CN111436377A - 一种抑菌除臭猫砂及其制备方法 - Google Patents
一种抑菌除臭猫砂及其制备方法 Download PDFInfo
- Publication number
- CN111436377A CN111436377A CN202010481790.5A CN202010481790A CN111436377A CN 111436377 A CN111436377 A CN 111436377A CN 202010481790 A CN202010481790 A CN 202010481790A CN 111436377 A CN111436377 A CN 111436377A
- Authority
- CN
- China
- Prior art keywords
- cat litter
- bacteriostatic
- starch
- deodorant
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种抑菌除臭猫砂及其制备方法，以植物纤维、淀粉、抑菌剂、海藻酸钠为原料，将原料进行混合，将混合后的物料进行造粒获得抑菌除臭猫砂；其中，抑菌剂为银盐、铜盐、锌盐中的一种或多种，混合过程中保持物料湿度为10～20％。本发明提供的抑菌除臭猫砂具有良好的生物相容性和抑菌性，通过能够缓慢释放抑菌活性成分，从而解决了抑制病菌的生长和抑制病菌滋长产生臭味的问题，降低了病菌的传播机率。
Description
技术领域
本发明属于宠物清洁用品制备技术领域，涉及一种抑菌除臭猫砂及其制备方法。
背景技术
公开该背景技术部分的信息仅仅旨在增加对本发明的总体背景的理解，而不必然被视为承认或以任何形式暗示该信息构成已经成为本领域一般技术人员所公知的现有技术。
随着消费水平和经济能力的提高，宠物饲养正在成为一种时尚并为越来越多的人所喜爱。宠物饲养过程中的排泄物容易滋生细菌并释放异味，一直是困扰宠物主人的问题，相关的产品也受到了人们的追捧。猫砂是用于处理宠物排泄物的材料，要求其有较好的吸水性，一般会与猫砂盆(或称猫厕所)一并使用。随着社会经济的不断发展，城市的规模也将不断扩大，而城市居住用地的缺乏就导致大多数的宠物需要和主人在一起生活。宠物猫砂就成为一种必不可少的宠物用品。目前市场上常用的猫砂一般都是结团性猫砂，这类猫砂根据猫咪排便习性，通过良好的吸水性、结团性来掩盖粪便和尿液，主要分为豆腐猫砂和膨润土猫砂。由于可以直接冲排进入居民排污管网，豆腐猫砂日渐成为猫砂市场的主流产品，但豆腐猫砂中的植物纤维和淀粉长时间使用均会滋生病菌，不具备抑菌能力，抑制臭味的能力也有限，限制了豆腐猫砂在宠物市场上的进一步推广。
发明内容
为了解决现有技术的不足，本发明的目的是提供一种抑菌除臭猫砂及其制备方法，该抑菌除臭猫砂具有良好的生物相容性和抑菌性，通过能够缓慢释放抑菌活性成分，从而解决了抑制病菌的生长和抑制病菌滋长产生臭味的问题，降低了病菌的传播机率。
为了实现上述目的，本发明的技术方案为：
一方面，一种抑菌除臭猫砂的制备方法，以植物纤维、淀粉、抑菌剂、海藻酸钠为原料，将原料进行混合，将混合后的物料进行造粒获得抑菌除臭猫砂；其中，抑菌剂为银盐、铜盐、锌盐中的一种或多种，混合过程中保持物料湿度为10～20％。
