CN112354829A - Cleaning method for protection plate of vacuum coating equipment - Google Patents
Cleaning method for protection plate of vacuum coating equipment Download PDFInfo
- Publication number
- CN112354829A CN112354829A CN202011088547.3A CN202011088547A CN112354829A CN 112354829 A CN112354829 A CN 112354829A CN 202011088547 A CN202011088547 A CN 202011088547A CN 112354829 A CN112354829 A CN 112354829A
- Authority
- CN
- China
- Prior art keywords
- coating equipment
- vacuum coating
- protection plate
- cleaning
- steps
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a cleaning method of a protective plate of vacuum coating equipment, which comprises the following steps of manufacturing raw materials; step two, cleaning a protection plate; step three, spraying and processing; step four, drying and baking; step five, post-treatment; the cleaning method for the protection plate of the vacuum coating equipment is low in cost, the compatibility of the soluble resin environment-friendly material and certain chemical ratio matched resin is realized, the soluble resin environment-friendly material does not change physically and chemically in the vacuum coating equipment due to external environmental conditions, a simple spraying device is used by applying constant air pressure, the soluble resin environment-friendly material is uniformly sprayed on the protection plate of the vacuum coating equipment, the sprayed surface is dried under the external environmental conditions with the temperature of more than 50 ℃, no dust pollution is generated, no environmental pollution is caused, facility equipment for treating the dust pollution and the environmental pollution can be saved, manual use is directly reduced by half, and the defects of the existing-stage cleaning method are effectively overcome.
Description
Technical Field
The invention relates to the technical field of cleaning of protection plates of vacuum coating equipment, in particular to a method for cleaning the protection plates of the vacuum coating equipment.
Background
The cleaning method in the present stage comprises two types, one type adopts a sand blasting machine to spray sand stones by using air pressure to treat a coating layer on a protective plate of the vacuum coating equipment, the other type adopts a chemical agent to react to treat the coating layer on the protective plate of the vacuum coating equipment, and effective maintenance is completed by cleaning the protective plate of the vacuum device coating equipment so that the vacuum coating equipment can normally run; in view of these drawbacks, it is necessary to design a cleaning method for a protection plate of a vacuum plating apparatus.
Disclosure of Invention
The invention aims to provide a method for cleaning a protection plate of vacuum coating equipment, which aims to solve the problems in the background technology.
In order to solve the technical problems, the invention provides the following technical scheme: a cleaning method for a protection plate of vacuum coating equipment comprises the following steps of manufacturing raw materials; step two, cleaning a protection plate; step three, spraying and processing; step four, drying and baking; step five, post-treatment;
in the first step, the preparation of the raw materials comprises the following steps:
1) manually selecting a soluble environment-friendly resin material, filtering and screening, and standing in a cool place;
2) pouring the selected soluble environment-friendly resin material into a reaction kettle, mixing and stirring until the solution becomes thin, and storing for later use;
wherein in the second step, the cleaning of the protection plate comprises the following steps:
1) manually spraying water to clean a protection plate of vacuum coating equipment, checking whether attachments exist on the surface, and removing the attachments by using a razor;
2) wiping with gauze until no water stain exists on the surface, and naturally drying for 10-20 min;
3) polishing with sand paper until the surface is smooth, then washing with water, and naturally drying;
wherein in the third step, the spraying process comprises the following steps:
1) manually cleaning the spraying machine, airing, then pouring the soluble environment-friendly resin material into the spraying machine, and stirring for 10-20 min;
2) applying constant air pressure, uniformly spraying the soluble environment-friendly resin material on a protective plate of vacuum coating equipment by using a spraying machine, and continuously spraying for 2-3 times;
3) manually inspecting the sprayed surface, and standing for 10-20 min;
wherein in the fourth step, the drying and baking comprises the following steps:
1) manually cleaning and disinfecting the baking machine, and placing the protection plate of the vacuum coating equipment inside the baking machine in order;
2) raising the temperature to 50-60 ℃, and drying the soluble environment-friendly resin material on the surface of the protective plate of the vacuum coating equipment;
in the fifth step, the vacuum coating equipment protection plate dried in the fourth step 2) is manually checked and then stored in a shady and cool place.
