CN111774519A - 一种覆膜砂专用水基涂料 - Google Patents
一种覆膜砂专用水基涂料 Download PDFInfo
- Publication number
- CN111774519A CN111774519A CN202010674245.8A CN202010674245A CN111774519A CN 111774519 A CN111774519 A CN 111774519A CN 202010674245 A CN202010674245 A CN 202010674245A CN 111774519 A CN111774519 A CN 111774519A
- Authority
- CN
- China
- Prior art keywords
- precoated sand
- water
- based paint
- stirring
- bentonite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种覆膜砂专用水基涂料,包括以下组分:纳基膨润土、聚醋酸乙烯酯乳液、聚合氯化铝、羧甲基纤维素、阿尔法氧化铝、石英粉、锆英粉以及水。本发明提供的覆膜砂专用水基涂料,在喷涂到覆膜砂壳表面时干燥快,附着力好,因使用阿尔法氧化铝和锆英粉,因此涂料耐火强度高,涂料干燥后表面涂层光滑,涂料浇铸完毕溃散性好,产品表面容易脱壳,此涂料性价比高制作简单,适合近似于硅溶胶铸造和覆膜砂不锈钢件的铸造使用。
Description
技术领域
本发明涉及一种覆膜砂专用水基涂料,属于覆膜砂铸造技术领域。
背景技术
覆膜砂铸造工艺是一种新型环保的铸造工艺,与精密铸造,硅溶胶铸造等工艺相比,覆膜砂工艺更加便捷、环保、生产周期短、成本低且排放量少。因此已经被很多铸造企业所使用,但是覆膜砂属于冷壳浇铸,覆膜砂原砂粒度为 70-140目,所有产品外观粗超度高,因此有必要设计一种覆膜砂专用水基涂料,以克服上述问题。
发明内容
本发明的目的在于针对覆膜砂铸造工艺制造的产品外观粗糙度高的问题,提供了一种覆膜砂专用水基涂料。
本发明提供一种覆膜砂专用水基涂料,其组分包括:纳基膨润土、聚醋酸乙烯酯乳液、聚合氯化铝、羧甲基纤维素、阿尔法氧化铝、石英粉、锆英粉以及水。
其中,覆膜砂专用水基涂料的组分按质量比计算包括:纳基膨润土2%、聚醋酸乙烯酯乳液2%、聚合氯化铝0.7%、羧甲基纤维素0.7%、阿尔法氧化铝 18%、石英粉18%、锆英粉25%以及水33.6%。
其中,纳基膨润土为300目纳基膨润土,羧甲基纤维素为300目羧甲基纤维素,石英粉为270目石英粉,锆英粉为325目锆英粉。
其中,覆膜砂专用水基涂料的制作方法包括以下步骤:
步骤一:用纳基膨润土加水搅拌发酵存放至少四小时以上;
步骤二:用聚合氯化铝加水搅拌发酵存放至少两小时以上;
步骤三:把搅拌好的纳基膨润土以及聚合氯化铝,加入到搅拌桶内一起搅拌二十分钟;
步骤四:再在搅拌桶内加入羧甲基纤维素、聚醋酸乙烯酯乳液以及水搅拌十分钟;
步骤五:再在搅拌桶内同时加入石英粉、锆英粉以及阿尔法氧化铝,搅拌四个小时;
步骤六:搅拌后封装完毕等待实用。
