CN111320775B - 一种环保型马桶的制造方法 - Google Patents

一种环保型马桶的制造方法 Download PDF

Info

Publication number
CN111320775B
CN111320775B CN201811439571.XA CN201811439571A CN111320775B CN 111320775 B CN111320775 B CN 111320775B CN 201811439571 A CN201811439571 A CN 201811439571A CN 111320775 B CN111320775 B CN 111320775B
Authority
CN
China
Prior art keywords
wall
weight
layer
parts
closestool
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201811439571.XA
Other languages
English (en)
Other versions
CN111320775A (zh
Inventor
邹晓虎
文起东
崔俊峰
文博
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Inner Mongolia Dongsheng Diatomite Technology Innovation Industrial Park Co ltd
Original Assignee
Inner Mongolia Dongsheng Diatomite Technology Innovation Industrial Park Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Inner Mongolia Dongsheng Diatomite Technology Innovation Industrial Park Co ltd filed Critical Inner Mongolia Dongsheng Diatomite Technology Innovation Industrial Park Co ltd
Priority to CN201811439571.XA priority Critical patent/CN111320775B/zh
Publication of CN111320775A publication Critical patent/CN111320775A/zh
Application granted granted Critical
Publication of CN111320775B publication Critical patent/CN111320775B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种环保型马桶的制造方法，属于生活用品制造方法领域。所述马桶包括桶体，便圈，盖板，冲水桶，冲水桶盖，其中，所述桶体从内壁向外壁依次为桶体壁亚克力层，桶体壁硅藻土层，桶体壁氨基高分子聚合物层，所述桶体壁亚克力层的制造方法如下:第一，制作桶体的模具，第二，将模具进行烘干处理，第三，制备成浆料；第四，将步骤三中制成的浆料灌入步骤二中的模具中进行加热至80摄氏度进行保温处理然后冷却至室温进行脱模处理从而获得制成的亚克力材料桶体。本发明不仅可以吸附卫生间里的异味，还能对其进行分解，从而可以长久地保持卫生间的良好环境，同时减轻人们的打扫卫生的劳动强度。

Description

一种环保型马桶的制造方法
技术领域
本发明涉及一种环保型马桶的制造方法，属于生活用品制造方法领域。
背景技术
