CN111333427A - 一种氧化镁掺杂系列均质料及其制备方法 - Google Patents
一种氧化镁掺杂系列均质料及其制备方法 Download PDFInfo
- Publication number
- CN111333427A CN111333427A CN202010393986.9A CN202010393986A CN111333427A CN 111333427 A CN111333427 A CN 111333427A CN 202010393986 A CN202010393986 A CN 202010393986A CN 111333427 A CN111333427 A CN 111333427A
- Authority
- CN
- China
- Prior art keywords
- parts
- magnesium oxide
- mixture
- homogeneous material
- mixer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及耐火材料领域，具体涉及一种氧化镁掺杂系列均质料及其制备方法，以下重量份数的原料配制而成：均化矾土86~94份，三氧化二铁0.8~1.8份，氧化镁2~6份，硅粉3~5.5份，二氧化硅微粉3~7份。本发明制备的氧化镁掺杂系列均质料具有良好的高温性能，热膨胀系数低，抗热震性好，抗碱能力和抗侵蚀性能力好。
Description
技术领域
本发明涉及耐火材料领域,尤其涉及一种氧化镁掺杂系列均质料及其制备方法。
背景技术
在近年来耐火原料趋向综合化、绿色化、特性化的背景下，对传统耐火原料进行改性合成变成为行业的研究和应用热点。通过在矾土原矿中添加少量氧化物，以改善、调整矾土原料的高温使用性能，已被实践证明可行。随着高炉炼铁炉渣碱度的提高和转炉炼钢趋于碱性化，在均质矾土中掺杂氧化镁，对均质矾土进行改性以提高材料的抗碱能力和抗侵蚀性，从提高材料的使用寿命的技术路线，具有良好的社会效益和经济效益。
发明内容
本发明的目的在于提供一种氧化镁掺杂系列均质料及其制备方法，利用在均质矾土合成过程中加入氧化镁，有利于形成多相复合的优良结构，改善材料在特殊环境下的高温使用性能。
为了实现上述目的,本发明提供如下的技术方案:
一种氧化镁掺杂系列均质料及其制备方法，由以下份数的原料配制而成：
均化矾土86~94份，三氧化二铁0.8~1.8份，氧化镁2~6份，硅粉3~5.5份，二氧化硅微粉3~7份。
优选的，所述的氧化镁掺杂系列均质料中均质矾土和氧化镁的重量份数为：
均质矾土88~94份，氧化镁3~6份。
优选的，所述的一种氧化镁掺杂系列均质料及其制备方法，包括以下步骤：
（1）按权利要求1中的比例用电子秤称取三氧化二铁、硅粉、二氧化硅微粉后，用混合机将上述物质混合，得到混合物A；
（2）按权利要求1中的比例用电子秤称取均化矾土、氧化镁，用混合机将上述物质混合，得到混合物B；
（3）将混合物A、混合物B使用搅拌混合机混合。
优选的，所述步骤（1）中，用混合机将上诉物质混合4-6分钟，得到混合物A。
优选的，所述步骤（3）中，将混合物A、混合物B使用搅拌混合机混合。
本发明的有益效果在于：
1.镁铝尖晶石氧化镁，顽火辉石氧化镁，镁橄榄石氧化镁和莫来石等的熔点都很高，具有良好的高温性能。
2. 三元化合物堇青石热膨胀系数低，抗热震性好。
具体实施方式
实施例1：
本发明提供一种氧化镁掺杂系列均质料及其制备方法，由以下重量份数的原料配制而成：
均化矾土86~94份，三氧化二铁0.8~1.8份，氧化镁2~6份，硅粉3~5.5份，二氧化硅微粉3~7份。
上述氧化镁掺杂系列均质料及其制备方法，包括以下步骤：
（1）按上述比例用电子秤称取三氧化二铁、硅粉、二氧化硅微粉后，用混合机将上述物质混合，得到混合物A；
（2）按上述比例用电子秤称取均化矾土、氧化镁，用混合机将上述物质混合，得到混合物B；
（3）将混合物A、混合物B使用搅拌混合机混合。
为了使混合物A混合的更加均匀且不至于混合太久浪费时间，上述步骤（1）中，用混合机将上述物质混合4-6分钟，得到混合物A。
为了使成品混合的更加均匀且提高混合效率，所述步骤（3）中，将混合物A、混合物B使用搅拌混合机混合5-9分钟。
