CN107158451A - 破壁艾绒卫生巾芯片 - Google Patents
破壁艾绒卫生巾芯片 Download PDFInfo
- Publication number
- CN107158451A CN107158451A CN201710332654.8A CN201710332654A CN107158451A CN 107158451 A CN107158451 A CN 107158451A CN 201710332654 A CN201710332654 A CN 201710332654A CN 107158451 A CN107158451 A CN 107158451A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- mixed liquor
- sanitary napkin
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种破壁艾绒卫生巾芯片，所述混合液包括以下重量份数的原料：艾叶20～30份、负离子粉5～10份、远红外纳米粉15～20份、纳米银粉10～15份和去离子水100～200份。本发明的破壁艾绒卫生巾芯片采用超微粉碎技术，对艾叶进行细胞破壁处理，使其活性成分充分释放，从而显著提高人体对艾叶精华的吸收能力，另外利用破壁艾叶粉、负离子粉、远红外纳米粉及纳米银粉等成分的作用优势和相互协同作用，使制备得到的卫生巾复合芯片应用于卫生巾时，疏通气血、温经散寒、调理痛经、缓解不适、舒缓情绪及安神镇静等作用。
Description
技术领域
本发明涉及卫生用品技术领域，具体而言，涉及一种破壁艾绒卫生巾芯片。
背景技术
卫生巾是女性月经期间，常用的卫生用品，它是一种具吸收力的物质，主要的材质为棉、不织布、纸浆或以上材质复合物所形成的高分子聚合物和高分子聚合物复合纸。卫生巾的背胶是不透水材质，可将经血保留在卫生巾中，用来吸收女性月经来潮时，自阴道流出的经血。
女性在经期，敏感部位的皮肤最易受损伤。调查表明，73％的女性会在经期时感到阴道瘙痒、灼痛，这多是由于使用不透气的卫生巾造成的，另外，80％以上的女性会出现痛经现象，因此，要安度经期，选择合适的卫生巾至关重要。卫生巾一般由表面层、中间锁水层和背胶三部分构成，使用时就要从这三部分的材料及作用考虑。
发明内容
有鉴于此，本发明提供的一种用于卫生巾复合芯片的混合液、卫生巾复合芯片及卫生巾，更好的克服了上述现有技术存在的问题和缺陷，利用经细胞破壁处理的艾叶及负离子粉、远红外纳米粉等成分的作用优势和相互协同作用，可以使制备得到的卫生巾达到疏通气血、温宫暖宫、调理痛经、缓解不适、舒缓情绪等目的。
一种用于卫生巾复合芯片的混合液，所述混合液包括以下重量份数的原料：艾叶20～30份、负离子粉5～10份、远红外纳米粉15～20份、纳米银粉10～15份和去离子水100～200份。
进一步地，所述混合液还包括以下重量份数的原料：磁粉3～8份。
进一步地，所述混合液还包括以下重量份数的原料：没药5～10份和乳香5～10份。
进一步地，所述负离子粉为电气石托玛琳粉。
进一步地，所述远红外纳米粉为纳米陶瓷粉。
本发明还提供了一种用于卫生巾复合芯片的混合液的制备方法，包括以下步骤：
(1)按上述的混合液的原料的重量份数称取各原料；
(2)将上述称取的艾叶采用超微粉碎技术进行破壁处理，得到破壁艾叶粉；
(3)将上述破壁艾叶药粉与负离子粉、远红外纳米粉，纳米银粉及去离子水混合均匀，即得。
进一步地，所述卫生巾复合芯片由无纺布浸泡在如上述的混合液中，然后干燥得到。
进一步地，所述无纺布为水刺无纺布。
进一步地，所述干燥过程为真空冷冻干燥。