人们经常受到室内装饰材料污染的影响，装饰材料不环保，会对室内环境带来污染，危害人体健康。卫生间是人们经常使用的个人空间，在卫生间里，不仅会出现一般装修装饰材料不环保造成的污染问题，比如，在卫生间里使用漆料涂刷后造成的气味过重且长久不易散去的问题，而且，卫生间里一般比较潮湿通风不良，经常会出现一些刺激性气味的有害物质，危害人体健康。为了去除卫生间异味，使人们呼吸到新鲜空气，现有的措施一般是采用在卫生间放置香料、放置吸潮吸气味的马桶垫来将卫生间里的气味进行吸附从而营造良好的卫生间环境。但现有的这些技术措施，需要额外的在卫生间里加入一些物品，造成卫生间的空间浪费，并且需要时常进行更换，非常麻烦。而且，这些现有的技术措施只能吸附卫生间里的异味，不能对其进行分解，从而不能长久地保持卫生间的良好环境。
发明内容
本发明的目的是克服现有的技术措施中的缺点，提供一种环保型马桶的制造方法，这样制造出的马桶，不仅可以吸附卫生间里的异味，还能对其进行分解，从而可以长久地保持卫生间的良好环境，同时减轻人们的打扫卫生的劳动强度。
为了实现本发明的目的，本发明提供了一种环保型马桶的制造方法，所述马桶包括桶体，便圈，盖板，冲水桶，冲水桶盖，其中，所述桶体从内壁向外壁依次为桶体壁亚克力层，桶体壁硅藻土层，桶体壁氨基高分子聚合物层，所述桶体壁亚克力层的制造方法如下:第一，制作桶体的模具，第二，将模具加热到50-60摄氏度进行烘干处理，第三，在玻璃容器中加入90重量份的甲基丙烯酸甲酯，1重量份的过氧化二苯酰，1重量份的邻苯二甲酸二丁酯和1重量份的碳酸钙，并逐步加热至90摄氏度左右，同时进行搅拌5-20分钟，然后冷却至50摄氏度左右，制成浆料；第四，将步骤三中制成的浆料灌入步骤二中的模具中进行加热至80摄氏度进行保温处理1.5小时然后冷却至室温进行脱模处理从而获得制成的亚克力材料桶体。
进一步，上述环保型马桶的制造方法中，所述桶体壁硅藻土层的制造方法如下：首先，将50-60重量份的硅藻土，10-15重量份的植物纤维和5-10重量份的膨润土放入分散机中进行分散处理；然后加入1-15重量份的发泡剂进行搅拌以便充分进行溶解从而获得硅藻土分散液；接着，可以加入5-10重量份的二氧化钛，0.1-5重量份的HEPES和/或0.0000001-0.01重量份的纳米金。最后，加入英国壳牌化学公司生产的叔碳酸乙烯酯共聚乳液从而制成硅藻土涂料。
进一步，上述环保型马桶的制造方法中，以氨基对二苯甲酸为配体,以过渡金属盐:硝酸锌、醋酸锌提供无机组分,通过容积热法合成多孔材料的金属有机配位聚合物,形成的氨基高分子聚合物可以通过涂覆方法涂覆在所述桶体壁硅藻土层上形成所述桶体壁氨基高分子聚合物层。
另外，所述便圈，所述盖板，所述冲水桶以及所述冲水桶盖的壁的结构从内壁向外壁依次为壁亚克力层，壁硅藻土层，壁氨基高分子聚合物层。
本发明具有如下的技术效果：
1、节省了卫生间的空间。
2、减轻了人们的劳动强度。
3、可以长久保持卫生间的良好环境。
附图说明
图1为本发明中一种环保型马桶的立体示意图。
图2为本发明中马桶的桶体的壁结构示意图。
图3为本发明中马桶的便圈的壁结构示意图。
图4为为本发明中马桶的盖板的壁结构示意图。
图5为本发明中马桶的冲水桶的壁结构示意图。
图6为本发明中马桶的冲水桶盖的壁结构示意图。
图7为本发明中马桶的桶体的壁制造流程图。
具体实施方式
以下实施例用于说明本发明，但不用来限制本发明的范围。若未特别指明，实施例中所用的技术手段为本领域技术人员所熟知的常规手段，所用原料均为市售商品。
如图所示，图1为本发明中一种环保型马桶的立体示意图。图2为本发明中马桶的桶体的壁结构示意图。图3为本发明中马桶的便圈的壁结构示意图。图4为为本发明中马桶的盖板的壁结构示意图。图5为本发明中马桶的冲水桶的壁结构示意图。图6为本发明中马桶的冲水桶盖的壁结构示意图。图7为本发明中马桶的桶体的壁制造流程图。在图中，1为桶体，2为便圈，3为盖板，4为冲水桶，5为冲水桶盖，11为桶体壁亚克力层，12为桶体壁硅藻土层，13为桶体壁氨基高分子聚合物层，21为便圈壁亚克力层，22为便圈壁硅藻土层，23为便圈壁氨基高分子聚合物层，31为盖板壁亚克力层，32为盖板壁硅藻土层，33为盖板壁氨基高分子聚合物层，41为冲水桶壁亚克力层，42为冲水桶壁硅藻土层，43为冲水桶壁氨基高分子聚合物层，51为冲水桶盖壁亚克力层，52为冲水桶盖壁硅藻土层，53为冲水桶盖壁氨基高分子聚合物层。
