CN111139597A - Polyester laying cloth and preparation method and application thereof - Google Patents
Polyester laying cloth and preparation method and application thereof Download PDFInfo
- Publication number
- CN111139597A CN111139597A CN201911196381.4A CN201911196381A CN111139597A CN 111139597 A CN111139597 A CN 111139597A CN 201911196381 A CN201911196381 A CN 201911196381A CN 111139597 A CN111139597 A CN 111139597A
- Authority
- CN
- China
- Prior art keywords
- cloth
- preparation
- polyester
- drying
- materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a polyester laying cloth and a preparation method and application thereof, wherein the preparation method comprises the following steps: step one, selecting materials: selecting PPS fibers and spun-bonded filament fibers as base materials; step two, cleaning: cleaning the PPS fibers and the spun-bonded filament fibers selected in the step one by a cleaning machine; step three, drying: putting the PPS fibers and the spun-bonded filament fibers cleaned in the second step into a dryer respectively for drying; step four, preparing materials: respectively carrying out air flow drawing on the preparation materials dried in the third step to form a net shape with uniformly laid filaments, and preparing a base cloth layer and a crude fiber layer; step five, superposition: sequentially overlapping the base cloth layer and the coarse fiber layer in the fourth step; step six, prewetting: sending the cloth overlapped in the fifth step to a spunlace area for mesh surface pre-wetting; step seven, softening: and D, soaking the pre-wetted cloth in the step six into a groove with a softening agent for softening.
Description
Technical Field
The invention belongs to the technical field of cloth liner production, and particularly relates to a polyester cloth liner and a preparation method and application thereof.
Background
The polyester is a general term for a polymer obtained by polycondensation of a polyhydric alcohol and a polybasic acid. Mainly polyethylene terephthalate (PET), and conventionally includes linear thermoplastic resins such as polybutylene terephthalate (PBT) and polyarylate. Is an engineering plastic with excellent performance and wide application. It can also be made into polyester fiber and polyester film. Polyesters include polyester resins and polyester elastomers. The polyester resin further includes polyethylene terephthalate (PET), polybutylene terephthalate (PBT), Polyarylate (PAR), and the like. Polyester elastomer (TPEE) is generally polymerized from dimethyl terephthalate, 1, 4-butanediol and polybutanol, the chain segment includes a hard segment part and a soft segment part, and is a thermoplastic elastomer, in the process of manufacturing a tire, a cloth liner is usually used to divide rubber materials placed in a roll.
Disclosure of Invention
The invention aims to provide a polyester laying cloth and a preparation method and application thereof, so as to solve the problems in the background technology.
In order to achieve the purpose, the invention adopts the following technical scheme:
a polyester laying cloth and a preparation method and application thereof comprise the following steps:
step one, selecting materials: selecting PPS fibers and spun-bonded filament fibers as base materials;
step two, cleaning: cleaning the PPS fibers and the spun-bonded filament fibers selected in the step one by a cleaning machine;
step three, drying: putting the PPS fibers and the spun-bonded filament fibers cleaned in the second step into a dryer respectively for drying;
step four, preparing materials: respectively carrying out air flow drawing on the preparation materials dried in the third step to form a net shape with uniformly laid filaments, and preparing a base cloth layer and a crude fiber layer;
step five, superposition: sequentially overlapping the base cloth layer and the coarse fiber layer in the fourth step;
step six, prewetting: sending the cloth overlapped in the fifth step to a spunlace area for mesh surface pre-wetting;
step seven, softening: soaking the pre-wetted cloth in the step six into a groove with a softening agent for softening;
step eight, drying: feeding the cloth softened in the step seven into an oven for drying;
step nine, finished product inspection: and (5) inspecting and packaging the dried cloth in the step eight.
Preferably, the drying temperature in the third step is preferably 120-130 ℃.
Preferably, the softener in the seventh step is one of a fatty oil-based softener and a pine oil-based softener.
