CN111923548A - 一种抗菌香烟接装纸及其印刷工艺 - Google Patents
一种抗菌香烟接装纸及其印刷工艺 Download PDFInfo
- Publication number
- CN111923548A CN111923548A CN202010804590.9A CN202010804590A CN111923548A CN 111923548 A CN111923548 A CN 111923548A CN 202010804590 A CN202010804590 A CN 202010804590A CN 111923548 A CN111923548 A CN 111923548A
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- tipping paper
- layer
- cigarette tipping
- ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗菌香烟接装纸及其印刷工艺，其技术方案是：包括基层，所述基层顶部固定连接有两个防水层，两个所述防水层内侧固定连接有透气层，所述防水层顶部固定连接有抗菌层，所述防水层由PP聚丙烯材料制成，所述透气层由PP聚乙烯透气膜材料制成，一种抗菌香烟接装纸及其印刷工艺有益效果是：通过设置透气层夹在两个防水层内侧，有效对由PP聚乙烯透气膜材料制成的透气层进行保护，保证本发明的透气能力，同时通过设置由银离子抗菌剂涂覆制成的抗菌层，可有效对细菌进行杀灭作用，并且通过在印刷油墨中添加丙凝乳液、壳聚糖和高分子水凝胶等物质，使得印刷油墨具有较好的防水能力，同时还具有隔菌杀菌能力。
Description
技术领域
本发明涉及香烟接装纸生产技术领域，具体涉及一种抗菌香烟接装纸及其印刷工艺。
背景技术
根据中国消费者协会公开发表的数据，我国香烟年均消费量达92亿1千2百万支左右，估计接触钱币后吸烟的消费者占1/3(据调査各种面值的流通货币，大肠杆菌的检出率为46.5％，每张纸币带菌2.7万至8.2亿个，每张纸币平均带菌90力个)；上厕所后吸烟的占l/3；手摸、捏、拿其它东西、包括捏鼻涕、搔痒等后吸烟的消费者占1/3。几乎所有的人都知道进食前要洗手，但是很少有吸烟者能意识到抽烟前也应该注意手指的卫生。吸烟者不可能作到每时每刻都保持手指的清洁卫生，用被细菌等微生物污染的手指去拿香烟的过滤嘴，再将其放入口中，病菌也将随之进入了人体；另外，相互敬烟是人们出于礼貌的一种习惯。然而这个递烟的过程就成了交叉感染各种传染疾病的过程。曾有人做过实验，将连续7天内在多种场合接受别人递给的过滤嘴香烟112支立即放入无菌的塑料袋内，经微生物学检验，发现75％的嘴棒表面都有不同程度地带有各种致病菌，其中有甲肝病毒、乙肝病毒、大肠杆菌等，另有残余鼻涕和粪便痕迹。因此，香烟在吸食、传递过程中存在着卫生安全隐患，中国消费者协会于2001年5月31日“世界无烟日”前夕发布第六号消费警示“吸烟是病从口入的重要途径之一”。因此，使接装纸具有广谱的抗菌性能，防止细菌特别是消化道、呼吸道传染病菌和食物中毒病原菌污染接装纸，从而预防吸烟者通过巻烟过滤嘴为媒介所导致的疾病的发生，这对于保障吸烟者的身体健康具有重要的意义。
而目前现有技术中香烟接装纸往往不具备抗菌能力，生产香烟后，香烟长期放置或使用时接触后，容易滋生和沾染细菌，影响食用安全
因此，发明一种抗菌香烟接装纸及其印刷工艺很有必要。
发明内容
