CN112662211A - Inorganic floor gloss oil, inorganic floor gloss oil dispersion method and dispersion equipment - Google Patents
Inorganic floor gloss oil, inorganic floor gloss oil dispersion method and dispersion equipment Download PDFInfo
- Publication number
- CN112662211A CN112662211A CN202110063905.3A CN202110063905A CN112662211A CN 112662211 A CN112662211 A CN 112662211A CN 202110063905 A CN202110063905 A CN 202110063905A CN 112662211 A CN112662211 A CN 112662211A
- Authority
- CN
- China
- Prior art keywords
- inorganic
- fixedly connected
- gloss oil
- percent
- main body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses inorganic floor gloss oil which comprises the following components: mixing purified water and hydroxyethyl cellulose according to a proportion, dispersing at a high speed after mixing, adding other components according to the sequence of the wetting agent, the defoaming agent, the film-forming assistant, the potassium silicate, the lithium silicate, the silica sol, the pure phenyl silicon emulsion, the inorganic thickening agent and the antiseptic agent BIT at a low speed, and dispersing at a low speed; and performing N-layer thin coating, wherein the interlayer drying time of the N-layer thin coating is more than or equal to 2 hours. Through the mode, the inorganic floor gloss oil provided by the invention is used for finishing the surface of an inorganic floor coating after being coated, can form a smooth transparent film on the surface of the floor, is mainly used for an indoor underground garage, has the characteristics of high hardness and good wear resistance, has good glossiness and has a protection effect on the floor.
Description
Technical Field
The invention relates to the field of inorganic coatings, in particular to inorganic floor gloss oil, a dispersion method of the inorganic floor gloss oil and dispersion equipment.
Background
The inorganic paint is an inorganic polymer paint which is composed of inorganic polymer, dispersed and activated metal, metal oxide nano material and rare earth ultrafine powder, and is an inorganic polymer anticorrosive coating firmly combined with a substrate through chemical bonds, has no pollution to the environment, long service life and anticorrosive performance reaching the international advanced level, and is a high-tech upgrading product meeting the environmental protection requirement.
The inorganic floor gloss oil is one of a plurality of inorganic materials, compared with some organic coatings, the inorganic floor gloss oil has small pollution to the environment in the production and use processes, and most products use water as a dispersion medium and have no adverse effects on the environment and health. Meanwhile, the inorganic floor gloss oil has aging resistance and certain physical and chemical properties which are difficult to achieve by most of organic coatings with the same production cost, so that the inorganic floor gloss oil has better technical and economic properties. Meanwhile, the inorganic floor gloss oil can be integrated with the base layer, so that the adhesive force is particularly good.
The coating dispersion equipment mainly aims at crushing, dispersing, emulsifying and mixing slurry liquid raw materials with different viscosities, and performs high-speed strong shearing, impacting, crushing and dispersing on materials through novel high-efficiency stirring equipment with upper and lower sawteeth of a dispersion disc so as to achieve the functions of rapid mixing, dissolving, dispersing and refining, and is high-efficiency equipment for stirring, dispersing and dissolving solids such as coatings. The inorganic coating material dispersing machine in the prior art has some defects, such as low stirring and dispersing efficiency, easy accumulation of the coating material at the bottom of the equipment when the coating material is filled, and inconvenient detection of the capacity of the coating material.
Disclosure of Invention
The invention mainly solves the technical problem of how to provide the inorganic floor gloss oil which is used for finishing the inorganic floor coating after surface coating, ensures thorough drying of the interlayer by multiple times of thin coating, can form a smooth transparent film on the floor surface by a method that the drying time of the interlayer is not less than 2 hours, is mainly used for an indoor underground garage, has the characteristics of high hardness and good wear resistance, has good glossiness and has a protection effect on the floor.
In order to solve the technical problems, the invention adopts a technical scheme that: the inorganic floor gloss oil comprises the following components: the water-based anti-corrosion coating comprises the following components in percentage by mass: 15 to 25 percent of purified water, 0.05 to 0.2 percent of hydroxyethyl cellulose, 0.1 to 0.2 percent of wetting agent, 0.1 to 0.3 percent of defoaming agent, 0.3 to 1.0 percent of film-forming additive, 3 to 15 percent of potassium silicate, 5 to 15 percent of lithium silicate, 35 to 45 percent of silica sol, 10 to 20 percent of pure silicon emulsion, 0.5 to 1.0 percent of inorganic thickener and 0.1 to 0.5 percent of antiseptic and bactericide BIT.
