CN111100518A - Colored iron wall paint - Google Patents
Colored iron wall paint Download PDFInfo
- Publication number
- CN111100518A CN111100518A CN201911426309.6A CN201911426309A CN111100518A CN 111100518 A CN111100518 A CN 111100518A CN 201911426309 A CN201911426309 A CN 201911426309A CN 111100518 A CN111100518 A CN 111100518A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- agent
- component
- iron
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a color iron wall paint which comprises a component A and a component B, wherein the component A comprises the following raw materials in parts by weight: 70-85 parts of ferroferric oxide powder, 3-8 parts of water-based acrylic emulsion, 0.5-2 parts of film-forming additive, 8-10 parts of pearl powder, 3-8 parts of water and 1-2 parts of cross-linking agent; the component B comprises the following raw materials in parts by weight: 0.02 to 0.3 portion of mildew-proof preservative, 0.5 to 3 portions of water-based dispersant, 0.2 to 0.8 portion of organic silicon defoamer, 0.1 to 0.8 portion of thickening agent and 5 to 12 portions of curing agent; the weight ratio of the component A to the component B is as follows: 1: 1; according to the invention, by utilizing the principle that the ferroferric oxide powder can adsorb iron and magnetic products and mixing the water-based acrylic emulsion, the ferroferric oxide powder and the pearl powder to prepare the colored iron-based wall paint, a user can attach other magnetic articles to the wall surface, so that the decorative effect and the personalized effect of the wall surface are enhanced.
Description
Technical Field
The invention relates to the field of wall paint, in particular to color iron wall paint.
Background
The traditional wall paint is coated on the wall surface, and only has the painting effect. The color iron-based wall paint can make the wall surface colorful and has magnetism absorption property only by being coated on the wall surface according to the common painting process, and mainly plays a role in individuation of DIY, so that the color iron-based wall paint is urgently invented to meet the requirements of more customers.
Disclosure of Invention
In order to solve the problems, the invention provides a colored ferrous wall paint.
The invention is realized by the following technical scheme:
the invention provides a color iron wall paint which comprises a component A and a component B, wherein the component A comprises the following raw materials in parts by weight: 70-85 parts of ferroferric oxide powder, 3-8 parts of water-based acrylic emulsion, 0.5-2 parts of film-forming additive, 8-10 parts of pearl powder, 3-8 parts of water and 1-2 parts of cross-linking agent.
The component B comprises the following raw materials in parts by weight: 0.02 to 0.3 portion of mildew-proof preservative, 0.5 to 3 portions of water-based dispersant, 0.2 to 0.8 portion of organic silicon defoamer, 0.1 to 0.8 portion of thickening agent and 5 to 12 portions of curing agent;
the weight ratio of the component A to the component B is as follows: 1: 1.
furthermore, the particle size of the ferroferric oxide powder is 800-1000 meshes.
Further, the ferroferric oxide powder is at least one of ferrosilicon aluminum powder, ferrosilicon aluminum powder and ferrite.
Further, iron silicon powder: ferrite: 30 parts of iron-silicon-aluminum powder: 20: 20.
further, aqueous acrylic emulsion: film-forming auxiliary agent: pearl powder: water: crosslinking agent 5: 0.5: 8: 1.
further, the mildew-proof preservative: aqueous dispersant: and (3) organic silicon defoaming agent: thickening agent: curing agent 0.5: 0.5: 0.5: 1: 5.
further, iron silicon powder: ferrite: aluminum ferrosilicon powder 25: 25: 20.
further, aqueous acrylic emulsion: film-forming auxiliary agent: pearl powder: water: crosslinking agent ═ 3: 9: 8: 1.
further, the mildew-proof preservative: aqueous dispersant: and (3) organic silicon defoaming agent: thickening agent: curing agent 0.5: 0.7: 0.3: 1: 6.
the invention has the beneficial effects that: the color iron wall paint disclosed by the invention is firstly manufactured into an iron wall capable of directly adsorbing any magnetic product/material by utilizing the principle that the ferroferric oxide powder can adsorb iron and magnetic products, a user can attach other magnetic articles to the wall surface to enhance the decorative effect of the wall surface, and the iron wall paint is very easy to use.
