CN111423716A - 一种医用塑料薄膜及其制备方法 - Google Patents

一种医用塑料薄膜及其制备方法 Download PDF

Info

Publication number
CN111423716A
CN111423716A CN202010376220.XA CN202010376220A CN111423716A CN 111423716 A CN111423716 A CN 111423716A CN 202010376220 A CN202010376220 A CN 202010376220A CN 111423716 A CN111423716 A CN 111423716A
Authority
CN
China
Prior art keywords
parts
layer
plastic film
medical plastic
mainly contains
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202010376220.XA
Other languages
English (en)
Inventor
王小卿
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangzhou Yueshen Medical Equipment Co ltd
Original Assignee
Guangzhou Yueshen Medical Equipment Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangzhou Yueshen Medical Equipment Co ltd filed Critical Guangzhou Yueshen Medical Equipment Co ltd
Priority to CN202010376220.XA priority Critical patent/CN111423716A/zh
Publication of CN111423716A publication Critical patent/CN111423716A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种医用塑料薄膜及其制备方法；所述的医用塑料薄膜主要原料包括二元醇、二异氰酸酯、聚酯多元醇，添加的改性物质有：丙烯酸乙酯、三氟化硼乙醚、三氟甲磺酸铜、溴化锂、三醋酸锰、甲基丙烯酸羟乙酯、丁腈橡胶、过氧化笨甲酰、对苯二酚、硅烷偶联剂、气相二氧化硅；本发明所提供的医用薄膜材料有优良的透氧率及抗菌性，使用该薄膜生产的定位袋在放疗、手术、康复、急救、残疾人体位矫正等方面使用，体感舒适，有良好的包裹性；对手术过程中血管和神经受损情况能有效的避免，使压疮风险大大降低，同时易于清理消毒，且制备方法简单易行，适于大范围推广应用。

Description

一种医用塑料薄膜及其制备方法
技术领域
本发明涉及医疗材料技术领域，具体涉及一种医用塑料薄膜及其制备方法。
背景技术
众所周知，临床上有大量病人需要进行体位固定，例如：
1、手术后为促进血液循环机免除二次伤害，受伤部位需要保持比心脏高15-20cm的位置，现在医院一般采用枕头、书本垫高，或者绳索吊起等方式，但是这些方式弊端很明显，如枕头数量不够用、塌陷后影响血液的回流，容易脏污等；使用书本、绳索吊起解决不了体位固定，对部分骨折患者还可能带来二次伤害，并且病人会感觉硬，生痛，甚至产生压疮；这时可用良肢位垫来解决上述问题，但良肢位垫需要做到无毒、便于清理消毒，柔软舒适、与皮肤长时间接触体温不会明显上升，不会觉得太热难受，就需要良好的薄膜材料；本发明提供的薄膜材料非常舒适柔软，包裹性好，不会产生压疮；同时该薄膜透氧率高达到12000cm3/m2•d•Pa以上，而医用理想材料tpu，tpe为5000cm3/m2•d•Pa左右，tpu的硬度一般在邵氏硬度98以上，该薄膜邵氏硬度一般在90以下，从而薄膜身体组织放置其上，与皮肤接触长时间放置在24度的温度下不升温，超过24度的环境下升温不超过2.5度，体感非常舒适。
