CN112095224A - Non-woven fabric for clothing lining and preparation process - Google Patents
Non-woven fabric for clothing lining and preparation process Download PDFInfo
- Publication number
- CN112095224A CN112095224A CN202010974688.9A CN202010974688A CN112095224A CN 112095224 A CN112095224 A CN 112095224A CN 202010974688 A CN202010974688 A CN 202010974688A CN 112095224 A CN112095224 A CN 112095224A
- Authority
- CN
- China
- Prior art keywords
- parts
- woven fabric
- fiber yarns
- resin film
- permethrin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a non-woven fabric for a garment lining and a preparation process thereof, belonging to the technical field of lining non-woven fabrics, and the non-woven fabric comprises the following components in parts by weight: 40-55 parts of polypropylene homopolymer, 20-35 parts of fatty amide, 10-16 parts of carbon fiber yarns, 18-23 parts of resin film powder, 15-21 parts of aramid fiber yarns, 3-5 parts of dispersing agent, 2-3 parts of fiber stabilizer, 22-38 parts of polycarbonate, 10-15 parts of epoxy resin and 0.2-0.5 part of permethrin. According to the invention, the carbon fiber yarns, the resin film powder and the aramid fiber yarns are added, so that the tensile strength of the non-woven fabric can be effectively enhanced, and meanwhile, the epoxy resin and the permethrin are added, so that the hardness of the non-woven fabric can be effectively increased, and the deformation capacity of the garment lining in the later use process is reduced.
Description
Technical Field
The invention relates to a non-woven fabric and a preparation process thereof, in particular to a non-woven fabric for a garment lining and a preparation process thereof, belonging to the technical field of lining non-woven fabrics.
Background
Nonwoven fabrics, also known as nonwovens, are composed of oriented or random fibers. It is called cloth because of its appearance and certain properties; the non-woven fabric has the characteristics of moisture resistance, air permeability, flexibility, light weight, no combustion supporting, easy decomposition, no toxicity or irritation, rich color, low price, recycling and the like.
The existing non-woven fabric is used as the inner lining of clothes, the stretch-resistant effect of the lining material is weaker, the non-woven fabric is easy to deform after being washed by water for a long time, the original appearance of the clothes cannot be ensured, and the attractiveness is influenced.
Disclosure of Invention
The invention mainly aims to overcome the defects in the prior art and provides a non-woven fabric for a garment lining and a preparation process thereof.
The purpose of the invention can be achieved by adopting the following technical scheme:
a non-woven fabric for a garment lining comprises the following components in parts by weight: 40-55 parts of polypropylene homopolymer, 20-35 parts of fatty amide, 10-16 parts of carbon fiber yarns, 18-23 parts of resin film powder, 15-21 parts of aramid fiber yarns, 3-5 parts of dispersing agent, 2-3 parts of fiber stabilizer, 22-38 parts of polycarbonate, 10-15 parts of epoxy resin and 0.2-0.5 part of permethrin.
Preferably, the composition comprises the following components in parts by weight: 42-50 parts of polypropylene homopolymer, 25-30 parts of fatty amide, 12-16 parts of carbon fiber yarns, 20-23 parts of resin film powder, 15-20 parts of aramid fiber yarns, 3-5 parts of dispersing agent, 2-3 parts of fiber stabilizer, 25-38 parts of polycarbonate, 10-15 parts of epoxy resin and 0.2-0.5 part of permethrin.
Preferably, the composition comprises the following components in parts by weight: 45 parts of polypropylene homopolymer, 28 parts of fatty amide, 15 parts of carbon fiber yarns, 22 parts of resin film powder, 18 parts of aramid fiber yarns, 4 parts of dispersing agent, 2.1 parts of fiber stabilizer, 29 parts of polycarbonate, 13 parts of epoxy resin and 0.4 part of permethrin.
Preferably, the composition comprises the following components in parts by weight: 48 parts of polypropylene homopolymer, 29 parts of fatty amide, 15 parts of carbon fiber yarns, 22 parts of resin film powder, 19 parts of aramid fiber yarns, 4 parts of dispersing agent, 2 parts of fiber stabilizer, 37 parts of polycarbonate, 14 parts of epoxy resin and 0.4 part of permethrin.
Preferably, the resin film powder is ABS resin film powder.
Preferably, the dispersant is one or more of paraffin, magnesium stearate or polyethylene wax.
Preferably, the fiber stabilizer is lignocellulose.
