CN111055557A - 一种新型复合面料，及其制作工艺 - Google Patents

一种新型复合面料，及其制作工艺 Download PDF

Info

Publication number
CN111055557A
CN111055557A CN201911356718.3A CN201911356718A CN111055557A CN 111055557 A CN111055557 A CN 111055557A CN 201911356718 A CN201911356718 A CN 201911356718A CN 111055557 A CN111055557 A CN 111055557A
Authority
CN
China
Prior art keywords
layer
parts
composite fabric
bonding
sewing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201911356718.3A
Other languages
English (en)
Inventor
高晓航
陈文娟
张奇芳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujian Honggang Textile Technology Co ltd
Original Assignee
Fujian Honggang Textile Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujian Honggang Textile Technology Co ltd filed Critical Fujian Honggang Textile Technology Co ltd
Priority to CN201911356718.3A priority Critical patent/CN111055557A/zh
Publication of CN111055557A publication Critical patent/CN111055557A/zh
Pending legal-status Critical Current

Abstract

本发明属于纺织面料技术领域，尤其涉及一种新型复合面料，及其制作工艺。本发明通过贴身面料由内及外依次为吸脂杀菌层、内侧混纺层、粘结缝制层、外侧混纺层以及空气抑菌层的方式，达到面料内外两侧针对性杀菌抑菌的效果。本发明具有复合面料内外侧针对性杀菌效果好，内侧针对性杀灭绿脓杆菌、外侧针对性杀灭脑膜炎球菌和结核杆菌，内侧吸收油脂后易透过排出，两层式混纺布料牢固，粘结缝制组合的连接方式透气性好、方便油脂排出，以及复合面料整体制作工艺简单有效的优点。

Description

一种新型复合面料，及其制作工艺
技术领域
本发明属于纺织面料技术领域，尤其涉及一种新型复合面料，及其制作工艺。
背景技术
复合面料，指的是一类至少具有两项有益效果的多层面料组合，例如兼具防风、抗菌、阻燃以及防静电等功能。另一方面，现有的抗菌面料其抗菌层仅仅涂在面料外侧面，因此该面料用于贴身穿时，对皮肤上的细菌就缺少针对性的抗菌杀菌效果，所以市场上急需一种根据空气中和皮肤上主体细菌不同的特性，进行内外两侧针对性抗菌的新型复合面料。
