CN112226301A - 电气、机械设备带电绝缘清洗剂、制备方法及应用 - Google Patents
电气、机械设备带电绝缘清洗剂、制备方法及应用 Download PDFInfo
- Publication number
- CN112226301A CN112226301A CN202011367456.3A CN202011367456A CN112226301A CN 112226301 A CN112226301 A CN 112226301A CN 202011367456 A CN202011367456 A CN 202011367456A CN 112226301 A CN112226301 A CN 112226301A
- Authority
- CN
- China
- Prior art keywords
- parts
- cleaning agent
- electrical
- mechanical equipment
- cleaning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种电气、机械设备带电绝缘清洗剂，以重量份数计，由以下成分制成：三氯乙烯15‑20份，二乙烯基乙二醇20‑25份，乙酸乙酯5‑10份，乙酸甲酯16‑35份。该清洗剂清洗彻底，干净，有机溶剂可完全挥发，不留残迹；对金属材料和复合材料及油漆表面安全无腐蚀。
Description
技术领域
本发明涉及一种电气、机械设备带电绝缘清洗剂、制备方法及应用，属于工业清洗剂领域。
背景技术
电气设备的保养，十分重要的环节在于清洗。对于电气设备的清洗需要将电气设备断电拆卸后，方可进行清洗。对于机械设备的清洗，需要先断电再人工进行打磨清洗。因此操作复杂、费时费力。本发明的带电绝缘清洗剂可直接在电气、机械设备正常通电情况下，进行人工喷洗。用于电器的清洗剂应具有三个基本特征:绝缘性、抗腐蚀性、安全性。目前市面上使用的多数绝缘清洗剂或气味大，或易燃烧，或对橡胶、塑料等有轻微腐蚀性。通常用于电气设备的清洗剂有:酒精、煤油、汽油、二甲苯、溶剂油、丙酮等，对绝缘要求高的电器，也采用四氯化碳或氟氯烷等清洗剂，前几种清洗剂都是易燃品，且不同程度的导电;有些清洗剂虽对金属无腐蚀性，但对塑料、油漆却有很强的溶解性;二甲苯、溶剂油、丙酮有较强的毒性。
中国专利CN202010823235.6公开了一种电力电气带电维保清洗剂及其制备方法，包括净洗剂、三氯乙烯、表面活性剂、无水乙醇、抗静电剂、聚有机硅氧烷和石脑油轻溶剂，所述净洗剂、三氯乙烯、表面活性剂、无水乙醇、抗静电剂、聚有机硅氧烷和石脑油轻溶剂按重量份数计为净洗剂0.5-1.5份、三氯乙烯60-80份、表面活性剂1-3份、无水乙醇3-5份、抗静电剂3-5份、聚有机硅氧烷2-3份和石脑油轻溶剂20-30份。本发明提供的一种电力电气带电维保清洗剂绝缘性能强，能够在高压带电环境下工作，对电气设备无损害，清洗效率高，残留物少，设备表面绝缘能力明显增强，制备方法简单，成本低。该专利中无水乙醇易燃易爆，使用时具有一定的危险性。
中国专利CN201210098796.X公开了一种电器设备清洗剂及其制备方法，清洗剂重量配比分别为醇醚类溶剂：1-5％；二氯甲烷5-10％；四氯乙烯30-50％；柠烯0-10％；碳氢溶剂余量；制备方法为：将碳氢溶剂在储料罐(底物为锥状)中静止24小时以上。按配比量加入到不锈钢反应釜中，依次加入醇醚溶剂、二氯甲烷、四氯乙烯、柠烯搅拌20-30分钟经干燥器和过滤器后即为电气设备清洗剂。本发明不含三氟三氯乙烷(F-113)、1，1，1三氯乙烷、三氯乙烯、四氯化碳等ODS类原料，安全环保，臭氧破坏系数0.00；清洗力强净洗力为99.9％，对矿物油迹、焊迹、粉尘等污垢清除能力强；可带电清洗，耐压值大于25KV；化学性质稳定对线路板、金属材质无腐蚀；本发明的清洗剂可完全挥发无残留。该专利中的二氯甲烷及四氯乙烯都在2A类致癌物清单中，对人体、大气有巨大危害。