Preferably, the use ratio of the carbon fiber yarns to the aramid fiber yarns is 2: 3.
a preparation process of non-woven fabric for clothing linings comprises the following steps:
step 1: comprises the following components in parts by weight: melting and mixing polypropylene homopolymer, fatty amide, carbon fiber yarns, resin film powder, aramid fiber yarns, a dispersing agent, a fiber stabilizing agent, polycarbonate, epoxy resin and permethrin, tiling the mixture into a net through a net machine, and performing spunlace to obtain a semi-finished non-woven fabric;
step 2: and (3) soaking the semi-finished non-woven fabric in ethanol for 1-3 hours, taking out after full soaking, and hot-pressing and ironing the semi-finished non-woven fabric into fabric through a rolling mill to obtain the non-woven fabric for the clothing lining.
Preferably, the hot-pressing ironing temperature of the rolling mill is 180-190 ℃.
The invention has the beneficial technical effects that: according to the non-woven fabric for the garment lining and the preparation process thereof, the carbon fiber yarns, the resin film powder and the aramid fiber yarns are added, so that the tensile strength of the non-woven fabric can be effectively enhanced, and meanwhile, the epoxy resin and the permethrin are added, so that the hardness of the non-woven fabric can be effectively increased, and the deformation capacity of the garment lining in the later use process is reduced.
Detailed Description
In order to make the technical solutions of the present invention more clear and definite for those skilled in the art, the present invention is further described in detail with reference to the following examples, but the embodiments of the present invention are not limited thereto.
The non-woven fabrics for clothing inside lining that this embodiment provided, by weight, include: 40-55 parts of polypropylene homopolymer, 20-35 parts of fatty amide, 10-16 parts of carbon fiber yarns, 18-23 parts of resin film powder, 15-21 parts of aramid fiber yarns, 3-5 parts of dispersing agent, 2-3 parts of fiber stabilizer, 22-38 parts of polycarbonate, 10-15 parts of epoxy resin and 0.2-0.5 part of permethrin.
Comprises the following components in parts by weight: 42-50 parts of polypropylene homopolymer, 25-30 parts of fatty amide, 12-16 parts of carbon fiber yarns, 20-23 parts of resin film powder, 15-20 parts of aramid fiber yarns, 3-5 parts of dispersing agent, 2-3 parts of fiber stabilizer, 25-38 parts of polycarbonate, 10-15 parts of epoxy resin and 0.2-0.5 part of permethrin.
Comprises the following components in parts by weight: 45 parts of polypropylene homopolymer, 28 parts of fatty amide, 15 parts of carbon fiber yarns, 22 parts of resin film powder, 18 parts of aramid fiber yarns, 4 parts of dispersing agent, 2.1 parts of fiber stabilizer, 29 parts of polycarbonate, 13 parts of epoxy resin and 0.4 part of permethrin.
Comprises the following components in parts by weight: 48 parts of polypropylene homopolymer, 29 parts of fatty amide, 15 parts of carbon fiber yarns, 22 parts of resin film powder, 19 parts of aramid fiber yarns, 4 parts of dispersing agent, 2 parts of fiber stabilizer, 37 parts of polycarbonate, 14 parts of epoxy resin and 0.4 part of permethrin.
The resin film powder is ABS resin film powder. The dispersing agent is one or more of paraffin, magnesium stearate or polyethylene wax. The fiber stabilizer is lignocellulose. The use ratio of the carbon fiber yarns to the aramid fiber yarns is 2: 3.
a preparation process of non-woven fabric for clothing linings comprises the following steps:
step 1: comprises the following components in parts by weight: melting and mixing polypropylene homopolymer, fatty amide, carbon fiber yarns, resin film powder, aramid fiber yarns, a dispersing agent, a fiber stabilizing agent, polycarbonate, epoxy resin and permethrin, tiling the mixture into a net through a net machine, and performing spunlace to obtain a semi-finished non-woven fabric;
step 2: and (3) soaking the semi-finished non-woven fabric in ethanol for 1-3 hours, taking out after full soaking, and hot-pressing and ironing the semi-finished non-woven fabric into fabric through a rolling mill to obtain the non-woven fabric for the clothing lining. The hot-pressing ironing temperature of the rolling mill is 180-190 ℃.
Example 1:
a non-woven fabric for a garment lining comprises the following components in parts by weight: 42 parts of polypropylene homopolymer, 25 parts of fatty amide, 12 parts of carbon fiber yarns, 20 parts of resin film powder, 15 parts of aramid fiber yarns, 3 parts of dispersing agent, 2 parts of fiber stabilizer, 25 parts of polycarbonate, 10 parts of epoxy resin and 0.2 part of permethrin.
A preparation process of non-woven fabric for clothing linings comprises the following steps:
step 1: comprises the following components in parts by weight: melting and mixing polypropylene homopolymer, fatty amide, carbon fiber yarns, resin film powder, aramid fiber yarns, a dispersing agent, a fiber stabilizing agent, polycarbonate, epoxy resin and permethrin, tiling the mixture into a net through a net machine, and performing spunlace to obtain a semi-finished non-woven fabric;
step 2: and (3) soaking the semi-finished non-woven fabric in ethanol for 1h, taking out after full soaking, and hot-pressing and ironing the semi-finished non-woven fabric into fabric through a rolling mill to obtain the non-woven fabric for the clothing lining.