Detailed Description
In order to more clearly and completely illustrate the technical scheme of the invention, the invention is further explained as follows:
experimental example 1
The invention provides a colored iron-based wall paint, and ferroferric oxide powder used in the colored iron-based wall paint is ferrosilicon aluminum powder, ferrosilicon aluminum powder and ferrite.
Further, iron silicon powder: ferrite: 30 parts of iron-silicon-aluminum powder: 20: 20.
further, aqueous acrylic emulsion: film-forming auxiliary agent: pearl powder: water: crosslinking agent 5: 0.5: 8: 1.
further, the mildew-proof preservative: aqueous dispersant: and (3) organic silicon defoaming agent: thickening agent: curing agent 0.5: 0.5: 0.5: 1: 5.
in this example, iron silicon powder: 30 parts, ferrite (action: making the particles more uniform): 20 parts of iron-silicon-aluminum powder: 20 parts of water-based acrylic emulsion: 5 parts of efficient film-forming additive: 0.5 part, pearl powder: 8 parts of water: 8 parts, a crosslinking agent: 1 part of antiseptic and mildew-proof agent: 0.5 part, aqueous dispersant: 0.5 part, silicone defoamer: 0.5 part, thickening agent: 1 part, curing agent: 5 parts of the raw materials.
In this embodiment, the aqueous acrylic emulsion in the color iron-based wall paint component can be converted into polyurethane emulsion, and the magnetic powder can be formed by mixing multiple magnetic powders.
In this embodiment, the film-forming agent is dodecanol, the antiseptic and antifungal agent is an isothiazolinone derivative, the dispersant is a fatty acid ethylene oxide adduct, the defoaming agent is silicone oil, the thickener is hydroxyethyl cellulose ether, the curing agent is an isocyanate, and the crosslinking agent is a titanate crosslinking agent.
The characteristics and interrelation of the components are as follows: the iron-silicon-aluminum powder is used as an iron base material, the water-based acrylic emulsion is used as a carrier, and the pearl powder is used as a color component.
The preparation method of the colored iron wall paint comprises the following steps: firstly, mixing iron-silicon powder, soft magnetic ferrite and iron-silicon-aluminum powder, adding a cross-linking agent, putting the mixture into a stirrer together, uniformly mixing at a low speed of 100-200 r/min, then adding an aqueous acrylic emulsion and other additives (including an anti-corrosion mildew inhibitor, an efficient film-forming additive, an aqueous dispersant, a thickening agent, a curing agent and pearl powder), increasing the rotating speed of the stirrer to 1000-20000 r/min, and finally adding an antifoaming agent. The magnetic paint is coated on the wall surface in a roller or spraying mode, so that the wall surface has magnetism and corresponding color.
The color iron wall paint disclosed by the invention is firstly manufactured into an iron wall capable of directly adsorbing any magnetic product/material by utilizing the principle that the ferroferric oxide powder can adsorb iron and magnetic products, a user can attach other magnetic articles to the wall surface to enhance the decorative effect of the wall surface, and the iron wall paint is very easy to use.
Experimental example 2
The invention provides a colored iron-based wall paint, and ferroferric oxide powder used in the colored iron-based wall paint is ferrosilicon aluminum powder, ferrosilicon aluminum powder and ferrite.
Further, iron silicon powder: ferrite: aluminum ferrosilicon powder 25: 25: 20.
further, aqueous acrylic emulsion: film-forming auxiliary agent: pearl powder: water: crosslinking agent ═ 3: 9: 8: 1.
further, the mildew-proof preservative: aqueous dispersant: and (3) organic silicon defoaming agent: thickening agent: curing agent 0.5: 0.7: 0.3: 1: 6.
in this example, iron silicon powder: 25 parts of soft magnetic ferrite, 25 parts of iron-silicon-aluminum powder: 20 parts of water-based acrylic emulsion: 3 parts of efficient film-forming additive: 0.5 part, pearl powder: 9 parts of water: 8 parts, a crosslinking agent: 1 part of antiseptic and mildew-proof agent: 0.5 part, aqueous dispersant: 0.7 part, silicone defoamer: 0.3 part, thickener: 1 part, curing agent: 6 parts.
