CN111826182A - 一种炼焦配煤的配方 - Google Patents
一种炼焦配煤的配方 Download PDFInfo
- Publication number
- CN111826182A CN111826182A CN202010695782.0A CN202010695782A CN111826182A CN 111826182 A CN111826182 A CN 111826182A CN 202010695782 A CN202010695782 A CN 202010695782A CN 111826182 A CN111826182 A CN 111826182A
- Authority
- CN
- China
- Prior art keywords
- coal
- coking
- asphalt
- equal
- coal blending
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种炼焦配煤的配方,主要针对在配煤中添加沥青提高配煤炼焦质量的方法,在传统配方的基础上增加对沥青质量的优化,使用具有如下质量标准的改质沥青:软化点为105‑115℃,甲苯不溶物占比28‑34%,喹啉不溶物占比8‑14%,β树脂含量≥18%,结焦值≥56%,挥发分占比54%,灰分≤0.3%,硫分占比0.62%,以实现大幅提高沥青在改善配煤炼焦效果方面的作用。
Description
技术领域
本发明涉及炼焦配煤技术领域,特别是一种炼焦配煤的配方。
背景技术
目前煤炭市场紧张,许多公司的存煤结构中弱粘结性气煤的存煤量比较大、中等变质程度强粘结性的库存煤量降低,如高硫肥煤、主焦煤等,而且瘦煤也难保证生产的正常使用,致使焦炭强度下降、弱粘结性使得颗粒间无法粘结导致粒度过小,焦炭热态指标变差,焦炭质量难以满足市场的需求。
现有技术已经开始尝试在配煤的配方中添加沥青或石油焦来提高弱粘结性的炼焦煤配量,改善配煤质量,但因沥青和石油焦品质过低的缘故,往往使得该配煤的M10(耐磨强度)不够,反应性和反应性强度也有所欠缺,其中硫分的含量也无明显减少。
发明内容
本发明的目的是为了解决上述现有技术的不足而提供一种降低混沥青配煤耐磨强度、降低反应性、提高反应性强度及减少硫分含量的炼焦配煤的配方。
为了实现上述目的,本发明所设计的一种炼焦配煤的配方,包括改质沥青5-15份,单种炼焦煤95-85份,所述单种炼焦煤包括气肥煤、肥煤、干燥无灰基挥发分大于29%的1/3焦煤、干燥无灰基挥发分小于27%的焦煤、瘦煤,其特征在于,所述改质沥青具有如下质量标准:软化点为105-115℃,甲苯不溶物占比28-34%,喹啉不溶物占比8-14%,β树脂含量≥18%,结焦值≥56%,挥发分占比54%,灰分≤0.3%,硫分占比0.62%。
本发明得到的炼焦配煤的配方,使用经筛选后软化点在105-115℃且灰分和硫分占比分别为0.3%以下和0.62%以下的改质沥青,使得该配煤质量大幅提升,成本降低,与普通的散沥青炼焦形成的焦炭抗碎强度升高4%以上,M10降低4%以上,反应性提高1%以上,反应性强度升高3%以上,硫分含量减少。
具体实施方式
为使对本发明的配方有进一步的了解与认识,用实验案例及操作过程进行阐述说明,说明如下:
本发明炼焦配煤的配方,包括改质沥青2份,单种炼焦煤98份,所述单种炼焦煤包括气肥煤、肥煤、干燥无灰基挥发分大于29%的1/3焦煤、干燥无灰基挥发分小于27%的焦煤、瘦煤,所述改质沥青具有如下质量标准:软化点为105-115℃,甲苯不溶物占比28-34%,喹啉不溶物占比8-14%,β树脂含量≥18%,结焦值≥56%,挥发分占比54%,灰分≤0.3%,硫分占比0.62%。
配煤方案,如下表:
表1 配煤方案
煤种 | 基准(份数) | 配用改质沥青(份数) | 配用散沥青(份数) |
焦煤 | 35 | 35 | 35 |
1/3焦煤 | 11 | 11 | 11 |
肥煤 | 10 | 8 | 8 |
气煤 | 17 | 17 | 17 |
瘦煤 | 24 | 24 | 24 |
其他 | 3 | 3 | 3 |
改质沥青 | 0 | 2 | 0 |
散沥青 | 0 | 0 | 2 |
实施例1:
以表1配煤方案将软化点105℃,甲苯不溶物占比28%,喹啉不溶物占比14%,β树脂含量14%,结焦值58%,挥发分占比54%,灰分占比0.26%,硫分占比0.62%的改质沥青和散沥青配入2%,进行40kg小焦炉焦性试验。试验结果如下表:
表2 实施例1焦炭质量分析
配比 | M40/% | M10/% | CRI/% | CSR/% | 硫分/% |
基准 | 76.5 | 16.8 | 30.2 | 40.5 | 1.6 |
改质沥青 | 82.1 | 11.0 | 28.7 | 46.7 | 1.3 |
散沥青 | 77.9 | 15.2 | 29.9 | 43.1 | 1.5 |
由表格数据可知,配入改质沥青与散沥青后,焦炭的机械强度、热强度及硫分占比均得到改善;同时,改质沥青的配用结果优于散沥青,焦炭抗碎强度提高4.2%,耐磨强度降低4.2%,反应性降低1.2%,反应后强度升高3.6%。
实施例2:
以表1配煤方案将软化点115℃,甲苯不溶物占比34%,喹啉不溶物占比8%,β树脂含量18%,结焦值56%,挥发分占比54%,灰分占比0.3%,硫分占比0.62%的改质沥青和散沥青配入2%,进行40kg小焦炉焦性试验。试验结果如下表:
表3 实施例2焦炭质量分析
配比 | M40/% | M10/% | CRI/% | CSR/% | 硫分/% |
基准 | 76.4 | 16.7 | 30.3 | 40.4 | 1.6 |
改质沥青 | 81.9 | 11.1 | 27.7 | 47.1 | 1.3 |
散沥青 | 77.8 | 15.2 | 29.8 | 43.2 | 1.5 |
由表格数据可知,配入改质沥青与散沥青后,焦炭的机械强度、热强度及硫分占比均得到改善;同时,改质沥青的配用结果优于散沥青,焦炭抗碎强度提高4.1%,耐磨强度降低4.1%,反应性降低2.1%,反应后强度升高3.9%。
综上所述,将配煤中的散沥青使用改质沥青进行替换可以大幅改善炼焦后形成的焦炭的质量。
Claims (1)
1.一种炼焦配煤的配方,包括改质沥青2份,单种炼焦煤98份,所述单种炼焦煤包括气肥煤、肥煤、干燥无灰基挥发分大于29%的1/3焦煤、干燥无灰基挥发分小于27%的焦煤、瘦煤,其特征在于,所述改质沥青具有如下质量标准:软化点为105-115℃,甲苯不溶物占比28-34%,喹啉不溶物占比8-14%,β树脂含量≥18%,结焦值≥56%,挥发分占比54%,灰分≤0.3%,硫分占比0.62%。