发明内容
本发明的目的在于提供一种免拆洗、带电清洗、清洁效果好、不腐蚀金属材料铝和非金属材料及油漆表面的电气、机械设备清洗剂，其无刺激性气味，不燃烧，对橡胶、塑料等有机物的侵蚀性非常低。
本发明提供了一种电气、机械设备带电绝缘清洗剂，以重量份数计，由以下成分制成：
三氯乙烯15-20份，
二乙烯基乙二醇20-25份，
乙酸乙酯5-10份，
乙酸甲酯16-35份。
本发明优选的技术方案如下：
三氯乙烯20-25份，
二乙烯基乙二醇20-25份，
乙酸乙酯5-10份，
乙酸甲酯16-35份。
本发明更优选的技术方案如下：
一种电气、机械设备带电绝缘清洗剂，以重量份数计，由以下成分制成：
三氯乙烯18份，
二乙烯基乙二醇24份，
乙酸乙酯8份，
乙酸甲酯22份。
本发明配方中，乙酸乙酯的用量要小于乙酸甲酯的用量，如果乙酸乙酯的用量大于乙酸甲酯的用量，会对飞机的漆层造成较大影响。
本发明清洗剂的制备方法如下：
将三氯乙烯、二乙烯基乙二醇、乙酸乙酯、乙酸甲酯按比例混合即可。
本发明的使用方法：
喷淋清洗：将161#喷枪接上压缩空气，并将喷枪吸液管插入清洗剂桶中，打开空气开关，将161#喷枪对准需要清洗的部位进行喷洗。
本发明主要用途：
本品主要用于清洗引起电气设备故障的油污、铁屑、碳粉等污物，可以延长电气设备使用寿命，预防设备故障。
电气设备：用于清洗电动机、发电机、配电开关柜、变电设备、配电室设备、大型电磁阀门、切换开关、自控开关、电焊机、小功率手动工具等，清洗上述电气设备时不会对电气设备的绝缘产生影响。
机械设备：用于清洗机械设备，如油压机械的油缸，各种过滤器、齿轮箱、轴承、铰链机构等机械设备和各种金属零部件。
本发明的有益效果：
1、本品属溶剂型产品，虽然原液使用，由于本品清洗能力强，但用量少，清洗成本，本发明产品与同类型清洗剂相比，只需要同类型清洗剂用量的3/4；
2、清洗彻底，干净，有机溶剂可完全挥发，不留残迹；
3、本品对金属材料和复合材料及油漆表面安全无腐蚀；
4、绝缘性能好，耐电压25KV以上；可带电进行清洗，在清洗过程中不影响电气设备的性能。
具体实施方式
实施例1
一种电气、机械设备带电绝缘清洗剂，以重量份数计，由以下成分制成：
三氯乙烯10份
二乙烯基乙二醇23份
乙酸乙酯7份
乙酸甲酯20份。
实施例2
一种电气、机械设备带电绝缘清洗剂，以重量份数计，由以下成分制成：
三氯乙烯13份
二乙烯基乙二醇20份
乙酸乙酯6份
乙酸甲酯21份。
实施例3
一种电气、机械设备带电绝缘清洗剂，以重量份数计，由以下成分制成：
三氯乙烯12份
二乙烯基乙二醇20份
乙酸乙酯8份
乙酸甲酯24份。
实施例4
一种电气、机械设备带电绝缘清洗剂，以重量份数计，由以下成分制成：
三氯乙烯15份
二乙烯基乙二醇22份
乙酸乙酯7份
乙酸甲酯20份。
实施例5
一种电气、机械设备带电绝缘清洗剂，以重量份数计，由以下成分制成：
三氯乙烯17份
二乙烯基乙二醇25份
乙酸乙酯9份
乙酸甲酯20份。
实施例6
一种电气、机械设备带电绝缘清洗剂，以重量份数计，由以下成分制成：
三氯乙烯18份
二乙烯基乙二醇24份
乙酸乙酯8份
乙酸甲酯22份。
对比例1
将实施例6中的二乙烯基乙二醇替换为乙二醇，配方如下：
一种电气、机械设备带电绝缘清洗剂，以重量份数计，由以下成分制成：
三氯乙烯18份
乙二醇24份
乙酸乙酯8份
乙酸甲酯22份。
对比例2
一种电气、机械设备带电绝缘清洗剂，以重量百分比计，由以下成分制成：
三氯乙烯18份
二乙烯基乙二醇24份
乙酸乙酯30份
乙酸甲酯0份。
对比例3
一种电气、机械设备带电绝缘清洗剂，以重量百分比计，由以下成分制成：