本发明还提供了一种卫生巾，包括外保护层、棉表层以及位于中间层的锁水层，所述棉表层与所述锁水层之间设置有如上述的卫生巾复合芯片，所述锁水层的两侧设有防侧漏导流槽。
与现有技术相比，本发明的破壁艾绒卫生巾芯片的有益效果是：
(1)、本发明采用超微粉碎技术，对艾叶进行细胞破壁处理，使其活性成分充分释放，从而显著提高人体对艾叶精华的吸收能力，另外利用破壁艾叶粉、负离子粉、远红外纳米粉及纳米银粉等成分的作用优势和相互协同作用，使制备得到的卫生巾复合芯片应用于卫生巾时，疏通气血、温经散寒、调理痛经、缓解不适、舒缓情绪及安神镇静等作用。
(2)进一步地，本发明在混合液的原料中加入磁粉，利用强磁场刺激人体经络穴位，可以起到疏通经络、调节神经、促进气血运行的作用；强磁场也可以促进机体的血液循环，加强新陈代谢，起到良好的消炎消肿、镇痛安神及促进睡眠的作用，进一步提升混合液增强免疫力、促进新陈代谢、缓解痛经、舒缓情绪及安神镇静等功效。还通过在混合液的原料中加入没药和乳香，进一步提升通经止痛的功效。
为使本发明的上述目的、特征和优点能更明显易懂，下文特举较佳实施例，作详细说明如下。
附图说明
为了更清楚地说明本发明实施例的技术方案，下面将对实施例中所需要使用的附图作简单地介绍，应当理解，以下附图仅示出了本发明的某些实施例，因此不应被看作是对范围的限定，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他相关的附图。
图1为本发明的卫生巾的结构示意图；
图2为本发明的卫生巾剖面示意图A～A。
主要元件符号说明：
1-卫生巾；
100-外保护层；
200-锁水层；
300-棉表层；
400-卫生巾复合芯片；
500-防侧漏导流槽。
具体实施方式
为了便于理解本发明，下面结合实施例的方式对本发明的技术方案做详细说明，在下面的描述中阐述了很多具体细节以便于充分理解本发明。
但是本发明能够以很多不同于在此描述的其它方式来实施，本领域技术人员可以在不违背本发明内涵的情况下做类似改进，因此本发明不受下面公开的具体实施的限制。
除非另有限定，本文使用的所有技术以及科学术语具有与本发明所属领域普通技术人员通常理解的相同的含义。当存在矛盾时，以本说明书中的定义为准。
如本文所用之术语：
“由……制备”与“包含”同义。本文中所用的术语“包含”、“包括”、“具有”、“含有”或其任何其它变形，意在覆盖非排它性的包括。例如，包含所列要素的组合物、步骤、方法、制品或装置不必仅限于那些要素，而是可以包括未明确列出的其它要素或此种组合物、步骤、方法、制品或装置所固有的要素。
连接词“由……组成”排除任何未指出的要素、步骤或组分。如果用于权利要求中，此短语将使权利要求为封闭式，使其不包含除那些描述的材料以外的材料，但与其相关的常规杂质除外。当短语“由……组成”出现在权利要求主体的子句中而不是紧接在主题之后时，其仅限定在该子句中描述的要素；其它要素并不被排除在作为整体的所述权利要求之外。
当量、浓度、或者其它值或参数以范围、优选范围、或一系列上限优选值和下限优选值限定的范围表示时，这应当被理解为具体公开了由任何范围上限或优选值与任何范围下限或优选值的任一配对所形成的所有范围，而不论该范围是否单独公开了。例如，当公开了范围“1～5”时，所描述的范围应被解释为包括范围“1～4”、“1～3”、“1～2”、“1～2和4～5”、“1～3和5”等。当数值范围在本文中被描述时，除非另外说明，否则该范围意图包括其端值和在该范围内的所有整数和分数。
“和/或”用于表示所说明的情况的一者或两者均可能发生，例如，A和/或B包括(A和B)和(A或B)；
