CN112535758A - Hollow conical incense and preparation method thereof - Google Patents
Hollow conical incense and preparation method thereof Download PDFInfo
- Publication number
- CN112535758A CN112535758A CN202011591350.1A CN202011591350A CN112535758A CN 112535758 A CN112535758 A CN 112535758A CN 202011591350 A CN202011591350 A CN 202011591350A CN 112535758 A CN112535758 A CN 112535758A
- Authority
- CN
- China
- Prior art keywords
- incense
- mixture
- powder
- diameter
- die
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a hollow conical incense and a preparation method thereof, wherein the hollow conical incense is prepared by humidifying and rolling raw materials to prepare a mixture; then filling the mixture into a first right cone mould, inserting a second right cone mould with smaller diameter and height of the bottom surface than the first mould and smooth appearance into the first cone mould from the circle center of the bottom surface of the first mould, and extruding the redundant mixture; standing for 5-6min for molding, taking out the right cone mold II, then opening the cone mold I, standing at room temperature, and naturally drying to obtain hollow conical incense. Through the difference of the diameter and the height of the bottom surfaces of the first die and the second die, the transverse thickness of the incense is gradually reduced from the middle to the bottom, so that the shape that the diameter of the upper part of the incense is small, but the transverse thickness of the incense is large, and the diameter of the lower part of the incense is large, but the transverse thickness of the incense is small is formed, and therefore, the combustion amount in each time period is equivalent when the incense is combusted.
Description
Technical Field
The invention relates to a hollow conical incense and a preparation method thereof.
Background
The incense is prepared from original incense materials and spices by simple processing such as cleaning, drying, cutting and the like. The habit of incense comes from religious belief. According to the appearance characteristics, the incense can be divided into original incense materials, line incense, coil incense, tower incense, incense pill, incense powder, incense seal, balm, coating incense, incense soup, sachet, incense pillow and the like.
Ancient Chinese incenses have many apparatuses, mainly including a smoking furnace and a smoking cage. However, with the rapid development of socio-economy, the variety of cross-domain, cross-industry and cross-regional work is more and more, and a considerable part of people often run on the way of business. Frequent business trips often lead to physical and mental fatigue, and also require the entrance of strange and not particularly sanitary hotels and hotels, and the sleep quality is also particularly poor. If a piece of incense is added, the incense can not only play a role in dispelling fatigue, soothing the nerves and calming the nerves, but also can remove peculiar smell in a room, and has better sleep in a hard business trip. However, when the existing incense is used, a smoking oven or a smoking cage device is required, and even if the devices are not used, in order to prevent burning ashes from directly falling to the floor to cause fire, be inconvenient to clean and the like, a metal plate (similar to a mosquito incense plate) for placing incense and storing ashes needs to be carried. However, for the people who often go on a business trip, it is very inconvenient to carry the smoking oven, the smoking cage or the metal plate with them.
At present, tower incense (shown in figures 1-2), also called as incense tower, is available on the market, and conical incense can be put in an incense burner for direct fumigation; or placing the tower incense on a nonflammable medium such as ceramic or glass. However, the tower incense is conical and has a small upper part and a large lower part, so when the tower incense is burnt to the upper part, the fragrance is insufficient; however, when the fuel is burned to the lower part, the fragrance tends to be too strong.
Disclosure of Invention
The invention aims to provide a hollow conical incense and a preparation method thereof, aiming at overcoming the defects of the prior art.
