CN111287005A - 一种绿色抗菌杀菌释放负氧离子服装 - Google Patents
一种绿色抗菌杀菌释放负氧离子服装 Download PDFInfo
- Publication number
- CN111287005A CN111287005A CN202010087674.5A CN202010087674A CN111287005A CN 111287005 A CN111287005 A CN 111287005A CN 202010087674 A CN202010087674 A CN 202010087674A CN 111287005 A CN111287005 A CN 111287005A
- Authority
- CN
- China
- Prior art keywords
- parts
- negative oxygen
- oxygen ion
- powder
- intermediate product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种绿色抗菌杀菌释放负氧离子服装，该服装在改性染料中浸染后烘干而成；改性染料的组成为：以重量份计，水性染料96～98.5份及负氧离子粉1.5～4份，其中，负氧离子粉包括以下组分：以重量份计，叶绿素15～28份、儿茶素19～25份、茶多酚10～15份、纳米氧化锌粉20～50份、二氧化硒0.6～2.5份、八钛酸钾3～10份、砷化镓0.5～4份、蛭石粉1～6份、纳米气凝胶粉5～20份。该绿色抗菌杀菌释放负氧离子服装具备抗菌杀菌功能的同时，还能长期释放负氧离子，提升实用性能。
Description
技术领域
本发明涉及生活用品技术领域，特别涉及一种绿色抗菌杀菌释放负氧离子服装。
背景技术
负氧离子别称是空气维生素、维他命，长寿素。一般在密闭室内的空气负离子浓度为50－100个/cm3；一般含量在700个/cm3以上(如旷野或公园)可让人感到空气清新，有益健康。因此负离子被誉为“空气维生素”。国内外医学专家通过临床验证，空气中含适量天然负离子具有以下功能：
(1)、提高人体氧气转化能力，加速新陈代谢，使人心情舒畅并产生理疗治愈作用。负离子能激活肌体多种酶；使吸氧增加20％，二氧化碳排除量增加14.5％。
(2)、降低血压，改善心肌功能。负离子能调整血液的酸碱度。活化细胞，提高细胞的各种功能，并保持离子平衡；能净化血液，抑制血清胆固醇形成。
(3)、改善睡眠效果，提高免疫力。负离子具有安定自律神经，控制交感神经，防止神经衰弱；增加脑α波，减轻疲劳等作用。
(4)、控制炎症、镇痛、抗癌，对肝硬化、糖尿病、神经麻痹均有治疗效果。
(5)、杀菌功能。负离子与细菌、病毒结合，使其产生结构性改变而死亡。
(6)、消除臭味。负离子能与空气中被污染的正离子中和，从而消除异味。
(7)、吸附烟雾粉尘。负离子和碧玺晶体表面静电场协同作用，吸附空气烟雾粉尘。
现代化的社会拥有很多高科技电子设备，使现代人方便，但电器设备会产生对人体不利的正离子(通称疲倦离子)，我们长时间暴露在电视、手机、计算机和新式电子设备下，它们所发出的正离子不断渗透至我们的体内以及饮食酸化，造成身、心疲倦，减弱免疫系统、降低血液循环、加速细胞老化，长期下来会心脏、高血压、皮肤斑点、肌肉骨头酸痛或是各种疾病。因此，若能设计出长期有效的绿色抗菌杀菌释放负氧离子的服装，对人类生活健康将有着重大意义和广泛的应用前景。
发明内容
