CN111690228A - Degradable high-brightness white silver spraying-free material and preparation method thereof - Google Patents
Degradable high-brightness white silver spraying-free material and preparation method thereof Download PDFInfo
- Publication number
- CN111690228A CN111690228A CN202010586336.6A CN202010586336A CN111690228A CN 111690228 A CN111690228 A CN 111690228A CN 202010586336 A CN202010586336 A CN 202010586336A CN 111690228 A CN111690228 A CN 111690228A
- Authority
- CN
- China
- Prior art keywords
- parts
- free material
- pigment
- white silver
- degradable high
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a degradable high-brightness white silver spraying-free material and a preparation method thereof, wherein the high-brightness white silver spraying-free material comprises, by weight, 100 parts of ABS resin, 0.5-5 parts of metal aluminum powder, 0.1-2 parts of pigment, 0.5-5 parts of pearl powder, 0.5-5 parts of dispersing agent, 1-10 parts of degradation assistant, 0.1-1 part of antioxidant and 0.1-1 part of stabilizer. According to the invention, the material with high metal texture and high bright silver color effect is prepared by compounding three components of metal aluminum powder, pearl powder and pigment, and the brightness of the material can reach 31 through a test of a hexagonal instrument; in addition, the high-brightness white silver spraying-free material has the capability of degrading under anaerobic conditions by adding the degradation auxiliary agent, and is beneficial to environmental protection.
Description
Technical Field
The invention relates to the field of spraying-free materials, in particular to a degradable high-brightness white silver spraying-free material and a preparation method thereof.
Background
With the improvement of environmental awareness of people, a spraying-free material which is green, environment-friendly, low-carbon and has special color becomes one of the solutions for replacing spraying. The spraying-free plastic is characterized in that special pearl powder or pigment is added into a plastic raw material, and through design formula and technical modification, the produced plastic particles can be directly injection-molded, so that the appearance effects of various pearls, colors, plush and metals are met. The spraying-free material is a material which can realize the colorful appearance effect by direct injection molding without spraying.
However, the existing spraying-free materials are mainly researched to realize a certain color effect by adding single metal powder or pigment, and the research on the realization of high metal texture by compounding metal powder, pearl powder, pigment and the like is still less; and at present, almost no research on the high-brightness white silver spraying-free material with the degradation function exists in the market.
Accordingly, the prior art is yet to be improved and developed.
Disclosure of Invention
In view of the defects of the prior art, the invention aims to provide a high-brightness white silver spraying-free material with a degradation function and a preparation method thereof.
The technical scheme of the invention is as follows:
the degradable high-brightness white silver spraying-free material comprises, by weight, 100 parts of ABS resin, 0.5-5 parts of metal aluminum powder, 0.1-2 parts of pigment, 0.5-5 parts of pearl powder, 0.5-5 parts of dispersant, 1-10 parts of degradation additive, 0.1-1 part of antioxidant and 0.1-1 part of stabilizer.
The degradable high-brightness white silver spraying-free material comprises, by weight, 100 parts of ABS resin, 1.5 parts of metal aluminum powder, 0.3 part of pigment, 1.5 parts of pearl powder, 2 parts of dispersing agent, 3 parts of degradation auxiliary agent, 0.2 part of antioxidant and 0.2 part of stabilizer.
The degradable high-brightness white silver spraying-free material is characterized in that the pearl powder is of a flaky structure.
The degradable high-brightness white silver paint-free material is characterized in that the pigment is one or more of monoazo pigment, disazo pigment, lake pigment, phthalocyanine pigment and reward ring pigment.
The degradable high-brightness white silver spraying-free material is characterized in that the degradation auxiliary agent is Ecoplastic technology Limited degradation master batch.
The degradable high-brightness white silver spraying-free material is characterized in that the dispersing agent is PE wax or stearic acid amide.
The degradable high-brightness white silver spraying-free material is characterized in that the antioxidant is one or more of hindered phenol antioxidant and phosphite antioxidant.
The degradable high-brightness white silver spraying-free material is characterized in that the stabilizer is copper salt.
A preparation method of a degradable high-brightness white silver spraying-free material comprises the following steps:
weighing ABS resin, metal aluminum powder, pearl powder, pigment, stabilizer, antioxidant, prodegradant and dispersant according to weight parts for later use;
putting the weighed materials into a stirrer, and stirring for 5-20min at the rotating speed of 100-300 r/min;
pouring the stirred material into a hopper of a single-screw extruder for extrusion granulation, wherein the process parameters of the extruder are that the screw temperature is 200-;
and granulating the extruded material by a granulator to obtain the degradable high-brightness white silver spraying-free material.