In a preferred embodiment, the components are calculated according to the mass percentage: 15% of purified water, 0.2% of hydroxyethyl cellulose, 0.15% of wetting agent, 0.2% of defoaming agent, 0.3% of film-forming assistant, 1.0% of potassium silicate, 15% of lithium silicate, 45% of silica sol, 20% of pure silicon emulsion, 1.0% of inorganic thickener and 0.5% of antiseptic bactericide BIT.
In a preferred embodiment, the components are calculated according to the mass percentage: 25% of purified water, 0.05% of hydroxyethyl cellulose, 0.1% of wetting agent, 0.1% of defoaming agent, 0.3% of film-forming assistant, 3% of potassium silicate, 5% of lithium silicate, 35% of silica sol, 10% of pure silicon emulsion, 0.5% of inorganic thickener and 0.1% of antiseptic and bactericide BIT.
In a preferred embodiment, the components are calculated according to the mass percentage: 20% of purified water, 0.1% of hydroxyethyl cellulose, 0.15% of wetting agent, 0.2% of defoaming agent, 0.5% of film-forming assistant, 6% of potassium silicate, 10% of lithium silicate, 42% of silica sol, 20% of pure silicon emulsion, 0.85% of inorganic thickener and 0.2% of antiseptic bactericide BIT.
The inorganic floor gloss oil dispersing method comprises the inorganic floor gloss oil and is used for spraying the inorganic floor gloss oil, and the method specifically comprises the following operation steps:
s1: mixing purified water and hydroxyethyl cellulose according to a ratio, dispersing at a high speed after mixing,
s2: adding other components in the sequence of a wetting agent, a defoaming agent, a film-forming assistant, potassium silicate, lithium silicate, silica sol, pure phenyl silicone emulsion, an inorganic thickener and an antiseptic bactericide BIT at low speed, and dispersing at low speed;
s3: and performing N-layer thin coating, wherein the interlayer drying time of the N-layer thin coating is more than or equal to 2 hours.
In a preferred embodiment, in the step S1, the time for high-speed dispersion after mixing is 40 minutes;
in the step S2, the time for low-speed dispersion after adding other components is 20-30 minutes;
in the step S3, the number of N thin coatings is 2-3.
An inorganic terrace gloss oil dispersion device is used for spraying the inorganic terrace gloss oil, and comprises a main body, wherein a bulk material cylinder is arranged in the main body and close to the edge of the top of the main body, a second motor is fixedly connected to the left side wall of the main body, the output end of the second motor extends to the inner part of the main body and is fixedly connected with a rotating rod, one end of the rotating rod penetrates through two ends of the bulk material cylinder and is rotatably connected with the left inner side wall of the main body through a bearing, a fixed rod is fixedly connected to the surface of the rotating rod, and one end of the fixed rod is fixedly connected with the inner side wall of the bulk material cylinder; the bottom of the main body is fixedly connected with a box body, the left side wall and the right side wall of the box body are both provided with a heat dissipation opening, and the interior of the heat dissipation opening is fixedly connected with a dust screen; the front of main part just is close to left side fixedly connected with display panel, the left side inside wall fixedly connected with level sensor of main part, pass through electric connection between level sensor and the display panel.
In a preferred embodiment, a first motor is fixedly connected to the inner bottom of the box body, an output end of the first motor extends to the inner portion of the main body, a rotating shaft is fixedly connected to the inner portion of the main body, turbine stirrers are fixedly connected to the surface of the rotating shaft, and the number of the turbine stirrers is multiple.
In a preferred embodiment, a connecting rod is fixedly connected inside the main body and below the bulk material barrel, and the inner side wall of the connecting rod, which is far away from the main body, is rotatably connected with one end of the rotating shaft through a bearing.
In a preferred embodiment, the top of the main body is provided with a feeding hole, the left side wall, the right side wall and the edge close to the bottom of the main body are fixedly connected with discharging pipes, and the surfaces of the discharging pipes are fixedly connected with electromagnetic valves.
In a preferred embodiment, the front surface of the box body is rotatably connected with a door body through a hinge, and the front surface of the door body, close to the right side edge, is fixedly connected with a handle.