为此，本发明提供一种抗菌香烟接装纸及其印刷工艺，通过设置透气层夹在两个防水层内侧，有效对由PP聚乙烯透气膜材料制成的透气层进行保护，保证本发明的透气能力，同时通过设置由银离子抗菌剂涂覆制成的抗菌层，可有效对细菌进行杀灭作用，并且通过在印刷油墨中添加丙凝乳液、壳聚糖和高分子水凝胶等物质，使得印刷油墨具有较好的防水能力，同时还具有隔菌杀菌能力，以解决现有技术中香烟接装纸往往不具备抗菌能力，生产香烟后，香烟长期放置容易滋生细菌，影响食用安全的问题。
为了实现上述目的，本发明提供如下技术方案：一种抗菌香烟接装纸及其印刷工艺，包括基层，所述基层顶部固定连接有两个防水层，两个所述防水层内侧固定连接有透气层，所述防水层顶部固定连接有抗菌层。
优选的，所述防水层由PP聚丙烯材料制成。
优选的，所述透气层由PP聚乙烯透气膜材料制成。
优选的，所述抗菌层由银离子抗菌剂涂覆制成。
优选的，包括主料和配料，所述主料包括油墨和工业乙醇，所述配料包括丙凝乳液、壳聚糖和高分子水凝胶。
优选的，所述主料中各成分质量份数分别为：
油墨：80-90份
工业乙醇：10-20份。
优选的，所述配料中各成分质量份数分别为：
丙凝乳液：5-20份
壳聚糖：10-15份
高分子水凝胶：5-15份。
优选的，所述工业乙醇浓度为85％。
优选的，包括以下印刷步骤：
S1，将主料中的油墨和工业乙醇以及配料中的丙凝乳液、壳聚糖和高分子水凝胶混合并充分搅拌，使其混合均匀，得到混合油墨；
S2，将混合油墨加热升温并持续搅拌20min，加热温度为50-80℃，加热时长为20min，而后使得混合溶液降温至常温。
S3，将降温后的混合油墨填充至印刷机器的油墨盒内部，而后使用印刷机器对抗菌香烟接装纸进行印刷工作；
S4，进印刷后的抗菌香烟接装纸进行烘烤干燥，烘烤温度为90-120℃，烘烤时长为5min。
本发明的有益效果是：
本发明通过设置透气层夹在两个防水层内侧，有效对由PP聚乙烯透气膜材料制成的透气层进行保护，保证本发明的透气能力，同时通过设置由银离子抗菌剂涂覆制成的抗菌层，可有效对细菌进行杀灭作用，并且通过在印刷油墨中添加丙凝乳液、壳聚糖和高分子水凝胶等物质，使得印刷油墨具有较好的防水能力，同时还具有隔菌杀菌能力，配合抗菌层可进一步提升本发明细菌滋生的可能，提高本发明的卫生标准，使用更加安全可靠，并且丙凝乳液和两个防水层的防水能力也可较好的保证本发明印刷的油墨遇水时不易晕散，提升印刷质量。
附图说明
图1为本发明提供的整体结构示意图；
图中：1基层、2防水层、3透气层、4抗菌层。
具体实施方式
以下结合附图对本发明的优选实施例进行说明，应当理解，此处所描述的优选实施例仅用于说明和解释本发明，并不用于限定本发明。
实施例1：
参照附图1，本发明提供的一种抗菌香烟接装纸及其印刷工艺，包括基层1，所述基层1顶部固定连接有两个防水层2，两个所述防水层2内侧固定连接有透气层3，所述防水层2顶部固定连接有抗菌层4；
进一步地，所述防水层2由PP聚丙烯材料制成；
进一步地，所述透气层3由PP聚乙烯透气膜材料制成；
进一步地，所述抗菌层4由银离子抗菌剂涂覆制成；
进一步地，包括主料和配料，所述主料包括油墨和工业乙醇，所述配料包括丙凝乳液、壳聚糖和高分子水凝胶；
进一步地，所述主料中各成分质量份数分别为：
油墨：90份
工业乙醇：10份，利用工业乙醇作为溶剂可较好的调整油墨浓度和粘稠度，从而取得最为优异的印刷效果；
进一步地，所述配料中各成分质量份数分别为：
丙凝乳液：20份
壳聚糖：10份
高分子水凝胶：5份，丙凝乳液具有极好的防水防腐能力且安全无毒，壳聚糖具有较好的杀菌能力，而高分子水凝胶则具有较好的隔菌能力，极大程度减少细菌滋生；
进一步地，所述工业乙醇浓度为85％；
包括以下印刷步骤：
S1，将主料中的油墨和工业乙醇以及配料中的丙凝乳液、壳聚糖和高分子水凝胶混合并充分搅拌，使其混合均匀，得到混合油墨；
S2，将混合油墨加热升温并持续搅拌20min，加热温度为80℃，加热时长为20min，而后使得混合溶液降温至常温。