2、外科手术中人体定位袋基本使用尼龙贴合tpu材料，该材料抽真空后体感生硬，甚至生痛，大手术时不少患者产生压疮，另外由于尼龙布是织造工艺，会有经纬的纹理，有血液残留时很难清洗消毒；如果使用本发明所提供的薄膜能产生良好的包裹性，体感舒适，压疮风险大大降低，易于清理消毒。
3、放疗等靶向治疗时，需要进行人体精准固定，而直线加速器的床板为碳纤维材料，之前的人体固定袋材料为尼龙贴合材料，放置在床板会滑动，需要使用加固条进行再加固等方式，病人体感生硬疼痛，但是使用本发明提供的薄膜材料的定位袋，不需要加固定条，放置在碳纤维床板上也不会滑动，并且包裹性非常好，病人没有疼痛感，不需要使用固定条，减少了操作时间，还能节省成本。
因此，本发明所提供的医用塑料薄膜能很大程度的解决患者的痛苦，在临床上发挥着重要作用。
发明内容
为了克服现有技术的不足，本发明提供一种医用塑料薄膜及其制备方法，该医用塑料薄膜能产生良好的包裹性，体感舒适，压疮风险大大降低，易于清理消毒；还有良好的抗菌性。
实现本发明的目的可以通过采取如下技术方案达到：
一种医用塑料薄膜，包括如下按重量份计的各组分：
二元醇：12-15份；
二异氰酸酯：30-35份；
聚酯多元醇：45-50份；
改性物质：3-5份；
其中改性物质包括有按重量份计的各组分：
丙烯酸乙酯：40-42份；
三氟化硼乙醚：1-2份；
三氟甲磺酸铜：0.1-0.2份；
溴化锂：0.1-0.2份；
三醋酸锰：0.2-0.3份；
甲基丙烯酸羟乙酯：5-6份；
丁腈橡胶：17-18份；
过氧化笨甲酰：5-6份；
对苯二酚：0.2-0.3份；
硅烷偶联剂：1-2份；
气相二氧化硅：2-3份。
优选地，所述医用塑料薄膜为层状结构，包括有耐磨层、粘结层、透气层、粘结层和承力层，所述耐磨层中主要含有丙烯酸乙酯、二异氰酸酯，所述粘结层主要含有丁腈橡胶、催化剂和二元醇，所述透气层主要含有甲基丙烯酸羟乙酯和稳定剂，所述粘结层主要含有过氧化笨甲酰、对苯二酚和二元醇，所述承力层主要含有硅烷偶联剂、气相二氧化硅和聚酯多元醇。
优选地，所述催化剂为三氟化硼乙醚、三氟甲磺酸铜、溴化锂、三醋酸锰；所述稳定剂为对苯二酚。
所述医用塑料薄膜的制备方法，包括以下步骤：
1）、按5层不同功能的层数按照重量配比，各层的原料混合搅拌均匀，烘干水分；
2）、将每层的原料分别下料至相对应的5层螺杆挤出机中，每层设置相应的温度，挤出机内温度约220-240度，模头口模温度约170-185度
3）、再经过流延成型延；
4）、再经过加热纵向拉升至需要生产的厚度；
5）、冷却薄膜同时按需要的宽度裁边收卷。
相比现有技术，本发明的有益效果在于：
第一，本发明提供的薄膜材料非常舒适柔软，包裹性好，不会产生压疮；同时该薄膜透氧率高达到12000cm3/m2•d•Pa以上；该薄膜邵氏硬度一般在90以下，从而薄膜身体组织放置其上，与皮肤接触长时间放置升温极其慢，体感非常舒适。
第二，本发明医用薄膜材料能产生良好的包裹性，体感舒适，压疮风险大大降低，易于清理消毒。
第三，本发明提供的薄膜材料放置在碳纤维床板上也不会滑动，并且包裹性非常好，病人没有疼痛感，不需要使用固定条，减少了操作时间，还能节省成本。
第四，本发明医用塑料薄膜还具有优异的抗菌性；且制备方法简单易行，适于大范围推广应用。