In a preferred embodiment, a mounting assembly is fixedly connected to the front of the main body and located on the right side of the display panel, and a control button is movably connected to the front of the mounting assembly.
In a preferred embodiment, the bottom of the box body is fixedly connected with a supporting leg, and the bottom of the supporting leg is fixedly connected with a foot pad.
In a preferred embodiment, the inner bottom of the main body is inclined downward.
The invention has the beneficial effects that: the method is used for finishing the inorganic floor coating after surface coating, ensures thorough drying between layers by multiple times of thin coating, ensures that the drying time between layers is not less than 2 hours, can form a smooth transparent film on the floor surface, is mainly used for an indoor underground garage, has the characteristics of high hardness and good wear resistance, has good glossiness and has a protection effect on the floor.
Drawings
In order to more clearly illustrate the technical solutions in the embodiments of the present invention, the drawings needed to be used in the description of the embodiments are briefly introduced below, it is obvious that the drawings in the following description are only some embodiments of the present invention, and other drawings can be obtained by those skilled in the art without inventive efforts, wherein:
FIG. 1 is a flow chart of the dispersion spraying process of inorganic floor gloss oil according to the present invention;
FIG. 2 is a schematic view of the parameter ratio of an inorganic floor gloss oil according to the present invention;
FIG. 3 is a perspective view of the external structure of an inorganic floor gloss oil dispersion apparatus according to the present invention;
FIG. 4 is a front view of the internal structure of an inorganic floor gloss oil dispersion apparatus according to the present invention;
FIG. 5 is a front view of the external structure of an inorganic floor gloss oil dispersion apparatus according to the present invention;
fig. 6 is a schematic structural view of a turbine agitator of the inorganic floor gloss oil dispersing apparatus according to the present invention.
Illustration of the drawings:
1. a main body; 2. a box body; 3. a first motor; 4. a heat dissipation port; 5. a dust screen; 6. a second motor; 7. rotating the rod; 8. a bulk cylinder; 9. fixing the rod; 10. a feed inlet; 11. a bearing; 12. a connecting rod; 13. a liquid level sensor; 14. a turbine agitator; 15. a discharge pipe; 16. an electromagnetic valve; 17. a support leg; 18. a foot pad; 19. a door body; 20. a handle; 21. a display panel; 22. mounting the component; 23. a control button; 24. and rotating the shaft.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
Referring to fig. 1-6, in one embodiment of the present invention, an inorganic floor polish is provided, which includes the following embodiments.
Example 1
An inorganic floor gloss oil, comprising the following components: the water-based anti-corrosion coating comprises the following components in percentage by mass: 15 to 25 percent of purified water, 0.05 to 0.2 percent of hydroxyethyl cellulose, 0.1 to 0.2 percent of wetting agent, 0.1 to 0.3 percent of defoaming agent, 0.3 to 1.0 percent of film-forming additive, 3 to 15 percent of potassium silicate, 5 to 15 percent of lithium silicate, 35 to 45 percent of silica sol, 10 to 20 percent of pure silicon emulsion, 0.5 to 1.0 percent of inorganic thickener and 0.1 to 0.5 percent of antiseptic and bactericide BIT.
In the implementation process, the specific parameters are as shown in the table:
the inorganic floor gloss oil dispersing method comprises the inorganic floor gloss oil and is used for spraying the inorganic floor gloss oil, and the method specifically comprises the following operation steps:
s1: mixing purified water and hydroxyethyl cellulose according to a ratio, dispersing at a high speed after mixing,
s2: adding other components in the sequence of a wetting agent, a defoaming agent, a film-forming assistant, potassium silicate, lithium silicate, silica sol, pure phenyl silicone emulsion, an inorganic thickener and an antiseptic bactericide BIT at low speed, and dispersing at low speed;
s3: and performing N-layer thin coating, wherein the interlayer drying time of the N-layer thin coating is more than or equal to 2 hours.
In the step S1, the time for high-speed dispersion after mixing is 40 minutes, and in the step S2, the time for low-speed dispersion after adding other components is 20 to 30 minutes; in the step S3, the number of N thin coatings is 2-3.