本发明提供了一种绿色抗菌杀菌释放负氧离子服装，解决了现有技术中服装的功能性有待提升的技术问题，实现了使服装具备抗菌杀菌功能的同时，还能长期释放负氧离子，提升实用性能的技术效果。
本发明提供了一种绿色抗菌杀菌释放负氧离子服装，所述床单被套在改性染料中浸染后烘干而成；
所述改性染料的组成为：以重量份计，水性染料96～98.5份及负氧离子粉1.5～4份，其中，
所述负氧离子粉包括以下组分：以重量份计，叶绿素15～28份、儿茶素19～25份、茶多酚10～15份、纳米氧化锌粉20～50份、二氧化硒0.6～2.5份、八钛酸钾3～10份、砷化镓0.5～4份、蛭石粉1～6份、纳米气凝胶粉5～20份。
作为优选，所述改性染料的组成为：以重量份计，水性染料97.5份及负氧离子粉2.5份。
作为优选，所述改性染料通过在所述水性染料中加入所述负氧离子粉后搅拌均匀制得。
作为优选，所述负氧离子粉包括以下组分：以重量份计，所述叶绿素20份、儿茶素20份、茶多酚10份、纳米氧化锌粉30份、二氧化硒1份、八钛酸钾5份、砷化镓1份、蛭石粉3份、纳米气凝胶粉10份。
作为优选，所述负氧离子粉的制备过程包括：
将所述纳米氧化锌、所述二氧化硒、所述八钛酸钾、所述砷化镓、所述蛭石粉进行第一阶段搅拌，获得第一中间产物；
将所述第一中间产物进行煅烧，获得第二中间产物；
待所述第二中间产物冷却后，将所述叶绿素、所述儿茶素及所述茶多酚添加到所述第二中间产物中进行第二阶段搅拌；
再将所述纳米气凝胶粉添加到所述第二中间产物中进行第三阶段搅拌，获得第三中间产物；
将生理盐水添加所述第三中间产物中进行研磨，获得第四中间产物；
将所述第四中间产物进行干燥，获得所述负氧离子粉。
本申请实施例中提供的一个或多个技术方案，至少具有如下技术效果或优点：
通过服装在改性染料中浸染后烘干而成；改性染料以传统水性染料及负氧离子粉为原料，在传统水性染料的染色基础上，通过负氧离子粉增加抗菌杀菌及释放负氧离子的功能；负氧离子粉包含的叶绿素、儿茶素、茶多酚是吸收二氧化碳释放氧气较多的植物，是普通植物的10倍以上。纳米氧化锌是抗氧化材料，二氧化硒是感光材料、八钛酸钾是阻热和隔热材料将感光吸附，砷化镓是超导材料将吸附的紫外线在夜晚也能释放，蛭石粉是膨胀系数较高的材料，纳米气凝胶是多孔纳米材料，将上述材料填满在气凝胶内，发热时依靠蛭石粉的膨胀将紫外线照射叶绿素、茶多酚和儿茶素，实现长期释放负氧离子的功能。这样，解决了现有技术中服装的功能性有待提升的技术问题，实现了使服装具备抗菌杀菌功能的同时，还能长期释放负氧离子，提升实用性能的技术效果。
附图说明
图1为本申请实施例提供的改性染料制备过程的流程示意图。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚，下面将结合附图对本发明实施方式作进一步地详细描述。
本发明提供的一种绿色抗菌杀菌释放负氧离子服装，服装在改性染料中浸染后烘干而成；该服装材质可以是天然纤维、合成纤维，或者天然纤维与合成纤维的混纺。
改性染料的组成为：以重量份计，水性染料96～98.5份及负氧离子粉1.5～4份，其中，
负氧离子粉包括以下组分：以重量份计，叶绿素15～28份、儿茶素19～25份、茶多酚10～15份、纳米氧化锌粉20～50份、二氧化硒0.6～2.5份、八钛酸钾3～10份、砷化镓0.5～4份、蛭石粉1～6份、纳米气凝胶粉5～20份。
纳米氧化锌同时具有纳米材料和传统氧化锌的双重特性，作为一种纳米材料，具有高效的生物学活性、吸收率高、抗氧化能力强、安全稳定等特性，本申请利用了纳米氧化锌的抗氧化性能。