Example 2:
a non-woven fabric for a garment lining comprises the following components in parts by weight: 43 parts of polypropylene homopolymer, 26 parts of fatty amide, 13 parts of carbon fiber yarns, 21 parts of resin film powder, 16 parts of aramid fiber yarns, 4 parts of dispersing agent, 2 parts of fiber stabilizer, 26 parts of polycarbonate, 11 parts of epoxy resin and 0.3 part of permethrin.
A preparation process of non-woven fabric for clothing linings comprises the following steps:
step 1: comprises the following components in parts by weight: melting and mixing polypropylene homopolymer, fatty amide, carbon fiber yarns, resin film powder, aramid fiber yarns, a dispersing agent, a fiber stabilizing agent, polycarbonate, epoxy resin and permethrin, tiling the mixture into a net through a net machine, and performing spunlace to obtain a semi-finished non-woven fabric;
step 2: and (3) soaking the semi-finished non-woven fabric in ethanol for 1h, taking out after full soaking, and hot-pressing and ironing the semi-finished non-woven fabric into fabric through a rolling mill to obtain the non-woven fabric for the clothing lining.
Example 3:
a non-woven fabric for a garment lining comprises the following components in parts by weight: 45 parts of polypropylene homopolymer, 28 parts of fatty amide, 15 parts of carbon fiber yarns, 22 parts of resin film powder, 18 parts of aramid fiber yarns, 4 parts of dispersing agent, 2.1 parts of fiber stabilizer, 29 parts of polycarbonate, 13 parts of epoxy resin and 0.4 part of permethrin.
A preparation process of non-woven fabric for clothing linings comprises the following steps:
step 1: comprises the following components in parts by weight: melting and mixing polypropylene homopolymer, fatty amide, carbon fiber yarns, resin film powder, aramid fiber yarns, a dispersing agent, a fiber stabilizing agent, polycarbonate, epoxy resin and permethrin, tiling the mixture into a net through a net machine, and performing spunlace to obtain a semi-finished non-woven fabric;
step 2: and (3) soaking the semi-finished non-woven fabric in ethanol for 1-3 hours, taking out after full soaking, and hot-pressing and ironing the semi-finished non-woven fabric into fabric through a rolling mill to obtain the non-woven fabric for the clothing lining.
Example 4:
a non-woven fabric for a garment lining comprises the following components in parts by weight: 48 parts of polypropylene homopolymer, 29 parts of fatty amide, 15 parts of carbon fiber yarns, 22 parts of resin film powder, 19 parts of aramid fiber yarns, 4 parts of dispersing agent, 2 parts of fiber stabilizer, 37 parts of polycarbonate, 14 parts of epoxy resin and 0.4 part of permethrin.
A preparation process of non-woven fabric for clothing linings comprises the following steps:
step 1: comprises the following components in parts by weight: melting and mixing polypropylene homopolymer, fatty amide, carbon fiber yarns, resin film powder, aramid fiber yarns, a dispersing agent, a fiber stabilizing agent, polycarbonate, epoxy resin and permethrin, tiling the mixture into a net through a net machine, and performing spunlace to obtain a semi-finished non-woven fabric;
step 2: and (3) soaking the semi-finished non-woven fabric in ethanol for 1-3 hours, taking out after full soaking, and hot-pressing and ironing the semi-finished non-woven fabric into fabric through a rolling mill to obtain the non-woven fabric for the clothing lining.
Example 5:
a non-woven fabric for a garment lining comprises the following components in parts by weight: 50 parts of polypropylene homopolymer, 30 parts of fatty amide, 16 parts of carbon fiber yarns, 23 parts of resin film powder, 20 parts of aramid fiber yarns, 5 parts of dispersing agent, 3 parts of fiber stabilizer, 38 parts of polycarbonate, 15 parts of epoxy resin and 0.5 part of permethrin.
A preparation process of non-woven fabric for clothing linings comprises the following steps:
step 1: comprises the following components in parts by weight: melting and mixing polypropylene homopolymer, fatty amide, carbon fiber yarns, resin film powder, aramid fiber yarns, a dispersing agent, a fiber stabilizing agent, polycarbonate, epoxy resin and permethrin, tiling the mixture into a net through a net machine, and performing spunlace to obtain a semi-finished non-woven fabric;
step 2: and (3) soaking the semi-finished non-woven fabric in ethanol for 1h, taking out after full soaking, and hot-pressing and ironing the semi-finished non-woven fabric into fabric through a rolling mill to obtain the non-woven fabric for the clothing lining.
