CN111410551A - 一种植物纤维发泡墙体保温材料及其制备方法 - Google Patents
一种植物纤维发泡墙体保温材料及其制备方法 Download PDFInfo
- Publication number
- CN111410551A CN111410551A CN202010355961.XA CN202010355961A CN111410551A CN 111410551 A CN111410551 A CN 111410551A CN 202010355961 A CN202010355961 A CN 202010355961A CN 111410551 A CN111410551 A CN 111410551A
- Authority
- CN
- China
- Prior art keywords
- heat
- parts
- wall
- straws
- plant fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种植物纤维发泡墙体保温材料及其制备方法,包括选用农作物秸秆50‑80份,麦秸20份,棉秆5‑15份,麻秆10‑20份玉米秆10‑20份,改性外加剂50‑80份,硅酸盐水泥50‑80份,无机防火保温板外墙防火保温板3块,粉煤灰漂珠2‑4份、玻璃漂珠2‑4份、普通膨胀珍珠岩2‑4份、聚苯颗粒2‑4份。该植物纤维发泡墙体保温材料及其制备方法,共同承受房屋所收到的外力,使房屋具有了良好的抗震性能,无机保温材料保温材料全封闭、无接缝、无空腔,没有冷热桥产生,并且不但做外墙外保温还可以做外墙内保温,或者外墙内外同时保温,及屋顶的保温和地热的隔热层,降低导热系数,提高蓄热系数,增强粘结强度,利于建筑隔热保温,可达到节能环保效果,提高安全系数。
Description
技术领域
本发明涉及植物纤维发泡墙体技术领域,具体为一种植物纤维发泡墙体保温材料及其制备方法。
背景技术
植物纤维水泥板具有良好的安全防火性能,其燃烧性可达到国家规定的难燃A级的防火标准,耐火极限可达1.5~2.0h,被明火烧灼时无有害气体生成,利用植物纤维水泥板,中间填以保温材料(如草泥)芯层组成复合墙体再与框板组合框板式结构,共同承受房屋所收到的外力,使房屋具有了良好的抗震性能,这种结构的节能量达到建设部颁布的“二级节能标准”以上,抗震能力在7.5级以上,其内部保温效果不佳。
现有的植物纤维发泡墙体在制作中导热系数大,蓄热系数过小,粘结强度过低,不利于建筑隔热保温,既不节能环保,安全系数过低,为此,我们推出一种植物纤维发泡墙体保温材料及其制备方法。
发明内容
本发明的目的在于提供一种植物纤维发泡墙体保温材料及其制备方法,以解决上述背景技术中提出的现有的植物纤维发泡墙体在制作中导热系数大,蓄热系数过小,粘结强度过低,不利于建筑隔热保温,既不节能环保,安全系数过低的问题。
为实现上述目的,本发明提供如下技术方案:一种植物纤维发泡墙体保温材料及其制备方法,包括选用农作物秸秆50-80份,麦秸20份,棉秆5-15 份,麻秆10-20份玉米秆10-20份,改性外加剂50-80份,硅酸盐水泥50-80 份,无机防火保温板外墙防火保温板3块,粉煤灰漂珠2-4份、玻璃漂珠2-4 份、普通膨胀珍珠岩2-4份、聚苯颗粒2-4份。
优选的,所述植物纤维水泥板的制备方法步骤为;
原材料主要包括植物纤维增强材料、基体胶凝材料以及少量的改性外加剂,植物纤维增强材料主要为农作物秸秆,如麦秸、棉秆、麻秆以及玉米秆等;胶凝材料主要为普通硅酸盐水泥,在板材中起基体的作用,由于植物纤维中某些萃取物会影响水泥的凝结硬化作用,故生产过程中必须加入少量的改性外加剂,以保证水泥胶凝材料的正常凝结。
优选的,所述该植物纤维水泥板,中间填以保温材料(如草泥)芯层组成复合墙体再与框板组合框板式结构。
优选的,所述该无机防火保温板外墙防火保温板采用膨胀型防火保温材料,以金羚牌无机无碱无腐蚀外墙防火保温板胶粘剂为粘接剂,用专用的机械锚固定件将该防火保温板贴挂在外墙上,然后抹抗裂砂浆,压入玻璃纤维网格布形成结构保护层。
优选的,所述无机防火保温板外墙制作工艺;