二氧化硒是感光材料；八钛酸钾是阻热和隔热材料将感光吸附；砷化镓是超导材料将吸附的紫外线在夜晚也能释放；蛭石粉是膨胀系数较高的材料；纳米气凝胶是多孔纳米材料，将上述材料填满在孔内。发热时依靠蛭石粉的膨胀将紫外线照射叶绿素、茶多酚和儿茶素，实现长期释放负氧离子的功能。叶绿素、茶多酚和儿茶素吸收二氧化碳释放氧气，氧气中含有丰富大中小阴离子(小阴离子即负氧离子)，此小阴离子有吸附分解甲醛、异味、苯和tvoc的功能，还可以杀死各种病毒。
进一步的，改性染料的组成为：以重量份计，水性染料97.5份及负氧离子粉2.5份。改性染料通过在水性染料中加入负氧离子粉后搅拌均匀制得。
作为一种优选的实施例，负氧离子粉包括以下组分：以重量份计，叶绿素20份、儿茶素20份、茶多酚10份、纳米氧化锌粉30份、二氧化硒1份、八钛酸钾5份、砷化镓1份、蛭石粉3份、纳米气凝胶粉10份。
进一步的，负氧离子粉的制备过程包括：
S1：将设定配比的纳米氧化锌、二氧化硒、八钛酸钾、砷化镓、蛭石粉进行第一阶段搅拌，获得第一中间产物；
S2：将第一中间产物进行煅烧，获得第二中间产物；
S3：待第二中间产物冷却后，将叶绿素、儿茶素及茶多酚添加到第二中间产物中进行第二阶段搅拌；
S4：再将纳米气凝胶粉添加到第二中间产物中进行第三阶段搅拌，获得第三中间产物；
S5：将生理盐水添加第三中间产物中进行研磨，获得第四中间产物；
S6：将第四中间产物进行干燥，获得负氧离子粉。
进一步的，第一阶段搅拌的时间控制为25～60分钟；煅烧的时间控制为7～10小时；第二阶段搅拌的时间控制在25～40分钟；第三阶段搅拌的时间控制在45～100分钟；研磨的时间控制在10～20小时。作为一种优选的实施例，第一阶段搅拌的时间控制为30分钟；煅烧的时间控制为8小时；第二阶段搅拌的时间控制在30分钟；第三阶段搅拌的时间控制在60分钟；研磨的时间控制在12小时。
另外，参见附图1，改性染料的制备过程为：在上述负氧离子粉制备完成后，进行步骤S7：将设定配比的负氧离子粉加入水性染料中，搅拌均匀后获得改性染料。
下面通过具体实施例来详细介绍改性染料的制备过程，所有原料都以重量份计算：
实施例1
S1：将纳米氧化锌粉28份、二氧化硒1份、八钛酸钾4份、砷化镓0.6份、蛭石粉1.5份置于不锈钢搅拌罐中进行第一阶段搅拌，获得第一中间产物；第一阶段搅拌的时间控制为30分钟；
S2：将第一中间产物置于高温炉中进行煅烧，获得第二中间产物；煅烧的时间控制为8小时；
S3：待第二中间产物冷却后，将第二中间产物置于不锈钢搅拌罐中，再将叶绿素19份、儿茶素20份、茶多酚10份添加到不锈钢搅拌罐中进行第二阶段搅拌；第二阶段搅拌的时间控制在35分钟；
S4：将纳米气凝胶粉8份添加到不锈钢搅拌罐中进行第三阶段搅拌，获得第三中间产物；第三阶段搅拌的时间控制在70分钟；
S5：将第三中间产物置于砂磨机中，添加生理盐水12份，进行研磨获得第四中间产物；研磨的时间控制在12小时；
S6：将第四中间产物置于喷雾干燥机中进行喷雾干燥，获得负氧离子粉；
S7：将2份负氧离子粉加入98份水性染料中，搅拌均匀后获得改性染料。
实施例2
S1：将纳米氧化锌粉30份、二氧化硒1份、八钛酸钾5份、砷化镓1份、蛭石粉3份置于不锈钢搅拌罐中进行第一阶段搅拌，获得第一中间产物；第一阶段搅拌的时间控制为30分钟；
S2：将第一中间产物置于高温炉中进行煅烧，获得第二中间产物；煅烧的时间控制为8小时；
S3：待第二中间产物冷却后，将第二中间产物置于不锈钢搅拌罐中，再将叶绿素20份、儿茶素20份、茶多酚10份添加到不锈钢搅拌罐中进行第二阶段搅拌；第二阶段搅拌的时间控制在30分钟；