本发明向猫砂中引入海藻酸钠，对抗菌剂起到稳定化的作用，通过实验发现，混合过程中的湿度影响猫砂性能，当湿度小于10％时，制备的猫砂中海藻酸钠难以对抗菌剂产生稳定作用，当湿度大于20％时，无法通过造粒制备猫砂。当湿度为10％～20％时，能够保证制备获得猫砂，而且获得的猫砂中能够对抑菌活性成分进行缓慢释放。
另一方面，一种抑菌除臭猫砂，由上述制备方法获得。
本发明的有益效果为：
1.本发明通过添加海藻酸钠，对抗菌剂起到稳定化的作用；同时，通过混合湿度控制猫砂的形成及抑菌活性成分进行缓慢释放，既能延长猫砂的抑菌时间，又能防止重金属对宠物猫的伤害。
2.本发明提供的猫砂具有良好的抑菌除臭性能，猫砂抑菌率最高可达99.9％。
具体实施方式
应该指出，以下详细说明都是示例性的，旨在对本发明提供进一步的说明。除非另有指明，本文使用的所有技术和科学术语具有与本发明所属技术领域的普通技术人员通常理解的相同含义。
需要注意的是，这里所使用的术语仅是为了描述具体实施方式，而非意图限制根据本发明的示例性实施方式。如在这里所使用的，除非上下文另外明确指出，否则单数形式也意图包括复数形式，此外，还应当理解的是，当在本说明书中使用术语“包含”和/或“包括”时，其指明存在特征、步骤、操作、器件、组件和/或它们的组合。
鉴于现有猫砂不具备抑菌能力的问题，本发明提出了一种抑菌除臭猫砂及其制备方法。
本发明的一种典型实施方式，提供了一种抑菌除臭猫砂的制备方法，以植物纤维、淀粉、抑菌剂、海藻酸钠为原料，将原料进行混合，将混合后的物料进行造粒获得抑菌除臭猫砂；其中，抑菌剂为银盐、铜盐、锌盐中的一种或多种，混合过程中保持物料湿度为12～15％。
银盐、铜盐、锌盐可以作为抑菌剂，但是在利用猫砂处理猫粪便时，宠物猫需要接触猫砂，粪便中是水分使重金属盐中的重金属离子电离，此时重金属离子容易对宠物猫产生伤害。本发明向猫砂中引入海藻酸钠，对抗菌剂起到稳定化的作用，通过实验发现，混合过程中的湿度影响猫砂性能，当湿度小于10％时，制备的猫砂中海藻酸钠难以对抗菌剂产生稳定作用，当湿度大于20％时，无法通过造粒制备猫砂。当湿度为10％～20％时，能够保证制备获得猫砂，而且获得的猫砂中能够对抑菌活性成分进行缓慢释放，防止宠物猫接触过多重金属离子，从而避免伤害。
本发明所述的银盐为阳离子为银离子、阴离子为酸根阴离子，且溶于水的化合物，例如硝酸银等。
本发明所述的铜盐为阳离子为二价铜离子、阴离子为酸根阴离子，且溶于水的化合物，例如硝酸铜、硫酸铜、氯化铜等。
本发明所述的锌盐为阳离子为锌离子、阴离子为酸根阴离子，且溶于水的化合物，例如硝酸锌、硫酸锌、氯化锌等。
该实施方式的一些实施例中，植物纤维、淀粉、抑菌剂、海藻酸钠的质量比为20～70：20～70：0.1～5：0.5～10。
该实施方式的一些实施例中，原料包括粘合剂。
在一种或多种实施例中，植物纤维与粘合剂的质量比为20～70:0～8.5。
在一种或多种实施例中，所述粘合剂为瓜尔豆胶或羧甲基纤维素钠。
该实施方式的一些实施例中，原料包括泡打粉。
在一种或多种实施例中，植物纤维与泡打粉的质量比为20～70:0～5。
该实施方式的一些实施例中，所述的植物纤维选自豌豆纤维、大豆纤维。
该实施方式的一些实施例中，所述的淀粉选自玉米淀粉、木薯淀粉、小麦淀粉、大米淀粉、糯米淀粉中的一种或几种。
该实施方式的一些实施例中，造粒后进行杀菌、烘干。
