CN112450134B - 一种适用于稻虾种养模式的矿物改良剂及其制备使用方法 - Google Patents
一种适用于稻虾种养模式的矿物改良剂及其制备使用方法 Download PDFInfo
- Publication number
- CN112450134B CN112450134B CN202011194542.9A CN202011194542A CN112450134B CN 112450134 B CN112450134 B CN 112450134B CN 202011194542 A CN202011194542 A CN 202011194542A CN 112450134 B CN112450134 B CN 112450134B
- Authority
- CN
- China
- Prior art keywords
- rice
- crayfish
- mineral
- mineral modifier
- breeding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种适用于稻虾种养模式的矿物改良剂，主要成分为30～50％的β‑硅酸二钙和50～70％的γ‑硅酸二钙。其制备方法包括以下步骤：(1)将钙质材料和硅质材料粉磨至细度为150～300目；(2)将钙质材料和硅质材料混合后烧制；(3)将煅烧后的产物冷却至100℃以下；(4)将烧制后的物料粉磨至80～200目，即制成矿物改良剂。本发明制备的矿物改良剂具有对小龙虾养殖池塘土壤消毒，改善小龙虾养殖水体pH，补充水体钙含量，促进小龙虾生长，提高小龙虾产量，且能够有效促进后期水稻生长，降低水稻中重金属镉含量等一系列优点。
Description
技术领域
本发明涉及稻虾种养技术领域，尤其涉及一种适用于稻虾种养模式的矿物改良剂。
背景技术
目前稻虾种养模式是我国种养结合规模较大的一种农业生产方式，其中小龙虾养殖具有较大的社会需求量，且养殖小龙虾后生产水稻过程中不需要施用化肥和农药，生产的大米为绿色生态大米，具有较高的经济价值，适合建设发展高端大米品牌。在稻虾种养过程中，往往通过每亩撒施50kg～100kg石灰对池塘进行消毒，在小龙虾养殖过程中需要添加碱性物质调节水体pH，使水体pH保持在7.5～8.5之间，且需要添加较多的含钙物质，促进小龙虾的脱壳生长。这种种养方式在各项环节需根据养殖情况时刻进行调整，部分措施在调整时具有一定的延时性，可能会在一定程度上影响小龙虾的生长发育。另一方面，目前部分养殖小龙虾池塘在后期的水稻种植过程中出现大米镉超标的情况，在较大程度上影响大米的品质，降低稻虾种养模式的整体收益。
发明内容
本发明为解决现有技术中存在的不足，提供一种适用于稻虾种养模式的矿物改良剂及其制备和使用方法。
本发明的目的是通过以下技术方实现的：
一种适用于稻虾种养模式的矿物改良剂，其主要成分为30～50％的β-硅酸二钙和50～70％的γ-硅酸二钙。
相对于现有技术，本发明所述的矿物改良剂能够通过水化提高养殖区域土壤 pH，对养殖池塘进行消毒，提高养殖水体的pH，补充水体的钙含量，增加小龙虾生长速度，提高小龙虾产量，同时能够有效促进后期水稻生长，降低水稻中重金属镉的含量，提高稻米品质，增加稻虾养殖模式的整体收益。
进一步，一种适用于稻虾种养模式的矿物改良剂的制备方法，包括以下步骤：
S1备料：将钙质材料和硅质材料粉磨至细度为150～300目；
S2烧制：将钙质材料和硅质材料混合后烧制；
S3冷却：将煅烧后的产物冷却至100℃以下；
S4粉磨：将烧制后的物料冷却后粉磨至80～200目，即制成矿物改良剂。
进一步，步骤S1中，钙质材料为石灰石、白云石、工业副产物石灰或贝壳中的一种或几种。
进一步，步骤S1中，硅质材料为硅石、矽砂、硅灰石、膨润土或废弃混凝土中的一种或几种。
进一步，步骤S2中，钙质材料和硅质材料中CaO与SiO2的百分含量配比比值为1.8～2.5。
进一步，步骤S2中，烧制温度为1150～1450℃，烧制时间为0.5～3小时。
进一步，步骤S3中，先将煅烧后的产物冷却至500～650℃，保持该温度区间0.5～4小时，然后再迅速冷却至100℃以下。
同时，本发明还提供一种适用于稻虾种养模式的矿物改良剂的使用方法。