本发明具有以下有益效果:本发明提供的覆膜砂专用水基涂料,在喷涂到覆膜砂壳表面时干燥快,附着力好,因使用阿尔法氧化铝和锆英粉,因此涂料耐火强度高,涂料干燥后表面涂层光滑,涂料浇铸完毕溃散性好,产品表面容易脱壳,此涂料性价比高制作简单,适合近似于硅溶胶铸造和覆膜砂不锈钢件的铸造使用。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
本发明提供一种覆膜砂专用水基涂料,其组分包括:纳基膨润土、聚醋酸乙烯酯乳液、聚合氯化铝、羧甲基纤维素、阿尔法氧化铝、石英粉、锆英粉以及水。
在本实施例中,优选为覆膜砂专用水基涂料的组分按质量比计算包括:纳基膨润土2%、聚醋酸乙烯酯乳液2%、聚合氯化铝0.7%、羧甲基纤维素0.7%、阿尔法氧化铝18%、石英粉18%、锆英粉25%以及水33.6%。
其中,纳基膨润土为300目纳基膨润土,羧甲基纤维素为300目羧甲基纤维素,石英粉为270目石英粉,锆英粉为325目锆英粉。
本覆膜砂专用水基涂料的制作方法包括以下步骤:
步骤一:用纳基膨润土加水搅拌发酵存放至少四小时以上;
步骤二:用聚合氯化铝加水搅拌发酵存放至少两小时以上;
步骤三:把搅拌好的纳基膨润土以及聚合氯化铝,加入到搅拌桶内一起搅拌二十分钟;
步骤四:再在搅拌桶内加入羧甲基纤维素、聚醋酸乙烯酯乳液以及清水搅拌十分钟;
步骤五:再在搅拌桶内同时加入石英粉、锆英粉以及阿尔法氧化铝,搅拌四个小时;
步骤六:搅拌后封装完毕等待实用。
本用于覆膜砂铸造的专用水基涂料,提高了覆膜砂铸造产品外观光洁度,以求达到近似于硅溶胶铸造的工艺要求和覆膜砂不锈钢件的铸造工艺要求。
实施本发明实施例,具有如下有益效果:本发明提供的覆膜砂专用水基涂料,在喷涂到覆膜砂壳表面时干燥快,附着力好,因使用阿尔法氧化铝和锆英粉,因此涂料耐火强度高,涂料干燥后表面涂层光滑,涂料浇铸完毕溃散性好,产品表面容易脱壳,此涂料性价比高制作简单,适合近似于硅溶胶铸造和覆膜砂不锈钢件的铸造使用。
本说明书未作详细描述的内容属于本领域专业技术人员公知的现有技术。以上仅为本发明的较佳实施例而已,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (4)
1.一种覆膜砂专用水基涂料,其特征在于:所述覆膜砂专用水基涂料的组分包括:纳基膨润土、聚醋酸乙烯酯乳液、聚合氯化铝、羧甲基纤维素、阿尔法氧化铝、石英粉、锆英粉以及水。
2.如权利要求1所述的覆膜砂专用水基涂料,其特征在于:所述覆膜砂专用水基涂料的组分按质量比计算包括:纳基膨润土2%、聚醋酸乙烯酯乳液2%、聚合氯化铝0.7%、羧甲基纤维素0.7%、阿尔法氧化铝18%、石英粉18%、锆英粉25%以及水33.6%。
3.如权利要求2所述的覆膜砂专用水基涂料,其特征在于:所述纳基膨润土为300目纳基膨润土,所述羧甲基纤维素为300目羧甲基纤维素,所述石英粉为270目石英粉,所述锆英粉为325目锆英粉。
4.如权利要求1-3任意一项所述的覆膜砂专用水基涂料,其特征在于:所述覆膜砂专用水基涂料的制作方法包括以下步骤:
步骤一:用纳基膨润土加水搅拌发酵存放至少四小时以上;
步骤二:用聚合氯化铝加水搅拌发酵存放至少两小时以上;
步骤三:把搅拌好的纳基膨润土以及聚合氯化铝,加入到搅拌桶内一起搅拌二十分钟;
步骤四:再在搅拌桶内加入羧甲基纤维素、聚醋酸乙烯酯乳液以及水搅拌十分钟;
步骤五:再在搅拌桶内同时加入石英粉、锆英粉以及阿尔法氧化铝,搅拌四个小时;
步骤六:搅拌后封装完毕等待实用。