An inorganic floor gloss oil dispersion device comprises a main body 1, wherein a dispersion cylinder 8 is arranged inside the main body 1 and close to the top edge, a second motor 6 is fixedly connected to the left side wall of the main body 1, the output end of the second motor 6 extends to the inside of the main body 1 and is fixedly connected with a rotating rod 7, one end of the rotating rod 7, which penetrates through the two ends of the dispersion cylinder 8, is rotatably connected with the left inner side wall of the main body 1 through a bearing 11, a fixing rod 9 is fixedly connected to the surface of the rotating rod 7, one end of the fixing rod 9 is fixedly connected with the inner side wall of the dispersion cylinder 8, a first motor 3 is fixedly connected to the inner bottom of a box body 2, the output end of the first motor 3 extends to the inside of the main body 1 and is fixedly connected with a rotating shaft 24, a plurality of turbine stirrers 14 are fixedly connected to the surface of the rotating shaft 24, connecting rods, the inner side wall of the connecting rod 12 far away from the main body 1 is rotatably connected with one end of the rotating shaft 24 through the bearing 11, so that the stirring and dispersing operation is convenient;
the bottom of the main body 1 is fixedly connected with a box body 2, the left side wall and the right side wall of the box body 2 are both provided with a heat dissipation port 4, and a dustproof net 5 is fixedly connected inside the heat dissipation port 4, so that the functions of heat dissipation and dust prevention are conveniently realized;
the front of main part 1 just is close to left side fixedly connected with display panel 21, and the left inside wall fixedly connected with level sensor 13 of main part 1 plays the convenient effect of detecting the capacity of annotating inorganic terrace gloss oil through electric connection between level sensor 13 and the display panel 21.
During the use, start second motor 6 and drive dwang 7 and bulk bin 8 and rotate through pressing control button 23, carry out filling inorganic terrace gloss oil through feed inlet 10 after that, inorganic terrace gloss oil carries out the bulk bin through bulk bin 8 and handles the bottom that makes inorganic terrace gloss oil even equipment that falls to, and detect the capacity of inorganic terrace gloss oil filling through level sensor 13, start first motor 3 afterwards and drive axis of rotation 24 and turbine agitator 14 and stir dispersion treatment to inorganic terrace gloss oil.
Example 2
An inorganic floor gloss oil, comprising the following components: the water-based anti-corrosion coating comprises the following components in percentage by mass: 15% of purified water, 0.2% of hydroxyethyl cellulose, 0.15% of wetting agent, 0.2% of defoaming agent, 0.3% of film-forming assistant, 1.0% of potassium silicate, 15% of lithium silicate, 45% of silica sol, 20% of pure silicon emulsion, 1.0% of inorganic thickener and 0.5% of antiseptic bactericide BIT.
In the implementation process, the specific parameters are as shown in the table:
the inorganic floor gloss oil dispersing method comprises the inorganic floor gloss oil and is used for spraying the inorganic floor gloss oil, and the method specifically comprises the following operation steps:
s1: mixing purified water and hydroxyethyl cellulose according to a ratio, dispersing at a high speed after mixing,
s2: adding other components in the sequence of a wetting agent, a defoaming agent, a film-forming assistant, potassium silicate, lithium silicate, silica sol, pure phenyl silicone emulsion, an inorganic thickener and an antiseptic bactericide BIT at low speed, and dispersing at low speed;
s3: and performing N-layer thin coating, wherein the interlayer drying time of the N-layer thin coating is more than or equal to 2 hours.
In a preferred embodiment, in the step S1, the time for high-speed dispersion after mixing is 40 minutes.
In step S2, the time for the low-speed dispersion after the addition of the other components is 20 minutes.
In step S3, the number of N thin coats is 2.
An inorganic terrace gloss oil dispersion equipment: including main part 1, the inside of main part 1 just is close to top edge and is provided with scattered feed cylinder 8, and the left side wall fixedly connected with second motor 6 of main part 1, the output of second motor 6 extend to the inside fixedly connected with dwang 7 of main part 1, and the one end of dwang 7 runs through the both ends of loosing feed cylinder 8 and passes through bearing 11 and be connected with the left inside wall rotation of main part 1. The fixed surface of dwang 7 is connected with dead lever 9, the one end of dead lever 9 and the inside wall fixed connection of bulk material jar 8, the first motor 3 of interior bottom fixedly connected with of box 2, the output of first motor 3 extends to the inside fixedly connected with axis of rotation 24 of main part 1. The fixed surface of axis of rotation 24 is connected with turbine agitator 14, and the quantity of turbine agitator 14 is a plurality of, and the inside of main part 1 just is located the below fixedly connected with connecting rod 12 of bulk material jar 8, and the inside wall that main part 1 was kept away from to connecting rod 12 passes through bearing 11 and is connected with the one end rotation of axis of rotation 24, plays the effect that conveniently stirs the dispersion operation.