一种适用于稻虾种养模式的矿物改良剂，包括以下步骤：
S1：在冬季小龙虾养殖塘口清理时在农田土壤均匀撒施上述方法制备的矿物改良剂，旋耕1～2次；
S2：放浅水浸泡后，按照小龙虾养殖需要进行种植水草；
S3：按照小龙虾养殖需要进行池塘水位高度管理，养殖小龙虾；
S4：小龙虾养殖周期结束后，降低池塘水位，进行水稻种植。
进一步，步骤S1中，矿物改良剂的用量为每亩农田撒施200kg～500kg。
进一步，步骤S2中放浅水浸泡水位高度为3～5cm，间隔时间为5天。
具体实施方式
现结合具体实施例，对本发明作进一步的阐述。
实施例1
本实施例中，一种适用于稻虾种养模式的矿物改良剂，其主要成分为30～50％的β-硅酸二钙和50～70％的γ-硅酸二钙，其制备方法包括以下步骤：
S1备料：以石灰石和硅石为原材料，粉磨至细度为250目；
S2烧制：检测CaO和SiO2含量，将钙质材料和硅质材料按照CaO与SiO2百分含量配比比值为2.2进行混合，在1300℃烧制2小时；
S3冷却：将烧制后的物料冷却至550℃后保温2h，然后迅速冷却至100℃以下，
S4粉磨：将烧制后的物料粉磨至100目，即制成矿物改良剂。
实施例2
本实施例中，一种适用于稻虾种养模式的矿物改良剂，其制备方法包括以下步骤：
S1备料：以白云石和矽砂为原材料，粉磨至细度为300目；
S2烧制：检测CaO和SiO2含量，将钙质材料和硅质材料按照CaO与SiO2百分含量配比比值为1.8进行混合，在1200℃烧制2.5小时；
S3冷却：将烧制后的物料冷却至500℃后保温1h，然后迅速冷却至100℃以下，
S4粉磨：将烧制后的物料粉磨至100目，即制成矿物改良剂。
实施例3
本实施例中，一种适用于稻虾种养模式的矿物改良剂，其制备方法包括以下步骤：
S1备料：以石灰石和硅灰石、膨润土为原材料，粉磨至细度为150目；
S2烧制：检测CaO和SiO2含量，将钙质材料和硅质材料按照CaO与SiO2百分含量配比比值为2进行混合，在1400℃烧制2小时；
S3冷却：将烧制后的物料冷却至580℃后保温1.5h，然后迅速冷却至100℃以下，
S4粉磨：将烧制后的物料粉磨至120目，即制成矿物改良剂。
实施例4
选择4个面积大小为10亩左右的小龙虾养殖池塘，分别设置为以下四组进行种养试验：CK：不撒施矿物改良剂、T1：撒施实施例一所制备的矿物改良剂、 T2：撒施实施例二所制备的矿物改良剂、T3：撒施实施例三所制备的矿物改良剂。矿物改良剂的使用按照以下步骤进行：
S1：在冬季小龙虾养殖塘口清理时在农田土壤按照300kg/亩的用量均匀撒施矿物改良剂，旋耕2次；
S2：放浅水浸泡4cm，间隔5天，按照小龙虾养殖需要进行种植水草；
S3：按照小龙虾养殖需要进行池塘水位高度管理，养殖小龙虾；
S4：小龙虾养殖周期结束后，降低池塘水位，进行种植水稻。
因小龙虾养殖过程中需要根据水体的pH及钙离子的含量进行调整，整个试验结果以小龙虾的产量和水稻产量及水稻重金属镉含量作为对比参照。
1、不同实施例矿物改良剂对小龙虾产量的影响
由表1可知，施用本发明所述矿物改良剂能够明显增加小龙虾的产量，试验结果表明，施用矿物改良剂后小龙虾增产率为14.29％～21.01％。
表1小龙虾产量情况对比
2、不同实施例矿物改良剂对水稻产量的影响
由表2可知，施用本发明所述矿物改良剂能增加稻虾种养模式中水稻的产量，试验结果表明，施用矿物改良剂后水稻产量增加的幅度为5.2％～8.6％。
表2水稻产量情况对比
3、不同实施例对水稻重金属镉含量的影响
由表3可知，施用该矿物改良剂能够降低稻谷中重金属镉含量，试验结果表明，重金属镉含量降低的幅度在45.91％～51.89％之间。同时施用该矿物改良剂后，生产的水稻重金属镉含量均在国家食品安全标准(0.2mg/kg)以下。
表3稻谷中重金属镉含量对比
由表1、2、3可知，按照每亩施用300kg该矿物改良剂能够明显增加小龙虾及水稻的产量，同时可以降低稻谷中重金属镉的含量，有效增加了稻虾种养模式的经济效益。其作用原理如下：
