CN111961275A - 一种轻质高弹护膝、护肘的配方 - Google Patents
一种轻质高弹护膝、护肘的配方 Download PDFInfo
- Publication number
- CN111961275A CN111961275A CN202010812755.7A CN202010812755A CN111961275A CN 111961275 A CN111961275 A CN 111961275A CN 202010812755 A CN202010812755 A CN 202010812755A CN 111961275 A CN111961275 A CN 111961275A
- Authority
- CN
- China
- Prior art keywords
- parts
- opc
- agent
- elbow
- pad
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种轻质高弹护膝、护肘的配方,包括如下组分:7350(EVA)20‑25份、007(OPC INPUSE)14‑20份、010(OPC INFUSE)28‑35份、F110(三开)5‑10份、OE475(Engage)5‑10份、化锌1‑4份、脂酸0.1‑0.5份、脂酸锌0.2‑0.6份、AIC(助交联剂)0.2‑0.7份、G‑88(快速剂)0.1‑0.5份、无味DCP0.1‑0.5份、发泡剂AC1‑3.5份,包括如下步骤:S1将7350(EVA)、007(OPC INPUSE)、010(OPC INFUSE)、F110(三开)、OE475(Engage)、化锌、脂酸、脂酸锌、AIC(助交联剂)、G‑88(快速剂)、无味、发泡剂分类并生产产出布料或部件;S2将S1生产产出的布料或部件进行裁剪形成护膝、护肘部件;S3对部件进行拼接,从而产出护膝、护肘。该轻质高弹护膝、护肘的配方生产的一套护膝护肘重量只有市场重量四分之一的轻质高弹护膝。
Description
技术领域
本发明涉及护膝、护肘制备技术领域,具体为一种轻质高弹护膝、护肘的配方。
背景技术
护膝、护肘,专业体育用品,指的是用于保护手肘和膝盖关节的一种护具,随着社会发展,护膝、护肘基本上成为运动员必备的运动器材之一。手肘和膝盖是人们最坚硬的身体部位之一,运动员手肘和膝盖处出现伤病的机会是很低的,但是很多时候运动选手还是会佩戴护膝、护肘来预防肌肉损伤。
护膝和护肘的使用能够有效减少损伤,从而保护身体,从而达到安心运动,强身健体的目的。
但是现有的护膝、护肘密度高,一套护膝、护肘重量高于260克,反复使用容易破损,耐水解性差。
发明内容
本发明的目的在于提供一种轻质高弹护膝、护膝、护肘的配方,以解决上述背景技术提出的护膝、护肘密度高,一套护膝、护肘重量高于260克,反复使用容易破损,耐水解性差的问题。
为实现上述目的,本发明提供如下技术方案:一种轻质高弹护膝、护肘的配方,包括如下组分:7350(EVA)20-25份、007(OPC INPUSE)14-20份、010(OPC INFUSE)28-35份、F110(三开)5-10份、OE475(Engage)5-10份、化锌1-4份、脂酸0.1-0.5份、脂酸锌0.2-0.6份、AIC(助交联剂)0.2-0.7份、G-88(快速剂)0.1-0.5份、无味DCP0.1-0.5份、发泡剂AC1-3.5份,包括如下步骤:
S1将7350(EVA)、007(OPC INPUSE)、010(OPC INFUSE)、F110(三开)、OE475(Engage)、化锌、脂酸、脂酸锌、AIC(助交联剂)、G-88(快速剂)、无味、发泡剂分类并生产产出布料或部件;
S2将S1生产产出的布料或部件进行裁剪形成护膝、护肘部件;
S3对部件进行拼接,从而产出护膝、护肘。
优选的,所述7350(EVA)20份、007(OPC INPUSE)14份、010(OPC INFUSE)28份、F110(三开)5-份、OE475(Engage)5份、化锌1份、脂酸0.1份、脂酸锌0.2份、AIC(助交联剂)0.2份、G-88(快速剂)0.1份、无味DCP0.1份、发泡剂AC1份。
优选的,所述7350(EVA)25份、007(OPC INPUSE)20份、010(OPC INFUSE)35份、F110(三开)10份、OE475(Engage)10份、化锌4份、脂酸0.5份、脂酸锌0.6份、AIC(助交联剂)0.7份、G-88(快速剂)0.5份、无味DCP0.5份、发泡剂AC3.5份。
优选的,所述7350(EVA)22.5份、007(OPC INPUSE)17份、010(OPC INFUSE)21.5份、F110(三开)7.5份、OE475(Engage)7.5份、化锌2.5份、脂酸0.3份、脂酸锌0.4份、AIC(助交联剂)0.45份、G-88(快速剂)0.3份、无味DCP0.3份、发泡剂AC2份。
与现有技术相比,本发明的有益效果是:该轻质高弹护膝、护肘的配方生产的一套护膝护肘重量只有市场重量四分之一的轻质高弹护膝,不仅质量轻便,在使用时更加的方便,同时由于材质的使用,使得该护膝护肘更加耐磨损,不易破损,同时有效的提高了护膝护肘的水解性能。
具体实施方式
对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
实施例1
一种轻质高弹护膝、护肘的配方,包括如下组分:7350(EVA)20-25份、007(OPCINPUSE)14-20份、010(OPC INFUSE)28-35份、F110(三开)5-10份、OE475(Engage)5-10份、化锌1-4份、脂酸0.1-0.5份、脂酸锌0.2-0.6份、AIC(助交联剂)0.2-0.7份、G-88(快速剂)0.1-0.5份、无味DCP0.1-0.5份、发泡剂AC1-3.5份,包括如下步骤:
