CN112645779A - 一种改良酸性土壤的肥料及其制备方法 - Google Patents
一种改良酸性土壤的肥料及其制备方法 Download PDFInfo
- Publication number
- CN112645779A CN112645779A CN202011628606.1A CN202011628606A CN112645779A CN 112645779 A CN112645779 A CN 112645779A CN 202011628606 A CN202011628606 A CN 202011628606A CN 112645779 A CN112645779 A CN 112645779A
- Authority
- CN
- China
- Prior art keywords
- parts
- fertilizer
- humic acid
- soil
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种改良酸性土壤的肥料及其制备方法，涉及化肥领域；包括如下质量份计的组分：硅钙肥40～60份、磷酸一铵5～20份、硫酸钾5～20份、尿素20～30份、改性腐植酸1～10份、轻质碳酸钙1～10份、草木灰1～10份、生石灰1～10份、硅酸盐1～10份，微量元素0～5份。本发明的一种改良酸性土壤的肥料，能改良土壤的酸性，减少重金属元素的危害，提高土壤对肥料的利用率；腐植酸能与水中的金属离子离合，有利于营养元素向作物传送，并能改良土壤结构，有利于农作物的生长，同时腐植酸与金属离子有交换、吸附、螯合等作用；轻质碳酸钙具有多孔结构，能提高土壤的疏松程度。
Description
技术领域
本发明属于化肥领域，具体涉及一种改良酸性土壤的肥料及其制备方法。
背景技术
酸性土壤会使土壤有益微生物数量减少，从而影响有机质的分解和中氮、磷、钾、硫等元素的循环。而且还会造成病菌滋生，根系病害增加，如土壤酸化将会加重农作物根线虫病的滋生与蔓延等。当土壤pH值低于6时，红土壤中磷的固定率随着pH的降低而直线上升，大大降低了磷的有效利用率，成为影响农业发展的严重问题之一。此外，酸性土壤将会促进某些有毒元素的释放、活化、溶出，影响植物的健康。
发明内容
为了克服现有技术的不足，本发明的目的之一在于提供一种改良酸性土壤的肥料，能改良土壤的酸性，减少重金属元素的危害，提高土壤对肥料的利用率。
本发明的目的之二在于提供上述改良酸性土壤的肥料的制备方法。
本发明的目的之一采用如下技术方案实现：
提供一种改良酸性土壤的肥料，包括如下质量份计的组分：
硅钙肥40～60份、磷酸一铵5～20份、硫酸钾5～20份、尿素20～30份、改性腐植酸1～10份、轻质碳酸钙1～10份、草木灰1～10份、生石灰1～10份、硅酸盐1～10份，微量元素0～5份。
进一步地，所述微量元素为硼、锌、铁、锰、钼或镁中的至少一种。
进一步地，所述硅酸盐为碱性长石、高岭石或蒙脱石中的至少一种。
进一步地，所述改性腐植酸通过摩尔比为1.5-2:1的磷酸和氢氧化钾对腐植酸进行改性。
进一步地，包括如下质量份计的组分：
硅钙肥45～55份、磷酸一铵10～15份、硫酸钾5～10份、尿素20～25份、改性腐植酸5～10份、轻质碳酸钙1～5份、草木灰1～5份、生石灰1～5份、硅酸盐1～5份，微量元素1～5份。
本发明的目的之二采用如下技术方案实现：
一种改良酸性土壤的肥料的制备方法，包括以下步骤：
S1，将腐植酸和磷酸溶液加热搅拌，然后加入氢氧化钾进行中和处理，得到改性腐植酸，备用；
S2，在熔融锅中，加入硅钙肥和磷酸一铵，加热搅拌至得到熔融的料浆，然后溢流至一级混合锅中；
S3，在一级混合锅中，往熔融的料浆里加入尿素和硫酸钾，继续加热使物料保持熔融状态，混合后的熔融物溢流至二级混合锅；
S4，在二级混合锅中，往熔融的料浆里依次加入改性腐植酸、轻质碳酸钙、草木灰、生石灰、硅酸盐和微量元素，继续加热使物料保持熔融状态，得到混合熔融料浆；
