CN1118295A - 一种气体保护焊焊丝 - Google Patents

一种气体保护焊焊丝 Download PDF

Info

Publication number
CN1118295A
CN1118295A CN 95108258 CN95108258A CN1118295A CN 1118295 A CN1118295 A CN 1118295A CN 95108258 CN95108258 CN 95108258 CN 95108258 A CN95108258 A CN 95108258A CN 1118295 A CN1118295 A CN 1118295A
Authority
CN
China
Prior art keywords
welding wire
welding
weld
gas shielded
present
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 95108258
Other languages
English (en)
Inventor
于俊川
张有为
何长红
杨汝敬
刘振铭
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Central Iron and Steel Research Institute
Original Assignee
Central Iron and Steel Research Institute
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Central Iron and Steel Research Institute filed Critical Central Iron and Steel Research Institute
Priority to CN 95108258 priority Critical patent/CN1118295A/zh
Publication of CN1118295A publication Critical patent/CN1118295A/zh
Pending legal-status Critical Current

Abstract

本发明属于焊接材料领域。主要适用于低合金钢的焊接。该焊丝的化学成分包含有(重量％)C≤0.12，Si0.3—0.90％，Mn1.0—2.2，S≤0.025，P≤0.025，Ni0.5—1.5，Mo0.1—0.6，Ti0.05—0.2，Zr0.01—0.1，其余为铁。该焊丝与现有技术相比较具有焊缝性能好，焊接强度高和在负温度下使用效果更加明显等特点。

