CN111092337A - Automobile high-pressure waterproof connector and production process thereof - Google Patents
Automobile high-pressure waterproof connector and production process thereof Download PDFInfo
- Publication number
- CN111092337A CN111092337A CN201911364358.1A CN201911364358A CN111092337A CN 111092337 A CN111092337 A CN 111092337A CN 201911364358 A CN201911364358 A CN 201911364358A CN 111092337 A CN111092337 A CN 111092337A
- Authority
- CN
- China
- Prior art keywords
- silica gel
- pbt
- connecting wire
- waterproof
- conductive connecting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an automobile high-pressure waterproof connector and a production process thereof, wherein the production process comprises the following steps: (1) conducting corona treatment on the conductive connecting wire; (2) drying the PBT material; (3) the conductive connecting wire and the PBT material are subjected to injection molding; (4) brushing glue; (5) adding a silica gel material; (6) adding color paste; (7) processing a PBT shell and a silica gel material; (8) carrying out secondary vulcanization on the silica gel; (9) performing CCD full inspection; (10) and (4) high-pressure waterproof testing. The PBT shell of the connector produced by the invention is tightly combined with the waterproof silica gel ring, and has the advantages of good waterproof performance and durability.
Description
Technical Field
The invention relates to the technical field of mobile phones, in particular to an automobile high-voltage waterproof connector and a production process thereof.
Background
The waterproof connector can be applied to the environment with water, and the mechanical performance and the electrical performance in the connector can be ensured to be normally used under the condition of bearing certain water pressure.
The existing connector is poor in waterproof performance and complex in production process, particularly when glue is brushed, glue brushing is not uniform, whether 100% of positions where the silica gel is required to be attached can not be detected to brush the glue, so that the silica gel material cannot be well bonded on the PBT shell, and the waterproof performance is affected.
Disclosure of Invention
The invention aims to provide a high-pressure waterproof connector for an automobile and a production process thereof aiming at the defects of the prior art, and the connector produced by the process has the advantages of good waterproof performance and durability.
In order to achieve the purpose, the invention provides the following technical scheme:
the invention provides an automobile high-voltage waterproof connector which comprises a conductive connecting wire, a PBT shell coated on the periphery of the conductive connecting wire, and a waterproof silica gel ring arranged on the PBT shell.
The invention also provides a production process of the automobile high-pressure waterproof connector, which comprises the following steps:
(1) conducting corona treatment on the connecting wire: the treatment time is controlled to be 4-5 minutes, the temperature is controlled to be 50 +/-2 ℃, so that the surface of the conductive linking line is activated, and the adhesion with the PBT material is increased;
(2) drying the PBT material: drying at the drying temperature of 110-;
(3) and (3) injection molding processing of the conductive connecting wire and the PBT material: placing the conductive connecting wire into a mold, performing injection molding processing on the conductive connecting wire and the PBT material with an anti-static effect, controlling the temperature of the mold within 90-100 ℃, performing injection molding on the conductive connecting wire and the PBT material to form an integral part, and forming a PBT shell at the periphery of the conductive connecting wire;
(4) brushing glue: adding special glue mixed with 0.8% of fluorescent component outside the PBT shell, brushing the glue at the position where the silica gel is attached, and standing for 30 minutes in a constant-temperature and constant-humidity environment (the temperature is 24-28 ℃ and the humidity is 45% -55%) after the glue is brushed;
(5) adding a silica gel material: the silica gel material was divided into A, B fractions, which were passed through the apparatus at 0.8: 1, uniformly mixing;
(6) adding color paste: adding color paste into the mixed solution, wherein the adding proportion of the color paste is 3 percent of the total sum of the A, B components of the silica gel material;
(7) processing a PBT shell and a silica gel material: placing the conductive connecting wire coated with the PBT shell into a mold, performing injection molding processing on the conductive connecting wire and a silica gel material, and performing injection molding on the PBT shell to form a waterproof silica gel ring;
(8) and (3) silica gel secondary vulcanization: vulcanizing the waterproof silica gel ring for the second time, wherein the vulcanization temperature is 120 ℃, and the vulcanization time is 2 hours, so that the silica gel part of the product reaches a 100& vulcanization state;
(9) and (4) CCD full inspection: adjusting the CCD inspection equipment to be amplified by 50 times, and inspecting whether the waterproof silica gel ring is damaged or not and detecting the bubble defect;
(10) high-pressure waterproof test: the connector carries out high-pressure waterproof test, and the test condition is: the air pressure is 0.1Mpa, the air pressure detection time is 5s, and the leakage quantity is 0.01Mpa, so as to detect the waterproof performance of the connector.
Preferably, the glue amount in the step (4) is 0.035 to 0.045 g.