1)无机防火保温板的规格为:长度2500~3000mm、宽度600~1200mm、厚度5~30mm。
优选的,所述无机防火保温板垂直法试验步骤如下;
1)无机保温材料保温板可直接抹在毛坯墙上,其施工方法与水泥砂浆找平层相同,使用的机械,工具简单,施工便利,与其他保温系统比较有明显的施工期短、质量容易控制的优势。
2)无机保温材料保温板适用于各种墙体基层材质,各种形状复杂墙体的保温。全封闭、无接缝、无空腔,没有冷热桥产生。并且不但做外墙外保温还可以做外墙内保温,或者外墙内外同时保温。
3)无机保温材料保温系统无毒、无味、无放射性污染,对环境和人体无害。
4)热工性能好:无机保温材料保温板蓄热性能远大于有机保温材料,可用于南方的夏季隔热,同时其导热系数可以达到0.050W/m.K以下,而且导热性能可以方便地调整以配合力学强度的需要及实际使用功能的要求。
5)可以防止冷热桥传导,防止室内结露后产生的霉斑;
无机保温材料保温板与基层粘结强度高,不产生裂纹及空鼓。这一点在国内所有的保温材料相比具有一定的技术优势。
与现有技术相比,本发明的有益效果为该植物纤维发泡墙体,由于植物纤维中某些萃取物会影响水泥的凝结硬化作用,故生产过程中必须加入少量的改性外加剂,以保证水泥胶凝材料的正常凝结,利用植物纤维水泥板,中间填以保温材料(如农作物秸秆,如麦秸、棉秆、麻秆以及玉米秆等)芯层组成复合墙体再与框板组合框板式结构,共同承受房屋所收到的外力,使房屋具有了良好的抗震性能,无机保温材料保温材料全封闭、无接缝、无空腔,没有冷热桥产生,并且不但做外墙外保温还可以做外墙内保温,或者外墙内外同时保温,及屋顶的保温和地热的隔热层,降低导热系数,提高蓄热系数,增强粘结强度,利于建筑隔热保温,可达到节能环保效果,提高安全系数。
具体实施方式
下面将结合本发明实施例,对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
本发明提供一种技术方案:一种植物纤维发泡墙体保温材料及其制备方法,包括选用农作物秸秆50-80份,麦秸20份,棉秆5-15份,麻秆10-20 份玉米秆10-20份,改性外加剂50-80份,硅酸盐水泥50-80份,无机防火保温板外墙防火保温板3块,粉煤灰漂珠2-4份、玻璃漂珠2-4份、普通膨胀珍珠岩2-4份、聚苯颗粒2-4份。
优选的,所述植物纤维水泥板的制备方法步骤为;
原材料主要包括植物纤维增强材料、基体胶凝材料以及少量的改性外加剂,植物纤维增强材料主要为农作物秸秆,如麦秸、棉秆、麻秆以及玉米秆等;胶凝材料主要为普通硅酸盐水泥,在板材中起基体的作用,由于植物纤维中某些萃取物会影响水泥的凝结硬化作用,故生产过程中必须加入少量的改性外加剂,以保证水泥胶凝材料的正常凝结。
优选的,所述该植物纤维水泥板,中间填以保温材料(如草泥)芯层组成复合墙体再与框板组合框板式结构。
优选的,所述该无机防火保温板外墙防火保温板采用膨胀型防火保温材料,以金羚牌无机无碱无腐蚀外墙防火保温板胶粘剂为粘接剂,用专用的机械锚固定件将该防火保温板贴挂在外墙上,然后抹抗裂砂浆,压入玻璃纤维网格布形成结构保护层。
优选的,所述无机防火保温板外墙制作工艺;
1)无机防火保温板的规格为:长度2500~3000mm、宽度600~1200mm、厚度5~30mm。
所述无机防火保温板垂直法试验步骤如下;
1)无机保温材料保温板可直接抹在毛坯墙上,其施工方法与水泥砂浆找平层相同,使用的机械,工具简单,施工便利,与其他保温系统比较有明显的施工期短、质量容易控制的优势。
2)无机保温材料保温板适用于各种墙体基层材质,各种形状复杂墙体的保温。全封闭、无接缝、无空腔,没有冷热桥产生。并且不但做外墙外保温还可以做外墙内保温,或者外墙内外同时保温。
3)无机保温材料保温系统无毒、无味、无放射性污染,对环境和人体无害。
4)热工性能好:无机保温材料保温板蓄热性能远大于有机保温材料,可用于南方的夏季隔热,同时其导热系数可以达到0.050W/m.K以下,而且导热性能可以方便地调整以配合力学强度的需要及实际使用功能的要求。
5)可以防止冷热桥传导,防止室内结露后产生的霉斑;