In order to achieve the purpose, the invention adopts the following technical scheme:
a preparation method of hollow conical incense comprises the following steps:
(1) the raw materials are taken according to the parts by weight as follows: 10-12 parts of sandalwood powder, 2-4 parts of sticky powder, 0.1-0.2 part of chamomile essential oil, 0.2-0.3 part of tea tree essential oil, 2-3 parts of konjac glucomannan fine powder, 0.3-0.4 part of mint powder and 0.8-1.0 part of folium artemisiae argyi powder, and putting the mixture into a drying container;
(2) adding the coix seed water extract into the container in the step (1), and continuously rolling and kneading the mixture, wherein the mixture is prepared when the viscosity of the mixture is not sticky to the container;
(3) filling the mixture into a first right cone mould, inserting a second right cone mould with smaller diameter and height of the bottom surface than the first mould and smooth appearance into the first cone mould from the circle center of the bottom surface of the first mould, and extruding the redundant mixture;
(4) standing for 5-10min for molding, taking out the right cone mold II, then opening the cone mold I, standing at room temperature, and naturally drying to obtain hollow conical incense;
(5) adhering a round tinfoil paper at the bottom of the hollow conical incense, forming a small round hole with a diameter of 2-3mm at the center of the round tinfoil paper, and packaging the incense with thin paper to obtain the final product.
Preferably, the raw materials in the step (1) are as follows according to parts by weight: 11 parts of sandalwood powder, 3 parts of sticky powder, 0.1 part of chamomile essential oil, 0.2 part of tea tree essential oil, 2 parts of konjac glucomannan fine powder, 0.3 part of mint powder and 0.9 part of folium artemisiae argyi powder, and putting the mixture into a drying container.
Preferably, the preparation method of the coix seed water extract in the step (2) comprises the following steps: grinding Coicis semen into powder, adding 3-5 times of water, decocting at 80-90 deg.C for 3-4 hr to obtain Coicis semen water extractive solution, and cooling.
Preferably, the coix seed water extract in the step (2) is added in an amount such that the viscosity of the mixture after rolling does not stick to the container. The coix seed water extract is added for a small amount of times to prevent the mixture from being over-wet.
Preferably, the diameter of the bottom surface of the first die in the step (3) is 2-3cm, and the height of the bottom surface of the first die is 4-5 cm; the diameter of the bottom surface of the second die is 1cm smaller than that of the first die, and the height of the second die is 1-1.2cm smaller than that of the first die.
Preferably, the diameter of the round tin foil paper in the step (5) is 1cm larger than that of the bottom of the incense, and the part of the round tin foil paper, which exceeds the bottom of the incense, is folded upwards along the incense direction and wraps the periphery of the incense.
In order to achieve the purpose, the invention adopts the following technical scheme: the hollow conical incense prepared by the preparation method is provided.
The invention has the beneficial effects that:
1) according to the invention, konjac glucomannan fine powder is added into the mixed spice, so that the konjac glucomannan fine powder has strong toughness, good ductility and good adhesion and hydrophilicity, is easier to form in the tumbling mixing and molding processes, and ensures that the phenomena of powder discharge and powder falling are not easy to occur in the storage process of subsequent products;
2) the coix seed water extract has amphipathy and solubilization, and can achieve better humidity regulating effect with smaller dosage compared with water in the humidity regulating mixture process; the subsequent drying time of the incense is shortened by reducing the water consumption; moreover, the coix seed water extract is rich in oil substances such as coix seed ester and the like, so that the incense cannot be burnt out to influence use even if the coix seed water extract is left in the incense;
3) according to the invention, by setting the difference between the diameter and the height of the bottom surfaces of the first die and the second die, the transverse thickness of the incense is gradually reduced from the middle to the bottom, so that the shape that the diameter of the upper part of the incense is small, the transverse thickness of the incense is large, the diameter of the lower part of the incense is large, and the transverse thickness of the incense is small is formed, and therefore, the combustion amount in each time period is equivalent when the incense is combusted;
4) according to the invention, a round tinfoil paper is adhered to the bottom of each incense, a small round hole with the diameter of 2-3mm is formed in the center of the round tinfoil paper, and the tinfoil paper can resist flame and insulate heat; when the product is used, the tinfoil paper folded upwards is slightly opened, so that the tinfoil paper forms a small disc capable of containing ashes, the product is placed on the floor, the ashes generated in combustion can drop on the tinfoil paper, after the incense is burnt out, the ashes are wrapped by the tinfoil paper, and the garbage can is thrown into the garbage can.