S3，将降温后的混合油墨填充至印刷机器的油墨盒内部，而后使用印刷机器对抗菌香烟接装纸进行印刷工作；
S4，进印刷后的抗菌香烟接装纸进行烘烤干燥，烘烤温度为120℃，烘烤时长为5min。
实施例2：
参照附图1，本发明提供的一种抗菌香烟接装纸及其印刷工艺，包括基层1，所述基层1顶部固定连接有两个防水层2，两个所述防水层2内侧固定连接有透气层3，所述防水层2顶部固定连接有抗菌层4；
进一步地，所述防水层2由PP聚丙烯材料制成；
进一步地，所述透气层3由PP聚乙烯透气膜材料制成；
进一步地，所述抗菌层4由银离子抗菌剂涂覆制成；
进一步地，包括主料和配料，所述主料包括油墨和工业乙醇，所述配料包括丙凝乳液、壳聚糖和高分子水凝胶；
进一步地，所述主料中各成分质量份数分别为：
油墨：80份
工业乙醇：20份，利用工业乙醇作为溶剂可较好的调整油墨浓度和粘稠度，从而取得最为优异的印刷效果；
进一步地，所述配料中各成分质量份数分别为：
丙凝乳液：10份
壳聚糖：15份
高分子水凝胶：15份，丙凝乳液具有极好的防水防腐能力且安全无毒，壳聚糖具有较好的杀菌能力，而高分子水凝胶则具有较好的隔菌能力，极大程度减少细菌滋生；
进一步地，所述工业乙醇浓度为85％；
包括以下印刷步骤：
S1，将主料中的油墨和工业乙醇以及配料中的丙凝乳液、壳聚糖和高分子水凝胶混合并充分搅拌，使其混合均匀，得到混合油墨；
S2，将混合油墨加热升温并持续搅拌20min，加热温度为80℃，加热时长为20min，而后使得混合溶液降温至常温。
S3，将降温后的混合油墨填充至印刷机器的油墨盒内部，而后使用印刷机器对抗菌香烟接装纸进行印刷工作；
S4，进印刷后的抗菌香烟接装纸进行烘烤干燥，烘烤温度为120℃，烘烤时长为5min。
实施例3：
参照附图1，本发明提供的一种抗菌香烟接装纸及其印刷工艺，包括基层1，所述基层1顶部固定连接有两个防水层2，两个所述防水层2内侧固定连接有透气层3，所述防水层2顶部固定连接有抗菌层4；
进一步地，所述防水层2由PP聚丙烯材料制成；
进一步地，所述透气层3由PP聚乙烯透气膜材料制成；
进一步地，所述抗菌层4由银离子抗菌剂涂覆制成；
进一步地，包括主料和配料，所述主料包括油墨和工业乙醇，所述配料包括丙凝乳液、壳聚糖和高分子水凝胶；
进一步地，所述主料中各成分质量份数分别为：
油墨：90份
工业乙醇：10份，利用工业乙醇作为溶剂可较好的调整油墨浓度和粘稠度，从而取得最为优异的印刷效果；
进一步地，所述配料中各成分质量份数分别为：
丙凝乳液：5份
壳聚糖：15份
高分子水凝胶：5份，丙凝乳液具有极好的防水防腐能力且安全无毒，壳聚糖具有较好的杀菌能力，而高分子水凝胶则具有较好的隔菌能力，极大程度减少细菌滋生；
进一步地，所述工业乙醇浓度为85％；
包括以下印刷步骤：
S1，将主料中的油墨和工业乙醇以及配料中的丙凝乳液、壳聚糖和高分子水凝胶混合并充分搅拌，使其混合均匀，得到混合油墨；
S2，将混合油墨加热升温并持续搅拌20min，加热温度为60℃，加热时长为20min，而后使得混合溶液降温至常温。
S3，将降温后的混合油墨填充至印刷机器的油墨盒内部，而后使用印刷机器对抗菌香烟接装纸进行印刷工作；
S4，进印刷后的抗菌香烟接装纸进行烘烤干燥，烘烤温度为100℃，烘烤时长为5min。
实施例4：
参照附图1，本发明提供的一种抗菌香烟接装纸及其印刷工艺，包括基层1，所述基层1顶部固定连接有两个防水层2，两个所述防水层2内侧固定连接有透气层3，所述防水层2顶部固定连接有抗菌层4；
进一步地，所述防水层2由PP聚丙烯材料制成；
进一步地，所述透气层3由PP聚乙烯透气膜材料制成；
进一步地，所述抗菌层4由银离子抗菌剂涂覆制成；