S1将7350(EVA)、007(OPC INPUSE)、010(OPC INFUSE)、F110(三开)、OE475(Engage)、化锌、脂酸、脂酸锌、AIC(助交联剂)、G-88(快速剂)、无味、发泡剂分类并生产产出布料或部件;
S2将S1生产产出的布料或部件进行裁剪形成护膝、护肘部件;
S3对部件进行拼接,从而产出护膝、护肘。
进一步的,所述7350(EVA)20份、007(OPC INPUSE)14份、010(OPC INFUSE)28份、F110(三开)5-份、OE475(Engage)5份、化锌1份、脂酸0.1份、脂酸锌0.2份、AIC(助交联剂)0.2份、G-88(快速剂)0.1份、无味DCP0.1份、发泡剂AC1份。
一、物性测试
实施例2
一种轻质高弹护膝、护肘的配方,包括如下组分:7350(EVA)20-25份、007(OPCINPUSE)14-20份、010(OPC INFUSE)28-35份、F110(三开)5-10份、OE475(Engage)5-10份、化锌1-4份、脂酸0.1-0.5份、脂酸锌0.2-0.6份、AIC(助交联剂)0.2-0.7份、G-88(快速剂)0.1-0.5份、无味DCP0.1-0.5份、发泡剂AC1-3.5份,包括如下步骤:
S1将7350(EVA)、007(OPC INPUSE)、010(OPC INFUSE)、F110(三开)、OE475(Engage)、化锌、脂酸、脂酸锌、AIC(助交联剂)、G-88(快速剂)、无味、发泡剂分类并生产产出布料或部件;
S2将S1生产产出的布料或部件进行裁剪形成护膝、护肘部件;
S3对部件进行拼接,从而产出护膝、护肘。
进一步的,所述7350(EVA)25份、007(OPC INPUSE)20份、010(OPC INFUSE)35份、F110(三开)10份、OE475(Engage)10份、化锌4份、脂酸0.5份、脂酸锌0.6份、AIC(助交联剂)0.7份、G-88(快速剂)0.5份、无味DCP0.5份、发泡剂AC3.5份。
二、物性测试
实施例3
一种轻质高弹护膝、护肘的配方,包括如下组分:7350(EVA)20-25份、007(OPCINPUSE)14-20份、010(OPC INFUSE)28-35份、F110(三开)5-10份、OE475(Engage)5-10份、化锌1-4份、脂酸0.1-0.5份、脂酸锌0.2-0.6份、AIC(助交联剂)0.2-0.7份、G-88(快速剂)0.1-0.5份、无味DCP0.1-0.5份、发泡剂AC1-3.5份,包括如下步骤:
S1将7350(EVA)、007(OPC INPUSE)、010(OPC INFUSE)、F110(三开)、OE475(Engage)、化锌、脂酸、脂酸锌、AIC(助交联剂)、G-88(快速剂)、无味、发泡剂分类并生产产出布料或部件;
S2将S1生产产出的布料或部件进行裁剪形成护膝、护肘部件;
S3对部件进行拼接,从而产出护膝、护肘。
优选的,所述7350(EVA)22.5份、007(OPC INPUSE)17份、010(OPC INFUSE)21.5份、F110(三开)7.5份、OE475(Engage)7.5份、化锌2.5份、脂酸0.3份、脂酸锌0.4份、AIC(助交联剂)0.45份、G-88(快速剂)0.3份、无味DCP0.3份、发泡剂AC2份。
三、物性测试
尽管参照前述实施例对本发明进行了详细的说明,对于本领域的技术人员来说,其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分技术特征进行等同替换,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (4)
1.一种轻质高弹护膝、护肘的配方,包括如下组分:7350(EVA)20-25份、007(OPCINPUSE)14-20份、010(OPC INFUSE)28-35份、F110(三开)5-10份、OE475(Engage)5-10份、化锌1-4份、脂酸0.1-0.5份、脂酸锌0.2-0.6份、AIC(助交联剂)0.2-0.7份、G-88(快速剂)0.1-0.5份、无味DCP0.1-0.5份、发泡剂AC1-3.5份,其特征在于,包括如下步骤:
S1将7350(EVA)、007(OPC INPUSE)、010(OPC INFUSE)、F110(三开)、OE475(Engage)、化锌、脂酸、脂酸锌、AIC(助交联剂)、G-88(快速剂)、无味、发泡剂分类并生产产出布料或部件;
S2将S1生产产出的布料或部件进行裁剪形成护膝、护肘部件;
S3对部件进行拼接,从而产出护膝、护肘。
2.根据权利要求1所述的一种轻质高弹护膝、护肘的配方,其特征在于:所述7350(EVA)20份、007(OPC INPUSE)14份、010(OPC INFUSE)28份、F110(三开)5-份、OE475(Engage)5份、化锌1份、脂酸0.1份、脂酸锌0.2份、AIC(助交联剂)0.2份、G-88(快速剂)0.1份、无味DCP0.1份、发泡剂AC1份。
3.根据权利要求1所述的一种轻质高弹护膝、护肘的配方,其特征在于:所述7350(EVA)25份、007(OPC INPUSE)20份、010(OPC INFUSE)35份、F110(三开)10份、OE475(Engage)10份、化锌4份、脂酸0.5份、脂酸锌0.6份、AIC(助交联剂)0.7份、G-88(快速剂)0.5份、无味DCP0.5份、发泡剂AC3.5份。
4.根据权利要求1所述的一种轻质高弹护膝、护肘的配方,其特征在于:所述7350(EVA)22.5份、007(OPC INPUSE)17份、010(OPC INFUSE)21.5份、F110(三开)7.5份、OE475(Engage)7.5份、化锌2.5份、脂酸0.3份、脂酸锌0.4份、AIC(助交联剂)0.45份、G-88(快速剂)0.3份、无味DCP0.3份、发泡剂AC2份。