Table 1 shows the performance test of the nonwoven after 100 times of water washing
| Serial number | Tensile strength (MPa) | Degree of deformation |
| Example 1 | 5.1 | 2.1％ |
| Example 2 | 5.5 | 2.5％ |
| Example 3 | 5.8 | 2.8％ |
| Example 4 | 6.2 | 2.9％ |
| Example 5 | 5.3 | 2.6％ |
As described above, in this example, the nonwoven fabric for clothing interlining and the production process thereof according to the present example, and the nonwoven fabric for clothing interlining and the production process thereof according to the present example, it is understood from examples 1 to 5 that the nonwoven fabrics prepared in examples 3 and 4 have the best tensile strength and the best ability to maintain deformation. The tensile strength that adds carbon fiber silk, resin film powder and aramid fiber silk can effectual reinforcing non-woven fabrics, adds epoxy and permethrin simultaneously and can effectively increase the hardness of non-woven fabrics, reduces the ability that the clothing inside lining warp in the later stage use.
The above description is only for the purpose of illustrating the present invention and is not intended to limit the scope of the present invention, and any person skilled in the art can substitute or change the technical solution of the present invention and its conception within the scope of the present invention.
Claims (10)
1. A non-woven fabric for clothing linings is characterized by comprising the following components in parts by weight: 40-55 parts of polypropylene homopolymer, 20-35 parts of fatty amide, 10-16 parts of carbon fiber yarns, 18-23 parts of resin film powder, 15-21 parts of aramid fiber yarns, 3-5 parts of dispersing agent, 2-3 parts of fiber stabilizer, 22-38 parts of polycarbonate, 10-15 parts of epoxy resin and 0.2-0.5 part of permethrin.
2. The non-woven fabric for clothing lining according to claim 1, characterized by comprising, in parts by weight: 42-50 parts of polypropylene homopolymer, 25-30 parts of fatty amide, 12-16 parts of carbon fiber yarns, 20-23 parts of resin film powder, 15-20 parts of aramid fiber yarns, 3-5 parts of dispersing agent, 2-3 parts of fiber stabilizer, 25-38 parts of polycarbonate, 10-15 parts of epoxy resin and 0.2-0.5 part of permethrin.
3. The non-woven fabric for clothing lining according to claim 1, characterized by comprising, in parts by weight: 45 parts of polypropylene homopolymer, 28 parts of fatty amide, 15 parts of carbon fiber yarns, 22 parts of resin film powder, 18 parts of aramid fiber yarns, 4 parts of dispersing agent, 2.1 parts of fiber stabilizer, 29 parts of polycarbonate, 13 parts of epoxy resin and 0.4 part of permethrin.
4. The non-woven fabric for clothing lining according to claim 1, characterized by comprising, in parts by weight: 48 parts of polypropylene homopolymer, 29 parts of fatty amide, 15 parts of carbon fiber yarns, 22 parts of resin film powder, 19 parts of aramid fiber yarns, 4 parts of dispersing agent, 2 parts of fiber stabilizer, 37 parts of polycarbonate, 14 parts of epoxy resin and 0.4 part of permethrin.
5. The nonwoven fabric for clothing interlinings of claim 1, wherein the resin film powder is an ABS resin film powder.
6. The nonwoven fabric for clothing lining according to claim 1, wherein the dispersant is one or more of paraffin, magnesium stearate or polyethylene wax.
7. The non-woven fabric for clothing lining and the preparation process thereof according to claim 1, wherein the fiber stabilizer is lignocellulose.
8. The non-woven fabric for the garment lining and the preparation process of the non-woven fabric for the garment lining as claimed in claim 1, wherein the carbon fiber yarns and the aramid fiber yarns are used in a ratio of 2: 3.
9. a preparation process of non-woven fabric for clothing linings is characterized by comprising the following steps:
step 1: comprises the following components in parts by weight: melting and mixing polypropylene homopolymer, fatty amide, carbon fiber yarns, resin film powder, aramid fiber yarns, a dispersing agent, a fiber stabilizing agent, polycarbonate, epoxy resin and permethrin, tiling the mixture into a net through a net machine, and performing spunlace to obtain a semi-finished non-woven fabric;
step 2: and (3) soaking the semi-finished non-woven fabric in ethanol for 1-3 hours, taking out after full soaking, and hot-pressing and ironing the semi-finished non-woven fabric into fabric through a rolling mill to obtain the non-woven fabric for the clothing lining.
10. The preparation process of the non-woven fabric for the garment interlining, according to claim 9, is characterized in that the hot-pressing ironing temperature of the rolling mill is 180-190 ℃.