S5，将步骤S4所得的混合熔融料浆进行造粒，冷却，筛分后，得到肥料。
进一步地，步骤S1的具体工艺为：将质量比为1：1-2的腐植酸和磷酸溶液混合，60-70℃下加热搅拌30-40min，然后加入氢氧化钾进行中和处理，磷酸与氢氧化钾的摩尔比为1.5-2:1，将中和液进行烘干，得到改性腐植酸。腐植酸是动植物遗骸，主要是植物的遗骸，经过微生物的分解和转化，以及地球化学的一系列过程造成和积累起来的一类有机物质，腐植酸大分子的基本结构是芳环和脂环，环上连有羧基、羟基、羰基、醌基、甲氧基等官能团；通过磷酸的酸化处理能活化腐植酸，使可溶性钙等从腐植酸中游离出来，通过氢氧化钾中和，腐植酸能固定磷、钾等元素。
进一步地，步骤S2中，加热温度为160℃～170℃。
进一步地，步骤S3和步骤S4中，加热温度均为145℃～155℃。
进一步地，步骤S5中，在高塔造粒机中完成造粒。
相比现有技术，本发明的有益效果在于：
本发明的一种改良酸性土壤的肥料，能改良土壤的酸性，减少重金属元素的危害，提高土壤对肥料的利用率；腐植酸能与水中的金属离子离合，有利于营养元素向作物传送，并能改良土壤结构，有利于农作物的生长，同时腐植酸与金属离子有交换、吸附、螯合等作用；轻质碳酸钙具有多孔结构，能提高土壤的疏松程度，轻质碳酸钙具有较大的比表面积提供离子交换的通道；草木灰和生石灰具有碱性，能中和酸性的土壤；硅酸盐具有一定的粘结力使肥料更容易造粒成型，提高稳定性，同时可吸附的可溶性成分并施入土壤后缓慢释放；通过肥料各组分的协同作用，改良酸性土质，并提高作物抗逆能力。
具体实施方式
下面，结合与具体实施方式，对本发明做进一步描述，需要说明的是，在不相冲突的前提下，以下描述的各实施例之间或各技术特征之间可以任意组合形成新的实施例。
实施例1
硅钙肥45份、磷酸一铵10份、硫酸钾5份、尿素20份、改性腐植酸5份、轻质碳酸钙1份、草木灰1份、生石灰1份、碱性长石1份，微量元素1份；所述微量元素包括硼、锌、铁、锰和钼；硅钙肥中二氧化硅含量不低于35％，钙含量不低于20％。
一种改良酸性土壤的肥料的制备方法，包括以下步骤：
S1，将质量比为1:1的腐植酸和磷酸溶液混合，60℃下加热搅拌40min，然后加入氢氧化钾进行中和处理，磷酸与氢氧化钾的摩尔比为1.5:1，将中和液进行烘干，得到改性腐植酸；
S2，在熔融锅中，加入硅钙肥和磷酸一铵，160℃下加热搅拌至得到熔融的料浆，然后溢流至一级混合锅中；
S3，在一级混合锅中，往熔融的料浆里加入尿素和硫酸钾，继续150℃下加热使物料保持熔融状态，混合后的熔融物溢流至二级混合锅；
S4，在二级混合锅中，往熔融的料浆里依次加入改性腐植酸、轻质碳酸钙、草木灰、生石灰、硅酸盐和微量元素，继续145℃下加热使物料保持熔融状态，得到混合熔融料浆；
S5，将步骤S4所得的混合熔融料浆在高塔造粒机中进行造粒，冷却，筛分后，得到肥料。
实施例2
硅钙肥55份、磷酸一铵15份、硫酸钾10份、尿素25份、改性腐植酸10份、轻质碳酸钙5份、草木灰5份、生石灰5份、高岭石5份，微量元素5份；所述微量元素包括硼、镁、铁、锰和钼；硅钙肥中二氧化硅含量不低于35％，钙含量不低于20％。
一种改良酸性土壤的肥料的制备方法，包括以下步骤：
S1，将质量比为1:2的腐植酸和磷酸溶液混合，70℃下加热搅拌30min，然后加入氢氧化钾进行中和处理，磷酸与氢氧化钾的摩尔比为2:1，将中和液进行烘干，得到改性腐植酸；
S2，在熔融锅中，加入硅钙肥和磷酸一铵，170℃下加热搅拌至得到熔融的料浆，然后溢流至一级混合锅中；
S3，在一级混合锅中，往熔融的料浆里加入尿素和硫酸钾，继续155℃下加热使物料保持熔融状态，混合后的熔融物溢流至二级混合锅；
S4，在二级混合锅中，往熔融的料浆里依次加入改性腐植酸、轻质碳酸钙、草木灰、生石灰、硅酸盐和微量元素，继续150℃下加热使物料保持熔融状态，得到混合熔融料浆；
S5，将步骤S4所得的混合熔融料浆在高塔造粒机中进行造粒，冷却，筛分后，得到肥料。
实施例3