专利公开号为CN 110385900A，公开日为2019.10.29的中国发明专利公开了一种抗菌复合面料，包括面料层和防水膜层，所述面料层和防水膜层之间设置有胶黏层，所述防水膜层为抗菌TPU膜层；所述胶黏层包括1-10wt%的阻燃型环氧树脂和90-99wt%的热熔胶，且所述面料层经由阻燃整理剂进行阻燃整理。
但是该发明专利中的抗菌复合面料存在抗菌效果不全面的问题。
发明内容
本发明的目的是提供一种新型复合面料，及其制作工艺，其能通过贴身面料由内及外依次为吸脂杀菌层、内侧混纺层、粘结缝制层、外侧混纺层以及空气抑菌层的方式，达到面料内外两侧针对性杀菌抑菌的效果。本发明具有复合面料内外侧针对性杀菌效果好，内侧针对性杀灭绿脓杆菌、外侧针对性杀灭脑膜炎球菌和结核杆菌，内侧吸收油脂后易透过排出，两层式混纺布料牢固，粘结缝制组合的连接方式透气性好、方便油脂排出，以及复合面料整体制作工艺简单有效的优点。
本发明解决上述问题采用的技术方案是：一种新型复合面料，由内及外依次为吸脂杀菌层、内侧混纺层、粘结缝制层、外侧混纺层以及空气抑菌层，所述吸脂杀菌层的物料组成包括聚乙烯吡咯烷酮碘、三苯甲咪唑、乙酰壳多糖、茴香油、多孔填料、热固型丙烯酸树脂粘结剂、亲肤剂以及去离子水，以用于吸收并挥发油脂，和杀灭绿脓杆菌，所述空气抑菌层的物料组成包括载银膨润土、载银磷酸钙、复合硅胶抗菌剂、粘结硅胶以及去离子水，以用于杀灭脑膜炎球菌和结核杆菌。
在本发明中，皮肤上主要致病菌为绿脓杆菌，因此针对性地采用聚乙烯吡咯烷酮碘作为碘化物抑菌剂，采用三苯甲咪唑作为咪唑类杀菌剂，以用于阻断绿脓杆菌拟核区裸露DNA的转录。另一方面，面料外侧主要接触空气，因此所述载银膨润土以及载银磷酸钙通过银类杀菌剂的方式，杀灭空气细菌中主要的脑膜炎球菌和结核杆菌，但是该银类杀菌剂则对绿脓杆菌的杀菌抑菌效果一般，因此采用内外差别的针对性杀菌方式，可以达到内外侧针对性杀菌效果突出的优点。
进一步优选的技术方案在于：所述多孔填料为纳米级多孔碳化硅、纳米级多孔聚乙烯颗粒以及纳米级多孔氧化锆中的任意一种或其混合物；所述亲肤剂包括芦荟萃取物、洋金菊萃取物，以及用作萃取物基底的环状烯烃类聚合物。
在本发明中，所述多孔填料用于给油脂外排提供通道，保证复合面料的透气性和开孔透油脂效果，此外所述亲肤剂以所述环状烯烃类聚合物打底，混合多种天然植物萃取物，可以进一步保证所述复合面料在贴身穿着时的安全性和舒适性。
此外，纳米级的所述多孔填料，其粒径为25-560nm，通过其自身细腻的触感，来减轻所述吸脂杀菌层中固体颗粒感对皮肤的摩擦触感。
进一步优选的技术方案在于：所述复合硅胶抗菌剂为羧甲基壳聚糖、甲壳素以及医用硅胶的三者的共聚物。
在本发明中，所述复合硅胶抗菌剂兼具抗菌抑菌，和粘结效果，保证整个所述空气抑菌层的混合粘结强度，避免出现自身分离剥落的问题。
进一步优选的技术方案在于所述吸脂杀菌层包括按重量计的以下各组分：聚乙烯吡咯烷酮碘1-6份、三苯甲咪唑0.5-7.0份、乙酰壳多糖1-3份、茴香油3-4份、多孔填料5-8份、热固型丙烯酸树脂粘结剂45-65份、亲肤剂1-2份以及去离子水15-19份。
进一步优选的技术方案在于所述空气抑菌层（5）包括按重量计的以下各组分：载银膨润土1-2份、载银磷酸钙1-3份、复合硅胶抗菌剂5-6份、粘结硅胶25-30份以及去离子水11-15份。