三氯乙烯18份
二乙烯基乙二醇24份
乙酸乙酯0份
乙酸甲酯30份。
对比例4
一种电气、机械设备带电绝缘清洗剂，以重量份数计，由以下成分制成：
三氯乙烯18份
二乙烯基乙二醇24份
乙酸乙酯22份
乙酸甲酯8份。
以上实施例的性能试验结果见表1。
表1
以上对比例的测试结果见表2。
表2
相关测试方法如下：
1、产品的性能试验：
所有试验均用原液在未稀释状态下（加热到液态，下同）进行。
1.1闪点
按照ASTMD56，对产品的闪点进行测试，其结果应不低于60℃。
1.2冷热稳定性
按照HB5334-85第2.9条的要求进行，试验后的产品在规定的条件下恢复到常温时应均匀，无分层、无沉淀、无絮状物析出。
1.3长期存储稳定性
按照ASTMF1104进行试验，试验周期为低温15天和高温15天，结果应当符合ASTMF1104的要求，实验后的产品，应均匀，无分层，无沉淀无絮状物析出。
2、相容性试验
所有的试验均用原液进行。
2.1全浸腐蚀试验
2.1.1试验样件及编号：
a：符合QQ-A-250/13－T6的7075/T6有包铝层铝合金；
b：符合QQ-A-250/4－T3的2024/T3无包铝层铝合金，并经过敏化处理（495℃±5℃热处理40分钟，再用100℃水急冷）。
2.1.2试验及合格判定：
当按ASTMF483进行试验24小时后，试验样件的平均重量变不应超过8.2mg，也不能出现腐蚀现象；
2.2漆层软化试验
按ASTMF502进行试验后，试验样品不能使漆层硬度减小大于两个铅笔硬度级，也不应使漆层发生褪色、染色、龟裂、起泡的腐蚀现象。
2.3聚丙烯酸酯龟裂试验
当按ASTMF484对MIL-P-25690A型聚丙烯酸材料施加4500Psi的外部应力时，试验样品不得使样件产生龟裂、裂纹或浸蚀的腐蚀现象；
2.4聚碳酸脂龟裂试验
试验样件：通用电气公司的9600－116聚碳酸脂板，0.060±0.005英寸厚。
试验步骤：
1）给试验样件加载使其表面应力为2000Psi；
2）将浸有试验溶液的脱脂棉铺在加载下的试验件上，注意不要将溶液碰到试验样件的边缘；
3）十分钟后，解除应力，拿开脱脂棉；
4）试验样件上不应出现龟裂、裂纹、玷污或褪色的腐蚀现象，否则为不合格；
2.5应力腐蚀试验
按照ASTMF945进行试验，试板不能产生裂纹；用甲乙酮（MEK）作为对照液；材料采用6Al-4V钛合金；
2.6工频击穿电压
按照GB/T25097-2010进行试验，工频击穿电压≥25KV；
2.7清洗能力
按照GB/T25097-2010进行试验，对人工模拟污秽瓷片进行浸泡后，洗净率应达到80%，除盐率应达到80%。
Claims (6)
1.一种电气、机械设备带电绝缘清洗剂，其特征在于，以重量份数计，由以下成分制成：三氯乙烯15-20份，二乙烯基乙二醇20-25份，乙酸乙酯5-10份，乙酸甲酯16-35份。
2.根据权利要求1所述的电气、机械设备带电绝缘清洗剂，其特征在于，以重量份数计，由以下成分制成：三氯乙烯20-25份，二乙烯基乙二醇20-25份，乙酸乙酯5-10份，乙酸甲酯16-35份。
3.根据权利要求1所述的电气、机械设备带电绝缘清洗剂，其特征在于，以重量份数计，由以下成分制成：三氯乙烯18份，二乙烯基乙二醇24份，乙酸乙酯8份，乙酸甲酯22份。
4.根据权利要求1所述电气、机械设备带电绝缘清洗剂的制备方法，其特征在于，依次包括步骤：将三氯乙烯、二乙烯基乙二醇、乙酸乙酯、乙酸甲酯按比例混合即可。
5.权利要求1所述绝缘清洗剂在带电电气、机械设备清洗中的应用。
6.根据权利要求5所述绝缘清洗剂在带电电气、机械设备清洗中的应用，其特征在于，使用方法如下：将喷枪接上压缩空气，并将喷枪吸液管插入清洗剂桶中，打开空气开关，将喷枪对准需要清洗的部位进行喷洗。