CN112552638A - 一种白色的具有透度的abs复合材料及其制备方法 - Google Patents
一种白色的具有透度的abs复合材料及其制备方法 Download PDFInfo
- Publication number
- CN112552638A CN112552638A CN202011442979.XA CN202011442979A CN112552638A CN 112552638 A CN112552638 A CN 112552638A CN 202011442979 A CN202011442979 A CN 202011442979A CN 112552638 A CN112552638 A CN 112552638A
- Authority
- CN
- China
- Prior art keywords
- composite material
- antioxidant
- abs
- abs composite
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种白色的具有透度的ABS复合材料及其制备方法，所述复合材料组分为由ABS、硫酸钡、钛白粉和抗氧剂组成。本发明提高了材料的透光性能、提高了产品的白度，同时降低了材料成本。
Description
技术领域
本发明属于ABS复合材料及其制备领域，特别涉及一种白色的具有透度的ABS复合材料及其制备方法。
背景技术
ABS树脂是五大合成树脂之一，其抗冲击性、耐热性、耐低温性、耐化学药品性及电气性能优良，还具有易加工、制品尺寸稳定、表面光泽性好等特点，容易涂装、着色，还可以进行表面喷镀金属、焊接、热压和粘接等二次加工，广泛应用于机械、汽车、电子电器、仪器仪表、纺织和建筑等工业领域，是一种用途极广的热塑性工程塑料。今年来ABS材料被广泛的应用到空调面板、洗衣机外壳、电器开关面板等产品上。此类产品要求材料具有一定的透度，在数显打开的情况下能清晰的显示出数显的内容。但是ABS本身容易黄变，通过双螺杆挤出后，材料黄变明显导致透度下降，因此阻止或改善材料的黄变显的格外重要。
发明内容
本发明所要解决的技术问题是提供一种白色的具有透度的ABS复合材料及其制备方法，克服现有材料黄变明显导致透度下降的技术缺陷。
本发明的一种ABS复合材料，按质量百分比，原料组分为：
进一步地，按质量百分比，原料组分为：
所述ABS具有白色蓝底色相特点。
所述抗氧剂为单一抗氧剂或者复合抗氧剂。
所述抗氧剂为受阻酚类抗氧剂和/或亚磷酸酯类抗氧剂。
本发明的一种ABS复合材料的制备方法，包括：
按权利要求1所述配比称取原料，混合均匀后加入到双螺杆挤出机中，经过熔融共混挤出造粒，得到ABS复合材料。
所述熔融温度为200-220℃。
本发明的一种所述ABS复合材料在家用电器面板和外壳中的应用，如洗衣机面板、空调板面，智能开关面板、家用电器外壳。
有益效果
本发明复合材料由ABS、硫酸钡、钛白粉组成。本发明通过加入硫酸钡，提高了材料的透光性能、提高了产品的白度，同时降低了材料成本。
具体实施方式
下面结合具体实施例，进一步阐述本发明。应理解，这些实施例仅用于说明本发明而不用于限制本发明的范围。此外应理解，在阅读了本发明讲授的内容之后，本领域技术人员可以对本发明作各种改动或修改，这些等价形式同样落于本申请所附权利要求书所限定的范围。
(1)原料来源
苯乙烯类树脂，丙烯腈-丙烯酸丁酯-苯乙烯树脂，上海高桥石化公司，牌号ABS8434；
硫酸钡，市售；
钛白粉：市售；
抗氧剂为受阻酚抗氧剂与亚磷酸酯类抗氧剂按照质量比1:2的比例混合物，受阻酚抗氧剂为抗氧剂为Y-001，亚磷酸酯类抗氧剂为抗氧剂Y-002，二者均由Ciba公司生产提供。
(2)测试方法：
1.透光度测试：
将所得ABS复合材料产品在鼓风烘箱中于80℃干燥2小时后，用210℃的注塑温度注塑成83MM*54MM*2MM尺寸的表面无皮纹的光滑色板。
实验结束后，用X-rite7000A色差仪测量色板的Y值，Y值越大表示透光性越好。
2.白度测试：
将所得ABS复合材料产品在鼓风烘箱中于80℃干燥2小时后，用210℃的注塑温度注塑成83MM*54MM*2MM尺寸的表面无皮纹的光滑色板表
实验结束后，用X-rite7000A色差仪测量色板的L值，L值越大表示白度越白。
3.耐黄变测试：
将所得ABS复合材料产品在鼓风烘箱中于80℃干燥2小时后，用210℃的注塑温度注塑成83MM*54MM*2MM尺寸的表面无皮纹的光滑色板表
实验结束后，用X-rite7000A色差仪测量色板的b值，b值越小表示黄变越小，耐黄变性能越好。
实施例1-6
将ABS树脂、硫酸钡、抗氧剂、钛白粉按表1中的组成配方混合后加入到双螺杆挤出机(螺杆直径为35mm，长径比L/D＝48)的主机筒中。主机筒各段控制温度(从加料口至机头出口)分别为190℃、200℃、200℃、200℃、205℃，双螺杆转速为300转/分钟，挤出料条经过水槽冷却后切粒，即得ABS复合材料。
对比例1-3
按表1配比称取原料，混合后加入到双螺杆挤出机(螺杆直径为35mm，长径比L/D＝48)的主机筒中。主机筒各段控制温度(从加料口至机头出口)分别为190℃、200℃、200℃、200℃、205℃，双螺杆转速为300转/分钟，挤出料条经过水槽冷却后切粒，即得ABS复合材料。
表1实施例和对比例的组成配方(重量百分比)
表2实施例和对比例的性能数据表
由对照例3和实施例1-4结果可得出以下结论：硫酸钡对材料的透光度、白度、耐黄变性能有明显的提升，随着硫酸钡含量的提高，材料的透光率也在提高，当硫酸钡含量高于2％后，趋于稳定。由对照例1-2和实施例5-6可得出以下结论：硫酸钡相比抗氧剂更能提高材料的透光率，提升材料的耐黄变性能。由于硫酸钡相比抗氧剂成本低很多，因此可以降低材料成本。
Claims (8)
1.一种ABS复合材料，其特征在于，按质量百分比，原料组分为：
2.根据权利要求1所述复合材料，其特征在于，按质量百分比，原料组分为：
3.根据权利要求1所述复合材料，其特征在于，所述ABS具有白色蓝底色相。
4.根据权利要求1所述复合材料，其特征在于，所述抗氧剂为单一抗氧剂或者复合抗氧剂。
5.根据权利要求1所述复合材料，其特征在于，所述抗氧剂为受阻酚类抗氧剂和/或亚磷酸酯类抗氧剂。
6.一种ABS复合材料的制备方法，包括：
按权利要求1所述配比称取原料，混合均匀后加入到双螺杆挤出机中，经过熔融共混挤出造粒，得到ABS复合材料。
7.根据权利要求6所述制备方法，其特征在于，所述熔融温度为200-220℃。
8.一种权利要求1所述ABS复合材料在家用电器面板和外壳中的应用。