进一步优选的技术方案在于所述吸脂杀菌层物料的制备方法依次包括以下步：
S1、在搅拌反应釜中添加，占总量1/3的去离子水，并加热至45-52℃，保持200-260r/min的搅拌速率，依次添加所述聚乙烯吡咯烷酮碘、三苯甲咪唑、乙酰壳多糖以及茴香油，搅拌混合均匀，得到基料；
S2、将所述基料升温至65-70℃，添加热固型丙烯酸树脂粘结剂后保持搅拌5-6min，然后连续加入多孔填料，加入时间为2-3min，搅拌混合均匀，得到高密度中间料；
S3、以2-2.5℃/min的速率降温，并在35℃之间添加完剩下2/3的去离子水，搅拌混合均匀后冷却至室温，得到最后的所述吸脂杀菌层的待涂布物料。
在本发明中，所述多孔填料在混合中期加入，可以很好地避免其抢先与所述聚乙烯吡咯烷酮碘以及三苯甲咪唑集聚的问题，保证固体颗粒质地的所述多孔填料可以迅速混合，且混合均匀。
此外，所述多孔填料添加后，若温度下降的太快，则所述多孔填料之间、所述多孔填料与所述聚乙烯吡咯烷酮碘以及三苯甲咪唑的氢键之间就会出现团聚现象，因此上述2-2.5℃/min的速率降温可以很好地保证混合系统的长期均匀性，而所述去离子水分批加入，则用于主动降温，避免温度下降过慢的问题。
进一步优选的技术方案在于：步骤S2中，所述多孔填料采用插入管伸至液面5cm以下区域，并以空气鼓风吹入方式添加，所述多孔填料添加过程中搅拌速率为450-750r/min。
在本发明中，所述多孔填料若直接倾倒在所述基料页面上，则其外表面被完全润湿包裹的时间则大大延长，因此会增加其自身团聚的危险，所以采用上述空气鼓风吹入的方式，保证所述多孔填料直接“打入”液面以下，采用快速润湿的方式保证均匀混合。
进一步优选的技术方案在于：所述吸脂杀菌层（1）的厚度为0.10-0.15mm，涂布量为15-16g/m2，所述空气抑菌层（5）的厚度为0.20-0.35mm，涂布量为42-55g/m2。
进一步优选的技术方案在于：所述内侧混纺层为天丝纤维和羊毛纤维的混纺布料；所述外侧混纺层为天丝纤维和聚酯纤维的混纺布料；所述粘结缝制层包括平行间隔设置的粘结剂条带，以及在所述粘结剂条带之间设置的缝制线，所述缝制线在所述内侧混纺层上的针刺缝制深度小于在所述外侧混纺层上的针刺缝制深度。
在本发明中，所述天丝纤维以及羊毛纤维的组合，具有相对较好的亲肤效果，而所述粘结缝制层采用聚氨酯型粘结剂形成所述粘结剂条带，并间隔针织所述缝制线，保证整体连接强度和透气性效果，保证油脂吸收后可以快速排出，这是现有的全涂层的复合面料所做不到的。
此外，由于所述羊毛纤维与聚氨酯型粘结剂的粘结强度大于所述聚酯纤维，因此其针刺缝制深度就可以相对较小，最终保证内侧粘结强度一直，这样所述复合面料拉扯时内外侧受力形变幅度协调一致，保证所述复合面料的穿着耐久性。
一种新型复合面料的制作工艺，依次包括以下步骤：
步骤1、分别独立混纺编织所述内侧混纺层以及外侧混纺层，混合配制所述吸脂杀菌层以及空气抑菌层，并待用；
骤2、通过交替缝制和粘结的方式，在所述内侧混纺层和所述外侧混纺层之间形成所述粘结缝制层；
步骤3、在所述内侧混纺层上涂布所述吸脂杀菌层、在所述外侧混纺层上涂布所述空气抑菌层，形成最终的所述新型复合面料，
其中，所述空气抑菌层的混合温度为25-60℃，充分混合后冷却至室温带用，所述吸脂杀菌层以及空气抑菌层的涂布温度为65-75℃，涂布压力为75-225kg/cm2，采用网纹辊涂布方式进行。
