A decorative glass flake flashing material and a preparation method thereof comprise the following steps:
s1: raw material treatment: weighing glass, hollow microspheres, soda, an opacifier, an antioxidant, a light stabilizer, a colorant and a fluorescent powder coating according to specified components, ultrasonically cleaning the glass, drying the glass, putting the soda into a crusher, crushing the soda to obtain soda powder, and screening the soda powder through a 300-mesh screen;
s2: melting and stirring: according to the formula proportion, putting glass, hollow microspheres, soda powder, an opacifier, an antioxidant, a light stabilizer, a colorant and a fluorescent powder coating into a melting furnace, and melting the raw materials of each component to obtain a molten mixture;
s3: and (3) injection molding and demolding: injecting the molten mixture into a mold through an injection molding machine, annealing the mold after injection molding, subjecting the mixture to drastic temperature change and shape change during molding, leaving thermal stress in the mixture, putting the annealed mold into a cooling pool for cooling, and then demolding to obtain a semi-molded sheet material;
s4: crushing and forming: and putting the semi-formed sheet material into a crusher for crushing, and extruding and crushing the semi-formed sheet material to obtain the glass flake flashing material.
Preferably, in step S2, the temperature in the melting furnace is 1200 ℃ and the working time is 45 min.
Compared with the prior art, the invention has the beneficial effects that:
the invention provides a decorative glass flake flashing material, which is characterized in that hollow microspheres and emulsion are added into raw materials, so that the mechanical strength and the chemical thermal stability of the used material are improved; and the soda ash is utilized, so that bubbles generated in the melting and forming processes of the glass are effectively prevented, and the attractiveness of the formed material is improved; the light stability and the antioxidant improve the coloring effect of the colorant, and the fluorescent powder coating absorbs and stores light energy, so that the attractive effect is further improved at night; can process the preparation to glass, conveniently carry out flash of light material and promote, compare in traditional manufacturing approach, greatly reduced manufacturing cost.
Detailed Description
The first embodiment is as follows:
the invention provides a decorative glass flake flashing material, which comprises the following raw materials: 40% of glass, 20% of hollow microspheres, 15% of soda ash, 10% of opacifier, 3% of antioxidant, 3% of light stabilizer, 4% of colorant and 5% of fluorescent powder coating.
Wherein the colorant comprises MnO2、CoO、Co2O3、FeO、CdS、Fe2O3、Sb2S3And Cu2O。
A decorative glass flake flashing material and a preparation method thereof comprise the following steps:
s1: raw material treatment: weighing glass, hollow microspheres, soda, an opacifier, an antioxidant, a light stabilizer, a colorant and a fluorescent powder coating according to specified components, ultrasonically cleaning the glass, drying the glass, putting the soda into a crusher, crushing the soda to obtain soda powder, and screening the soda powder through a 300-mesh screen;
s2: melting and stirring: according to the formula proportion, putting glass, hollow microspheres, soda powder, an opacifier, an antioxidant, a light stabilizer, a colorant and a fluorescent powder coating into a melting furnace, and melting the raw materials of each component to obtain a molten mixture;
s3: and (3) injection molding and demolding: injecting the molten mixture into a mold through an injection molding machine, annealing the mold after injection molding, subjecting the mixture to drastic temperature change and shape change during molding, leaving thermal stress in the mixture, putting the annealed mold into a cooling pool for cooling, and then demolding to obtain a semi-molded sheet material;
s4: crushing and forming: and putting the semi-formed sheet material into a crusher for crushing, and extruding and crushing the semi-formed sheet material to obtain the glass flake flashing material.
In step S2, the temperature in the melting furnace is 1200 ℃ and the working time is 45 min.
Example two:
the invention provides a decorative glass flake flashing material, which comprises the following raw materials: 40% of glass, 20% of hollow microspheres, 15% of soda ash, 10% of opacifier, 3% of antioxidant, 3% of light stabilizer, 4% of colorant and 5% of fluorescent powder coating.
Wherein the colorant comprises MnO2、CoO、Co2O3、FeO、CdS、Fe2O3、Sb2S3And Cu2O。
A decorative glass flake flashing material and a preparation method thereof comprise the following steps:
s1: raw material treatment: weighing glass, hollow microspheres, soda, an opacifier, an antioxidant, a light stabilizer, a colorant and a fluorescent powder coating according to specified components, ultrasonically cleaning the glass, drying the glass, putting the soda into a crusher, crushing the soda to obtain soda powder, and screening the soda powder through a 300-mesh screen;
s2: melting and stirring: according to the formula proportion, putting glass, hollow microspheres, soda powder, an opacifier, an antioxidant, a light stabilizer, a colorant and a fluorescent powder coating into a melting furnace, and melting the raw materials of each component to obtain a molten mixture;
s3: and (3) injection molding and demolding: injecting the molten mixture into a mold through an injection molding machine, annealing the mold after injection molding, subjecting the mixture to drastic temperature change and shape change during molding, leaving thermal stress in the mixture, putting the annealed mold into a cooling pool for cooling, and then demolding to obtain a semi-molded sheet material;
s4: crushing and forming: and putting the semi-formed sheet material into a crusher for crushing, and extruding and crushing the semi-formed sheet material to obtain the glass flake flashing material.
In step S2, the temperature in the melting furnace is 1200 ℃ and the working time is 45 min.
