CN112341070A - 一种低孔隙率水泥防水涂料及其制备方法 - Google Patents
一种低孔隙率水泥防水涂料及其制备方法 Download PDFInfo
- Publication number
- CN112341070A CN112341070A CN202011206267.8A CN202011206267A CN112341070A CN 112341070 A CN112341070 A CN 112341070A CN 202011206267 A CN202011206267 A CN 202011206267A CN 112341070 A CN112341070 A CN 112341070A
- Authority
- CN
- China
- Prior art keywords
- parts
- waterproof coating
- cement
- low
- porosity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明涉及一种防水涂料，具体是一种低孔隙率水泥防水涂料及其制备方法,这种低孔隙率水泥防水涂料，其特征在于，包括以下重量份数的组分：水泥30‑40份，石英砂14‑28份，柠檬酸和碳酸钠的混合物5‑10份，粉状纳米二氧化硅0.1‑0.4份，结晶沉淀剂2‑6份，十二烷基乙氧基磺基甜菜碱0.5‑5份，消石灰1‑5份，减水剂0.5‑2份，硅烷偶联剂0.3‑0.5份，消泡剂0.4‑1.2份,本发明有益效果是在使用消泡剂时得到一种孔隙率最佳的防水涂料，从而提升其防水性能。
Description
技术领域
本发明涉及一种防水涂料，具体是一种低孔隙率水泥防水涂料及其制备方法。
背景技术
聚合物水泥防水涂料，简称JS防水涂料，J指聚合物，S指水泥，故JS就是聚合物水泥防水涂料。聚合物水泥防水涂料是一种以聚丙烯酸酯乳液、乙烯-醋酸乙烯酯共聚乳液等聚合物乳液与各种添加剂组成的有机液料。
聚合物水泥防水涂料是和水泥、石英砂、轻重质碳酸钙等无机填料及各种添加剂所组成的无机粉料通过合理配比、复合制成的一种双组份、水性建筑防水涂料。在建筑工程中，JS-复合防水涂料和水泥聚合物防水涂料是同一种材料。
聚合物水泥防水涂料是由合成高分子聚合物乳液（如聚丙烯酸酯、聚醋酸乙烯酯、丁苯橡胶乳液等）及各种添加剂优化组合而成的液料和配套的粉料（由特种水泥、石英粉及各种添加剂组成）复合而成的双组分防水涂料，是一种既具有合成高分子聚合物材料弹性高、又有无机材料耐久性好的防水材料。
但是该材料由于组分繁多，每种组分具体对该材料有何影响，如何选取最优的值，值得我们研究，其中孔隙率对防水涂料影响较大，而消泡剂又是是影响孔隙率一个重要的因素。
发明内容
本发明的目的在于提供一种低孔隙率水泥防水涂料及其制备方法，以解决上述背景技术中提出的问题。
这种低孔隙率水泥防水涂料，其特征在于，包括以下重量份数的组分：水泥30-40份，石英砂14-28份，柠檬酸和碳酸钠的混合物5-10份，粉状纳米二氧化硅0 .1-0.4份， 结晶沉淀剂2-6份，十二烷基乙氧基磺基甜菜碱0 .5-5份，消石灰1-5份，减水剂0 .5-2 份，硅烷偶联剂0.3-0.5份，消泡剂0.4-1.2份。
所述消泡剂为聚醚消泡剂。
这种低孔隙率水泥防水涂料的制备方法，其特征在于，包括以下步骤，将上述各组份在超声波条件下混合，并搅拌10-15min。
本发明有益效果是在使用消泡剂时得到一种孔隙率最佳的防水涂料，从而提升其防水性能。
具体实施方式
实施例一
这种低孔隙率水泥防水涂料，其特征在于，包括以下重量份数的组分：水泥30-40份，石英砂14-28份，柠檬酸和碳酸钠的混合物5-10份，粉状纳米二氧化硅0 .1-0.4份， 结晶沉淀剂2-6份，十二烷基乙氧基磺基甜菜碱0 .5-5份，消石灰1-5份，减水剂0 .5-2 份，硅烷偶联剂0.3-0.5份，消泡剂0.4份。
所述消泡剂为聚醚消泡剂。
这种低孔隙率水泥防水涂料的制备方法，其特征在于，包括以下步骤，将上述各组份在超声波条件下混合，并搅拌10-15min。
实施例二
这种低孔隙率水泥防水涂料，其特征在于，包括以下重量份数的组分：水泥30-40份，石英砂14-28份，柠檬酸和碳酸钠的混合物5-10份，粉状纳米二氧化硅0 .1-0.4份， 结晶沉淀剂2-6份，十二烷基乙氧基磺基甜菜碱0 .5-5份，消石灰1-5份，减水剂0 .5-2 份，硅烷偶联剂0.3-0.5份，消泡剂0.6份。
所述消泡剂为聚醚消泡剂。
这种低孔隙率水泥防水涂料的制备方法，其特征在于，包括以下步骤，将上述各组份在超声波条件下混合，并搅拌10-15min。
实施例三
这种低孔隙率水泥防水涂料，其特征在于，包括以下重量份数的组分：水泥30-40份，石英砂14-28份，柠檬酸和碳酸钠的混合物5-10份，粉状纳米二氧化硅0 .1-0.4份， 结晶沉淀剂2-6份，十二烷基乙氧基磺基甜菜碱0 .5-5份，消石灰1-5份，减水剂0 .5-2 份，硅烷偶联剂0.3-0.5份，消泡剂0.8份。