为了去除室内环境中的有机污染物，一般使用硅藻土进行物理吸附。硅藻土是一种属于藻类的植物性浮游生物，在海洋湖泊经沉淀而生成的堆积岩。该种单细胞植物性生物藻类，能够非同寻常地吸取水份中的硅酸盐，并形成多孔质的细胞壁，其遗骸沉淀石化后便形成了以硅盐酸为主要成分的“硅藻土”。这样的微孔结构使得硅藻土对室内环境中的有机污染物等有害气体有很好的吸收作用。但是，物理吸附的最大问题，就是存在饱和度。因此，必须对吸附在硅藻土中的有机污染物进行化学降解才能更加彻底地处理这些有害气体，保持环境卫生干净。而寻找一种高效的添加剂来促进化学降解或光催化的速度便成为迫切需要解决的问题。本发明人经过多次实验发现，纳米金对HEPES(4-羟乙基哌嗪乙磺酸)有很好的促进化学降解或光催化的作用。下面的表1为纳米金浓度在HEPES浓度一定时生成的H2O2的量的关系的实验数据。
表1
Figure BDA0001884363920000041
Figure BDA0001884363920000051
如表1所示，H2O2的生成量正比于HEPES氧化产物的生成量，HEPES的氧化产物在350纳米(nm)处有特征吸收峰，因此可以通过紫外可见分光光度计测定350nm处的特征吸收峰的强度来测定H2O2的相对生成量。
上述表1中数据表明，纳米金的浓度越高，在HEPES浓度一定时生成的H2O2的量越大。纳米金的浓度基本上与H2O2生成相对量成正比例关系。硅藻土所吸附的有机污染物更容易被H2O2所氧化降解。HEPES为光敏材料，其可以化学降解或者光催化有机污染物。这样，通过添加纳米金便可以增强HEPES的化学降解或者光催化能力。因此，通过在硅藻土材料中添加一定量的HEPES和纳米金便可以将硅藻土所吸附的有机污染物更快地由H2O2所氧化降解。
下面表2示出了硅藻土材料中加入HEPES和纳米金后对甲醛的氧化降解的能力的比较(玻璃密封实验舱为0.5立方米，降解时间为半小时)。
表2
Figure BDA0001884363920000052
如上表2所示，硅藻土材料中加入HEPES和纳米金后对甲醛的氧化降解的能力随着纳米金浓度的提高而大大增强。
另外，纳米金本身也可以化学降解硅藻土所吸附的有机污染物。
一般来说，二氧化钛为光催化剂，可以在光照条件下光催化降解有机污染物。同时加入HEPES和纳米金，既可以在光照条件下更好地光催化降解有机污染物，也可以在没有光照射的情况下对有机污染物进行降解。
在本发明的一个实施例中，硅藻土层可包括50-60重量份的硅藻土，0.0000001-0.01重量份的纳米金。
在本发明的另一个实施例中，硅藻土层可包括50-60重量份的硅藻土，0.1-5重量份的HEPES，0.0000001-0.01重量份的纳米金。
在本发明的再一个实施例中，硅藻土层可包括50-60重量份的硅藻土，5-10重量份的二氧化钛，0.1-5重量份的HEPES，0.0000001-0.01重量份的纳米金。
在本发明的又一个实施例中，硅藻土层可包括50-60重量份的硅藻土，10-15重量份的植物纤维，5-10重量份的膨润土，5-10重量份的二氧化钛，0.1-5重量份的HEPES，0.0000001-0.01重量份的纳米金。
另外，硅藻土层还可包括1-15重量份的发泡剂。
关于吸附材料的制备，具体来说，首先，将50-60重量份的硅藻土，10-15重量份的植物纤维和5-10重量份的膨润土放入分散机中进行分散处理；然后加入1-15重量份的发泡剂进行搅拌以便充分进行溶解从而获得硅藻土分散液；接着，可以加入5-10重量份的二氧化钛，0.1-5重量份的HEPES和/或0.0000001-0.01重量份的纳米金。最后，加入英国壳牌化学公司生产的叔碳酸乙烯酯共聚乳液从而制成硅藻土涂料。