进一步地，包括主料和配料，所述主料包括油墨和工业乙醇，所述配料包括丙凝乳液、壳聚糖和高分子水凝胶；
进一步地，所述主料中各成分质量份数分别为：
油墨：80份
工业乙醇：20份，利用工业乙醇作为溶剂可较好的调整油墨浓度和粘稠度，从而取得最为优异的印刷效果；
进一步地，所述配料中各成分质量份数分别为：
丙凝乳液：15份
壳聚糖：10份
高分子水凝胶：5份，丙凝乳液具有极好的防水防腐能力且安全无毒，壳聚糖具有较好的杀菌能力，而高分子水凝胶则具有较好的隔菌能力，极大程度减少细菌滋生；
进一步地，所述工业乙醇浓度为85％；
包括以下印刷步骤：
S1，将主料中的油墨和工业乙醇以及配料中的丙凝乳液、壳聚糖和高分子水凝胶混合并充分搅拌，使其混合均匀，得到混合油墨；
S2，将混合油墨加热升温并持续搅拌20min，加热温度为50℃，加热时长为20min，而后使得混合溶液降温至常温。
S3，将降温后的混合油墨填充至印刷机器的油墨盒内部，而后使用印刷机器对抗菌香烟接装纸进行印刷工作；
S4，进印刷后的抗菌香烟接装纸进行烘烤干燥，烘烤温度为100℃，烘烤时长为5min。
将上述实施例1-4中所制得的抗菌香烟接装纸进行试验检测，得到以下数据信息：
| 实施例1 | 实施例2 | 实施例3 | 实施例4 | |
| 防水能力 | 较好 | 好 | 非常好 | 较好 |
| 透气能力 | 好 | 较好 | 非常好 | 好 |
| 抗菌能力 | 非常好 | 较好 | 非常好 | 较好 |
根据上表可知，实施例1-4中所制得的抗菌香烟接装纸均具有较好的防水能力、透气能力和抗菌能力，其中实施例3所制得的抗菌香烟接装纸各方面性能最为优异。
以上所述，仅是本发明的较佳实施例，任何熟悉本领域的技术人员均可能利用上述阐述的技术方案对本发明加以修改或将其修改为等同的技术方案。因此，依据本发明的技术方案所进行的任何简单修改或等同置换，尽属于本发明要求保护的范围。
Claims (9)
1.一种抗菌香烟接装纸，其特征在于：包括基层(1)，所述基层(1)顶部固定连接有两个防水层(2)，两个所述防水层(2)内侧固定连接有透气层(3)，所述防水层(2)顶部固定连接有抗菌层(4)。
2.根据权利要求1所述的一种抗菌香烟接装纸，其特征在于：所述防水层(2)由PP聚丙烯材料制成。
3.根据权利要求1所述的一种抗菌香烟接装纸，其特征在于：所述透气层(3)由PP聚乙烯透气膜材料制成。
4.根据权利要求1所述的一种抗菌香烟接装纸，其特征在于：所述抗菌层(4)由银离子抗菌剂涂覆制成。
5.根据权利要求1所述的一种抗菌香烟接装纸，其特征在于：包括主料和配料，所述主料包括油墨和工业乙醇，所述配料包括丙凝乳液、壳聚糖和高分子水凝胶。
6.根据权利要求5所述的一种抗菌香烟接装纸，其特征在于：所述主料中各成分质量份数分别为：
油墨：80-90份
工业乙醇：10-20份。
7.根据权利要求5所述的一种抗菌香烟接装纸，其特征在于：所述配料中各成分质量份数分别为：
丙凝乳液：5-20份
壳聚糖：10-15份
高分子水凝胶：5-15份。
8.根据权利要求5所述的一种抗菌香烟接装纸，其特征在于：所述工业乙醇浓度为85％。
9.一种抗菌香烟接装纸的印刷工艺，其特征在于：包括以下印刷步骤：
S1，将主料中的油墨和工业乙醇以及配料中的丙凝乳液、壳聚糖和高分子水凝胶混合并充分搅拌，使其混合均匀，得到混合油墨；
S2，将混合油墨加热升温并持续搅拌20min，加热温度为50-80℃，加热时长为20min，而后使得混合溶液降温至常温。
S3，将降温后的混合油墨填充至印刷机器的油墨盒内部，而后使用印刷机器对抗菌香烟接装纸进行印刷工作；
S4，进印刷后的抗菌香烟接装纸进行烘烤干燥，烘烤温度为90-120℃，烘烤时长为5min。