According to the technical scheme, the reaction temperature in the step one 2) is kept at 20-30 ℃.
According to the technical scheme, a dryer can be used for drying in the step two 2).
According to the technical scheme, the processing temperature of the spraying machine in the step three 2) is 30-40 ℃.
According to the technical scheme, the drying in the step four 2) is naturally cooled.
According to the technical scheme, the vacuum coating equipment protection plate detected in the fifth step needs to be subjected to ultraviolet irradiation disinfection treatment.
Compared with the prior art, the invention has the following beneficial effects: the cleaning method for the protective plate of the vacuum coating equipment has low cost, and can be used for cleaning the protective plate of the vacuum coating equipment by the compatibility of the environment-friendly material of the soluble resin and the prepared resin with a certain chemical ratio, the soluble resin environment-friendly material does not change physically and chemically in vacuum coating equipment due to external environmental conditions, meanwhile, the vacuum is not influenced, no reaction gas is produced, the coating layer which has the binding force with the film layer and cannot fall is taken as a compatible reference, a simple spraying device is used by applying constant air pressure, so that the soluble resin environment-friendly material is uniformly sprayed on the protective plate of the vacuum coating equipment, the spraying surface of the soluble resin material is dried under the external environmental condition with the temperature of more than 50 ℃, the operation is simple, no dust pollution is generated, no environmental pollution is produced, the dust pollution and environmental pollution treatment facilities and equipment can be saved, the manual use is directly reduced by half, and the defects of the existing cleaning method are effectively overcome.
Drawings
The accompanying drawings, which are included to provide a further understanding of the invention and are incorporated in and constitute a part of this specification, illustrate embodiments of the invention and together with the description serve to explain the principles of the invention and not to limit the invention. In the drawings:
FIG. 1 is a process flow diagram of the present invention.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
Referring to fig. 1, the present invention provides a technical solution: a cleaning method for a protection plate of vacuum coating equipment comprises the following steps of manufacturing raw materials; step two, cleaning a protection plate; step three, spraying and processing; step four, drying and baking; step five, post-treatment;
in the first step, the preparation of the raw materials comprises the following steps:
1) manually selecting a soluble environment-friendly resin material, filtering and screening, and standing in a cool place;
2) pouring the selected soluble environment-friendly resin material into a reaction kettle, mixing and stirring, keeping the reaction temperature at 20-30 ℃ until the solution becomes diluted, and storing for later use;
wherein in the second step, the cleaning of the protection plate comprises the following steps:
1) manually spraying water to clean a protection plate of vacuum coating equipment, checking whether attachments exist on the surface, and removing the attachments by using a razor;
2) wiping with gauze until no water stain exists on the surface, naturally drying for 10-20min, or drying with a dryer;
3) polishing with sand paper until the surface is smooth, then washing with water, and naturally drying;
wherein in the third step, the spraying process comprises the following steps:
1) manually cleaning the spraying machine, airing, then pouring the soluble environment-friendly resin material into the spraying machine, and stirring for 10-20 min;
2) applying constant air pressure, uniformly spraying the soluble environment-friendly resin material on a protective plate of vacuum coating equipment by using a spraying machine, and continuously spraying for 2-3 times, wherein the processing temperature of the spraying machine is 30-40 ℃;
3) manually inspecting the sprayed surface, and standing for 10-20 min;
wherein in the fourth step, the drying and baking comprises the following steps:
1) manually cleaning and disinfecting the baking machine, and placing the protection plate of the vacuum coating equipment inside the baking machine in order;
2) raising the temperature to 50-60 ℃, drying the soluble environment-friendly resin material on the surface of the protective plate of the vacuum coating equipment, and naturally cooling after drying;
in the fifth step, the vacuum coating equipment protection plate dried in the fourth step 2) is manually checked, and the vacuum coating equipment protection plate after detection needs ultraviolet irradiation disinfection treatment and is then placed in a shady and cool place for storage.