S4：将纳米气凝胶粉10份添加到不锈钢搅拌罐中进行第三阶段搅拌，获得第三中间产物；第三阶段搅拌的时间控制在60分钟；
S5：将第三中间产物置于砂磨机中，添加生理盐水15份，进行研磨获得第四中间产物；研磨的时间控制在12小时；
S6：将第四中间产物置于喷雾干燥机中进行喷雾干燥，获得负氧离子粉；
S7：将2.5份负氧离子粉加入97.5份水性染料中，搅拌均匀后获得改性染料。
实施例3
S1：将纳米氧化锌粉35份、二氧化硒1.3份、八钛酸钾5.5份、砷化镓1.5份、蛭石粉3.5份置于不锈钢搅拌罐中进行第一阶段搅拌，获得第一中间产物；第一阶段搅拌的时间控制为40分钟；
S2：将第一中间产物置于高温炉中进行煅烧，获得第二中间产物；煅烧的时间控制为9小时；
S3：待第二中间产物冷却后，将第二中间产物置于不锈钢搅拌罐中，再将叶绿素21份、儿茶素22份、茶多酚11份添加到不锈钢搅拌罐中进行第二阶段搅拌；第二阶段搅拌的时间控制在35分钟；
S4：将纳米气凝胶粉13份添加到不锈钢搅拌罐中进行第三阶段搅拌，获得第三中间产物；第三阶段搅拌的时间控制在80分钟；
S5：将第三中间产物置于砂磨机中，添加生理盐水16份，进行研磨获得第四中间产物；研磨的时间控制在15小时；
S6：将第四中间产物置于喷雾干燥机中进行喷雾干燥，获得负氧离子粉；
S7：将3.5份负氧离子粉加入96.5份水性染料中，搅拌均匀后获得改性染料。
以上所述的具体实施方式，对本发明的目的、技术方案和有益效果进行了进一步详细说明，所应理解的是，以上所述仅为本发明的具体实施方式而已，并不用于限制本发明，凡在本发明的精神和原则之内，所做的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (5)
1.一种绿色抗菌杀菌释放负氧离子服装，其特征在于，所述服装在改性染料中浸染后烘干而成；
所述改性染料的组成为：以重量份计，水性染料96～98.5份及负氧离子粉1.5～4份，其中，
所述负氧离子粉包括以下组分：以重量份计，叶绿素15～28份、儿茶素19～25份、茶多酚10～15份、纳米氧化锌粉20～50份、二氧化硒0.6～2.5份、八钛酸钾3～10份、砷化镓0.5～4份、蛭石粉1～6份、纳米气凝胶粉5～20份。
2.如权利要求1所述的绿色抗菌杀菌释放负氧离子服装，其特征在于，所述改性染料的组成为：以重量份计，水性染料97.5份及负氧离子粉2.5份。
3.如权利要求1所述的绿色抗菌杀菌释放负氧离子服装，其特征在于，所述改性染料通过在所述水性染料中加入所述负氧离子粉后搅拌均匀制得。
4.如权利要求1所述的绿色抗菌杀菌释放负氧离子服装，其特征在于，所述负氧离子粉包括以下组分：以重量份计，所述叶绿素20份、儿茶素20份、茶多酚10份、纳米氧化锌粉30份、二氧化硒1份、八钛酸钾5份、砷化镓1份、蛭石粉3份、纳米气凝胶粉10份。
5.如权利要求1所述的绿色抗菌杀菌释放负氧离子服装，其特征在于，所述负氧离子粉的制备过程包括：
将所述纳米氧化锌、所述二氧化硒、所述八钛酸钾、所述砷化镓、所述蛭石粉进行第一阶段搅拌，获得第一中间产物；
将所述第一中间产物进行煅烧，获得第二中间产物；
待所述第二中间产物冷却后，将所述叶绿素、所述儿茶素及所述茶多酚添加到所述第二中间产物中进行第二阶段搅拌；
再将所述纳米气凝胶粉添加到所述第二中间产物中进行第三阶段搅拌，获得第三中间产物；
将生理盐水添加所述第三中间产物中进行研磨，获得第四中间产物；
将所述第四中间产物进行干燥，获得所述负氧离子粉。