Drawings
Fig. 1 is a perspective view of a conventional tower incense.
Fig. 2 is a longitudinal half sectional view of a conventional tower incense.
FIG. 3 is a perspective view of the hollow conical incense of the present invention.
Fig. 4 is a schematic perspective view of the product of the present invention.
Figure 5 is a longitudinal half-sectional view of a product of the invention.
Reference numerals: 100', existing conical tower incense; 100. hollow conical incense; 101. a conical cavity; 200. circular tinfoil paper; 201. folding edges; 210. a small round hole.
Detailed Description
In order to make the aforementioned and other features and advantages of the invention more comprehensible, embodiments accompanied with figures are described in detail below.
Example 1: as shown in FIGS. 3 to 5, a method for preparing hollow conical incense comprises the following steps:
(1) the raw materials are taken according to the parts by weight as follows: 10 parts of sandalwood powder, 4 parts of sticky powder, 0.1 part of chamomile essential oil, 0.3 part of tea tree essential oil, 2 parts of konjac glucomannan fine powder, 0.4 part of mint powder and 0.8 part of folium artemisiae argyi powder, and putting the mixture into a drying container;
(2) adding the coix seed water extract into the container in the step (1), and continuously rolling and kneading the mixture, wherein the mixture is prepared when the viscosity of the mixture is not sticky to the container;
(3) filling the mixture into a first right cone mould, inserting a second right cone mould with smaller diameter and height of the bottom surface than the first mould and smooth appearance into the first cone mould from the circle center of the bottom surface of the first mould, and extruding the redundant mixture;
(4) standing for 5min for molding, taking out the right cone mold II, then opening the cone mold I, standing at room temperature, and naturally drying to obtain hollow conical incense;
(5) adhering a round tinfoil paper to the bottom of the hollow conical incense, forming a small round hole with a diameter of 2mm at the center of the round tinfoil paper, and packaging the incense with thin paper to obtain the final product.
In this example 1, the preparation method of the mint powder of step (1) is: sun drying fresh stems and leaves of herba Menthae, and grinding into powder; the preparation method of the folium artemisiae argyi powder comprises the following steps: drying fresh folium Artemisiae Argyi in the sun, and grinding into powder for use.
In this example 1, the preparation method of the water extract of coix seed in step (2) comprises: grinding Coicis semen into powder, adding 3 times of water, decocting at 90 deg.C for 3 hr to obtain Coicis semen water extractive solution, and cooling.
In the embodiment 1, the diameter of the bottom surface of the first mold in the step (3) is 2cm, and the height is 4 cm; the diameter of the bottom surface of the second die is 1cm smaller than that of the first die, and the height of the second die is 1cm smaller than that of the first die.
In this embodiment 1, the diameter of the circular tin foil paper in step (5) is 1cm larger than the diameter of the bottom of the incense, and the part of the circular tin foil paper beyond the bottom of the incense is folded upwards along the incense direction to wrap the periphery of the incense.
As shown in figures 3-5, a hollow conical incense prepared by the preparation method.
Example 2: as shown in FIGS. 3 to 5, a method for preparing hollow conical incense comprises the following steps:
(1) the raw materials are taken according to the parts by weight as follows: 11 parts of sandalwood powder, 3 parts of sticky powder, 0.1 part of chamomile essential oil, 0.2 part of tea tree essential oil, 2 parts of konjac glucomannan fine powder, 0.3 part of mint powder and 0.9 part of folium artemisiae argyi powder, and putting the mixture into a drying container;
(2) adding the coix seed water extract into the container in the step (1), and continuously rolling and kneading the mixture, wherein the mixture is prepared when the viscosity of the mixture is not sticky to the container;
(3) filling the mixture into a first right cone mould, inserting a second right cone mould with smaller diameter and height of the bottom surface than the first mould and smooth appearance into the first cone mould from the circle center of the bottom surface of the first mould, and extruding the redundant mixture;
(4) standing for 8min for molding, taking out the right cone mold II, then opening the cone mold I, standing at room temperature, and naturally drying to obtain hollow conical incense;
(5) adhering a round tinfoil paper to the bottom of the hollow conical incense, forming a small round hole with a diameter of 3mm at the center of the round tinfoil paper, and packaging the incense with thin paper to obtain the final product.