实施例2：
本发明提供一种氧化镁掺杂系列均质料及其制备方法，由以下重量份数的原料配制而成：
均化矾土86份，三氧化二铁0.8份，氧化镁2份，硅粉3份，二氧化硅微粉3份。
上述氧化镁掺杂系列均质料及其制备方法，包括以下步骤：
（1）按上述比例用电子秤称取三氧化二铁、硅粉、二氧化硅微粉后，用混合机将上述物质混合，得到混合物A；
（2）按上述比例用电子秤称取均化矾土、氧化镁，用混合机将上述物质混合，得到混合物B；
（3）将混合物A、混合物B使用搅拌混合机混合。
为了使混合物A混合的更加均匀且不至于混合太久浪费时间，上述步骤（1）中，用混合机将上述物质混合4分钟，得到混合物A。
为了使成品混合的更加均匀且提高混合效率，所述步骤（3）中，将混合物A、混合物B使用搅拌混合机混合5分钟。
实施例3
本发明提供一种氧化镁掺杂系列均质料及其制备方法，由以下重量份数的原料配制而成：
均化矾土94份，三氧化二铁1.8份，氧化镁6份，硅粉5.5份，二氧化硅微粉7份。
上述氧化镁掺杂系列均质料及其制备方法，包括以下步骤：
（1）按上述比例用电子秤称取三氧化二铁、硅粉、二氧化硅微粉后，用混合机将上述物质混合，得到混合物A；
（2）按上述比例用电子秤称取均化矾土、氧化镁，用混合机将上述物质混合，得到混合物B；
（3）将混合物A、混合物B使用搅拌混合机混合。
为了使混合物A混合的更加均匀且不至于混合太久浪费时间，上述步骤（1）中，用混合机将上述物质混合6分钟，得到混合物A。
为了使成品混合的更加均匀且提高混合效率，所述步骤（3）中，将混合物A、混合物B使用搅拌混合机混合9分钟。
实施例4
本发明提供一种氧化镁掺杂系列均质料及其制备方法，由以下重量份数的原料配制而成：
均化矾土88份，三氧化二铁1份，氧化镁3份，硅粉4份，二氧化硅微粉4份。
上述氧化镁掺杂系列均质料及其制备方法，包括以下步骤：
（1）按上述比例用电子秤称取三氧化二铁、硅粉、二氧化硅微粉后，用混合机将上述物质混合，得到混合物A；
（2）按上述比例用电子秤称取均化矾土、氧化镁，用混合机将上述物质混合，得到混合物B；
（3）将混合物A、混合物B使用搅拌混合机混合。
为了使混合物A混合的更加均匀且不至于混合太久浪费时间，上述步骤（1）中，用混合机将上述物质混合5分钟，得到混合物A。
为了使成品混合的更加均匀且提高混合效率，所述步骤（3）中，将混合物A、混合物B使用搅拌混合机混合8分钟。
本发明提供的一种氧化镁掺杂系列均质料及其制备方法,在实际使用过程中,在均质矾土合成过程中加入氧化镁，有利于形成多相复合的优良结构，改善材料在特殊环境下的高温使用性系统内氧化物和大部分二元化合物，如镁铝尖晶石，顽火辉石，镁橄榄石和莫来石等的熔点都很高，具有良好的高温性能，三元化合物堇青石热膨胀系数低，抗热震性好，w(氧化铝)≥86%，w(三氧化二铁)≤1.8%，w(氧化镁) ≤6%，体积密度≥3.30g·cm-3，显气孔率≤8%，吸水率≤1.5%。
上述实施方式仅为本发明的优选实施方式，不能以此来限定本发明保护的范围，本领域的技术人员在本发明的基础上所做的任何非实质性的变化及替换均属于本发明所要求保护的范围。
Claims (5)
1.一种氧化镁掺杂系列均质料及其制备方法，其特征在于：由以下份数的原料配制而成：
均化矾土86~94份，三氧化二铁0.8~1.8份，氧化镁2~6份，硅粉3~5.5份，二氧化硅微粉3~7份。
2.根据权利要求1所述的一种氧化镁掺杂系列均质料及其制备方法，其特征在于：所述的氧化镁掺杂系列均质料中均质矾土和氧化镁的重量份数为：
均质矾土88~94份，氧化镁3~6份。
3.根据权利要求1所述的一种氧化镁掺杂系列均质料及其制备方法，其特征在于：包括以下步骤：
（1）按权利要求1中的比例用电子秤称取三氧化二铁、硅粉、二氧化硅微粉后，用混合机将上述物质混合，得到混合物A；
（2）按权利要求1中的比例用电子秤称取均化矾土、氧化镁，用混合机将上述物质混合，得到混合物B；
（3）将混合物A、混合物B使用搅拌混合机混合。
4.根据权利要求3所述的高铝质耐火浇注料的制备方法，其特征在于，所述步骤（1）中，用混合机将上诉物质混合4-6分钟，得到混合物A。
5.根据权利要求3所述的高铝质耐火浇注料的制备方法，其特征在于，所述步骤（3）中，将混合物A、混合物B使用搅拌混合机混合。