在本发明中，所述吸脂杀菌层以及空气抑菌层采用网纹辊涂布方式先后在内侧混纺层、粘结缝制层以及外侧混纺层三层结构上涂布，最终固化定型后，即为最终成型的所述复合面料，具有内外侧针对性杀菌、内侧吸脂快速外排以及整体穿着强度大、舒适性好的多个突出特点。
本发明通过贴身面料由内及外依次为吸脂杀菌层、内侧混纺层、粘结缝制层、外侧混纺层以及空气抑菌层的方式，达到面料内外两侧针对性杀菌抑菌的效果。本发明具有复合面料内外侧针对性杀菌效果好，内侧针对性杀灭绿脓杆菌、外侧针对性杀灭脑膜炎球菌和结核杆菌，内侧吸收油脂后易透过排出，两层式混纺布料牢固，粘结缝制组合的连接方式透气性好、方便油脂排出，以及复合面料整体制作工艺简单有效的优点。
附图说明
图1为本发明中新型复合面料的多层结构示意图。
图2为本发明中粘结缝制层的结构示意图。
具体实施方式
以下所述仅为本发明的较佳实施例，非对本发明的范围进行限定。
实施例1
如附图1以及附图2所示，一种新型复合面料，由内及外依次为吸脂杀菌层1、内侧混纺层2、粘结缝制层3、外侧混纺层4以及空气抑菌层5，所述吸脂杀菌层1的物料组成包括聚乙烯吡咯烷酮碘、三苯甲咪唑、乙酰壳多糖、茴香油、多孔填料、热固型丙烯酸树脂粘结剂、亲肤剂以及去离子水，以用于吸收并挥发油脂，和杀灭绿脓杆菌，所述空气抑菌层5的物料组成包括载银膨润土、载银磷酸钙、复合硅胶抗菌剂、粘结硅胶以及去离子水，以用于杀灭脑膜炎球菌和结核杆菌。
所述多孔填料为纳米级多孔碳化硅；所述亲肤剂包括芦荟萃取物、洋金菊萃取物，以及用作萃取物基底的环状烯烃类聚合物。
所述复合硅胶抗菌剂为羧甲基壳聚糖、甲壳素以及医用硅胶的三者的共聚物。
所述吸脂杀菌层1包括按重量计的以下各组分：聚乙烯吡咯烷酮碘1份、三苯甲咪唑0.5份、乙酰壳多糖1份、茴香油3份、多孔填料5份、热固型丙烯酸树脂粘结剂45份、亲肤剂1份以及去离子水15份。
所述空气抑菌层5包括按重量计的以下各组分：载银膨润土1份、载银磷酸钙2份、复合硅胶抗菌剂5份、粘结硅胶25份以及去离子水11份。
所述吸脂杀菌层1物料的制备方法依次包括以下步：
S1、在搅拌反应釜中添加，占总量1/3的去离子水，并加热至45℃，保持200r/min的搅拌速率，依次添加所述聚乙烯吡咯烷酮碘、三苯甲咪唑、乙酰壳多糖以及茴香油，搅拌混合均匀，得到基料；
S2、将所述基料升温至65℃，添加热固型丙烯酸树脂粘结剂后保持搅拌5min，然后连续加入多孔填料，加入时间为2min，搅拌混合均匀，得到高密度中间料；
S3、以2℃/min的速率降温，并在35℃之间添加完剩下2/3的去离子水，搅拌混合均匀后冷却至室温，得到最后的所述吸脂杀菌层1的待涂布物料。
步骤S2中，所述多孔填料采用插入管伸至液面5cm以下区域，并以空气鼓风吹入方式添加，所述多孔填料添加过程中搅拌速率为450r/min。
所述吸脂杀菌层1的厚度为0.10mm，密度为15g/m2，所述空气抑菌层5的厚度为0.20mm，涂布量为42g/m2。
所述内侧混纺层2为天丝纤维和羊毛纤维的混纺布料；所述外侧混纺层4为天丝纤维和聚酯纤维的混纺布料；所述粘结缝制层3包括平行间隔设置的粘结剂条带301，以及在所述粘结剂条带301之间设置的缝制线302，所述缝制线302在所述内侧混纺层2上的针刺缝制深度小于在所述外侧混纺层4上的针刺缝制深度。
