CN112164745A - 一种使用寿命长的高色域量子点膜 - Google Patents
一种使用寿命长的高色域量子点膜 Download PDFInfo
- Publication number
- CN112164745A CN112164745A CN202011098426.7A CN202011098426A CN112164745A CN 112164745 A CN112164745 A CN 112164745A CN 202011098426 A CN202011098426 A CN 202011098426A CN 112164745 A CN112164745 A CN 112164745A
- Authority
- CN
- China
- Prior art keywords
- quantum dot
- water
- layer
- dot film
- long
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供了一种使用寿命长的高色域量子点膜，包括PET基层、红外线吸收层、高反射层和水氧阻隔涂层，PET基层为PET材料在熔融后加入均匀分布的量子点凝固而成，PET基层的上下表面均设有第一水氧阻隔涂层，水氧阻隔涂层的上表面依次设有红外线吸收层、紫外线吸收层和蓝光吸收层，水氧阻隔涂层的下表面设有高反射层，量子点膜上下层设有第二水氧阻隔涂层，分别贴附在蓝光吸收层、高反射层的外表面。本方案有效的降低了水、氧、高温等对膜的影响，进而提高了量子点膜的使用寿命，红外线吸收层有效的降低了温度对量子点的影响，同时结合水氧阻隔涂层有效的降低了水、氧对量子点使用寿命的影响，进而提高了量子点膜的使用寿命。
Description
技术领域
本发明涉及量子点膜技术领域，特别是一种使用寿命长的高色域量子点膜。
背景技术
随着科技的发展，采用OLED显示已成为电子电器产品显示的一种主流发展趋势，当前采用OLED显示的中高端智能手机越来越多，但由于OLED存在生产良率低、生产成本高等问题，因此目前电子显示光源仍主要采用LED形式。
现有将量子点应用于LED显示的技术，仅在大尺寸电视上有了应用性进展，其色域较传统LED显示高出了40% NTSC，目前最高可至115% NTSC，但是，例如3M公司QDEF量子点膜、韩国以及国内一些厂家所生产的量子点膜材料，均存在不耐水氧而易导致膜材老化的问题，进而存在蓝边不良的情况，即便采用了增加上下两层阻隔膜的方式，也仍会出现老化边缘失效的问题，不仅如此，现在市面上这些的量子点膜的防刮效果也不理想，且在提高了色域后，光显示的均匀度却受到影响而变得比较差。
发明内容
本发明的目的是，克服现有技术的上述不足，而提供一种使用寿命长，降低水、氧、高温对量子点膜的影响，提高色域效果，光显均匀的使用寿命长的高色域量子点膜。
本发明的技术方案是：一种使用寿命长的高色域量子点膜，包括PET基层、红外线吸收层、高反射层和水氧阻隔涂层，PET基层为PET材料在熔融后加入均匀分布的量子点凝固而成，PET基层的上下表面均设有第一水氧阻隔涂层，水氧阻隔涂层的上表面依次设有红外线吸收层、紫外线吸收层和蓝光吸收层，水氧阻隔涂层的下表面设有高反射层，量子点膜上下层设有第二水氧阻隔涂层，分别贴附在蓝光吸收层、高反射层的外表面。
进一步，所述PET基层的厚度为150-400μm。
进一步，所述水氧阻隔涂层的厚度为20-60μm。
进一步，所述水氧阻隔涂层是以含氟树脂或高Tg的甲基丙烯酸酯对环氧树脂或聚氨酯或丙烯酸进行改性形成的疏水涂料；或者所述水氧阻隔涂层是由HEA或IBOA丙烯酸树脂经UV固化后形成的PMMA膜。
进一步，所述水氧阻隔涂层中还添加有用于提升抗黄变性能的紫外线吸收剂。
进一步，所述高反射层为金属镀层或纳米反射层。
进一步，所述纳米反射层为氮化钛、氮碳化钛、纳米铝、纳米银或纳米铜。
进一步，所述高反射层的厚度为10-50μm。
进一步，所述量子点膜的总厚度不小于0.1mm。
进一步，量子点纳米颗粒由IIB-VIA族元素或者IIIV-VA族元素组成，量子点纳米颗粒是以ZnS、PbS作为壳料，并在壳料中加入含镉、锌的CdS、CdSe、CdTe、ZnSe、GaN、InAs中的一种或多种组成的纳米材料。
本发明具有如下特点：本方案有效的降低了水、氧、高温等对膜的影响，进而提高了量子点膜的使用寿命，红外线吸收层有效的降低了温度对量子点的影响，同时结合水氧阻隔涂层有效的降低了水、氧对量子点使用寿命的影响，进而提高了量子点膜的使用寿命。
以下结合附图和具体实施方式对本发明的详细结构作进一步描述。
附图说明
图1-为本发明的结构示意图。
具体实施方式