In this embodiment 2, the preparation method of the water extract of coix seed in step (2) comprises: grinding Coicis semen into powder, adding 4 times of water, decocting at 85 deg.C for 3.5 hr to obtain Coicis semen water extractive solution, and cooling.
In the embodiment 2, the diameter of the bottom surface of the first mold in the step (3) is 2cm, and the height is 5 cm; the diameter of the bottom surface of the second die is 1cm smaller than that of the first die, and the height of the second die is 1.2cm smaller than that of the first die.
In this embodiment 2, the diameter of the circular tin foil paper in step (5) is 1cm larger than the diameter of the bottom of the incense, and the part of the circular tin foil paper beyond the bottom of the incense is folded upwards along the incense direction to wrap the periphery of the incense.
As shown in figures 3-5, a hollow conical incense prepared by the preparation method.
Example 3: as shown in FIGS. 3 to 5, a method for preparing hollow conical incense comprises the following steps:
(1) the raw materials are taken according to the parts by weight as follows: 12 parts of sandalwood powder, 2 parts of sticky powder, 0.2 part of chamomile essential oil, 0.2 part of tea tree essential oil, 3 parts of konjac glucomannan fine powder, 0.3 part of mint powder and 1.0 part of folium artemisiae argyi powder, and putting the mixture into a drying container;
(2) adding the coix seed water extract into the container in the step (1), and continuously rolling and kneading the mixture, wherein the mixture is prepared when the viscosity of the mixture is not sticky to the container;
(3) filling the mixture into a first right cone mould, inserting a second right cone mould with smaller diameter and height of the bottom surface than the first mould and smooth appearance into the first cone mould from the circle center of the bottom surface of the first mould, and extruding the redundant mixture;
(4) standing for 5-6min for molding, taking out the right cone mold II, then opening the cone mold I, standing at room temperature, and naturally drying to obtain hollow conical incense;
(5) adhering a round tinfoil paper at the bottom of the hollow conical incense, forming a small round hole with a diameter of 2-3mm at the center of the round tinfoil paper, and packaging the incense with thin paper to obtain the final product.
In this embodiment 3, the preparation method of the water extract of coix seed in step (2) comprises: grinding Coicis semen into powder, adding 5 times of water, decocting at 85 deg.C for 3.5h to obtain Coicis semen water extractive solution, and cooling.
In this example 3, the diameter of the bottom surface of the first mold of step (3) is 3cm, and the height is 5 cm; the diameter of the bottom surface of the second die is 1cm smaller than that of the first die, and the height of the second die is 1.1cm smaller than that of the first die.
In this embodiment 3, the diameter of the circular tin foil paper in step (5) is 1cm larger than the diameter of the bottom of the incense, and the part of the circular tin foil paper beyond the bottom of the incense is folded upwards along the incense direction to wrap the periphery of the incense.
As shown in figures 3-5, a hollow conical incense prepared by the preparation method.
Comparative example 1: compared with the embodiment 2, the difference is that: konjac glucomannan fine powder is not added.
Comparative example 2: compared with the embodiment 2, the difference is that: water is used to replace coix seed water extract.
Performance analysis:
1. analysis of Molding Effect
Comparing the incense prepared in the embodiment 2, the comparative example 1 and the comparative example 2, it can be seen that the incense in the embodiment 2 and the comparative example 2 has shorter forming time, better forming effect and no powder discharge and powder falling phenomena; the incense of comparative example 1 takes 8-12min to form, and the forming effect is not good.