此外，本发明要素或组分前的不定冠词“一种”和“一个”对要素或组分的数量要求(即出现次数)无限制性。因此“一个”或“一种”应被解读为包括一个或至少一个，井且单数形式的要素或组分也包括复数形式，除非所述数量明显旨指单数形式。
一种用于卫生巾复合芯片的混合液，所述混合液包括以下重量份数的原料：
艾叶20～30份如20份、22份、25份、28份或30份等；
负离子粉5～10份如5份、6份、7份、8份、9份或10份等；
远红外纳米粉15～20份如15份、16份、17份、18份、19份或20份等；
纳米银粉10～15份如10份、11份、12份、13份、14份或15份等；
和去离子水100～200份如100份、120份、150份、180份或200份等。
优选地，所述混合液还包括以下重量份数的原料：
磁粉3～8份如3份、4份、5份、6份、7份或8份等。
优选地，所述混合液还包括以下重量份数的原料：
没药5～10份如5份、6份、7份、8份、9份或10份等；
乳香5～10份如5份、6份、7份、8份、9份或10份等。
艾叶又称艾草、冰台、艾蒿、医草、灸草、蕲艾、黄草、家艾等；其味苦、微温、无毒，苦燥辛散，能理气血、温经脉、逐寒湿、止冷痛，为妇科用药。可用于治疗脘腹冷痛，经寒不调，宫冷等症状。
没药又称末药、明没药，味苦，平，为橄榄科植物没药树及同属植物树干皮部渗出的油胶树脂，具有活血止痛、消肿生肌的功效。主治胸腹淤痛，痛经，经闭，跌打损伤，目赤肿痛等症状。
乳香又称乳头香、塌香、马思达吉、天泽香、多伽罗香、浴香等。味辛，苦，微温。具有活血行气、通经止痛、消肿生肌等功效。主治心腹疼痛，风湿痹痛，经闭痛经，跌打淤痛，痈疽肿毒等。
负离子粉，是人类利用自然界产生负离子的原理，人工合成或者配比的一种复合矿物，一般都是电气石粉+镧系元素或者稀土元素。负离子粉具有活化细胞、净化血液、减轻疲劳、稳定植物神经、增强抗病能力、镇痛作用、延年益寿的功效。
纳米银粉具有抗菌、强效杀菌、渗透性强、修复再生、抗菌持久、平安无毒、无耐药性的特性和功效。活性银离子制剂，可供治疗疾病，更可以针对环境空间作消毒灭菌，银可说是自然物质中公认抗菌最好的一种，一般而言，抗生素大致能够杀死6种不同的病原体细菌，但银却可以杀死650种以上的细菌，且银物质是不具毒性，其主因为银本生具有的生物作用。活性银离子能够吸引细菌体内酶蛋白上的硫氢基(～SH)，迅速的结合在一起，并使含硫氢基之酵素失去活性，进而使细菌死亡。值得注意的是：当细菌被银离子杀死后，银离子又会从死去的细菌上游离出来，再持续对活细菌做重复的动作，直至所有的细菌被消灭，由此可知，纳米银的功效是属于长效型杀菌剂，一般而言，其效用最少可以保持一年。
远红外纳米粉是用特殊纳米复合技术精制而成的新型纳米复合远红外保健功能材料。纳米复合无机远红外保健材料具有与人体辐射吸收相应波长的高远红外辐射率，是良好的人体保健用远红外辐射材料，具有抗紫外线、杀菌消除异味、防病治病等功能，可以有效地改善人体微循环，促使正常微循环血流增加2～3倍，提高组织供氧，改善新陈代谢，增强免疫力。
另外，远红外纳米粉可令水份子活性化，提高身体的含氧量。人体约70％是水分，血液的水分比更高过80％，若血气不足，血液中的水分子便集结成惰性水(即四个氢分子和一个氧分子结合)，不能通过细胞膜；远红外线能使水分子产生共振并细化，变成独立水分子(即两个氢分子和一个氧分子结合)，提高身体的含氧量，细胞因而能恢复活力，精神更畅旺、头脑更灵活、进而能提高抗病能力，延缓衰老。
磁粉产生的磁场具有活络血液、增进血液含氧量，提高免疫力的作用。所述磁粉可列举为稀土永磁材料，稀土永磁材料是指稀土金属和过渡族金属形成的合金经一定的工艺制成的永磁材料，分钐钴(SmCo)永磁体和钕铁硼(NdFeB)永磁体。稀土永磁材料具有强磁能量场。利用强磁场刺激人体经络穴位，可以起到疏通经络、调节神经、促进气血运行的作用；强磁场也可以促进机体的血液循环，加强新陈代谢，起到良好的消炎消肿、镇痛安神及促进睡眠的作用。