具体实施方式
下面，结合具体实施方式，对本发明做进一步描述：
实施例1：
一种医用塑料薄膜，包括如下按重量份计的各组分：
二元醇：12-15份；
二异氰酸酯：30-35份；
聚酯多元醇：45-50份；
改性物质：3-5份；
其中改性物质包括有按重量份计的各组分：
丙烯酸乙酯：40-42份；
三氟化硼乙醚：1-2份；
三氟甲磺酸铜：0.1-0.2份；
溴化锂：0.1-0.2份；
三醋酸锰：0.2-0.3份；
甲基丙烯酸羟乙酯：5-6份；
丁腈橡胶：17-18份；
过氧化笨甲酰：5-6份；
对苯二酚：0.2-0.3份；
硅烷偶联剂：1-2份；
气相二氧化硅：2-3份。
所述医用塑料薄膜为层状结构，包括有耐磨层、粘结层、透气层、粘结层和承力层，所述耐磨层中主要含有丙烯酸乙酯、二异氰酸酯，所述粘结层主要含有丁腈橡胶、催化剂和二元醇，所述透气层主要含有甲基丙烯酸羟乙酯和稳定剂，所述粘结层主要含有过氧化笨甲酰、对苯二酚和二元醇，所述承力层主要含有硅烷偶联剂、气相二氧化硅和聚酯多元醇。
所述催化剂为三氟化硼乙醚、三氟甲磺酸铜、溴化锂、三醋酸锰；所述稳定剂为对苯二酚。
所述医用塑料薄膜的制备方法，包括以下步骤：
1）、按5层不同功能的层数按照重量配比，各层的原料混合搅拌均匀，烘干水分；
2）、将每层的原料分别下料至相对应的5层螺杆挤出机中，每层设置相应的温度，挤出机内温度约220-240度，模头口模温度约170-185度
3）、再经过流延成型延；
4）、再经过加热纵向拉升至需要生产的厚度；
5）、冷却薄膜同时按需要的宽度裁边收卷。
实施例2：
一种医用塑料薄膜，包括如下按重量份计的各组分：
二元醇：14-15份；
二异氰酸酯：32-35份；
聚酯多元醇：47-50份；
改性物质：4-5份；
其中改性物质包括有按重量份计的各组分：
丙烯酸乙酯：41-42份；
三氟化硼乙醚：1-2份；
三氟甲磺酸铜：0.1-0.2份；
溴化锂：0.1-0.2份；
三醋酸锰：0.2-0.3份；
甲基丙烯酸羟乙酯：5-6份；
丁腈橡胶：17-18份；
过氧化笨甲酰：5-6份；
对苯二酚：0.2-0.3份；
硅烷偶联剂：1-2份；
气相二氧化硅：2-3份。
所述医用塑料薄膜为层状结构，包括有耐磨层、粘结层、透气层、粘结层和承力层，所述耐磨层中主要含有丙烯酸乙酯、二异氰酸酯，所述粘结层主要含有丁腈橡胶、催化剂和二元醇，所述透气层主要含有甲基丙烯酸羟乙酯和稳定剂，所述粘结层主要含有过氧化笨甲酰、对苯二酚和二元醇，所述承力层主要含有硅烷偶联剂、气相二氧化硅和聚酯多元醇。
所述催化剂为三氟化硼乙醚、三氟甲磺酸铜、溴化锂、三醋酸锰；所述稳定剂为对苯二酚。
所述医用塑料薄膜的制备方法，包括以下步骤：
1）、按5层不同功能的层数按照重量配比，各层的原料混合搅拌均匀，烘干水分；
2）、将每层的原料分别下料至相对应的5层螺杆挤出机中，每层设置相应的温度，挤出机内温度约220-240度，模头口模温度约170-185度
3）、再经过流延成型延；
4）、再经过加热纵向拉升至需要生产的厚度；
5）、冷却薄膜同时按需要的宽度裁边收卷。
实施例3：
一种医用塑料薄膜，包括如下按重量份计的各组分：
二元醇：12-13份；
二异氰酸酯：30-33份；
聚酯多元醇：45-48份；
改性物质：3-4份；
其中改性物质包括有按重量份计的各组分：
丙烯酸乙酯：40-42份；
三氟化硼乙醚：1-2份；
三氟甲磺酸铜：0.1-0.2份；
溴化锂：0.1-0.2份；
三醋酸锰：0.2-0.3份；
甲基丙烯酸羟乙酯：5-6份；
丁腈橡胶：17-18份；
过氧化笨甲酰：5-6份；
对苯二酚：0.2-0.3份；
硅烷偶联剂：1-2份；
气相二氧化硅：2-3份。