In this embodiment, the water-based acrylic emulsion in the composition can be mutually converted with the polyurethane emulsion, the magnetic powder can be formed by mutually adding a plurality of magnetic powders, the film-forming aid dodecanol, the antiseptic and mildew-proof agent is an isothiazolinone derivative, the dispersing agent is a fatty acid ethylene oxide adduct, the defoaming agent is organic silicone oil, the thickening agent is hydroxyethyl cellulose ether, the curing agent is isocyanate, and the crosslinking agent is a titanate crosslinking agent.
In the present embodiment, the features and interrelation of the components are as follows: the iron-silicon-aluminum powder is used as an iron base material, the water-based acrylic emulsion is used as a carrier, and the pearl powder is used as a color component.
The preparation method of the colored iron wall paint comprises the following steps: firstly, mixing iron-silicon powder, soft magnetic ferrite and iron-silicon-aluminum powder, adding a cross-linking agent, putting the mixture into a stirrer together, uniformly mixing at a low speed of 100-200 r/min, then adding an aqueous acrylic emulsion and other auxiliaries (including an anti-corrosion mildew inhibitor, an efficient film-forming aid, an aqueous dispersant, a thickening agent, a curing agent and pearl powder), increasing the rotating speed of the stirrer to 1000-20000 r/min, and finally adding an organic silicon defoaming agent. The magnetic paint is coated on the wall surface in a roller or spraying mode, so that the wall surface has magnetism and corresponding color.
The color iron wall paint disclosed by the invention is firstly manufactured into an iron wall capable of directly adsorbing any magnetic product/material by utilizing the principle that the ferroferric oxide powder can adsorb iron and magnetic products, a user can attach other magnetic articles to the wall surface to enhance the decorative effect of the wall surface, and the iron wall paint is very easy to use.
Of course, the present invention may have other embodiments, and based on the embodiments, those skilled in the art can obtain other embodiments without any creative effort, and all of them are within the protection scope of the present invention.
Claims (9)
1. A colored iron wall paint is characterized in that: the adhesive comprises a component A and a component B, wherein the component A comprises the following raw materials in parts by weight: 70-85 parts of ferroferric oxide powder, 3-8 parts of water-based acrylic emulsion, 0.5-2 parts of film-forming additive, 8-10 parts of pearl powder, 3-8 parts of water and 1-2 parts of cross-linking agent;
the component B comprises the following raw materials in parts by weight: 0.02 to 0.3 portion of mildew-proof preservative, 0.5 to 3 portions of water-based dispersant, 0.2 to 0.8 portion of organic silicon defoamer, 0.1 to 0.8 portion of thickening agent and 5 to 12 portions of curing agent;
the weight ratio of the component A to the component B is as follows: 1: 1.
2. the colored ferrous wall paint of claim 1, wherein: the particle size of the ferroferric oxide powder is 800-1000 meshes.
3. The colored ferrous wall paint of claim 1, wherein: the ferroferric oxide powder is at least one of ferrosilicon aluminum powder, ferrosilicon aluminum powder and ferrite.
4. A colored ferrous wall paint according to claim 3, characterized in that: iron-silicon powder: ferrite: 30 parts of iron-silicon-aluminum powder: 20: 20.
5. the colored ferrous wall paint of claim 4, wherein: aqueous acrylic emulsion: film-forming auxiliary agent: pearl powder: water: crosslinking agent 5: 0.5: 8: 1.
6. the colored ferrous wall paint of claim 5, wherein: and (3) mildew-proof preservative: aqueous dispersant: and (3) organic silicon defoaming agent: thickening agent: curing agent 0.5: 0.5: 0.5: 1: 5.
7. a colored ferrous wall paint according to claim 3, characterized in that: iron-silicon powder: ferrite: aluminum ferrosilicon powder 25: 25: 20.
8. the colored ferrous wall paint of claim 7, wherein: aqueous acrylic emulsion: film-forming auxiliary agent: pearl powder: water: crosslinking agent ═ 3: 9: 8: 1.
9. the colored ferrous wall paint of claim 8, wherein: and (3) mildew-proof preservative: aqueous dispersant: and (3) organic silicon defoaming agent: thickening agent: curing agent 0.5: 0.7: 0.3: 1: 6.