Has the advantages that: the invention provides a degradable high-brightness white silver spraying-free material, which is a material with high metal texture and high-brightness white silver effect prepared by compounding three components of metal aluminum powder, pearl powder and pigment, wherein the brightness of the material can reach 31 by a hexagon instrument test; in addition, the high-brightness white silver spraying-free material has the capability of degrading under anaerobic conditions by adding the degradation auxiliary agent, and is beneficial to environmental protection.
Drawings
FIG. 1 is a flow chart of a preferred embodiment of the method for preparing a degradable high-brightness white silver spray-free material according to the present invention.
FIG. 2 is a graph showing the effect of injection molding of the degradable high-brightness white silver spray-free material prepared in example 1.
Detailed Description
The invention provides a degradable high-brightness white silver spraying-free material and a preparation method thereof, and the invention is further described in detail below in order to make the purpose, technical scheme and effect of the invention clearer and clearer. It should be understood that the specific embodiments described herein are merely illustrative of the invention and are not intended to limit the invention.
The spraying-free material is a novel environment-friendly material which can realize various pearlescent, colorful or metal appearance effects by adding special pearlescent powder or metal pigment and the like into specific resin and modifying the special compatible technology to directly perform injection molding. The existing spraying-free material system is divided into a three-dimensional flashing highlight non-flow mark series and a metallic pearly-luster effect series, the existing spraying-free material mainly comprises spraying-free composite PP, spraying-free PC, spraying-free ABS, spraying-free PC/ABS alloy and the like, the main application fields of the spraying-free material system comprise daily household appliances, intelligent homes, automobile interior/exterior trimming parts, 3C high-end consumer electronics, artificial intelligent machines, beauty instruments, cosmetic packages and the like, and the spraying-free material system can also conform to the market demands and development trends to send different product effects.
Compared with the traditional spraying material, the spraying-free material has the advantages of good one-step forming, no need of spraying to obtain gorgeous appearance, greenness, environmental protection, lower cost and higher design freedom.
However, the research of the current spray-free materials mainly focuses on adding single metal powder or pigment to realize a certain color effect, and the research on the combination of metal powder, pearl powder, pigment and the like to realize high metal texture is less; and at present, almost no research on the high-brightness white silver spraying-free material with the degradation function exists in the market.
Based on the above, the embodiment of the invention provides a degradable high-brightness white silver spray-free material, which is characterized by comprising, by weight, 100 parts of ABS resin, 0.5-5 parts of metal aluminum powder, 0.1-2 parts of pigment, 0.5-5 parts of pearl powder, 0.5-5 parts of dispersing agent, 1-10 parts of degradation assistant, 0.1-1 part of antioxidant and 0.1-1 part of stabilizer.
In this embodiment, the ABS resin is a graft copolymer of three monomers, namely Acrylonitrile (Acrylonitrile), 1, 3-Butadiene (Butadiene), and Styrene (Styrene), and the ABS resin is one of the most widely used polymers with the largest yield, organically integrates various properties of PS, SAN, and BS, and has excellent mechanical properties of toughness, hardness, and rigidity; the metal aluminum powder is used as metal addition powder of a spraying-free material, and can show the effect of metallic silver texture after being added; the pigment can be added to achieve the effects of increasing tinting strength and color saturation; the pearl powder can improve the decorative effect of the spraying-free material and more highlight the brightness of metallic silver.
Specifically, the metal aluminum powder mainly plays a silver effect, if the weight ratio of the metal aluminum powder is less than 0.5 part, the covering effect of the metal aluminum powder on plastics is poor, the silver color is not prominent, and if the weight ratio of the metal aluminum powder exceeds 5 parts, the dispersion of the metal aluminum powder is poor, so that the performance of the final spraying-free material is obviously reduced. The pearl powder is a lustrous pigment and is formed by coating mica with a plurality of metal oxide thin layers, and different pearl effects can be generated by changing the metal oxide thin layers; because the pearl powder has the characteristics of soft pearl luster like silk, starry flashing effect, effect of color variation along with angles and the like, the addition of the pearl powder in the embodiment mainly plays a role in highlighting the silver color, so that the silver color is more highlighted, if the addition proportion is lower than 0.5 part, the highlighting effect on the silver color is not obvious, and if the addition proportion is higher than 5 parts, the performance of the spraying-free material is influenced. The addition of the pigment mainly highlights whiteness, and the obtained spraying-free material is closer to the effect of paint spraying or electroplating.
In the embodiment, the material with high metal texture and high bright silver color effect is prepared by compounding three components of metal aluminum powder, pearl powder and pigment, and the brightness of the material can reach 31 by a test of a hexagon instrument; in addition, the high-brightness white silver spraying-free material has the capability of degrading under anaerobic conditions by adding the degradation auxiliary agent, and is beneficial to environmental protection.