Based on the above, the invention has the advantages that the cleaning method for the protection plate of the vacuum coating equipment has low cost, the compatibility of the environment-friendly material of the soluble resin and the prepared resin with a certain chemical ratio is realized, the environment-friendly material of the soluble resin does not change physically and chemically in the vacuum coating equipment due to external environmental conditions, the vacuum is not influenced, reaction gas is not produced, the coating layer has binding force with the film layer and is not dropped as a compatible reference, the simple spraying device is used by applying constant air pressure, the environment-friendly material of the soluble resin is uniformly sprayed on the protection plate of the vacuum coating equipment, the spraying surface of the soluble resin material is dried under the external environmental conditions with the temperature of more than 50 ℃, the operation is simple, no dust pollution is generated, no environmental pollution is produced, the facility equipment for treating the dust pollution and the environmental pollution can be saved, and the manual use is directly reduced by half, effectively solving the defects of the prior cleaning method.
It is noted that, herein, relational terms such as first and second, and the like may be used solely to distinguish one entity or action from another entity or action without necessarily requiring or implying any actual such relationship or order between such entities or actions. Also, the terms "comprises," "comprising," or any other variation thereof, are intended to cover a non-exclusive inclusion, such that a process, method, article, or apparatus that comprises a list of elements does not include only those elements but may include other elements not expressly listed or inherent to such process, method, article, or apparatus.
Finally, it should be noted that: although the present invention has been described in detail with reference to the foregoing embodiments, it will be apparent to those skilled in the art that changes may be made in the embodiments and/or equivalents thereof without departing from the spirit and scope of the invention. Any modification, equivalent replacement, or improvement made within the spirit and principle of the present invention should be included in the protection scope of the present invention.
Claims (6)
1. A cleaning method for a protection plate of vacuum coating equipment comprises the following steps of manufacturing raw materials; step two, cleaning a protection plate; step three, spraying and processing; step four, drying and baking; step five, post-treatment; the method is characterized in that:
in the first step, the preparation of the raw materials comprises the following steps:
1) manually selecting a soluble environment-friendly resin material, filtering and screening, and standing in a cool place;
2) pouring the selected soluble environment-friendly resin material into a reaction kettle, mixing and stirring until the solution becomes thin, and storing for later use;
wherein in the second step, the cleaning of the protection plate comprises the following steps:
1) manually spraying water to clean the protective plate of the vacuum coating equipment, checking whether attachments exist on the surface,
and removing with a razor;
2) wiping with gauze until no water stain exists on the surface, and naturally drying for 10-20 min;
3) polishing with sand paper until the surface is smooth, then washing with water, and naturally drying;
wherein in the third step, the spraying process comprises the following steps:
1) manually cleaning the spraying machine, airing, then pouring the soluble environment-friendly resin material into the spraying machine, and stirring for 10-20 min;
2) applying constant air pressure, uniformly spraying the soluble environment-friendly resin material on a protective plate of vacuum coating equipment by using a spraying machine, and continuously spraying for 2-3 times;
3) manually inspecting the sprayed surface, and standing for 10-20 min;
wherein in the fourth step, the drying and baking comprises the following steps:
1) manually cleaning and disinfecting the baking machine, and placing the protection plate of the vacuum coating equipment inside the baking machine in order;
2) raising the temperature to 50-60 ℃, and drying the soluble environment-friendly resin material on the surface of the protective plate of the vacuum coating equipment;
in the fifth step, the vacuum coating equipment protection plate dried in the fourth step 2) is manually checked and then stored in a shady and cool place.
2. The method for cleaning a protection plate of a vacuum coating equipment according to claim 1, wherein the method comprises the following steps: the reaction temperature in the step one 2) is kept between 20 and 30 ℃.
3. The method for cleaning a protection plate of a vacuum coating equipment according to claim 1, wherein the method comprises the following steps: in the second step 2), a dryer can also be used for drying.
4. The method for cleaning a protection plate of a vacuum coating equipment according to claim 1, wherein the method comprises the following steps: the processing temperature of the spraying machine in the step three 2) is 30-40 ℃.
5. The method for cleaning a protection plate of a vacuum coating equipment according to claim 1, wherein the method comprises the following steps: and naturally cooling after drying in the step four 2).
6. The method for cleaning a protection plate of a vacuum coating equipment according to claim 1, wherein the method comprises the following steps: and the vacuum coating equipment protection plate detected in the fifth step needs to be subjected to ultraviolet irradiation disinfection treatment.