优选地，所述负离子粉为电气石托玛琳粉。
上述托玛琳电气石在常温下就能发射出8～14μm的远红外线，与人体易于吸收的波段恰好匹配，特别容易被肌肤所吸收，因此可以改善人体的血液循环，有利于促进人体的新陈代谢，保持机体的正常能量活动，能够提高肌体的免疫力，增强组织的再生能力，因此非常有助于人体的保健；托玛琳电气石能够释放负离子，而负离子具有杀灭病菌及净化空气的作用，而人体自身产生的负离子远远达不到人体的需求，释放的“负离子”能清除导致机体老化的氧自由基，令机体细胞更加健康有活力。另外，托玛琳电气石还具有生物电作用，托玛琳电气石表面流动着微电流，可以调节和补充人体的生物电从而达到抗辐射的作用。
优选地，所述远红外纳米粉为纳米陶瓷粉。
优选地，所述洋甘菊提取物和所述芦荟提取物均为去离子水提取物。
综上所述，本发明本发明采用超微粉碎技术，对艾叶进行细胞破壁处理，使其活性成分充分释放，从而显著提高人体对艾叶精华的吸收能力，另外利用破壁艾叶粉、负离子粉、远红外纳米粉及纳米银粉等成分的作用优势和相互协同作用，使制备得到的卫生巾复合芯片应用于卫生巾时，疏通气血、温经散寒、调理痛经、缓解不适、舒缓情绪及安神镇静等作用。
进一步地，在上述混合液的原料中加入磁粉，利用强磁场刺激人体经络穴位，可以起到疏通经络、调节神经、促进气血运行的作用；强磁场也可以促进机体的血液循环，加强新陈代谢，起到良好的消炎消肿、镇痛安神及促进睡眠的作用，进一步提升混合液增强免疫力、促进新陈代谢、缓解痛经、舒缓情绪及安神镇静等功效。
还可以在混合液的原料中加入没药和乳香，进一步提升通经止痛的功效。
本发明还提供了一种用于卫生巾复合芯片的混合液的制备方法，包括以下步骤：
按上述所述的混合液的原料的重量份数称取各原料，然后混合均匀。
优选地，所述卫生巾复合芯片由无纺布浸泡在如上述的混合液中，然后干燥得到。
优选地，所述无纺布为水刺无纺布。
优选地，所述干燥过程为真空冷冻干燥。
参阅图1及图2，本发明还提供了一种卫生巾1，包括外保护层100、棉表层300以及位于中间层的锁水层200，所述棉表层300与所述锁水层200之间设置有如上所述的卫生巾复合芯片400，所述锁水层200的两侧设有防侧漏导流槽500。
为了便于理解本发明，下面结合实施例来进一步说明本发明的技术方案。申请人声明，本发明通过上述实施例来说明本发明的详细工艺设备和工艺流程，但本发明并不局限于上述详细工艺设备和工艺流程，即不意味着本发明应依赖上述详细工艺设备和工艺流程才能实施。所属技术领域的技术人员应该明了，对本发明的任何改进，对本发明产品各原料的等效替换及辅助成分的添加、具体方式的选择等，均落在本发明的保护范围和公开范围之内。
实施例1
一种用于卫生巾复合芯片的混合液，该混合液包括以下重量份数的原料：芦荟20份、负离子粉10份、远红外纳米粉20份、纳米银粉10份和去离子水100份。
上述用于卫生巾复合芯片的混合液的制备方法，具体制备步骤如下：
(1)按上述的混合液的原料的重量份数称取各原料，备用；
((2)将上述称取的艾叶采用超微粉碎技术进行破壁处理，得到破壁艾叶粉；
(3)将上述破壁艾叶粉与负离子粉、远红外纳米粉，纳米银粉及去离子水混合均匀，即得。
实施例2
一种用于卫生巾复合芯片的混合液，该混合液包括以下重量份数的原料：芦荟25份、负离子粉8份、远红外纳米粉17份、纳米银粉12份和去离子水150份。
上述用于卫生巾复合芯片的混合液的制备方法，具体制备步骤如下：
(1)按上述的混合液的原料的重量份数称取各原料，备用；
(2)将上述称取的艾叶采用超微粉碎技术进行破壁处理，得到破壁艾叶粉；