Preferably, the softening time in the seventh step is 9-10 minutes.
The invention has the technical effects and advantages that: compared with the prior art, the polyester laying cloth and the preparation method and the application thereof provided by the invention have the following advantages:
the polyester cloth liner PPS fiber prepared by the invention is combined with the spun-bonded filament fiber, and is softened after being compounded, so that the polyester cloth liner has the advantages of temperature resistance and oxidation resistance, and can be applied to various fields.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all embodiments. The specific embodiments described herein are merely illustrative of the invention and do not delimit the invention. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
Example one
A polyester laying cloth and a preparation method and application thereof comprise the following steps:
step one, selecting materials: selecting PPS fibers and spun-bonded filament fibers as base materials;
step two, cleaning: cleaning the PPS fibers and the spun-bonded filament fibers selected in the step one by a cleaning machine;
step three, drying: putting the PPS fibers and the spun-bonded filament fibers cleaned in the second step into a dryer respectively for drying;
step four, preparing materials: respectively carrying out air flow drawing on the preparation materials dried in the third step to form a net shape with uniformly laid filaments, and preparing a base cloth layer and a crude fiber layer;
step five, superposition: sequentially overlapping the base cloth layer and the coarse fiber layer in the fourth step;
step six, prewetting: sending the cloth overlapped in the fifth step to a spunlace area for mesh surface pre-wetting;
step seven, softening: soaking the pre-wetted cloth in the step six into a groove with a softening agent for softening;
step eight, drying: feeding the cloth softened in the step seven into an oven for drying;
step nine, finished product inspection: and (5) inspecting and packaging the dried cloth in the step eight.
Further, the drying temperature in the third step is preferably 120-130 ℃.
Further, the softening agent in the seventh step is one of a fatty oil-based softening agent and a pine oil-based softening agent.
Further, the softening time in the seventh step is preferably 9 to 10 minutes.
The industrial blanket prepared by the invention has the advantages of increased stiffness and density, and the blanket is anti-skid and anti-folding, has smooth surface, namely is not adhered, can be repeatedly used by adding the heat-setting calendering treatment process, improves the economic benefit of enterprises, reduces the investment and has stronger competitiveness in the market.
Finally, it should be noted that: although the present invention has been described in detail with reference to the foregoing embodiments, it will be apparent to those skilled in the art that modifications may be made to the embodiments or portions thereof without departing from the spirit and scope of the invention.
Claims (4)
1. A polyester laying cloth and a preparation method and application thereof are characterized in that: the method comprises the following steps:
step one, selecting materials: selecting PPS fibers and spun-bonded filament fibers as base materials;
step two, cleaning: cleaning the PPS fibers and the spun-bonded filament fibers selected in the step one by a cleaning machine;
step three, drying: putting the PPS fibers and the spun-bonded filament fibers cleaned in the second step into a dryer respectively for drying;
step four, preparing materials: respectively carrying out air flow drawing on the preparation materials dried in the third step to form a net shape with uniformly laid filaments, and preparing a base cloth layer and a crude fiber layer;
step five, superposition: sequentially overlapping the base cloth layer and the coarse fiber layer in the fourth step;
step six, prewetting: sending the cloth overlapped in the fifth step to a spunlace area for mesh surface pre-wetting;
step seven, softening: soaking the pre-wetted cloth in the step six into a groove with a softening agent for softening;
step eight, drying: feeding the cloth softened in the step seven into an oven for drying;
step nine, finished product inspection: and (5) inspecting and packaging the dried cloth in the step eight.
2. The polyester laying cloth as claimed in claim 1, and the preparation method and the application thereof, wherein the drying temperature in the third step is preferably 120-130 ℃.
3. The polyester laying cloth as claimed in claim 1, wherein the softener in the seventh step is one of a fatty oil softener and a pine oil softener.
4. The polyester laying cloth and the preparation method and the application thereof as claimed in claim 1, wherein the softening time in the seventh step is preferably 9-10 minutes.