Example three:
the invention provides a decorative glass flake flashing material, which comprises the following raw materials: 40% of glass, 20% of hollow microspheres, 15% of soda ash, 10% of opacifier, 3% of antioxidant, 3% of light stabilizer, 4% of colorant and 5% of fluorescent powder coating.
Wherein the colorant comprises MnO2、CoO、Co2O3、FeO、CdS、Fe2O3、Sb2S3And Cu2O。
A decorative glass flake flashing material and a preparation method thereof comprise the following steps:
s1: raw material treatment: weighing glass, hollow microspheres, soda, an opacifier, an antioxidant, a light stabilizer, a colorant and a fluorescent powder coating according to specified components, ultrasonically cleaning the glass, drying the glass, putting the soda into a crusher, crushing the soda to obtain soda powder, and screening the soda powder through a 300-mesh screen;
s2: melting and stirring: according to the formula proportion, putting glass, hollow microspheres, soda powder, an opacifier, an antioxidant, a light stabilizer, a colorant and a fluorescent powder coating into a melting furnace, and melting the raw materials of each component to obtain a molten mixture;
s3: and (3) injection molding and demolding: injecting the molten mixture into a mold through an injection molding machine, annealing the mold after injection molding, subjecting the mixture to drastic temperature change and shape change during molding, leaving thermal stress in the mixture, putting the annealed mold into a cooling pool for cooling, and then demolding to obtain a semi-molded sheet material;
s4: crushing and forming: and putting the semi-formed sheet material into a crusher for crushing, and extruding and crushing the semi-formed sheet material to obtain the glass flake flashing material.
In step S2, the temperature in the melting furnace is 1200 ℃ and the working time is 45 min.
The invention provides a decorative glass flake flashing material, which is characterized in that hollow microspheres and emulsion are added into raw materials, so that the mechanical strength and the chemical thermal stability of the used material are improved; and the soda ash is utilized, so that bubbles generated in the melting and forming processes of the glass are effectively prevented, and the attractiveness of the formed material is improved; the light stability and the antioxidant improve the coloring effect of the colorant, and the fluorescent powder coating absorbs and stores light energy, so that the attractive effect is further improved at night; can process the preparation to glass, conveniently carry out flash of light material and promote, compare in traditional manufacturing approach, greatly reduced manufacturing cost.
The above description is only for the preferred embodiment of the present invention, but the scope of the present invention is not limited thereto, and any person skilled in the art should be considered to be within the technical scope of the present invention, and the technical solutions and the inventive concepts thereof according to the present invention should be equivalent or changed within the scope of the present invention.
Claims (7)
1. The decorative glass flake flashing material is characterized by comprising the following raw materials: 40% of glass, 5-20% of hollow microspheres, 10-20% of soda ash, 10% of opacifier, 1-10% of antioxidant, 1-10% of light stabilizer, 1-10% of colorant and 1-10% of fluorescent powder coating, wherein the percentages are mass percentages.
2. The decorative glass flake glitter of claim 1, wherein the colorant comprises MnO2、CoO、Co2O3、FeO、CdS、Fe2O3、Sb2S3And Cu2O。
3. The glittering material for decorative glass flakes, according to claim 1, which comprises the following raw materials: 40% of glass, 20% of hollow microspheres, 15% of soda ash, 10% of opacifier, 3% of antioxidant, 3% of light stabilizer, 4% of colorant and 5% of fluorescent powder coating.
4. The glittering material for decorative glass flakes, according to claim 1, which comprises the following raw materials: 40% of glass, 5% of hollow microspheres, 20% of soda ash, 10% of opacifier, 3% of antioxidant, 10% of light stabilizer, 10% of colorant and 2% of fluorescent powder coating.
5. The glittering material for decorative glass flakes, according to claim 1, which comprises the following raw materials: 40% of glass, 20% of hollow microspheres, 5% of soda ash, 10% of opacifier, 10% of antioxidant, 5% of light stabilizer, 5% of colorant and 10% of fluorescent powder coating.
6. The decorative glass flake flashing material and the preparation method thereof are characterized by comprising the following steps:
s1: raw material treatment: weighing glass, hollow microspheres, soda, an opacifier, an antioxidant, a light stabilizer, a colorant and a fluorescent powder coating according to specified components, ultrasonically cleaning the glass, drying the glass, putting the soda into a crusher, crushing the soda to obtain soda powder, and screening the soda powder through a 300-mesh screen;
s2: melting and stirring: according to the formula proportion, putting glass, hollow microspheres, soda powder, an opacifier, an antioxidant, a light stabilizer, a colorant and a fluorescent powder coating into a melting furnace, and melting the raw materials of each component to obtain a molten mixture;
s3: and (3) injection molding and demolding: injecting the molten mixture into a mold through an injection molding machine, annealing the mold after injection molding, subjecting the mixture to drastic temperature change and shape change during molding, leaving thermal stress in the mixture, putting the annealed mold into a cooling pool for cooling, and then demolding to obtain a semi-molded sheet material;
s4: crushing and forming: and putting the semi-formed sheet material into a crusher for crushing, and extruding and crushing the semi-formed sheet material to obtain the glass flake flashing material.
7. The glittering glass flake material for decoration according to claim 6, wherein the melting furnace temperature is 1200 ℃ and the working time is 45min in step S2.