一种新型复合面料的制作工艺，依次包括以下步骤：
步骤1、分别独立混纺编织所述内侧混纺层2以及外侧混纺层4，混合配制所述吸脂杀菌层1以及空气抑菌层5，并待用；
步骤2、通过交替缝制和粘结的方式，在所述内侧混纺层2和所述外侧混纺层4之间形成所述粘结缝制层3；
步骤3、在所述内侧混纺层2上涂布所述吸脂杀菌层1、在所述外侧混纺层4上涂布所述空气抑菌层5，形成最终的所述新型复合面料，
其中，所述空气抑菌层5的混合温度为25℃，充分混合后冷却至室温带用，所述吸脂杀菌层1以及空气抑菌层5的涂布温度为65℃，涂布压力为115kg/cm2，采用网纹辊涂布方式进行。
在本实施例中，对最终获得的所述新型复合面料进行抗菌抑菌检测，检测依据和方法为：GB/T 20944.3-2008振荡法，所述新型复合面料采用内侧混纺层2、粘结缝制层3以及外侧混纺层4为面料基底层，单独涂布所述吸脂杀菌层1后检测绿脓杆菌、单独涂布所述空气抑菌层5后检测脑膜炎球菌和结核杆菌的方式进行，检测结果如下。
Figure DEST_PATH_IMAGE002
根据上表显示，所述吸脂杀菌层1以及空气抑菌层5具有针对性杀菌率高达99%，交叉杀菌率高于60%的优越性能，因此证明本实施例中所述吸脂杀菌层1以及空气抑菌层5针对性地内侧、外侧分别涂布方式具有针对性杀菌效果好的优点，明显高于任意一种成分内外侧统一涂布的方式。
实施例2
如附图1以及附图2所示，一种新型复合面料，由内及外依次为吸脂杀菌层1、内侧混纺层2、粘结缝制层3、外侧混纺层4以及空气抑菌层5，所述吸脂杀菌层1的物料组成包括聚乙烯吡咯烷酮碘、三苯甲咪唑、乙酰壳多糖、茴香油、多孔填料、热固型丙烯酸树脂粘结剂、亲肤剂以及去离子水，以用于吸收并挥发油脂，和杀灭绿脓杆菌，所述空气抑菌层5的物料组成包括载银膨润土、载银磷酸钙、复合硅胶抗菌剂、粘结硅胶以及去离子水，以用于杀灭脑膜炎球菌和结核杆菌。
所述多孔填料为纳米级多孔聚乙烯颗粒；所述亲肤剂包括芦荟萃取物、洋金菊萃取物，以及用作萃取物基底的环状烯烃类聚合物。
所述复合硅胶抗菌剂为羧甲基壳聚糖、甲壳素以及医用硅胶的三者的共聚物。
所述吸脂杀菌层1包括按重量计的以下各组分：聚乙烯吡咯烷酮碘2份、三苯甲咪唑3份、乙酰壳多糖2份、茴香油3份、多孔填料6份、热固型丙烯酸树脂粘结剂60份、亲肤剂1份以及去离子水18份。
所述空气抑菌层5包括按重量计的以下各组分：载银膨润土2份、载银磷酸钙3份、复合硅胶抗菌剂5份、粘结硅胶28份以及去离子水13份。
所述吸脂杀菌层1物料的制备方法依次包括以下步：
S1、在搅拌反应釜中添加，占总量1/3的去离子水，并加热至50℃，保持240r/min的搅拌速率，依次添加所述聚乙烯吡咯烷酮碘、三苯甲咪唑、乙酰壳多糖以及茴香油，搅拌混合均匀，得到基料；
S2、将所述基料升温至68℃，添加热固型丙烯酸树脂粘结剂后保持搅拌5min，然后连续加入多孔填料，加入时间为2min，搅拌混合均匀，得到高密度中间料；
S3、以2℃/min的速率降温，并在35℃之间添加完剩下2/3的去离子水，搅拌混合均匀后冷却至室温，得到最后的所述吸脂杀菌层1的待涂布物料。
步骤S2中，所述多孔填料采用插入管伸至液面5cm以下区域，并以空气鼓风吹入方式添加，所述多孔填料添加过程中搅拌速率为450r/min。