本发明的另一种实施方式，提供了一种抑菌除臭猫砂，由上述制备方法获得。
为了使得本领域技术人员能够更加清楚地了解本发明的技术方案，以下将结合具体的实施例详细说明本发明的技术方案。
实施例1：
豌豆纤维7Kg，玉米淀粉2Kg，硝酸银10g，海藻酸钠900g，将上述组分充分混合10min，混合过程中需保持物料湿度在10％，然后将混合好的上述组分通过输送设备投入制粒机进行制粒，制成的颗粒经微波杀菌设备进行低温杀菌3分钟，杀菌温度设置在摄氏50度，杀菌后的颗粒经自然降温后输送到分级筛，筛选合格尺寸的颗粒，得到猫砂成品1。
实施例2：
豌豆纤维2Kg，木薯淀粉7Kg，羧甲基纤维素钠850g，硝酸银10g，海藻酸钠50g，将上述组分充分混合10min，混合过程中需保持物料湿度在15％，然后将混合好的上述组分通过输送设备投入制粒机进行制粒，制成的颗粒经微波杀菌设备进行低温杀菌3分钟，杀菌温度设置在摄氏50度，杀菌后的颗粒经自然降温后输送到分级筛，筛选合格尺寸的颗粒，得到猫砂成品2。
实施例3：
大豆纤维2Kg，小麦淀粉6Kg，瓜尔豆胶200g，泡打粉500g，硫酸铜300g，海藻酸钠1Kg，将上述组分充分混合10min，混合过程中需保持物料湿度在15％，然后将混合好的上述组分通过输送设备投入制粒机进行制粒，制成的颗粒经微波杀菌设备进行低温杀菌3分钟，杀菌温度设置在摄氏50度，杀菌后的颗粒经自然降温后输送到分级筛，筛选合格尺寸的颗粒，得到猫砂成品3。
实施例4：
豌豆纤维5.3Kg，大米淀粉3Kg，瓜尔豆胶200g，硫酸锌500g，海藻酸钠1Kg，将上述组分充分混合10min，混合过程中需保持物料湿度在15％，然后将混合好的上述组分通过输送设备投入制粒机进行制粒，制成的颗粒经微波杀菌设备进行低温杀菌3分钟，杀菌温度设置在摄氏50度，杀菌后的颗粒经自然降温后输送到分级筛，筛选合格尺寸的颗粒，得到猫砂成品4。
实施例5：
大豆豆纤维4.2Kg，大米淀粉2Kg，糯米淀粉2kg，瓜尔豆胶300g，氯化铜300g，氯化锌200g，海藻酸钠1Kg，将上述组分充分混合10min，混合过程中需保持物料湿度在20％，然后将混合好的上述组分通过输送设备投入制粒机进行制粒，制成的颗粒经微波杀菌设备进行低温杀菌3分钟，杀菌温度设置在摄氏50度，杀菌后的颗粒经自然降温后输送到分级筛，筛选合格尺寸的颗粒，得到猫砂成品5。
实施例6：
大豆纤维2Kg，小麦淀粉6Kg，瓜尔豆胶200g，泡打粉500g，硫酸铜300g，海藻酸钠1Kg，将上述组分充分混合10min，混合过程中需保持物料湿度在9％，然后将混合好的上述组分通过输送设备投入制粒机进行制粒。产物以粉末为主，无法制成颗粒，物料之间界面清晰切相互分离，无明显反应。
实施例7：
大豆纤维2Kg，小麦淀粉6Kg，瓜尔豆胶200g，泡打粉500g，硫酸铜300g，海藻酸钠1Kg，将上述组分充分混合10min，混合过程中需保持物料湿度在21％，然后将混合好的上述组分通过输送设备投入制粒机进行制粒。混合物堵塞出料口，造成制粒设备内压力过大，无法实施制粒。
根据一次性使用卫生用品卫生标准GB15979-2002附录C进行测定各实施例的抑菌率，抑菌率及除臭效果见表1。
表1抑菌率及除臭效果