The bottom fixedly connected with box 2 of main part 1, thermovent 4 has all been seted up to the lateral wall about box 2, and thermovent 4's inside fixedly connected with dust screen 5 plays the convenient effect of dispelling the heat and dirt-proof. The front of main part 1 just is close to left side fixedly connected with display panel 21, and the left inside wall fixedly connected with level sensor 13 of main part 1 plays the convenient effect of detecting the capacity of annotating inorganic terrace gloss oil through electric connection between level sensor 13 and the display panel 21.
During the use, start second motor 6 and drive dwang 7 and bulk bin 8 and rotate through pressing control button 23, carry out filling inorganic terrace gloss oil through feed inlet 10 after that, inorganic terrace gloss oil carries out the bulk bin through bulk bin 8 and handles the bottom that makes inorganic terrace gloss oil even equipment that falls to, and detect the capacity of inorganic terrace gloss oil filling through level sensor 13, start first motor 3 afterwards and drive axis of rotation 24 and turbine agitator 14 and stir dispersion treatment to inorganic terrace gloss oil.
Example 3
An inorganic floor gloss oil, comprising the following components: the water-based anti-corrosion coating comprises the following components in percentage by mass: 25% of purified water, 0.05% of hydroxyethyl cellulose, 0.1% of wetting agent, 0.1% of defoaming agent, 0.3% of film-forming assistant, 3% of potassium silicate, 5% of lithium silicate, 35% of silica sol, 10% of pure silicon emulsion, 0.5% of inorganic thickener and 0.1% of antiseptic and bactericide BIT.
In the implementation process, the specific parameters are as shown in the table:
the inorganic floor gloss oil dispersing method comprises the inorganic floor gloss oil and is used for spraying the inorganic floor gloss oil, and the method specifically comprises the following operation steps:
s1: mixing purified water and hydroxyethyl cellulose according to a ratio, dispersing at a high speed after mixing,
s2: adding other components in the sequence of a wetting agent, a defoaming agent, a film-forming assistant, potassium silicate, lithium silicate, silica sol, pure phenyl silicone emulsion, an inorganic thickener and an antiseptic bactericide BIT at low speed, and dispersing at low speed;
s3: and performing N-layer thin coating, wherein the interlayer drying time of the N-layer thin coating is more than or equal to 2 hours.
In a preferred embodiment, in the step S1, the time for high-speed dispersion after mixing is 40 minutes;
in step S2, the time for low-speed dispersion after the addition of other components is 25 minutes;
in step S3, the number of N thin coats is 3.
An inorganic terrace gloss oil dispersion equipment: including main part 1, the inside of main part 1 and be close to top edge and be provided with the powder section of thick bamboo 8, the left side wall fixedly connected with second motor 6 of main part 1. The output of second motor 6 extends to the inside fixedly connected with dwang 7 of main part 1, and the one end of dwang 7 runs through the left inside wall rotation that bulk material jar 8 both ends passed through bearing 11 and main part 1 and is connected, and the fixed surface of dwang 7 is connected with dead lever 9, the one end of dead lever 9 and the inside wall fixed connection of bulk material jar 8. The interior bottom fixedly connected with first motor 3 of box 2, the output of first motor 3 extends to the inside fixedly connected with axis of rotation 24 of main part 1. The fixed surface of axis of rotation 24 is connected with turbine agitator 14, and the quantity of turbine agitator 14 is a plurality of, and the inside of main part 1 just is located the below fixedly connected with connecting rod 12 of bulk material jar 8, and the inside wall that main part 1 was kept away from to connecting rod 12 passes through bearing 11 and is connected with the one end rotation of axis of rotation 24, plays the effect that conveniently stirs the dispersion operation.