如附图所示：一种使用寿命长的高色域量子点膜，包括PET基层、红外线吸收层、高反射层和水氧阻隔涂层，PET基层为PET材料在熔融后加入均匀分布的量子点凝固而成，PET基层的上下表面均设有第一水氧阻隔涂层，水氧阻隔涂层的上表面依次设有红外线吸收层、紫外线吸收层和蓝光吸收层，水氧阻隔涂层的下表面设有高反射层，量子点膜上下层设有第二水氧阻隔涂层，分别贴附在蓝光吸收层、高反射层的外表面。
在另一个实施例中，量子点膜的最外层的上表面，即在第二水氧阻隔涂层上表面还设有防刮层，便于对量子点膜进行清理，避免灰尘影响清晰度。
在实施例中，PET基层的厚度为150-400μm。优选地，PET基层的厚度为200-350μm；更优地，PET基层的厚度为220/250/300/320μm；便于提高PET材料与量子点的结合，同时保证量子点的有需要使用数量，保证色域度，提高使用的清晰度。
在实施例中，水氧阻隔涂层的厚度为20-60μm。优选地，水氧阻隔涂层的厚度为25-55μm；更优地，水氧阻隔涂层的厚度为30/35/40/50μm，有效的提高了对水、氧的阻隔效果，同时提高了对量子点的保护效果，避免其受影响。优选地，水氧阻隔涂层是以含氟树脂或高Tg的甲基丙烯酸酯对环氧树脂或聚氨酯或丙烯酸进行改性形成的疏水涂料；或者水氧阻隔涂层是由HEA或IBOA丙烯酸树脂经UV固化后形成的PMMA膜。更优地，水氧阻隔涂层中还添加有用于提升抗黄变性能的紫外线吸收剂。
在实施例中，高反射层为金属镀层或纳米反射层。优选地，纳米反射层为氮化钛、氮碳化钛、纳米铝、纳米银或纳米铜。本发明采用的是纳米反射层，用纳米银制成；更优地，纳米银层的厚度为10-50μm，最佳地，纳米银的厚度为20/24/29/35/40μm，便于提高对电子显示器内部的温度的反射效果，降低温度对量子点的影响，进而提高其使用寿命。
在实施例中，量子点膜的总厚度不小于0.1mm；优选地，量子点膜的总厚度为0.2-0.7mm；更优地，量子点膜的总厚度为0.3-0.6mm；最佳地，量子点膜的总厚度为0.45/0.5/0.55mm。量子点纳米颗粒由IIB-VIA族元素或者IIIV-VA族元素组成，量子点纳米颗粒是以ZnS、PbS作为壳料，并在壳料中加入含镉、锌的CdS、CdSe、CdTe、ZnSe、GaN、InAs中的一种或多种组成的纳米材料。
本方案有效的降低了水、氧、高温等对膜的影响，进而提高了量子点膜的使用寿命，红外线吸收层有效的降低了温度对量子点的影响，同时结合水氧阻隔涂层有效的降低了水、氧对量子点使用寿命的影响，进而提高了量子点膜的使用寿命。
以上所述是本发明较佳实施例及其所运用的技术原理，对于本领域的技术人员来说，在不背离本发明的精神和范围的情况下，任何基于本发明技术方案基础上的等效变换、简单替换等显而易见的改变，均属于本发明保护范围之内。
Claims (10)
1.一种使用寿命长的高色域量子点膜，其特征在于：包括PET基层、红外线吸收层、高反射层和水氧阻隔涂层，PET基层为PET材料在熔融后加入均匀分布的量子点凝固而成，PET基层的上下表面均设有第一水氧阻隔涂层，水氧阻隔涂层的上表面依次设有红外线吸收层、紫外线吸收层和蓝光吸收层，水氧阻隔涂层的下表面设有高反射层，量子点膜上下层设有第二水氧阻隔涂层，分别贴附在蓝光吸收层、高反射层的外表面。
2.根据权利要求1所述的使用寿命长的高色域量子点膜，其特征在于：所述PET基层的厚度为150-400μm。
3.根据权利要求1所述的使用寿命长的高色域量子点膜，其特征在于：所述水氧阻隔涂层的厚度为20-60μm。
4.根据权利要求3所述的使用寿命长的高色域量子点膜，其特征在于：所述水氧阻隔涂层是以含氟树脂或高Tg的甲基丙烯酸酯对环氧树脂或聚氨酯或丙烯酸进行改性形成的疏水涂料；或者所述水氧阻隔涂层是由HEA或IBOA丙烯酸树脂经UV固化后形成的PMMA膜。
5.根据权利要求4所述的使用寿命长的高色域量子点膜，其特征在于：所述水氧阻隔涂层中还添加有用于提升抗黄变性能的紫外线吸收剂。
6.根据权利要求1所述的使用寿命长的高色域量子点膜，其特征在于：所述高反射层为金属镀层或纳米反射层。
7.根据权利要求6所述的使用寿命长的高色域量子点膜，其特征在于：所述纳米反射层为氮化钛、氮碳化钛、纳米铝、纳米银或纳米铜。
8.根据权利要求6所述的使用寿命长的高色域量子点膜，其特征在于：所述高反射层的厚度为10-50μm。
9.根据权利要求1-8任一项所述的使用寿命长的高色域量子点膜，其特征在于：所述量子点膜的总厚度不小于0.1mm。
10.根据权利要求1所述的使用寿命长的高色域量子点膜，其特征在于：量子点纳米颗粒由IIB-VIA族元素或者IIIV-VA族元素组成，量子点纳米颗粒是以ZnS、PbS作为壳料，并在壳料中加入含镉、锌的CdS、CdSe、CdTe、ZnSe、GaN、InAs中的一种或多种组成的纳米材料。