所述吸脂杀菌层1的厚度为0.10mm，密度为16g/m2，所述空气抑菌层5的厚度为0.20mm，涂布量为50g/m2。
所述内侧混纺层2为天丝纤维和羊毛纤维的混纺布料；所述外侧混纺层4为天丝纤维和聚酯纤维的混纺布料；所述粘结缝制层3包括平行间隔设置的粘结剂条带301，以及在所述粘结剂条带301之间设置的缝制线302，所述缝制线302在所述内侧混纺层2上的针刺缝制深度小于在所述外侧混纺层4上的针刺缝制深度。
一种新型复合面料的制作工艺，依次包括以下步骤：
步骤1、分别独立混纺编织所述内侧混纺层2以及外侧混纺层4，混合配制所述吸脂杀菌层1以及空气抑菌层5，并待用；
步骤2、通过交替缝制和粘结的方式，在所述内侧混纺层2和所述外侧混纺层4之间形成所述粘结缝制层3；
步骤3、在所述内侧混纺层2上涂布所述吸脂杀菌层1、在所述外侧混纺层4上涂布所述空气抑菌层5，形成最终的所述新型复合面料，
其中，所述空气抑菌层5的混合温度为45℃，充分混合后冷却至室温带用，所述吸脂杀菌层1以及空气抑菌层5的涂布温度为70℃，涂布压力为200kg/cm2，采用网纹辊涂布方式进行。
在本实施例中，对最终获得的所述新型复合面料进行抗菌抑菌检测，检测依据和方法为：GB/T 20944.3-2008振荡法，所述新型复合面料采用内侧混纺层2、粘结缝制层3以及外侧混纺层4为面料基底层，单独涂布所述吸脂杀菌层1后检测绿脓杆菌、单独涂布所述空气抑菌层5后检测脑膜炎球菌和结核杆菌的方式进行，检测结果如下。
Figure DEST_PATH_IMAGE004
根据上表显示，所述吸脂杀菌层1以及空气抑菌层5具有针对性杀菌率高达99%，交叉杀菌率高于60%的优越性能，因此证明本实施例中所述吸脂杀菌层1以及空气抑菌层5针对性地内侧、外侧分别涂布方式具有针对性杀菌效果好的优点，明显高于任意一种成分内外侧统一涂布的方式。
实施例3
如附图1以及附图2所示，一种新型复合面料，由内及外依次为吸脂杀菌层1、内侧混纺层2、粘结缝制层3、外侧混纺层4以及空气抑菌层5，所述吸脂杀菌层1的物料组成包括聚乙烯吡咯烷酮碘、三苯甲咪唑、乙酰壳多糖、茴香油、多孔填料、热固型丙烯酸树脂粘结剂、亲肤剂以及去离子水，以用于吸收并挥发油脂，和杀灭绿脓杆菌，所述空气抑菌层5的物料组成包括载银膨润土、载银磷酸钙、复合硅胶抗菌剂、粘结硅胶以及去离子水，以用于杀灭脑膜炎球菌和结核杆菌。
所述多孔填料为纳米级多孔聚乙烯颗粒；所述亲肤剂包括芦荟萃取物、洋金菊萃取物，以及用作萃取物基底的环状烯烃类聚合物。
所述复合硅胶抗菌剂为羧甲基壳聚糖、甲壳素以及医用硅胶的三者的共聚物。
所述吸脂杀菌层1包括按重量计的以下各组分：聚乙烯吡咯烷酮碘6份、三苯甲咪唑7份、乙酰壳多糖3份、茴香油4份、多孔填料6份、热固型丙烯酸树脂粘结剂60份、亲肤剂2份以及去离子水19份。
所述空气抑菌层5包括按重量计的以下各组分：载银膨润土2份、载银磷酸钙3份、复合硅胶抗菌剂6份、粘结硅胶30份以及去离子水15份。
所述吸脂杀菌层1物料的制备方法依次包括以下步：
S1、在搅拌反应釜中添加，占总量1/3的去离子水，并加热至52℃，保持260r/min的搅拌速率，依次添加所述聚乙烯吡咯烷酮碘、三苯甲咪唑、乙酰壳多糖以及茴香油，搅拌混合均匀，得到基料；
S2、将所述基料升温至70℃，添加热固型丙烯酸树脂粘结剂后保持搅拌5min，然后连续加入多孔填料，加入时间为3min，搅拌混合均匀，得到高密度中间料；