本发明所述的矿物改良剂经烧制后的主要成分为硅酸钙矿物。其制备方法步骤S2中通过调控钙质材料和硅质材料的比例，确保烧制成的硅酸钙矿物主要为硅酸二钙，当原材料中有白云石时，CaO与SiO2的百分含量配比比值可适当低于2，当原材料中没有白云石时，CaO与SiO2的百分含量配比比值需大于2；通过高温煅烧后形成的硅酸钙矿物主要为β-硅酸二钙；在500～650℃区间保温，可以促成β-硅酸二钙转化为γ-硅酸二钙；通过设定保温的时间可以调整烧制的硅酸钙矿物中β-硅酸二钙和γ-硅酸二钙的比例；通过快速降温，可以控制β-硅酸二钙的转化。因此步骤S3烧制后的产物主要为β-硅酸二钙和γ-硅酸二钙，其中β-硅酸二钙的含量为30～50％，γ-硅酸二钙的含量为50～70％，粉磨后制成所需要的矿物改良剂。
当将矿物改良剂用于稻虾种养时，矿物改良剂中的β-硅酸二钙在常温下能够水化产生水化硅酸钙胶体和氢氧化钙，且其水化速度缓慢持久，能够在很长时间内进行水化反应，持续增加水体中的Ca2+和OH-。而水化硅酸钙胶体可以和土壤及水体中CO2发生碳化反应，生产碳酸钙和硅酸，由于硅酸不稳定，可以吸附较多的阳离子，从而降低水体中氨氮的含量；另一方面种植的水草基本为藻类，硅能够很好的促进苔藓类、藻类植物的生长。由此达到增加水溶液中Ca2+含量，提高pH值，促进水草生长的目的。水草可以给小龙虾提供足够的食物，作为幼虾栖息躲藏地方，减少水中大型鱼类对幼虾的捕食，还可进行光合作用给水体中提供足够的氧气，进一步促进小龙虾的生长发育。
另一方面，矿物改良剂中的γ-硅酸二钙在常温下基本不发生水化反应或者水化反应程度很低，但γ-硅酸二钙具有较高的碳化活性，在小龙虾养殖周期结束后，池塘中的剩余水草翻压在土壤中，在腐解得过程中会产生大量CO2，且水稻根系的呼吸作用也会产生CO2，在较高浓度的CO2环境中，有水参与的情况下，γ- 硅酸二钙会发生碳化反应，直接生成碳酸钙和硅酸，从而促进水稻的生长发育和降低水稻重金属的含量。
相对于现有技术，本发明所述的矿物改良剂是利用β-硅酸二钙和γ-硅酸二钙的水化和碳化反应原理，结合小龙虾养殖及水稻种植过程中对Ca2+和水体pH值的需求，硅元素对相关作物生长的影响以及CO2产生和转化过程的基础知识而进行发明创作的。其能够通过水化提高养殖区域土壤pH，对养殖池塘进行消毒，提高养殖水体的pH，补充水体的钙含量，增加小龙虾生长速度，提高小龙虾产量，同时能够有效促进后期水稻生长，降低水稻中重金属镉的含量，提高稻米品质，增加稻虾养殖模式的整体收益。
以上所述实施例仅表达了本发明的一种实施方式，其描述较为具体和详细，但并不能因此而理解为对发明专利范围的限制。应当指出的是，对于本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。
Claims (5)
1.一种适用于稻虾种养模式的矿物改良剂，其特征在于，其成分包括30～50％的β-硅酸二钙和50～70％的γ-硅酸二钙；
所述适用于稻虾种养模式的矿物改良剂的制备方法包括以下步骤：
S1备料：将钙质材料和硅质材料粉磨至细度为150～300目；
S2烧制：将钙质材料和硅质材料混合后烧制；
S3冷却：将煅烧后的产物冷却至100℃以下；
S4粉磨：将烧制后的物料冷却后粉磨至80～200目，即制成矿物改良剂；
步骤S1中，钙质材料为石灰石、白云石、工业副产物石灰或贝壳中的一种或几种；
步骤S1中，硅质材料为硅石、矽砂、硅灰石、膨润土或废弃混凝土中的一种或几种；
步骤S2中，钙质材料和硅质材料中CaO与SiO2的百分含量配比比值为1.8～2.5。
2.根据权利要求1所述的一种适用于稻虾种养模式的矿改良剂，其特征在于：步骤S2中，烧制温度为1150～1450℃，烧制时间为0.5～3小时。
3.根据权利要求1所述的一种适用于稻虾种养模式的矿物改良剂，其特征在于：步骤S3中，先将煅烧后的产物冷却至500～650℃，保持该温度区间0.5～4小时，然后再迅速冷却至100℃以下。
4.一种适用于稻虾种养模式的矿物改良剂的使用方法，其特征在于，包括以下步骤：
S1：在冬季小龙虾养殖塘口清理时在农田土壤均匀撒施如权利要求1所述的矿物改良剂，旋耕1～2次；
S2：放浅水浸泡后，按照小龙虾养殖需要进行种植水草；
S3：按照小龙虾养殖需要进行池塘水位高度管理，养殖小龙虾；
S4：小龙虾养殖周期结束后，降低池塘水位，进行水稻种植。
5.根据权利要求4所述的矿物改良剂的使用方法，其特征在于：步骤S1中，矿物改良剂的用量为每亩农田撒施200kg～500kg；步骤S2中放浅水浸泡高度为3～5cm，间隔时间为5天。