The bottom fixedly connected with box 2 of main part 1, thermovent 4 has all been seted up to the lateral wall about box 2, and thermovent 4's inside fixedly connected with dust screen 5 plays the convenient effect of dispelling the heat and dirt-proof. The front of main part 1 just is close to left side fixedly connected with display panel 21, and the left inside wall fixedly connected with level sensor 13 of main part 1 plays the convenient effect of detecting the capacity of annotating inorganic terrace gloss oil through electric connection between level sensor 13 and the display panel 21. Feed inlet 10 has been seted up at the top of main part 1, the equal fixedly connected with discharging pipe 15 in edge just is close to the bottom about main part 1, discharging pipe 15's fixed surface is connected with solenoid valve 16, the front of box 2 is connected with a body 19 through the hinge rotation, the front of the body 19 just is close to right side edge fixedly connected with handle 20, the front of main part 1 just is located display panel 21's right side fixedly connected with installation component 22, the front swing joint of installation component 22 has control button 23, the bottom fixedly connected with landing leg 17 of box 2, the bottom fixedly connected with callus on the sole 18 of landing leg 17. During the use, start second motor 6 and drive dwang 7 and bulk cargo section of thick bamboo 8 and rotate through pressing control button 23, inorganic terrace gloss oil is filled through feed inlet 10 afterwards, inorganic terrace gloss oil carries out the bulk cargo through bulk cargo section of thick bamboo 8 and handles the even bottom that falls to the equipment of messenger inorganic terrace gloss oil, and detect the capacity of inorganic terrace gloss oil filling through level sensor 13, start first motor 3 afterwards and drive axis of rotation 24 and turbine agitator 14 and stir dispersion treatment to inorganic terrace gloss oil, after the bulk cargo is accomplished, open solenoid valve 16 and make inorganic terrace gloss oil flow out through discharging pipe 15 and collect can.
Example 4
An inorganic floor gloss oil, comprising the following components: the water-based anti-corrosion coating comprises the following components in percentage by mass: 20% of purified water, 0.1% of hydroxyethyl cellulose, 0.15% of wetting agent, 0.2% of defoaming agent, 0.5% of film-forming assistant, 6% of potassium silicate, 10% of lithium silicate, 42% of silica sol, 20% of pure silicon emulsion, 0.85% of inorganic thickener and 0.2% of antiseptic bactericide BIT.
In the implementation process, the specific parameters are as shown in the table:
s1: mixing purified water and hydroxyethyl cellulose according to a ratio, dispersing at a high speed after mixing,
s2: adding other components in the sequence of a wetting agent, a defoaming agent, a film-forming assistant, potassium silicate, lithium silicate, silica sol, pure phenyl silicone emulsion, an inorganic thickener and an antiseptic bactericide BIT at low speed, and dispersing at low speed;
s3: and performing N-layer thin coating, wherein the interlayer drying time of the N-layer thin coating is more than or equal to 2 hours.
In a preferred embodiment, in the step S1, the time for high-speed dispersion after mixing is 40 minutes;
in step S2, the time for low-speed dispersion after the addition of other components is 30 minutes;
in step S3, the number of N thin coats is 3.
An inorganic terrace gloss oil dispersion equipment: including main part 1, the inside of main part 1 and be close to top edge and be provided with the powder section of thick bamboo 8, the left side wall fixedly connected with second motor 6 of main part 1. The output of second motor 6 extends to the inside fixedly connected with dwang 7 of main part 1, and the one end of dwang 7 is run through the both ends of powder section of thick bamboo 8 and is passed through bearing 11 and be connected with the left inside wall rotation of main part 1. The fixed surface of dwang 7 is connected with dead lever 9, the one end of dead lever 9 and the inside wall fixed connection of bulk material jar 8, the first motor 3 of interior bottom fixedly connected with of box 2, the output of first motor 3 extends to the inside fixedly connected with axis of rotation 24 of main part 1. The fixed surface of axis of rotation 24 is connected with turbine agitator 14, and the quantity of turbine agitator 14 is a plurality of, and the inside of main part 1 just is located the below fixedly connected with connecting rod 12 of bulk material jar 8, and the inside wall that main part 1 was kept away from to connecting rod 12 passes through bearing 11 and is connected with the one end rotation of axis of rotation 24, plays the effect that conveniently stirs the dispersion operation.