如图1所示，本发明的环保型马桶包括桶体1，便圈2，盖板3，冲水桶4，冲水桶盖5。桶体1位于马桶的下部，其底部可以放置在卫生间的地板上，其出水口(未示出)可通过密封圈正对卫生间地板上的与污物排出管道相连的地漏以便将马桶中的污物冲入污物排出管道；便圈2位于桶体1上部，中间是与马桶上部开口相适应的中空形状，其四周可覆盖马桶上部开口的四周，以便用户坐于上面，并且便圈2在马桶上部开口靠近冲水桶4的一侧与桶体1铰接，从而便圈2可以向上掀开靠近冲水桶4或向下放下放置在桶体1上。盖板3位于便圈4上部，盖板4在马桶上部开口靠近冲水桶4的一侧与桶体1铰接，从而盖板4可以向上掀开靠近冲水桶4或向下放下放置在便圈2上覆盖便圈2和马桶上部开口。冲水桶4位于马桶后部的桶体1上部，冲水桶4中可以贮水并冲洗马桶。冲水桶4上部具有覆盖其上部开口的冲水桶盖5。
如图2所示，桶体1从内壁向外壁依次为桶体壁亚克力层11，桶体壁硅藻土层12，桶体壁氨基高分子聚合物层13。具体来说，马桶的桶体1的基体由亚克力材料制成，亚克力材料是有机材料,特点是色彩丰富,不吸水,而且对人体没有辐射,是一种健康环保的产品。与传统陶瓷相比，亚克力材料更易于清洁；韧性好，不易损坏；质地比较柔和，冬季不会有冰冷刺骨之感；色彩多变，可根据自己的需求制定个性化产品。当然，马桶的桶体1的基体也可以用陶瓷材料制成，然后在陶瓷材料制成的基体外部覆盖亚克力材料层，硅藻土层和氨基高分子聚合物层。在本发明中，使用的亚克力材料可以包括甲基丙烯酸甲酯(MMA)，过氧化二苯酰(BPO)，邻苯二甲酸二丁酯(DBP)，碳酸钙。具体来说，使用的亚克力材料可以包括70-90重量份的甲基丙烯酸甲酯(MMA)，1-5重量份的过氧化二苯酰(BPO)，1-5重量份的邻苯二甲酸二丁酯(DBP)和1-5重量份的碳酸钙。这样，可以使得亚克力材料的防水性、韧性更好。在一实施例中，按照重量配比计算，使用的亚克力材料可以包括80重量份的甲基丙烯酸甲酯(MMA)，3重量份的过氧化二苯酰(BPO)，1重量份的邻苯二甲酸二丁酯(DBP)和3重量份的碳酸钙。如图7所示，亚克力材料马桶的桶体的制作方法如下：第一，用铁、铝或铜材料制作桶体的模具，模具中空，可以从模具的一侧进行灌浆，模具其他侧都进行封闭；第二，将模具加热到50-60摄氏度进行烘干处理；第三，在玻璃容器中加入上述重量配比的甲基丙烯酸甲酯(MMA)，过氧化二苯酰(BPO)，邻苯二甲酸二丁酯(DBP)和碳酸钙，比如，90重量份的甲基丙烯酸甲酯(MMA)，1重量份的过氧化二苯酰(BPO)，1重量份的邻苯二甲酸二丁酯(DBP)和1重量份的碳酸钙，并逐步加热至90摄氏度左右，同时进行搅拌5-20分钟，然后冷却至50摄氏度左右，制成浆料；第四，将步骤三中制成的浆料灌入步骤二中的模具中进行加热至80摄氏度进行保温处理1.5小时然后冷却至室温进行脱模处理从而获得制成的亚克力材料桶体1。
如图2所示，桶体1还包括桶体壁硅藻土层12和桶体壁氨基高分子聚合物层13，从桶体的内壁向外壁依次为桶体壁亚克力层11，桶体壁硅藻土层12，桶体壁氨基高分子聚合物层13。桶体壁硅藻土层12与桶体壁亚克力层11接触，桶体壁氨基高分子聚合物层13与桶体壁硅藻土层12接触。桶体壁硅藻土层12包括50-60重量份的硅藻土，0.0000001-0.01重量份的纳米金。另外，硅藻土层可包括50-60重量份的硅藻土，0.1-5重量份的HEPES，0.0000001-0.01重量份的纳米金。另外，硅藻土层可包括50-60重量份的硅藻土，5-10重量份的二氧化钛，0.1-5重量份的HEPES，0.0000001-0.01重量份的纳米金。另外，硅藻土层可包括50-60重量份的硅藻土，10-15重量份的植物纤维，5-10重量份的膨润土，5-10重量份的二氧化钛，0.1-5重量份的HEPES，0.0000001-0.01重量份的纳米金。另外，硅藻土层还可包括1-15重量份的发泡剂。首先，将50-60重量份的硅藻土，10-15重量份的植物纤维和5-10重量份的膨润土放入分散机中进行分散处理；然后加入1-15重量份的发泡剂进行搅拌以便充分进行溶解从而获得硅藻土分散液；接着，可以加入5-10重量份的二氧化钛，0.1-5重量份的HEPES和/或0.0000001-0.01重量份的纳米金。