Preferably, the special glue in the step (4) is any one of SI-956-1 silica gel adhesive, silica gel adhesive and YB-827 adhesive.
Preferably, the silica gel material A in the step (5) comprises the following components: CHN-LIMS-60-A, B component is: CHN-LIMS-60-B.
Preferably, the temperature of the mold in the step (7) is set at 130 ℃ and 120 ℃, the thermal curing time is 35s, and the size tolerance of the silica gel product is +/-0.03 mm.
Compared with the prior art, the invention has the beneficial effects that: the PBT shell of the connector produced by the invention is tightly combined with the waterproof silica gel ring, and has the advantages of good waterproof performance and durability.
Drawings
Fig. 1 is a schematic structural view of a high-pressure waterproof connector according to the present invention;
in the figure, 1 is a conductive connecting wire, 2 is a PBT shell and 3 is a waterproof silica gel ring.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
The invention provides an automobile high-voltage waterproof connector which comprises a conductive connecting wire 1, a PBT shell 2 coated on the periphery of the conductive connecting wire 1, and a waterproof silica gel ring 3 arranged on the PBT shell 2.
The invention also provides a production process of the automobile high-pressure waterproof connector.
Example 1
A production process of an automobile high-pressure waterproof connector comprises the following steps:
(1) conducting corona treatment on the connecting wire: the treatment time is controlled to be 4-5 minutes, the temperature is controlled to be 50 +/-2 ℃, so that the surface of the conductive linking line is activated, and the adhesion with the PBT material is increased;
(2) drying the PBT material: drying at 110 ℃ for 4 hours, and drying the water contained in the PBT material;
(3) and (3) injection molding processing of the conductive connecting wire and the PBT material: placing the conductive connecting wire into a mold, performing injection molding processing on the conductive connecting wire and a PBT material with an anti-static effect, controlling the temperature of the mold within 90-100 ℃, performing injection molding on the conductive connecting wire and the PBT material to form an integral part, and forming a PBT shell at the periphery of the conductive connecting wire so as to achieve the sealing and anti-static effects;
(4) brushing glue: adding special glue mixed with 0.8% of fluorescent component outside the PBT shell, wherein the special glue is any one of SI-956-1 silica gel adhesive, silica gel adhesive and YB-827 adhesive; the glue amount is 0.035 g, the glue must be brushed to the position that silica gel adheres to, add phosphor powder can detect whether 100% of the position that needs silica gel to adhere to brush the glue, need to keep standstill for 30 minutes in the environment of 24 degrees C of temperature and humidity 45% at constant temperature and humidity after brushing the glue, make the glue ingredient permeate to PBT outer cover completely;
(5) adding a silica gel material: the silica gel material was divided into A, B fractions, which were passed through the apparatus at 0.8: 1, uniformly mixing; wherein the component A is as follows: CHN-LIMS-60-A, B component is: CHN-LIMS-60-B;
(6) adding color paste: adding color paste into the mixed solution, wherein the adding proportion of the color paste is 3 percent of the total sum of the A, B components of the silica gel material, and adding specific color into the product;
(7) processing a PBT shell and a silica gel material: placing the conductive connecting wire coated with the PBT shell into a mold, performing injection molding processing on the conductive connecting wire and a silica gel material, and performing injection molding on the PBT shell to form a waterproof silica gel ring; wherein the temperature of the die is set at 120 ℃, the thermosetting time is 35s, and the dimensional tolerance of the silica gel product is +/-0.03 mm;
(8) and (3) silica gel secondary vulcanization: vulcanizing the waterproof silica gel ring for the second time, wherein the vulcanization temperature is 120 ℃, and the vulcanization time is 2 hours, so that the silica gel part of the product reaches a 100& vulcanization state;
(9) and (4) CCD full inspection: adjusting the CCD inspection equipment to be amplified by 50 times, and inspecting whether the waterproof silica gel ring is damaged or not and detecting the bubble defect;
(10) high-pressure waterproof test: the connector carries out high-pressure waterproof test, and the test condition is: the air pressure is 0.1Mpa, the air pressure detection time is 5s, and the leakage quantity is 0.01Mpa, so as to detect the waterproof performance of the connector.