无机保温材料保温板与基层粘结强度高,不产生裂纹及空鼓,这一点在国内所有的保温材料相比具有一定的技术优势。
该植物纤维发泡墙体保温材料机及其制备,其施工方法与水泥砂浆找平层相同,使用的机械,工具简单,施工便利,与其他保温系统比较有明显的施工期短、质量容易控制的优势,植物纤维增强材料主要为农作物秸秆,如麦秸、棉秆、麻秆以及玉米秆等;胶凝材料主要为普通硅酸盐水泥,在板材中起基体的作用,由于植物纤维中某些萃取物会影响水泥的凝结硬化作用,故生产过程中必须加入少量的改性外加剂,以保证水泥胶凝材料的正常凝结,以金羚牌无机无碱无腐蚀外墙防火保温板胶粘剂为粘接剂,用专用的机械锚固定件将该防火保温板贴挂在外墙上,然后抹抗裂砂浆,压入玻璃纤维网格布形成结构保护层,由于植物纤维中某些萃取物会影响水泥的凝结硬化作用,故生产过程中必须加入少量的改性外加剂,以保证水泥胶凝材料的正常凝结,利用植物纤维水泥板,中间填以保温材料(如农作物秸秆,如麦秸、棉秆、麻秆以及玉米秆等)芯层组成复合墙体再与框板组合框板式结构,共同承受房屋所收到的外力。
尽管参照前述实施例对本发明进行了详细的说明,对于本领域的技术人员来说,其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分技术特征进行等同替换,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (6)
1.一种植物纤维发泡墙体保温材料及其制备方法,其特征在于:包括选用农作物秸秆50-80份,麦秸20份,棉秆5-15份,麻秆10-20份玉米秆10-20份,改性外加剂50-80份,硅酸盐水泥50-80份,无机防火保温板外墙防火保温板3块,粉煤灰漂珠2-4份、玻璃漂珠2-4份、普通膨胀珍珠岩2-4份、聚苯颗粒2-4份。
2.根据权利要求1所述的一种植物纤维发泡墙体保温材料及其制备方法,其特征在于:所述植物纤维水泥板的制备方法步骤为;
原材料主要包括植物纤维增强材料、基体胶凝材料以及少量的改性外加剂,植物纤维增强材料主要为农作物秸秆,如麦秸、棉秆、麻秆以及玉米秆等;胶凝材料主要为普通硅酸盐水泥,在板材中起基体的作用,由于植物纤维中某些萃取物会影响水泥的凝结硬化作用,故生产过程中必须加入少量的改性外加剂,以保证水泥胶凝材料的正常凝结。
3.根据权利要求2所述的一种植物纤维发泡墙体保温材料及其制备方法,其特征在于:所述该植物纤维水泥板,中间填以保温材料(如草泥)芯层组成复合墙体再与框板组合框板式结构。
4.根据权利要求1所述的一种植物纤维发泡墙体保温材料及其制备方法,其特征在于:所述该无机防火保温板外墙防火保温板采用膨胀型防火保温材料,以金羚牌无机无碱无腐蚀外墙防火保温板胶粘剂为粘接剂,用专用的机械锚固定件将该防火保温板贴挂在外墙上,然后抹抗裂砂浆,压入玻璃纤维网格布形成结构保护层。
5.根据权利要求4所述的一种植物纤维发泡墙体保温材料及其制备方法,其特征在于:所述无机防火保温板外墙制作工艺;
1)无机防火保温板的规格为:长度2500~3000mm、宽度600~1200mm、厚度5~30mm。
6.根据权利要求5所述的一种植物纤维发泡墙体保温材料及其制备方法,其特征在于:所述无机防火保温板垂直法试验步骤如下;
1)无机保温材料保温板可直接抹在毛坯墙上,其施工方法与水泥砂浆找平层相同,使用的机械,工具简单,施工便利,与其他保温系统比较有明显的施工期短、质量容易控制的优势。
2)无机保温材料保温板适用于各种墙体基层材质,各种形状复杂墙体的保温。全封闭、无接缝、无空腔,没有冷热桥产生。并且不但做外墙外保温还可以做外墙内保温,或者外墙内外同时保温。
3)无机保温材料保温系统无毒、无味、无放射性污染,对环境和人体无害。
4)热工性能好:无机保温材料保温板蓄热性能远大于有机保温材料,可用于南方的夏季隔热,同时其导热系数可以达到0.050W/m.K以下,而且导热性能可以方便地调整以配合力学强度的需要及实际使用功能的要求。
5)可以防止冷热桥传导,防止室内结露后产生的霉斑;
无机保温材料保温板与基层粘结强度高,不产生裂纹及空鼓。这一点在国内所有的保温材料相比具有一定的技术优势。