In some embodiments, the pearlescent powder has a flake structure, and compared with pearlescent powder with a cubic and spherical structure, the pearlescent powder with the same volume fraction has a more obvious covering effect and a prominent highlight effect.
In some embodiments, the pigment is one or more of a monoazo pigment, a disazo pigment, a lake pigment, a phthalocyanine pigment, and a premium ring pigment, but is not limited thereto.
In some embodiments, the prodegradant is an Ecoplastic Technology Limited degranulation masterbatch. The Ecoplastic Technology Limited degradation master batch is an environment-friendly biodegradable plastic master batch, and the degradation master batch is added into the spraying-free material, so that the spraying-free material has better degradation capability under anaerobic conditions, and the environment pollution is avoided. The degradable high-brightness white silver spraying-free material is characterized in that the dispersing agent is PE wax or stearic acid amide.
In some embodiments, the antioxidant is one or more of a hindered phenolic antioxidant and a phosphite antioxidant, but is not limited thereto.
In some embodiments, the stabilizer is a copper salt, but is not limited thereto.
In some embodiments, the dispersant is a PE wax or a stearic acid amide, but is not limited thereto.
In some embodiments, there is also provided a method of preparing a degradable high brilliant white silver spray-free material, as shown in fig. 1, comprising the steps of:
s10, weighing the ABS resin, the metal aluminum powder, the pearl powder, the pigment, the stabilizer, the antioxidant, the prodegradant and the dispersant according to the parts by weight for later use;
s20, putting the weighed materials into a stirrer, and stirring for 5-20min at the rotating speed of 100-300 r/min;
s30, pouring the stirred materials into a hopper of a single-screw extruder for extrusion granulation, wherein the process parameters of the extruder are that the screw temperature is 200-;
and S40, cutting the extruded material into particles by a granulator to obtain the degradable high-brightness white silver spraying-free material.
The preparation method of the degradable high-brightness white silver spraying-free material provided by the embodiment is simple and easy to operate, the material with high metal texture and high-brightness white silver effect is prepared by compounding three components of metal aluminum powder, pearl powder and pigment, and the brightness of the material can reach 31 through a test of a hexagon instrument; in addition, the high-brightness white silver spraying-free material has the capability of degrading under anaerobic conditions by adding the degradation auxiliary agent, and is beneficial to environmental protection.
The degradable high-brightness white silver spray-free material and the preparation method and performance thereof are further explained by the following specific examples:
example 1
The degradable high-brightness white silver spraying-free material comprises, by weight, 100 parts of ABS resin, 1.5 parts of metal aluminum powder, 0.3 part of pigment, 1.5 parts of pearl powder, 2 parts of dispersing agent, 3 parts of degradation auxiliary agent, 0.2 part of antioxidant and 0.2 part of stabilizer.
A preparation method of a degradable bright white silver spraying-free material comprises the following steps:
weighing ABS resin, metal aluminum powder, pearl powder, pigment, stabilizer, antioxidant, prodegradant and dispersant according to the weight parts for later use;
putting the weighed materials into a stirrer, and stirring for 15min at the rotating speed of 100 r/min;
pouring the stirred material into a hopper of a single-screw extruder for extrusion granulation, wherein the process parameters of the extruder are that the screw temperature is 200 ℃ and the screw rotating speed is 150 r/min;
granulating the extruded material by a granulator to obtain the degradable high-brightness white silver spraying-free material
After the spray-free material prepared in the embodiment is injection molded, the effect graph is shown in fig. 2, and the brightness of the spray-free material is tested to be 31 by a hexagon instrument; after the spray-free material is injection molded, 12% degradation can be realized in 45 days under anaerobic conditions according to ASTM D5511, and the degradation products mainly comprise methane and carbon dioxide.
Example 2
The degradable high-brightness white silver spraying-free material comprises, by weight, 100 parts of ABS resin, 5 parts of metal aluminum powder, 2 parts of pigment, 4 parts of pearl powder, 4 parts of dispersing agent, 5 parts of degradation assistant, 0.5 part of antioxidant and 0.5 part of stabilizer.
A preparation method of a degradable bright white silver spraying-free material comprises the following steps:
weighing ABS resin, metal aluminum powder, pearl powder, pigment, stabilizer, antioxidant, prodegradant and dispersant according to weight parts for later use;
putting the weighed materials into a stirrer, and stirring for 10min at the rotating speed of 300 r/min;
pouring the stirred material into a hopper of a single-screw extruder for extrusion granulation, wherein the process parameters of the extruder are that the screw temperature is 220 ℃ and the screw rotating speed is 200 r/min;
and granulating the extruded material by a granulator to obtain the degradable high-brightness white silver spraying-free material.