S3、以2.5℃/min的速率降温，并在35℃之间添加完剩下2/3的去离子水，搅拌混合均匀后冷却至室温，得到最后的所述吸脂杀菌层1的待涂布物料。
步骤S2中，所述多孔填料采用插入管伸至液面5cm以下区域，并以空气鼓风吹入方式添加，所述多孔填料添加过程中搅拌速率为750r/min。
所述吸脂杀菌层1的厚度为0.15mm，密度为16g/m2，所述空气抑菌层5的厚度为0.35mm，涂布量为55g/m2。
所述内侧混纺层2为天丝纤维和羊毛纤维的混纺布料；所述外侧混纺层4为天丝纤维和聚酯纤维的混纺布料；所述粘结缝制层3包括平行间隔设置的粘结剂条带301，以及在所述粘结剂条带301之间设置的缝制线302，所述缝制线302在所述内侧混纺层2上的针刺缝制深度小于在所述外侧混纺层4上的针刺缝制深度。
一种新型复合面料的制作工艺，依次包括以下步骤：
步骤1、分别独立混纺编织所述内侧混纺层2以及外侧混纺层4，混合配制所述吸脂杀菌层1以及空气抑菌层5，并待用；
步骤2、通过交替缝制和粘结的方式，在所述内侧混纺层2和所述外侧混纺层4之间形成所述粘结缝制层3；
步骤3、在所述内侧混纺层2上涂布所述吸脂杀菌层1、在所述外侧混纺层4上涂布所述空气抑菌层5，形成最终的所述新型复合面料，
其中，所述空气抑菌层5的混合温度为60℃，充分混合后冷却至室温带用，所述吸脂杀菌层1以及空气抑菌层5的涂布温度为75℃，涂布压力为220kg/cm2，采用网纹辊涂布方式进行。
在本实施例中，对最终获得的所述新型复合面料进行抗菌抑菌检测，检测依据和方法为：GB/T 20944.3-2008振荡法，所述新型复合面料采用内侧混纺层2、粘结缝制层3以及外侧混纺层4为面料基底层，单独涂布所述吸脂杀菌层1后检测绿脓杆菌、单独涂布所述空气抑菌层5后检测脑膜炎球菌和结核杆菌的方式进行，检测结果如下。
Figure DEST_PATH_IMAGE006
根据上表显示，所述吸脂杀菌层1以及空气抑菌层5具有针对性杀菌率高达99%，交叉杀菌率高于60%的优越性能，因此证明本实施例中所述吸脂杀菌层1以及空气抑菌层5针对性地内侧、外侧分别涂布方式具有针对性杀菌效果好的优点，明显高于任意一种成分内外侧统一涂布的方式。
上面结合附图对本发明的实施方式作了详细说明，但是本发明不限于上述实施方式，在所述技术领域普通技术人员所具备的知识范围内，还可以在不脱离本发明宗旨的前提下做出各种修改。这些都是不具有创造性的修改，只要在本发明的权利要求范围内都受到专利法的保护。

Claims (10)

1.一种新型复合面料，其特征在于：由内及外依次为吸脂杀菌层（1）、内侧混纺层（2）、粘结缝制层（3）、外侧混纺层（4）以及空气抑菌层（5），所述吸脂杀菌层（1）的物料组成包括聚乙烯吡咯烷酮碘、三苯甲咪唑、乙酰壳多糖、茴香油、多孔填料、热固型丙烯酸树脂粘结剂、亲肤剂以及去离子水，以用于吸收并挥发油脂，和杀灭绿脓杆菌，所述空气抑菌层（5）的物料组成包括载银膨润土、载银磷酸钙、复合硅胶抗菌剂、粘结硅胶以及去离子水，以用于杀灭脑膜炎球菌和结核杆菌。
2.根据权利要求1所述的一种新型复合面料，其特征在于：所述多孔填料为纳米级多孔碳化硅、纳米级多孔聚乙烯颗粒以及纳米级多孔氧化锆中的任意一种或其混合物；所述亲肤剂包括芦荟萃取物、洋金菊萃取物，以及用作萃取物基底的环状烯烃类聚合物。