最后，加入英国壳牌化学公司生产的叔碳酸乙烯酯共聚乳液从而制成硅藻土涂料。该硅藻土涂料涂覆在亚克力材料桶体1上形成桶体壁硅藻土层。另外，桶体壁氨基高分子聚合物层13由氨基高分子聚合物形成，氨基高分子聚合物跟醛类的物质发生反应将把空气中游离的甲醛捕捉，反应生成类氨基酸类的物质和水。氨基高分子聚合物可以包括氨基对二苯甲酸和锌的硝酸盐。即以氨基对二苯甲酸为配体,以过渡金属盐:硝酸锌、醋酸锌提供无机组分,通过容积热法合成多孔材料的金属有机配位聚合物,形成的氨基高分子聚合物可以通过涂覆方法涂覆在桶体壁硅藻土层上形成桶体壁氨基高分子聚合物层，也可以通过粘结方法将形成的氨基高分子聚合物覆盖在桶体壁硅藻土层上形成桶体壁氨基高分子聚合物层。另外，氨基高分子聚合物层13也可以为其他的金属有机骨架材料(MOFs)，有三维的孔结构，具有气体吸附性质。另外，在金属有机骨架材料中，可以加入荧光剂或一些清香剂、除菌清洁剂。这样，便可以在黑暗中发出光亮或者缓慢释放清香剂、抗菌清洁剂以便进行消毒和净化。
如图3-图6所示，便圈2的壁从内向外包括便圈壁亚克力层21，便圈壁硅藻土层22，便圈壁氨基高分子聚合物层23，盖板3的壁从内向外包括盖板壁亚克力层31，盖板壁硅藻土层32，盖板壁氨基高分子聚合物层33，冲水桶4的壁从内向外包括冲水桶壁亚克力层41，冲水桶壁硅藻土层42，冲水桶壁氨基高分子聚合物层43，冲水桶盖5的壁从内向外包括冲水桶盖壁亚克力层51，冲水桶盖壁硅藻土层52，冲水桶盖壁氨基高分子聚合物层53。便圈2、盖板3、冲水桶4和冲水桶盖5的壁与桶体1的壁的结构和制作方法类似，具体参照关于桶体1的壁的结构和制作方法。当然，壁氨基高分子聚合物层也可以为其他的金属有机骨架材料(MOFs)，有三维的孔结构，具有气体吸附性质。另外，在金属有机骨架材料中，可以加入荧光剂或一些清香剂、除菌清洁剂。这样，便可以在黑暗中发出光亮或者缓慢释放清香剂、抗菌清洁剂以便进行消毒和净化。
以上所述仅为本发明的较佳实例，并不用以限制本发明，凡在本发明的精神原则之内所作的任何修改、等同替换和改进等，均应包含在本发明的保护范围之内。

Claims (2)

1.一种环保型马桶的制造方法，所述马桶包括桶体，便圈，盖板，冲水桶，冲水桶盖，其特征在于，所述桶体从内壁向外壁依次为桶体壁亚克力层，桶体壁硅藻土层，桶体壁氨基高分子聚合物层，所述桶体壁亚克力层的制造方法如下:第一，制作桶体的模具，第二，将模具加热到50-60摄氏度进行烘干处理，第三，在玻璃容器中加入90重量份的甲基丙烯酸甲酯，1重量份的过氧化二苯酰，1重量份的邻苯二甲酸二丁酯和1重量份的碳酸钙，并逐步加热至90摄氏度，同时进行搅拌5-20分钟，然后冷却至50摄氏度，制成浆料；第四，将步骤三中制成的浆料灌入步骤二中的模具中进行加热至80摄氏度进行保温处理1.5小时然后冷却至室温进行脱模处理从而获得制成的亚克力材料桶体；所述桶体壁硅藻土层的制造方法如下：首先，将50-60重量份的硅藻土，10-15重量份的植物纤维和5-10重量份的膨润土放入分散机中进行分散处理；然后加入1-15重量份的发泡剂进行搅拌以便充分进行溶解从而获得硅藻土分散液；接着，加入5-10重量份的二氧化钛，0.1-5重量份的HEPES和0.0000001-0.01重量份的纳米金；最后，加入英国壳牌化学公司生产的叔碳酸乙烯酯共聚乳液从而制成硅藻土涂料；以氨基对二苯甲酸为配体,以过渡金属盐、硝酸锌、醋酸锌提供无机组分,通过溶剂热法合成多孔材料的金属有机配位聚合物,形成的氨基高分子聚合物通过涂覆方法涂覆在所述桶体壁硅藻土层上形成所述桶体壁氨基高分子聚合物层。
2.根据权利要求1所述的环保型马桶的制造方法，其特征在于，所述便圈，所述盖板，所述冲水桶以及所述冲水桶盖的壁的结构从内壁向外壁依次为壁亚克力层，壁硅藻土层，壁氨基高分子聚合物层。
CN201811439571.XA 2018-11-29 2018-11-29 一种环保型马桶的制造方法 Active CN111320775B (zh)