金属离子含量测试：各取10g猫砂分别浸入100mL去离子水和动物尿液(猫尿)中，浸泡20min后取5mL溶液利用电感耦合等离子体发射光谱仪(ICP-OES)进行测定。
表2金属离子含量
测试结果表明实施例猫砂经尿液浸泡后会释放金属离子。
未沾染尿液的豆腐猫砂由于密度较轻，容易沾附在猫身上，猫需要通过舔舐来清理这部分沾附的猫砂，但猫不会以猫砂为食物进行吞咽。在猫清理猫砂的过程中，游离盐释放出的金属离子将随唾液进入动物体内。以一只2.5公斤重的成年猫每天使用1公斤猫砂为例，如果采用直接添加金属盐抑菌的豆腐猫砂，猫将从一公斤上述实施例猫砂中可能摄取的最大金属离子量分别为：实施例1、实施例2，各含Ag+635mg，超出12倍银离子的动物半数致死剂量：50mg(2.5Kg×20mg/Kg)；实施例3，Cu2+7680mg，实施例4，Cu2+11302mg，实施例5，Zn2+9538mg，Cu2+11261mg，超出中华人民共和国农业部第2625号关于饲料添加剂安全使用规范的公告中铜元素和锌元素在配合饲料或全混合日粮中的最高限量：Cu125mg/Kg，Zn200mg/Kg，将危害宠物及饲养人的健康。而使用海藻酸抑菌混悬液制备的豆腐猫砂，猫将从一公斤上述实施例猫砂中可能摄取的最大金属离子量分别为：实施例1、实施例2，各含Ag+10μg，低于美国环保署(EPA)发布的每日服银参考剂量：12.5μg(2.5Kg×5μg/Kg)；实施例3，Cu2+89mg，实施例3，Zn2+124mg，实施例4，Zn2+114mg或Cu2+114mg，符合农业部第2625号关于饲料添加剂安全使用规范中铜和锌元素的添加量；从而在保证抗菌效果的同时将金属盐抑菌剂对宠物的危害基本消除。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，对于本领域的技术人员来说，本发明可以有各种更改和变化。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (10)
1.一种抑菌除臭猫砂的制备方法，其特征是，以植物纤维、淀粉、抑菌剂、海藻酸钠为原料，将原料进行混合，将混合后的物料进行造粒获得抑菌除臭猫砂；其中，抑菌剂为银盐、铜盐、锌盐中的一种或多种，混合过程中保持物料湿度为10～20％。
2.如权利要求1所述的抑菌除臭猫砂的制备方法，其特征是，植物纤维、淀粉、抑菌剂、海藻酸钠的质量比为20～70：20～70：0.1～5：0.5～10。
3.如权利要求1所述的抑菌除臭猫砂的制备方法，其特征是，原料包括粘合剂。
4.如权利要求3所述的抑菌除臭猫砂的制备方法，其特征是，植物纤维与粘合剂的质量比为20～70:0～8.5；
或，所述粘合剂为瓜尔豆胶或羧甲基纤维素钠。
5.如权利要求1所述的抑菌除臭猫砂的制备方法，其特征是，原料包括泡打粉。
6.如权利要求5所述的抑菌除臭猫砂的制备方法，其特征是，植物纤维与泡打粉的质量比为20～70:0～5。
7.如权利要求1所述的抑菌除臭猫砂的制备方法，其特征是，所述的植物纤维选自豌豆纤维、大豆纤维。
8.如权利要求1所述的抑菌除臭猫砂的制备方法，其特征是，所述的淀粉选自玉米淀粉、木薯淀粉、小麦淀粉、大米淀粉、糯米淀粉中的一种或几种。
9.如权利要求1所述的抑菌除臭猫砂的制备方法，其特征是，造粒后进行杀菌、烘干。
10.一种抑菌除臭猫砂，其特征是，由权利要求1～9任一所述的制备方法获得。