Example 2
A production process of an automobile high-pressure waterproof connector comprises the following steps:
(1) conducting corona treatment on the connecting wire: the treatment time is controlled to be 4-5 minutes, the temperature is controlled to be 50 +/-2 ℃, so that the surface of the conductive linking line is activated, and the adhesion with the PBT material is increased;
(2) drying the PBT material: drying at 115 ℃ for 4 hours, and drying the water contained in the PBT material;
(3) and (3) injection molding processing of the conductive connecting wire and the PBT material: placing the conductive connecting wire into a mold, performing injection molding processing on the conductive connecting wire and a PBT material with an anti-static effect, controlling the temperature of the mold within 90-100 ℃, performing injection molding on the conductive connecting wire and the PBT material to form an integral part, and forming a PBT shell at the periphery of the conductive connecting wire so as to achieve the sealing and anti-static effects;
(4) brushing glue: adding special glue mixed with 0.8% of fluorescent component outside the PBT shell, wherein the special glue is any one of SI-956-1 silica gel adhesive, silica gel adhesive and YB-827 adhesive; the glue amount is 0.04 g, the glue is required to be brushed at the position where the silica gel is attached, the fluorescent powder is added to detect whether the glue is brushed at the position where the silica gel is required to be attached by 100%, and the glue is required to be kept stand for 30 minutes at a constant temperature and humidity in an environment with the temperature of 26 ℃ and the humidity of 50% after being brushed so that the glue component can be completely permeated into the PBT shell;
(5) adding a silica gel material: the silica gel material was divided into A, B fractions, which were passed through the apparatus at 0.8: 1, uniformly mixing; wherein the component A is as follows: CHN-LIMS-60-A, B component is: CHN-LIMS-60-B;
(6) adding color paste: adding color paste into the mixed solution, wherein the adding proportion of the color paste is 3 percent of the total sum of the A, B components of the silica gel material, and adding specific color into the product;
(7) processing a PBT shell and a silica gel material: placing the conductive connecting wire coated with the PBT shell into a mold, performing injection molding processing on the conductive connecting wire and a silica gel material, and performing injection molding on the PBT shell to form a waterproof silica gel ring; wherein the temperature of the die is set at 120 ℃, the thermosetting time is 35s, and the dimensional tolerance of the silica gel product is +/-0.03 mm;
(8) and (3) silica gel secondary vulcanization: vulcanizing the waterproof silica gel ring for the second time, wherein the vulcanization temperature is 120 ℃, and the vulcanization time is 2 hours, so that the silica gel part of the product reaches a 100& vulcanization state;
(9) and (4) CCD full inspection: adjusting the CCD inspection equipment to be amplified by 50 times, and inspecting whether the waterproof silica gel ring is damaged or not and detecting the bubble defect;
(10) high-pressure waterproof test: the connector carries out high-pressure waterproof test, and the test condition is: the air pressure is 0.1Mpa, the air pressure detection time is 5s, and the leakage quantity is 0.01Mpa, so as to detect the waterproof performance of the connector.
Example 3
A production process of an automobile high-pressure waterproof connector comprises the following steps:
(1) conducting corona treatment on the connecting wire: the treatment time is controlled to be 4-5 minutes, the temperature is controlled to be 50 +/-2 ℃, so that the surface of the conductive linking line is activated, and the adhesion with the PBT material is increased;
(2) drying the PBT material: drying at 120 ℃ for 4 hours, and drying the water contained in the PBT material;
(3) and (3) injection molding processing of the conductive connecting wire and the PBT material: placing the conductive connecting wire into a mold, performing injection molding processing on the conductive connecting wire and a PBT material with an anti-static effect, controlling the temperature of the mold within 90-100 ℃, performing injection molding on the conductive connecting wire and the PBT material to form an integral part, and forming a PBT shell at the periphery of the conductive connecting wire so as to achieve the sealing and anti-static effects;
(4) brushing glue: adding special glue mixed with 0.8% of fluorescent component outside the PBT shell, wherein the special glue is any one of SI-956-1 silica gel adhesive, silica gel adhesive and YB-827 adhesive; the glue amount is 0.045 g, the glue is required to be brushed at the position where the silica gel is attached, the fluorescent powder is added to detect whether the glue is brushed at the position where the silica gel is required to be attached by 100%, the glue is required to be kept stand for 30 minutes at a constant temperature and humidity after being brushed, and the glue is enabled to completely permeate into the PBT shell at the temperature of 28 ℃ and the humidity of 55%;
(5) adding a silica gel material: the silica gel material was divided into A, B fractions, which were passed through the apparatus at 0.8: 1, uniformly mixing; wherein the component A is as follows: CHN-LIMS-60-A, B component is: CHN-LIMS-60-B;
(6) adding color paste: adding color paste into the mixed solution, wherein the adding proportion of the color paste is 3 percent of the total sum of the A, B components of the silica gel material, and adding specific color into the product;
(7) processing a PBT shell and a silica gel material: placing the conductive connecting wire coated with the PBT shell into a mold, performing injection molding processing on the conductive connecting wire and a silica gel material, and performing injection molding on the PBT shell to form a waterproof silica gel ring; wherein the temperature of the die is set at 120 ℃, the thermosetting time is 35s, and the dimensional tolerance of the silica gel product is +/-0.03 mm;
(8) and (3) silica gel secondary vulcanization: vulcanizing the waterproof silica gel ring for the second time, wherein the vulcanization temperature is 120 ℃, and the vulcanization time is 2 hours, so that the silica gel part of the product reaches a 100& vulcanization state;
(9) and (4) CCD full inspection: adjusting the CCD inspection equipment to be amplified by 50 times, and inspecting whether the waterproof silica gel ring is damaged or not and detecting the bubble defect;
(10) high-pressure waterproof test: the connector carries out high-pressure waterproof test, and the test condition is: the air pressure is 0.1Mpa, the air pressure detection time is 5s, and the leakage quantity is 0.01Mpa, so as to detect the waterproof performance of the connector.