(3)将上述破壁艾叶粉与负离子粉、远红外纳米粉，纳米银粉及去离子水混合均匀，即得。
实施例3
一种用于卫生巾复合芯片的混合液，该混合液包括以下重量份数的原料：芦荟30份、负离子粉5份、远红外纳米粉15份、纳米银粉15份和去离子水200份。
上述用于卫生巾复合芯片的混合液的制备方法，具体制备步骤如下：
(1)按上述的混合液的原料的重量份数称取各原料，备用；
(2)将上述称取的艾叶采用超微粉碎技术进行破壁处理，得到破壁艾叶粉；
(3)将上述破壁艾叶粉与负离子粉、远红外纳米粉，纳米银粉及去离子水混合均匀，即得。
实施例4
一种用于卫生巾复合芯片的混合液，该混合液包括以下重量份数的原料：芦荟20份、没药5份、乳香5份、负离子粉10份、远红外纳米粉20份、纳米银粉10份、磁粉3份和去离子水100份。
上述用于卫生巾复合芯片的混合液的制备方法，具体制备步骤如下：
(1)按上述的混合液的原料的重量份数称取各原料，备用；
(2)将上述称取的艾叶、没药和乳香混合均匀，然后采用超微粉碎技术进行破壁处理，得到混合药粉；
(3)将上述混合药粉与负离子粉、远红外纳米粉、纳米银粉、磁粉及去离子水混合均匀，即得。
实施例5
一种用于卫生巾复合芯片的混合液，该混合液包括以下重量份数的原料：芦荟22份、没药6份、乳香6份、负离子粉9份、远红外纳米粉19份、纳米银粉11份、磁粉4份和去离子水120份。
上述用于卫生巾复合芯片的混合液的制备方法，具体制备步骤如下：
(1)按上述的混合液的原料的重量份数称取各原料，备用；
(2)将上述称取的艾叶、没药和乳香混合均匀，然后采用超微粉碎技术进行破壁处理，得到混合药粉；
(3)将上述混合药粉与负离子粉、远红外纳米粉、纳米银粉、磁粉及去离子水混合均匀，即得。
实施例6
一种用于卫生巾复合芯片的混合液，该混合液包括以下重量份数的原料：芦荟25份、没药8份、乳香8份、负离子粉8份、远红外纳米粉18份、纳米银粉13份、磁粉5份和去离子水150份。
上述用于卫生巾复合芯片的混合液的制备方法，具体制备步骤如下：
(1)按上述的混合液的原料的重量份数称取各原料，备用；
(2)将上述称取的艾叶采用超微粉碎技术进行破壁处理，得到破壁艾叶粉；
(3)将上述破壁艾叶粉与负离子粉、远红外纳米粉，纳米银粉及去离子水混合均匀，即得。
实施例7
一种用于卫生巾复合芯片的混合液，该混合液包括以下重量份数的原料：芦荟28份、没药9份、乳香9份、负离子粉6份、远红外纳米粉16份、纳米银粉14份、磁粉7份和去离子水180份。
上述用于卫生巾复合芯片的混合液的制备方法，具体制备步骤如下：
(1)按上述的混合液的原料的重量份数称取各原料，备用；
(2)将上述称取的艾叶、没药和乳香混合均匀，然后采用超微粉碎技术进行破壁处理，得到混合药粉；
(3)将上述混合药粉与负离子粉、远红外纳米粉、纳米银粉、磁粉及去离子水混合均匀，即得。
实施例8
一种用于卫生巾复合芯片的混合液，该混合液包括以下重量份数的原料：芦荟30份、没药10份、乳香10份、负离子粉5份、远红外纳米粉15份、纳米银粉15份、磁粉8份和去离子水200份。
上述用于卫生巾复合芯片的混合液的制备方法，具体制备步骤如下：
(1)按上述的混合液的原料的重量份数称取各原料，备用；
(2)将上述称取的艾叶、没药和乳香混合均匀，然后采用超微粉碎技术进行破壁处理，得到混合药粉；
(3)将上述混合药粉与负离子粉、远红外纳米粉、纳米银粉、磁粉及去离子水混合均匀，即得。
实施例9
由上述实施例1～8所述的混合液来制备卫生巾复合芯片，具体步骤如下：
(1)将水刺无纺布浸泡浸泡在所述混合液中；
(2)采用冷冻干燥机将经步骤(1)浸泡后的水刺无纺布完全干燥。
具体情况见下表1.