硅钙肥50份、磷酸一铵12份、硫酸钾8份、尿素22份、改性腐植酸8份、轻质碳酸钙3份、草木灰3份、生石灰2份、蒙脱石2份，微量元素2份；所述微量元素包括硼、锌、铁、锰、钼和镁；硅钙肥中二氧化硅含量不低于35％，钙含量不低于20％。
一种改良酸性土壤的肥料的制备方法，包括以下步骤：
S1，将质量比为1:2的腐植酸和磷酸溶液混合，70℃下加热搅拌30min，然后加入氢氧化钾进行中和处理，磷酸与氢氧化钾的摩尔比为2:1，将中和液进行烘干，得到改性腐植酸；
S2，在熔融锅中，加入硅钙肥和磷酸一铵，170℃下加热搅拌至得到熔融的料浆，然后溢流至一级混合锅中；
S3，在一级混合锅中，往熔融的料浆里加入尿素和硫酸钾，继续150℃下加热使物料保持熔融状态，混合后的熔融物溢流至二级混合锅；
S4，在二级混合锅中，往熔融的料浆里依次加入改性腐植酸、轻质碳酸钙、草木灰、生石灰、硅酸盐和微量元素，继续150℃下加热使物料保持熔融状态，得到混合熔融料浆；
S5，将步骤S4所得的混合熔融料浆在高塔造粒机中进行造粒，冷却，筛分后，得到肥料。
性能测试
试田栽培：取3块呈酸性的水稻田，分别使用实施例1-3的肥料按照50千克/亩进行施肥，施肥进行播种，测定土壤pH值的变化和水稻的产量，结果如表1所示。
表1：测试结果
如表1所示，本发明的一种改良酸性土壤的肥料，能改良土壤的酸性，减少重金属元素的危害，提高土壤对肥料的利用率。
上述实施方式仅为本发明的优选实施方式，不能以此来限定本发明保护的范围，本领域的技术人员在本发明的基础上所做的任何非实质性的变化及替换均属于本发明所要求保护的范围。
Claims (10)
1.一种改良酸性土壤的肥料，其特征在于，包括如下质量份计的组分：
硅钙肥40～60份、磷酸一铵5～20份、硫酸钾5～20份、尿素20～30份、改性腐植酸1～10份、轻质碳酸钙1～10份、草木灰1～10份、生石灰1～10份、硅酸盐1～10份，微量元素0～5份。
2.如权利要求1所述的一种改良酸性土壤的肥料，其特征在于：所述微量元素为硼、锌、铁、锰、钼或镁中的至少一种。
3.如权利要求1所述的一种改良酸性土壤的肥料，其特征在于：所述硅酸盐为碱性长石、高岭石或蒙脱石中的至少一种。
4.如权利要求1所述的一种改良酸性土壤的肥料，其特征在于：所述改性腐植酸通过摩尔比为1.5-2:1的磷酸和氢氧化钾对腐植酸进行改性。
5.如权利要求1所述的一种改良酸性土壤的肥料，其特征在于：包括如下质量份计的组分：
硅钙肥45～55份、磷酸一铵10～15份、硫酸钾5～10份、尿素20～25份、改性腐植酸5～10份、轻质碳酸钙1～5份、草木灰1～5份、生石灰1～5份、硅酸盐1～5份，微量元素1～5份。
6.权利要求1-5任意一项所述的一种改良酸性土壤的肥料的制备方法，其特征在于，包括以下步骤：
S1，将腐植酸和磷酸溶液加热搅拌，然后加入氢氧化钾进行中和处理，得到改性腐植酸，备用；
S2，在熔融锅中，加入硅钙肥和磷酸一铵，加热搅拌至得到熔融的料浆，然后溢流至一级混合锅中；
S3，在一级混合锅中，往熔融的料浆里加入尿素和硫酸钾，继续加热使物料保持熔融状态，混合后的熔融物溢流至二级混合锅；
S4，在二级混合锅中，往熔融的料浆里依次加入改性腐植酸、轻质碳酸钙、草木灰、生石灰、硅酸盐和微量元素，继续加热使物料保持熔融状态，得到混合熔融料浆；
S5，将步骤S4所得的混合熔融料浆进行造粒，冷却，筛分后，得到肥料。
7.如权利要求6所述的一种改良酸性土壤的肥料的制备方法，其特征在于，步骤S1的具体工艺为：将质量比为1：1-2的腐植酸和磷酸溶液混合，60-70℃下加热搅拌30-40min，然后加入氢氧化钾进行中和处理，磷酸与氢氧化钾的摩尔比为1.5-2:1，将中和液进行烘干，得到改性腐植酸。
8.如权利要求6所述的一种改良酸性土壤的肥料的制备方法，其特征在于，步骤S2中，加热温度为160℃～170℃。
9.如权利要求6所述的一种改良酸性土壤的肥料的制备方法，其特征在于，步骤S3和步骤S4中，加热温度均为145℃～155℃。
10.如权利要求6所述的一种改良酸性土壤的肥料的制备方法，其特征在于，步骤S5中，在高塔造粒机中完成造粒。