It is to be noted that the terms "comprises," "comprising," or any other variation thereof, are intended to cover a non-exclusive inclusion, such that a process, method, article, or apparatus that comprises a list of elements does not include only those elements but may include other elements not expressly listed or inherent to such process, method, article, or apparatus. Without further limitation, an element defined by the phrase "comprising an … …" does not exclude the presence of other identical elements in a process, method, article, or apparatus that comprises the element.
Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (6)
1. The high-voltage waterproof connector for the automobile is characterized by comprising a conductive connecting wire, a PBT shell coated on the periphery of the conductive connecting wire and a waterproof silica gel ring arranged on the PBT shell.
2. The production process of the automobile high-pressure waterproof connector is characterized by comprising the following steps of:
(1) conducting corona treatment on the connecting wire: the treatment time is controlled to be 4-5 minutes, the temperature is controlled to be 50 +/-2 ℃, so that the surface of the conductive linking line is activated, and the adhesion with the PBT material is increased;
(2) drying the PBT material: drying at the drying temperature of 110-;
(3) and (3) injection molding processing of the conductive connecting wire and the PBT material: placing the conductive connecting wire into a mold, performing injection molding processing on the conductive connecting wire and a PBT material with an anti-static effect, controlling the temperature of the mold within 90-100 ℃, performing injection molding on the conductive connecting wire and the PBT material to form an integral part, and forming a PBT shell at the periphery of the conductive connecting wire so as to achieve the sealing and anti-static effects;
(4) brushing glue: adding special glue mixed with 0.8% of fluorescent component outside the PBT shell, brushing the glue at the position where the silica gel is attached, and standing for 30 minutes in a constant-temperature and constant-humidity environment (the temperature is 24-28 ℃ and the humidity is 45% -55%) after the glue is brushed;
(5) adding a silica gel material: the silica gel material was divided into A, B fractions, which were passed through the apparatus at 0.8: 1, uniformly mixing;
(6) adding color paste: adding color paste into the mixed solution, wherein the adding proportion of the color paste is 3 percent of the total sum of the A, B components of the silica gel material, and adding specific color into the product;
(7) processing a PBT shell and a silica gel material: placing the conductive connecting wire coated with the PBT shell into a mold, performing injection molding processing on the conductive connecting wire and a silica gel material, and performing injection molding on the PBT shell to form a waterproof silica gel ring;
(8) and (3) silica gel secondary vulcanization: vulcanizing the waterproof silica gel ring for the second time, wherein the vulcanization temperature is 120 ℃, and the vulcanization time is 2 hours, so that the silica gel part of the product reaches a 100& vulcanization state;
(9) and (4) CCD full inspection: adjusting the CCD inspection equipment to be amplified by 50 times, and inspecting whether the waterproof silica gel ring is damaged or not and detecting the bubble defect;
(10) high-pressure waterproof test: the connector carries out high-pressure waterproof test, and the test condition is: the air pressure is 0.1Mpa, the air pressure detection time is 5s, and the leakage quantity is 0.01Mpa, so as to detect the waterproof performance of the connector.
3. The process for producing a high-pressure waterproof connector for automobiles as claimed in claim 2, wherein the amount of glue used in step (4) is 0.035 to 0.045 g.
4. The production process of the high-pressure waterproof connector for the automobile as claimed in claim 2, wherein the special glue in the step (4) is any one of SI-956-1 silica gel adhesive, silica gel adhesive and YB-827 adhesive.
5. The production process of the automobile high-pressure waterproof connector according to claim 2, wherein the component A of the silica gel material in the step (5) is: CHN-LIMS-60-A, B component is: CHN-LIMS-60-B.
6. The process for producing a high-pressure waterproof connector of an automobile as claimed in claim 2, wherein the mold temperature in step (7) is set at 130 ℃ C.120, the thermosetting time is 35s, and the dimensional tolerance of the silica gel product is + -0.03 mm.