所述消泡剂为聚醚消泡剂。
这种低孔隙率水泥防水涂料的制备方法，其特征在于，包括以下步骤，将上述各组份在超声波条件下混合，并搅拌10-15min。
实施例四
这种低孔隙率水泥防水涂料，其特征在于，包括以下重量份数的组分：水泥30-40份，石英砂14-28份，柠檬酸和碳酸钠的混合物5-10份，粉状纳米二氧化硅0 .1-0.4份， 结晶沉淀剂2-6份，十二烷基乙氧基磺基甜菜碱0 .5-5份，消石灰1-5份，减水剂0 .5-2 份，硅烷偶联剂0.3-0.5份，消泡剂1.2份。
所述消泡剂为聚醚消泡剂。
这种低孔隙率水泥防水涂料的制备方法，其特征在于，包括以下步骤，将上述各组份在超声波条件下混合，并搅拌10-15min。
对照组一
这种低孔隙率水泥防水涂料，其特征在于，包括以下重量份数的组分：水泥30-40份，石英砂14-28份，柠檬酸和碳酸钠的混合物5-10份，粉状纳米二氧化硅0 .1-0.4份， 结晶沉淀剂2-6份，十二烷基乙氧基磺基甜菜碱0 .5-5份，消石灰1-5份，减水剂0 .5-2 份，硅烷偶联剂0.3-0.5份。
这种低孔隙率水泥防水涂料的制备方法，其特征在于，包括以下步骤，将上述各组份在超声波条件下混合，并搅拌10-15min。
对照组二
这种低孔隙率水泥防水涂料，其特征在于，包括以下重量份数的组分：水泥30-40份，石英砂14-28份，柠檬酸和碳酸钠的混合物5-10份，粉状纳米二氧化硅0 .1-0.4份， 结晶沉淀剂2-6份，十二烷基乙氧基磺基甜菜碱0.5-5份，消石灰1-5份，减水剂0 .5-2 份，硅烷偶联剂0.3-0.5份。
这种低孔隙率水泥防水涂料的制备方法，将上述各组份混合，并搅拌10-15min。
对照组三
这种低孔隙率水泥防水涂料，其特征在于，包括以下重量份数的组分：水泥30-40份，石英砂14-28份，柠檬酸和碳酸钠的混合物5-10份，粉状纳米二氧化硅0 .1-0.4份， 结晶沉淀剂2-6份，十二烷基乙氧基磺基甜菜碱0 .5-5份，消石灰1-5份，减水剂0 .5-2 份，硅烷偶联剂0.3-0.5份，消泡剂0.6份。
所述消泡剂为聚醚消泡剂。
这种低孔隙率水泥防水涂料的制备方法，将上述各组份混合，并搅拌10-15min。
结构参见下表1。
表1.
综上，随着消泡剂用量增加空隙率先减小后增大，吸水率减小后增大，拉伸强度先增大后减小，在超声波条件下，由于共聚物被打散，缩孔和微裂率减小，所以孔隙率较小，吸水率小，从而防水效果上升，由上可知在本发明中消泡剂用量0.6份为最优。
Claims (7)
1.一种低孔隙率水泥防水涂料，其特征在于，包括以下重量份数的组分：水泥30-40份，石英砂14-28份，柠檬酸和碳酸钠的混合物5-10份，粉状纳米二氧化硅0 .1-0.4份， 结晶沉淀剂2-6份，十二烷基乙氧基磺基甜菜碱0 .5-5份，消石灰1-5份，减水剂0 .5-2 份，硅烷偶联剂0.3-0.5份，消泡剂0.4-1.2份。
2.根据权利要求1所述的一种低孔隙率水泥防水涂料，所述消泡剂为聚醚消泡剂。
3.根据权利要求1所述的一种低孔隙率水泥防水涂料，其特征在于，包括以下重量份数的组分：水泥30-40份，石英砂14-28份，柠檬酸和碳酸钠的混合物5-10份，粉状纳米二氧化硅0 .1-0.4份， 结晶沉淀剂2-6份，十二烷基乙氧基磺基甜菜碱0 .5-5份，消石灰1-5份，减水剂0 .5-2 份，硅烷偶联剂0.3-0.5份，消泡剂0.4份。
4.根据权利要求1所述的一种低孔隙率水泥防水涂料，其特征在于，包括以下重量份数的组分：水泥30-40份，石英砂14-28份，柠檬酸和碳酸钠的混合物5-10份，粉状纳米二氧化硅0 .1-0.4份， 结晶沉淀剂2-6份，十二烷基乙氧基磺基甜菜碱0 .5-5份，消石灰1-5份，减水剂0 .5-2 份，硅烷偶联剂0.3-0.5份，消泡剂0.6份。
5.根据权利要求1所述的一种低孔隙率水泥防水涂料，其特征在于，包括以下重量份数的组分：水泥30-40份，石英砂14-28份，柠檬酸和碳酸钠的混合物5-10份，粉状纳米二氧化硅0 .1-0.4份， 结晶沉淀剂2-6份，十二烷基乙氧基磺基甜菜碱0 .5-5份，消石灰1-5份，减水剂0 .5-2 份，硅烷偶联剂0.3-0.5份，消泡剂0.8份。
6.根据权利要求1所述的一种低孔隙率水泥防水涂料，其特征在于，包括以下重量份数的组分：水泥30-40份，石英砂14-28份，柠檬酸和碳酸钠的混合物5-10份，粉状纳米二氧化硅0 .1-0.4份， 结晶沉淀剂2-6份，十二烷基乙氧基磺基甜菜碱0 .5-5份，消石灰1-5份，减水剂0 .5-2 份，硅烷偶联剂0.3-0.5份，消泡剂1.2份。
7.一种低孔隙率水泥防水涂料的制备方法，其特征在于，包括以下步骤，将上述各组份在超声波条件下混合，并搅拌10-15min。