The bottom fixedly connected with box 2 of main part 1, thermovent 4 has all been seted up to the lateral wall about box 2, and thermovent 4's inside fixedly connected with dust screen 5 plays the convenient effect of dispelling the heat and dirt-proof. The front of main part 1 just is close to left side fixedly connected with display panel 21, and the left inside wall fixedly connected with level sensor 13 of main part 1 plays the convenient effect of detecting the capacity of annotating inorganic terrace gloss oil through electric connection between level sensor 13 and the display panel 21. Feed inlet 10 has been seted up at the top of main part 1, the equal fixedly connected with discharging pipe 15 in edge just is close to the bottom about main part 1, discharging pipe 15's fixed surface is connected with solenoid valve 16, the front of box 2 is connected with a body 19 through the hinge rotation, the front of the body 19 just is close to right side edge fixedly connected with handle 20, the front of main part 1 just is located display panel 21's right side fixedly connected with installation component 22, the front swing joint of installation component 22 has control button 23, the bottom fixedly connected with landing leg 17 of box 2, the bottom fixedly connected with callus on the sole 18 of landing leg 17. During the use, start second motor 6 and drive dwang 7 and bulk bin 8 and rotate through pressing control button 23, carry out filling inorganic terrace gloss oil through feed inlet 10 after that, inorganic terrace gloss oil carries out the bulk bin through bulk bin 8 and handles the bottom that makes inorganic terrace gloss oil even equipment that falls to, and detect the capacity of inorganic terrace gloss oil filling through level sensor 13, start first motor 3 afterwards and drive axis of rotation 24 and turbine agitator 14 and stir dispersion treatment to inorganic terrace gloss oil.
Therefore, the invention has the following advantages:
(1) the coating is used for finishing the surface of the inorganic floor coating, the interlayer drying is ensured through multiple times of thin coating, and the interlayer drying time is not less than 2 hours, so that a smooth transparent film can be formed on the surface of the floor;
(2) the inorganic floor gloss oil dispersing equipment has a simple and reasonable structure, can well overcome the defects of the prior art, and effectively improves the stirring and dispersing efficiency of the coating; the inorganic terrace gloss oil dispersing equipment can effectively improve the heat dispersion performance of the equipment and ensure the normal operation of the equipment by arranging the heat dispersion port and the dustproof net;
(3) this inorganic terrace gloss oil dispersion equipment can make the even bottom that falls to the equipment of coating effectively through setting up the bulk cargo section of thick bamboo, is favorable to preventing that coating from storing up in the equipment bottom, can improve bulk cargo efficiency, and this inorganic terrace gloss oil dispersion equipment through setting up level sensor, can detect the capacity of annotating coating effectively, prevents that the interior coating of equipment from filling too much, influences the effect of stirring bulk cargo efficiency.
The above description is only an embodiment of the present invention, and not intended to limit the scope of the present invention, and all modifications of equivalent structures and equivalent processes, which are made by the present specification, or directly or indirectly applied to other related technical fields, are included in the scope of the present invention.
Claims (14)
1. The inorganic floor gloss oil is characterized by comprising the following components: the water-based anti-corrosion coating comprises the following components in percentage by mass: 15 to 25 percent of purified water, 0.05 to 0.2 percent of hydroxyethyl cellulose, 0.1 to 0.2 percent of wetting agent, 0.1 to 0.3 percent of defoaming agent, 0.3 to 1.0 percent of film-forming additive, 3 to 15 percent of potassium silicate, 5 to 15 percent of lithium silicate, 35 to 45 percent of silica sol, 10 to 20 percent of pure silicon emulsion, 0.5 to 1.0 percent of inorganic thickener and 0.1 to 0.5 percent of antiseptic and bactericide BIT.
2. The inorganic floor gloss oil of claim 1, wherein the components are calculated according to mass percent: 15% of purified water, 0.2% of hydroxyethyl cellulose, 0.15% of wetting agent, 0.2% of defoaming agent, 0.3% of film-forming assistant, 1.0% of potassium silicate, 15% of lithium silicate, 45% of silica sol, 20% of pure silicon emulsion, 1.0% of inorganic thickener and 0.5% of antiseptic bactericide BIT.
3. The inorganic floor gloss oil of claim 1, wherein the components are calculated according to mass percent: 25% of purified water, 0.05% of hydroxyethyl cellulose, 0.1% of wetting agent, 0.1% of defoaming agent, 0.3% of film-forming assistant, 3% of potassium silicate, 5% of lithium silicate, 35% of silica sol, 10% of pure silicon emulsion, 0.5% of inorganic thickener and 0.1% of antiseptic and bactericide BIT.