所述医用塑料薄膜为层状结构，包括有耐磨层、粘结层、透气层、粘结层和承力层，所述耐磨层中主要含有丙烯酸乙酯、二异氰酸酯，所述粘结层主要含有丁腈橡胶、催化剂和二元醇，所述透气层主要含有甲基丙烯酸羟乙酯和稳定剂，所述粘结层主要含有过氧化笨甲酰、对苯二酚和二元醇，所述承力层主要含有硅烷偶联剂、气相二氧化硅和聚酯多元醇。
所述催化剂为三氟化硼乙醚、三氟甲磺酸铜、溴化锂、三醋酸锰；所述稳定剂为对苯二酚。
所述医用塑料薄膜的制备方法，包括以下步骤：
1）、按5层不同功能的层数按照重量配比，各层的原料混合搅拌均匀，烘干水分；
2）、将每层的原料分别下料至相对应的5层螺杆挤出机中，每层设置相应的温度，挤出机内温度约220-240度，模头口模温度约170-185度
3）、再经过流延成型延；
4）、再经过加热纵向拉升至需要生产的厚度；
5）、冷却薄膜同时按需要的宽度裁边收卷。
实施例4：
一种医用塑料薄膜，包括如下按重量份计的各组分：
二元醇：15份；
二异氰酸酯：32份；
聚酯多元醇：50份；
改性物质：3份；
其中改性物质包括有按重量份计的各组分：
丙烯酸乙酯：40份；
三氟化硼乙醚：1份；
三氟甲磺酸铜：0.1份；
溴化锂：0.1份；
三醋酸锰：0.2份；
甲基丙烯酸羟乙酯：5份；
丁腈橡胶：17份；
过氧化笨甲酰：5份；
对苯二酚：0.2份；
硅烷偶联剂：1份；
气相二氧化硅：2份。
所述医用塑料薄膜为层状结构，包括有耐磨层、粘结层、透气层、粘结层和承力层，所述耐磨层中主要含有丙烯酸乙酯、二异氰酸酯，所述粘结层主要含有丁腈橡胶、催化剂和二元醇，所述透气层主要含有甲基丙烯酸羟乙酯和稳定剂，所述粘结层主要含有过氧化笨甲酰、对苯二酚和二元醇，所述承力层主要含有硅烷偶联剂、气相二氧化硅和聚酯多元醇。
所述催化剂为三氟化硼乙醚、三氟甲磺酸铜、溴化锂、三醋酸锰；所述稳定剂为对苯二酚。
所述医用塑料薄膜的制备方法，包括以下步骤：
1）、按5层不同功能的层数按照重量配比，各层的原料混合搅拌均匀，烘干水分；
2）、将每层的原料分别下料至相对应的5层螺杆挤出机中，每层设置相应的温度，挤出机内温度约220-240度，模头口模温度约170-185度
3）、再经过流延成型延；
4）、再经过加热纵向拉升至需要生产的厚度；
5）、冷却薄膜同时按需要的宽度裁边收卷。
实施例5：
一种医用塑料薄膜，包括如下按重量份计的各组分：
二元醇：12份；
二异氰酸酯：35份；
聚酯多元醇：50份；
改性物质：3份；
其中改性物质包括有按重量份计的各组分：
丙烯酸乙酯：42份；
三氟化硼乙醚：2份；
三氟甲磺酸铜：0.2份；
溴化锂：0.2份；
三醋酸锰：0.3份；
甲基丙烯酸羟乙酯：6份；
丁腈橡胶：18份；
过氧化笨甲酰：6份；
对苯二酚：0.3份；
硅烷偶联剂：2份；
气相二氧化硅：3份。
所述医用塑料薄膜为层状结构，包括有耐磨层、粘结层、透气层、粘结层和承力层，所述耐磨层中主要含有丙烯酸乙酯、二异氰酸酯，所述粘结层主要含有丁腈橡胶、催化剂和二元醇，所述透气层主要含有甲基丙烯酸羟乙酯和稳定剂，所述粘结层主要含有过氧化笨甲酰、对苯二酚和二元醇，所述承力层主要含有硅烷偶联剂、气相二氧化硅和聚酯多元醇。
所述催化剂为三氟化硼乙醚、三氟甲磺酸铜、溴化锂、三醋酸锰；所述稳定剂为对苯二酚。
所述医用塑料薄膜的制备方法，包括以下步骤：
1）、按5层不同功能的层数按照重量配比，各层的原料混合搅拌均匀，烘干水分；
2）、将每层的原料分别下料至相对应的5层螺杆挤出机中，每层设置相应的温度，挤出机内温度约220-240度，模头口模温度约170-185度
3）、再经过流延成型延；
4）、再经过加热纵向拉升至需要生产的厚度；
5）、冷却薄膜同时按需要的宽度裁边收卷。
实施例6：
一种医用塑料薄膜，包括如下按重量份计的各组分：
二元醇：13份；
二异氰酸酯：34份；
