CN111154313A - Compound paint thinner - Google Patents
Compound paint thinner Download PDFInfo
- Publication number
- CN111154313A CN111154313A CN201811326770.XA CN201811326770A CN111154313A CN 111154313 A CN111154313 A CN 111154313A CN 201811326770 A CN201811326770 A CN 201811326770A CN 111154313 A CN111154313 A CN 111154313A
- Authority
- CN
- China
- Prior art keywords
- parts
- oil
- paint thinner
- thinner
- zeolite powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a composite paint thinner, which comprises the following components in parts by weight: zeolite powder: 55-60 parts; linseed oil: 30-38 parts; sunflower seed oil: 3-8 parts; manganese naphthenate: 1-6 parts; dichloromethane: 0.5-2 parts; the preparation method comprises the steps of adding zeolite powder, linseed oil and sunflower seed oil into an oxidation kettle according to corresponding weight parts, uniformly stirring, heating to 85 ℃, blowing air into oil through an air pipe to oxidize the oil and automatically heating to 105-110 ℃, continuously blowing air for oxidization at the temperature until the relative density is measured to reach 0.929-0.930, then adding dichloromethane and manganese naphthenate according to corresponding weight parts, uniformly stirring, and continuously blowing for 35min to obtain the finished product of the paint thinner, wherein the prepared paint thinner can reach the dilution requirement and reduce the loss of enterprises and consumers.
Description
Technical Field
The invention relates to the technical field of chemical production, in particular to a composite paint thinner.
Background
When people buy paint coatings, the paint coatings are generally matched with a diluent, the diluent is a liquid substance which is added with good miscibility with resin and is used for reducing the viscosity of the resin and improving the processing performance, and the diluent comprises a reactive diluent and a non-reactive diluent. The thermosetting resin in paint coating needs to be added with thinner to reduce its viscosity for further processing, and these thinner are all organic solvents which are cheaper than resin in practice, so as to reduce the processing cost, however, in the prior art, because the configuration of the thinner is not reasonable, the thinner in the production cannot achieve the required dilution effect, especially for thick paint, and brings loss to manufacturers and consumers.
Disclosure of Invention
In order to solve the technical problems, the invention provides the composite paint thinner, the preparation method is reasonable in configuration, and the prepared paint thinner can meet the dilution requirement and reduce the loss of enterprises and consumers.
The purpose of the invention is realized by the following technical scheme: a composite paint thinner comprising:
(1) the components are as follows: zeolite powder: 55-60 parts; linseed oil: 30-38 parts; sunflower seed oil: 3-8 parts; manganese naphthenate: 1-6 parts; dichloromethane: 0.5-2 parts;
(2) adding zeolite powder, linseed oil and sunflower seed oil into an oxidation kettle according to the corresponding weight part ratio, uniformly stirring, heating to 85 ℃, blowing air into oil through an air pipe to oxidize the oil and automatically heating to 105-110 ℃, continuously blowing air for oxidization at the temperature until the relative density is measured to reach 0.929-0.930, then installing the corresponding weight part ratio, adding dichloromethane and manganese naphthenate, uniformly stirring, and continuously blowing for 35min to obtain the finished product of the oil thinner.
The invention relates to a composite paint thinner, which comprises the following components in parts by weight: zeolite powder: 55-60 parts; linseed oil: 30-38 parts; sunflower seed oil: 3-8 parts; manganese naphthenate: 1-6 parts; dichloromethane: 0.5-2 parts; the preparation method comprises the steps of adding zeolite powder, linseed oil and sunflower seed oil into an oxidation kettle according to corresponding weight parts, uniformly stirring, heating to 85 ℃, blowing air into oil through an air pipe to oxidize the oil and automatically heating to 105-110 ℃, continuously blowing air for oxidization at the temperature until the relative density is measured to reach 0.929-0.930, then adding dichloromethane and manganese naphthenate according to corresponding weight parts, uniformly stirring, and continuously blowing for 35min to obtain the finished product of the paint thinner, wherein the prepared paint thinner can reach the dilution requirement and reduce the loss of enterprises and consumers.
Detailed Description
Example 1
The embodiment of the invention provides a composite paint thinner, which comprises: the composition comprises the following components in parts by weight: zeolite powder: 58 parts of a mixture; linseed oil: 34 parts of (a); sunflower seed oil: 5 parts of a mixture; manganese naphthenate: 2 parts of (1); dichloromethane: 1 part; and (2) adding the zeolite powder, the linseed oil and the sunflower seed oil into an oxidation kettle according to the corresponding weight part ratio, uniformly stirring, heating to 85 ℃, blowing air into the oil through an air pipe to oxidize the oil and automatically heating to 105 plus 110 ℃, continuously blowing air at the temperature for oxidization until the relative density reaches 0.929-0.930, then adding dichloromethane and manganese naphthenate according to the corresponding weight part ratio, uniformly stirring, and continuously blowing for 35min to obtain the finished product of the paint thinner.
Example 2
This example is substantially the same as the embodiment of example 1, except that: the weight portion ratio of each component is as follows: zeolite powder: 55 parts of (1); linseed oil: 30 parts of (1); sunflower seed oil: 3 parts of a mixture; manganese naphthenate: 1 part; dichloromethane: 0.5 part.
Example 3
This example is substantially the same as the embodiment of example 1, except that: the weight portion ratio of each component is as follows: zeolite powder: 60 parts; linseed oil: 35 parts of (B); sunflower seed oil: 8 parts of a mixture; manganese naphthenate: 4 parts of a mixture; dichloromethane: and 2 parts.
The compound paint thinner disclosed by the invention is reasonable in preparation method, and the prepared paint thinner can meet the dilution requirement and reduce the loss of enterprises and consumers.
Finally, it should be noted that: the above description is only a preferred embodiment of the present invention, and not intended to limit the present invention, and it will be obvious to those skilled in the art that the technical solutions described in the foregoing embodiments may be adjusted, or some technical features may be equivalently replaced, and any modifications, equivalents, improvements, etc. made within the spirit and principle of the present invention should be included in the protection scope of the present invention.
Claims (1)
1. A composite paint thinner, comprising:
(1) the components are as follows: zeolite powder: 55-60 parts; linseed oil: 30-38 parts; sunflower seed oil: 3-8 parts; manganese naphthenate: 1-6 parts; dichloromethane: 0.5-2 parts;
(2) adding zeolite powder, linseed oil and sunflower seed oil into an oxidation kettle according to the corresponding weight part ratio, uniformly stirring, heating to 85 ℃, blowing air into oil through an air pipe to oxidize the oil and automatically heating to 105-110 ℃, continuously blowing air for oxidization at the temperature until the relative density is measured to reach 0.929-0.930, then installing the corresponding weight part ratio, adding dichloromethane and manganese naphthenate, uniformly stirring, and continuously blowing for 35min to obtain the finished product of the oil thinner.