2. Analysis of drying and Combustion Effect
The incense prepared in the example 2, the comparative example 1 and the comparative example 2 is dried and combusted in the same environment, and the comparison shows that the incense in the example 2 has the shortest drying time and has no intermediate combustion and extinguishment phenomenon in the process of sampling and pilot combustion; the incense drying time of the comparative example 1 is 10-15min longer than that of the incense drying time of the example 2, and only 5% of the samples are burnt and extinguished midway in the process of sampling and burning; the drying time of the incense in the comparative example 2 is 20-30min longer than that of the incense in the example 2, and 15% of midway burning and extinguishing phenomena appear in the process of sampling and burning the test sample.
It should be understood, however, that the description herein of specific embodiments is not intended to limit the invention to the particular forms disclosed, but on the contrary, the intention is to cover all modifications, equivalents, and alternatives falling within the spirit and scope of the invention as defined by the appended claims.
Claims (7)
1. A preparation method of hollow conical incense is characterized in that: the method comprises the following steps:
(1) the raw materials are taken according to the parts by weight as follows: 10-12 parts of sandalwood powder, 2-4 parts of sticky powder, 0.1-0.2 part of chamomile essential oil, 0.2-0.3 part of tea tree essential oil, 2-3 parts of konjac glucomannan fine powder, 0.3-0.4 part of mint powder and 0.8-1.0 part of folium artemisiae argyi powder, and putting the mixture into a drying container;
(2) adding the coix seed water extract into the container in the step (1), and continuously rolling and kneading the mixture, wherein the mixture is prepared when the viscosity of the mixture is not sticky to the container;
(3) filling the mixture into a first right cone mould, inserting a second right cone mould with smaller diameter and height of the bottom surface than the first mould and smooth appearance into the first cone mould from the circle center of the bottom surface of the first mould, and extruding the redundant mixture;
(4) standing for 5-10min for molding, taking out the right cone mold II, then opening the cone mold I, standing at room temperature, and naturally drying to obtain hollow conical incense;
(5) adhering a round tinfoil paper at the bottom of the hollow conical incense, forming a small round hole with a diameter of 2-3mm at the center of the round tinfoil paper, and packaging the incense with thin paper to obtain the final product.
2. The method of claim 1, wherein the method comprises: the method comprises the following steps of (1) taking the following raw materials in parts by weight: 11 parts of sandalwood powder, 3 parts of sticky powder, 0.1 part of chamomile essential oil, 0.2 part of tea tree essential oil, 2 parts of konjac glucomannan fine powder, 0.3 part of mint powder and 0.9 part of folium artemisiae argyi powder, and putting the mixture into a drying container.
3. The method of claim 1, wherein the method comprises: the preparation method of the coix seed water extract in the step (2) comprises the following steps: grinding Coicis semen into powder, adding 3-5 times of water, decocting at 80-90 deg.C for 3-4 hr to obtain Coicis semen water extractive solution, and cooling.
4. The method of claim 1, wherein the method comprises: the adding amount of the coix seed water extract in the step (2) is based on the condition that the viscosity of the mixture is not sticky to a container after the mixture is rolled and kneaded.
5. The method of claim 1, wherein the method comprises: the diameter of the bottom surface of the first die in the step (3) is 2-3cm, and the height of the bottom surface of the first die is 4-5 cm; the diameter of the bottom surface of the second die is 1cm smaller than that of the first die, and the height of the second die is 1-1.2cm smaller than that of the first die.
6. The method of claim 1, wherein the method comprises: the diameter of the round tin foil paper in the step (5) is 1-1.5cm larger than that of the bottom of the incense, and the part which exceeds the bottom of the incense is folded upwards along the incense direction and wraps the periphery of the incense.
7. A hollow, conical incense manufactured by the method of any of claims 1 to 6.