聚酯多元醇：49份；
改性物质：4份；
其中改性物质包括有按重量份计的各组分：
丙烯酸乙酯：41份；
三氟化硼乙醚：1.5份；
三氟甲磺酸铜：0.15份；
溴化锂：0.15份；
三醋酸锰：0.25份；
甲基丙烯酸羟乙酯：5.5份；
丁腈橡胶：17.5份；
过氧化笨甲酰：5.5份；
对苯二酚：0.25份；
硅烷偶联剂：1.5份；
气相二氧化硅：2.5份。
所述医用塑料薄膜为层状结构，包括有耐磨层、粘结层、透气层、粘结层和承力层，所述耐磨层中主要含有丙烯酸乙酯、二异氰酸酯，所述粘结层主要含有丁腈橡胶、催化剂和二元醇，所述透气层主要含有甲基丙烯酸羟乙酯和稳定剂，所述粘结层主要含有过氧化笨甲酰、对苯二酚和二元醇，所述承力层主要含有硅烷偶联剂、气相二氧化硅和聚酯多元醇。
所述催化剂为三氟化硼乙醚、三氟甲磺酸铜、溴化锂、三醋酸锰；所述稳定剂为对苯二酚。
所述医用塑料薄膜的制备方法，包括以下步骤：
1）、按5层不同功能的层数按照重量配比，各层的原料混合搅拌均匀，烘干水分；
2）、将每层的原料分别下料至相对应的5层螺杆挤出机中，每层设置相应的温度，挤出机内温度约220-240度，模头口模温度约170-185度
3）、再经过流延成型延；
4）、再经过加热纵向拉升至需要生产的厚度；
5）、冷却薄膜同时按需要的宽度裁边收卷。
验证实施例
为了检测本发明各实施例中所述的塑料薄膜的效果，在每个实施例所述的塑料薄膜成品进行试验评分检测；根据检测情况进行打分，满分为100分，求得平均分，结果见表1。
表1、医用塑料薄膜的性能检测表
Figure DEST_PATH_IMAGE002
从表中可以看出，本发明具有优良的性能，其中实施例4 的性能最佳。
对于本领域的技术人员来说，可根据以上描述的技术方案以及构思，做出其它各种相应的改变，而所有的这些改变形都应该属于本发明权利要求的保护范围之内。

Claims (4)

1.一种医用塑料薄膜，其特征在于：包括如下按重量份计的各组分：
二元醇：12-15份；
二异氰酸酯：30-35份；
聚酯多元醇：45-50份；
改性物质：3-5份；
其中改性物质包括有按重量份计的各组分：
丙烯酸乙酯：40-42份；
三氟化硼乙醚：1-2份；
三氟甲磺酸铜：0.1-0.2份；
溴化锂：0.1-0.2份；
三醋酸锰：0.2-0.3份；
甲基丙烯酸羟乙酯：5-6份；
丁腈橡胶：17-18份；
过氧化笨甲酰：5-6份；
对苯二酚：0.2-0.3份；
硅烷偶联剂：1-2份；
气相二氧化硅：2-3份。
2.根据权利要求1所述的医用塑料薄膜，其特征在于：所述医用塑料薄膜为层状结构，包括有耐磨层、粘结层、透气层、粘结层和承力层，所述耐磨层中主要含有丙烯酸乙酯、二异氰酸酯，所述粘结层主要含有丁腈橡胶、催化剂和二元醇，所述透气层主要含有甲基丙烯酸羟乙酯和稳定剂，所述粘结层主要含有过氧化笨甲酰、对苯二酚和二元醇，所述承力层主要含有硅烷偶联剂、气相二氧化硅和聚酯多元醇。
3.根据权利要求2所述的医用塑料薄膜，其特征在于：所述催化剂为三氟化硼乙醚、三氟甲磺酸铜、溴化锂、三醋酸锰；所述稳定剂为对苯二酚。
4.一种如权利要求3所述的医用塑料薄膜的制备方法，其特征在于包括如下步骤：
1）、按5层不同功能的层数按照重量配比，各层的原料混合搅拌均匀，烘干水分；
2）、将每层的原料分别下料至相对应的5层螺杆挤出机中，每层设置相应的温度，挤出机内温度约220-240度，模头口模温度约170-185度
3）、再经过流延成型延；
4）、再经过加热纵向拉升至需要生产的厚度；
5）、冷却薄膜同时按需要的宽度裁边收卷。
CN202010376220.XA 2020-05-07 2020-05-07 一种医用塑料薄膜及其制备方法 Pending CN111423716A (zh)