表1
| 制备组 | 制备条件 |
| 9～1组：实施例1+水刺无纺布 | 采用冷冻干燥机至完全干燥 |
| 9～2组：实施例2+水刺无纺布 | 采用冷冻干燥机至完全干燥 |
| 9～3组：实施例3+水刺无纺布 | 采用冷冻干燥机至完全干燥 |
| 9～4组：实施例4+水刺无纺布 | 采用冷冻干燥机至完全干燥 |
| 9～5组：实施例5+水刺无纺布 | 采用冷冻干燥机至完全干燥 |
| 9～6组：实施例6+水刺无纺布 | 采用冷冻干燥机至完全干燥 |
| 9～8组：实施例7+水刺无纺布 | 采用冷冻干燥机至完全干燥 |
| 9～8组：实施例8+水刺无纺布 | 采用冷冻干燥机至完全干燥 |
实施例1～9之一所述各原料均为市售产品。
上述仅为本发明的优选实施例而已，并不用于限制本发明，对于本领域的技术人员来说，本发明配方及制备工艺可以有各种更改和变化。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (10)
1.一种用于卫生巾复合芯片的混合液，其特征在于：所述混合液包括以下重量份数的原料：艾叶20～30份、负离子粉5～10份、远红外纳米粉15～20份、纳米银粉10～15份和去离子水100～200份。
2.根据权利要求1所述的混合液，其特征在于：所述混合液还包括以下重量份数的原料：磁粉3～8份。
3.根据权利要求1所述的混合液，其特征在于：所述混合液还包括以下重量份数的原料：没药5～10份和乳香5～10份。
4.根据权利要求1所述的混合液，其特征在于：所述负离子粉为电气石托玛琳粉。
5.根据权利要求1所述的混合液，其特征在于：所述远红外纳米粉为纳米陶瓷粉。
6.一种用于卫生巾复合芯片的混合液的制备方法，其特征在于：包括以下步骤：
(1)按权利要求1所述的混合液的原料的重量份数称取各原料；
(2)将上述称取的艾叶采用超微粉碎技术进行破壁处理得到破壁艾叶粉；
(3)将步骤(1)得到的破壁艾叶粉与负离子粉、远红外纳米粉，纳米银粉及去离子水混合均匀，即得。
7.一种卫生巾复合芯片，其特征在于：所述卫生巾复合芯片由无纺布浸泡在如权利要求1所述的混合液中，然后干燥得到。
8.根据权利要求7所述的卫生巾复合芯片，其特征在于：所述无纺布为水刺无纺布。
9.根据权利要求7所述的卫生巾复合芯片，其特征在于：所述干燥过程为真空冷冻干燥。
10.一种卫生巾，包括外保护层、棉表层以及位于中间层的锁水层，其特征在于：所述棉表层与所述锁水层之间设置有如权利要求7所述的卫生巾复合芯片，所述锁水层的两侧设有防侧漏导流槽。