4. The inorganic floor gloss oil of claim 1, wherein the components are calculated according to mass percent: 20% of purified water, 0.1% of hydroxyethyl cellulose, 0.15% of wetting agent, 0.2% of defoaming agent, 0.5% of film-forming assistant, 6% of potassium silicate, 10% of lithium silicate, 42% of silica sol, 20% of pure silicon emulsion, 0.85% of inorganic thickener and 0.2% of antiseptic bactericide BIT.
5. An inorganic floor polish dispersion method, comprising the inorganic floor polish of any one of claims 1 to 4, for spraying the inorganic floor polish, specifically comprising the following steps:
s1: mixing purified water and hydroxyethyl cellulose according to a ratio, dispersing at a high speed after mixing,
s2: adding other components in the sequence of a wetting agent, a defoaming agent, a film-forming assistant, potassium silicate, lithium silicate, silica sol, pure phenyl silicone emulsion, an inorganic thickener and an antiseptic bactericide BIT at low speed, and dispersing at low speed;
s3: and performing N-layer thin coating, wherein the interlayer drying time of the N-layer thin coating is more than or equal to 2 hours.
6. The inorganic floor polish dispersion method of claim 5, wherein,
in the step S1, the time for the high-speed dispersion after the mixing is 40 minutes;
in the step S2, the time for low-speed dispersion after adding other components is 20-30 minutes;
in the step S3, the number of N thin coatings is 2-3.
7. An inorganic terrace gloss oil dispersion device, which is used for dispersing the inorganic terrace gloss oil according to any one of the above claims 1 to 4, and is characterized in that the inorganic terrace gloss oil spraying device comprises a main body (1), wherein a dispersion cylinder (8) is arranged inside the main body (1) and close to the edge of the top part, a second motor (6) is fixedly connected to the left side wall of the main body (1), the output end of the second motor (6) extends to the inside of the main body (1) and is fixedly connected with a rotating rod (7), one end of the rotating rod (7) penetrates through the two ends of the dispersion cylinder (8) and is rotatably connected with the left inner side wall of the main body (1) through a bearing (11), a fixing rod (9) is fixedly connected to the surface of the rotating rod (7), and one end of the fixing rod (9) is fixedly connected with the inner side wall of the dispersion cylinder (8); the bottom of the main body (1) is fixedly connected with a box body (2), the left side wall and the right side wall of the box body (2) are both provided with a heat dissipation opening (4), and the interior of the heat dissipation opening (4) is fixedly connected with a dust screen (5); the front of main part (1) just is close to left side fixedly connected with display panel (21), the left inside wall fixedly connected with level sensor (13) of main part (1), through electric connection between level sensor (13) and display panel (21).
8. The inorganic terrace gloss oil dispersion equipment according to claim 7, wherein the inner bottom of the box body (2) is fixedly connected with a first motor (3), the output end of the first motor (3) extends to the inner part of the main body (1) and is fixedly connected with a rotating shaft (24), the surface of the rotating shaft (24) is fixedly connected with a turbine stirrer (14), and the number of the turbine stirrers (14) is multiple.
9. The inorganic terrace gloss oil dispersion equipment according to claim 7, wherein a connecting rod (12) is fixedly connected inside the main body (1) and below the dispersion barrel (8), and the inner side wall of the connecting rod (12) far away from the main body (1) is rotatably connected with one end of the rotating shaft (24) through a bearing (11).
10. The inorganic terrace gloss oil dispersion equipment according to claim 7, wherein the top of the main body (1) is provided with a feed inlet (10), the left and right side walls of the main body (1) and the edge close to the bottom are fixedly connected with discharge pipes (15), and the surface of the discharge pipes (15) is fixedly connected with an electromagnetic valve (16).
11. The inorganic terrace gloss oil dispersion equipment according to claim 7, wherein the front surface of the box body (2) is rotatably connected with a door body (19) through a hinge, and the front surface of the door body (19) and the edge close to the right side edge are fixedly connected with a handle (20).
12. The inorganic terrace gloss oil dispersion equipment according to claim 7, wherein the front of the main body (1) is fixedly connected with a mounting component (22) on the right side of the display panel (21), and the front of the mounting component (22) is movably connected with a control button (23).
13. The inorganic terrace gloss oil dispersion equipment according to claim 7, characterized in that the bottom of the box body (2) is fixedly connected with a leg (17), and the bottom of the leg (17) is fixedly connected with a foot pad (18).
14. The inorganic floor gloss oil dispersion equipment of claim 7, characterized in that: the inner bottom of the main body (1) is arranged obliquely downwards.