After injection molding, the brightness of the spray-free material prepared in the embodiment is 27 by a hexagon instrument; after the spray-free material is injection molded, 15% degradation can be realized in 45 days under anaerobic conditions according to ASTM D5511, and the degradation products mainly comprise methane and carbon dioxide.
Example 3
The degradable high-brightness white silver spraying-free material comprises, by weight, 100 parts of ABS resin, 1 part of metal aluminum powder, 0.5 part of pigment, 3 parts of pearl powder, 2 parts of dispersing agent, 4 parts of prodegradant, 0.6 part of antioxidant and 0.6 part of stabilizer.
A preparation method of a degradable bright white silver spraying-free material comprises the following steps:
weighing ABS resin, metal aluminum powder, pearl powder, pigment, stabilizer, antioxidant, prodegradant and dispersant according to weight parts for later use;
putting the weighed materials into a stirrer, and stirring for 16min at the rotating speed of 250 r/min;
pouring the stirred material into a hopper of a single-screw extruder for extrusion granulation, wherein the process parameters of the extruder are that the screw temperature is 240 ℃ and the screw rotating speed is 200 r/min;
and granulating the extruded material by a granulator to obtain the degradable high-brightness white silver spraying-free material.
After injection molding, the brightness of the spray-free material prepared in the embodiment is 29 by a hexagon instrument; after the spray-free material is injection molded, 10% degradation can be realized in 45 days under anaerobic conditions according to ASTM D5511, and the degradation products mainly comprise methane and carbon dioxide.
In conclusion, the invention provides a degradable high-brightness white silver spraying-free material, which is prepared by compounding three components of metal aluminum powder, pearl powder and pigment, wherein the material has high metal texture and high-brightness white silver effect, and the brightness of the material can reach 31 by a test of a hexagon instrument; in addition, the high-brightness white silver spraying-free material has the capability of degrading under anaerobic conditions by adding the degradation auxiliary agent, and is beneficial to environmental protection.
It is to be understood that the invention is not limited to the examples described above, but that modifications and variations may be effected thereto by those of ordinary skill in the art in light of the foregoing description, and that all such modifications and variations are intended to be within the scope of the invention as defined by the appended claims.
Claims (9)
1. The degradable high-brightness white silver spraying-free material is characterized by comprising, by weight, 100 parts of ABS resin, 0.5-5 parts of metal aluminum powder, 0.1-2 parts of pigment, 0.5-5 parts of pearl powder, 0.5-5 parts of dispersant, 1-10 parts of prodegradant, 0.1-1 part of antioxidant and 0.1-1 part of stabilizer.
2. The degradable high-brightness white silver spray-free material according to claim 1, which comprises 100 parts by weight of ABS resin, 1.5 parts by weight of metal aluminum powder, 0.3 parts by weight of pigment, 1.5 parts by weight of pearl powder, 2 parts by weight of dispersant, 3 parts by weight of prodegradant, 0.2 parts by weight of antioxidant and 0.2 parts by weight of stabilizer.
3. The degradable high brilliant white silver paint-free material according to any one of claims 1 to 2, wherein the pearl powder has a flake structure.
4. The degradable high brilliant white silver paint-free material of claims 1-2, wherein the pigment is one or more of monoazo pigment, disazo pigment, lake pigment, phthalocyanine pigment and premium ring pigment.
5. The degradable high-brightness white-silver spray-free material according to any one of claims 1 to 2, wherein the prodegradant is an Ecoplastic Technology Limited prodegradant.
6. The degradable high-brightness white silver spray-free material according to any one of claims 1-2, wherein the dispersant is PE wax or stearic acid amide.
7. The degradable high-brightness white silver spray-free material according to any one of claims 1 to 2, wherein the antioxidant is one or more of hindered phenol antioxidant and phosphite antioxidant.
8. The degradable high-brightness white silver spray-free material according to any one of claims 1-2, wherein the stabilizer is a copper salt.
9. A process for preparing the degradable high brilliant white silver spray-free material according to any one of claims 1 to 8, comprising the steps of:
weighing ABS resin, metal aluminum powder, pearl powder, pigment, stabilizer, antioxidant, prodegradant and dispersant according to weight parts for later use;
putting the weighed materials into a stirrer, and stirring for 5-20min at the rotating speed of 100-300 r/min;
pouring the stirred material into a hopper of a single-screw extruder for extrusion granulation, wherein the process parameters of the extruder are that the screw temperature is 200-;
and granulating the extruded material by a granulator to obtain the degradable high-brightness white silver spraying-free material.