Description

一种气体保护焊焊丝
本发明属于焊接材料领域。主要适用于压力容器、工程机械、管线等低合金钢的焊接。
目前由于低合金钢的迅速发展，以及焊接结构在负温下服役已日趋广泛，例如管线、海洋工程，液化石油容器以及工程矿山机械等都需要在负温下使用。因此对焊缝金属和母材的韧性在使用要求上是越来越苛刻。在现有技术中能够使用在负温下的气体保护焊丝并不多。例如美国专利US3424892介绍了一种气体保护焊焊丝。该焊丝的主要缺点是成份限制严格，磷、硫均限制0.01％以下，因此该焊丝在一般钢铁厂是无法生产的。再有日本神户钢厂的MG60焊丝，该焊丝的主要缺点是随使用温度的降低，其焊缝金属力学性能也降低，因此该焊丝用作负温下使用也有所欠缺。
本发明的目的是提出一种焊缝强度高，负温使用效果好和适用范围广的气体保护焊焊丝。
气体保护焊是一种采用Ar＋CO2或Ar＋O2/CO2保护的电弧焊方法，通常比手工焊的效率高、质量好，抗裂能力强和可实现全位置自动焊等优点。焊丝是气体保护焊不可缺少的材料。因此根据本发明目的所提出的气体保护焊焊丝的特点，我们所设计的这种气体保护焊焊丝的具体化学成份为(重量％)C≤0.12，Si 0.3-0.90％，Mn 1.0-2.2，S≤0.025，P≤0.025，Ni 0.5-1.5，Mo0.1-0.6，Ti 0.05-0.2，Zr 0.01-0.1，其余为Fe。在本发明的焊丝中低C、低S、P主要是为了保证焊缝金属具有高的塑性韧性和抗裂性。一定的Mn、Si含量是熔池的脱氧所必要的，控制Mn、8i的含量，可以改善焊接工艺和提高焊缝力学性能。在本发明焊丝钢中加入Ti 0.05-0.12％和Zr 0.01-0.1％，其目的是为了改善施焊抗气孔性和提高低温冲击韧性。在本发明焊丝中加入Ni0.5-1.5％是为了提高焊缝的韧性和强度，改善焊缝的组织性能和低温冲击韧性。Mo的加入可以提高焊接强度和改善焊缝组织性能。可防止每层焊的回火软化。
本发明焊丝还具有生产工艺简单，按本发明所设计焊丝成份可采用电弧炉进行冶炼，然后再经铸锭、锻方坯、热轧、拉丝、镀铜和成品打轴等工序即可完成该焊丝的生产程序。
本发明气体保护焊丝具有良好的焊接工艺性，该焊丝可以在CO2或Ar＋O2/CO2气体保护下进行焊接。该焊丝与现有技术焊丝相比较具有焊缝金属抗裂性能好，可适用于大线能量的焊接，焊缝金属的力学性能高，其屈服强度均大于450MPa，-40℃冲击功均大于50J的效果，而且该焊丝还有焊缝成型美观、飞溅小、无气孔和可以全方位焊接等特点。该焊丝不仅可以施焊于中国的15MVN等钢种，而且还可施焊于美国的ASTMA533、英国的BS4360。西德的STE47、STE51等多种板材或管材，其焊缝金属具有与母材相对应的高强度和良好的韧性，而且还具有抗回火脆性及时效敏感性。焊接时不需预热，也可保证根部无裂。
实施例
我们的实施例是在本发明焊丝成份范围内，对三种不同成份含量材料进行冶炼铸锭、锻造、热轧、拉丝、镀铜和成品打轴等工序生产的焊丝所做的试验，其对比材料是日本神户的MG60焊丝和国产的H08Mn2SiA，本发明焊丝与对比焊丝的具体化学成份见表1。各项性能的对比试验条件均是采用Ar＋50％CO2混合气体，对22mm厚的15MnVN钢进行焊接。表2是本发明焊丝与日本神户MG60焊丝和H08Mn2SiA焊丝的焊缝金属力学性能对比。表3为本发明焊丝在三种不同线能量下焊接其焊缝的力学性能。从以上表中的对比可以看出。本发明焊丝与对比焊丝的焊缝金属力学性能，在室温时本发明焊丝其各项性能略优于对比焊丝，而在负温度时性能对比的优越性就更加明显，随温度降低，其效果增强。所以本发明焊丝不但有很好的金属力学性能，更具有很宽的使用温度。可在大线能量下焊接。
表1实施例相应焊丝的化学成分(重量％)
     序 号  C  Si  Mn     S     P   Ni   Mo   Ti   Zr   Fe
    本发明     1  0.071  0.45  1.78  0.016  0.015  1.12  0.20  0.075  0.021 余
    2  0.052  0.46  1.37  0.016  0.015  1.42  0.51  0.073  0.15 余
    3  0.046  0.45  1.45  0.015  0.015  0.81  0.33  0.15  0.075 余
H08Mn2SiA  0.08  0.70  1.82  0.020  0.019  /   /   /    / 余
MG60(日本) 0.071  0.50  1.30  0.01  0.017   /  0.30   /    / 余
表2本发明焊丝与对比焊丝焊缝金属力学性能
   序 号  σbMPa σsMPa  δ5％  ψ％  20℃AKVJ   0℃AKVJ  -20℃AKVJ  -40℃AKVJ
本发明     1  574  477     27  74     185  178     126     80
    2  533  545     26  73     194  190     157     116
    3  582  489     26  74     189  177     169     121
 H08Mn2SiA  571  465     25  70     146  110     78     43
日本神户MG60  670  520   22.6  69     182  160     100     67
表3实施例不同焊接线量情况下焊缝金属性能
序号 线能量KJ/cm           拉伸性能               AKV(J)
σbMPa  σsMPa  δ5％   ψ％ 20℃  0℃   -20℃   -40℃
本发明 1  15.830.245.3  590550520  490465457  23.327.629.2  66.074.974.7  196205179  190185149     164167137     14116398
2  15.830.245.3  655585585  585485458  21.923.124.6  68.474.370.1  159164165  152139133     121127115     818083
3  15.830.245.3  605555535  530465453  21.024.726.8  69.471.371.9  145178169  97147127     8512779     607757

Claims (1)

1、一种适用于气体保护焊焊丝，其特征在于该焊丝的具体化学成份为(重量％)C≤0.12，Si 0.3-0.90，Mn 1.0-2.2，S≤0.025，P≤0.025，Ni 0.5-1.5，Mo 0.1-0.6，Ti 0.05-0.2，Zr 0.01-0.1，其余为Fe。
CN 95108258 1995-07-21 1995-07-21 一种气体保护焊焊丝 Pending CN1118295A (zh)