3.根据权利要求1所述的一种新型复合面料，其特征在于：所述复合硅胶抗菌剂为羧甲基壳聚糖、甲壳素以及医用硅胶的三者的共聚物。
4.根据权利要求1所述的一种新型复合面料，其特征在于所述吸脂杀菌层（1）包括按重量计的以下各组分：聚乙烯吡咯烷酮碘1-6份、三苯甲咪唑0.5-7.0份、乙酰壳多糖1-3份、茴香油3-4份、多孔填料5-8份、热固型丙烯酸树脂粘结剂45-65份、亲肤剂1-2份以及去离子水15-19份。
5.根据权利要求1所述的一种新型复合面料，其特征在于所述空气抑菌层（5）包括按重量计的以下各组分：载银膨润土1-2份、载银磷酸钙1-3份、复合硅胶抗菌剂5-6份、粘结硅胶25-30份以及去离子水11-15份。
6.根据权利要求1或4所述的一种新型复合面料，其特征在于所述吸脂杀菌层（1）物料的制备方法依次包括以下步：
S1、在搅拌反应釜中添加，占总量1/3的去离子水，并加热至45-52℃，保持200-260r/min的搅拌速率，依次添加所述聚乙烯吡咯烷酮碘、三苯甲咪唑、乙酰壳多糖以及茴香油，搅拌混合均匀，得到基料；
S2、将所述基料升温至65-70℃，添加热固型丙烯酸树脂粘结剂后保持搅拌5-6min，然后连续加入多孔填料，加入时间为2-3min，搅拌混合均匀，得到高密度中间料；
S3、以2-2.5℃/min的速率降温，并在35℃之间添加完剩下2/3的去离子水，搅拌混合均匀后冷却至室温，得到最后的所述吸脂杀菌层（1）的待涂布物料。
7.根据权利要求6所述的一种新型复合面料，其特征在于：步骤S2中，所述多孔填料采用插入管伸至液面5cm以下区域，并以空气鼓风吹入方式添加，所述多孔填料添加过程中搅拌速率为450-750r/min。
8.根据权利要求1所述的一种新型复合面料，其特征在于：所述吸脂杀菌层（1）的厚度为0.10-0.15mm，涂布量为15-16g/m2，所述空气抑菌层（5）的厚度为0.20-0.35mm，涂布量为42-55g/m2。
9.根据权利要求1所述的一种新型复合面料，其特征在于：所述内侧混纺层（2）为天丝纤维和羊毛纤维的混纺布料；所述外侧混纺层（4）为天丝纤维和聚酯纤维的混纺布料；所述粘结缝制层（3）包括平行间隔设置的粘结剂条带（301），以及在所述粘结剂条带（301）之间设置的缝制线（302），所述缝制线（302）在所述内侧混纺层（2）上的针刺缝制深度小于在所述外侧混纺层（4）上的针刺缝制深度。
10.一种如权利要求1所述的新型复合面料的制作工艺，其特征在于依次包括以下步骤：
步骤1、分别独立混纺编织所述内侧混纺层（2）以及外侧混纺层（4），混合配制所述吸脂杀菌层（1）以及空气抑菌层（5），并待用；
步骤2、通过交替缝制和粘结的方式，在所述内侧混纺层（2）和所述外侧混纺层（4）之间形成所述粘结缝制层（3）；
步骤3、在所述内侧混纺层（2）上涂布所述吸脂杀菌层（1）、在所述外侧混纺层（4）上涂布所述空气抑菌层（5），形成最终的所述新型复合面料，
其中，所述空气抑菌层（5）的混合温度为25-60℃，充分混合后冷却至室温带用，所述吸脂杀菌层（1）以及空气抑菌层（5）的涂布温度为65-75℃，涂布压力为75-225kg/cm2，采用网纹辊涂布方式进行。
CN201911356718.3A 2019-12-25 2019-12-25 一种新型复合面料，及其制作工艺 Pending CN111055557A (zh)