CN1110546A - 牙种植体的表面氧化改性方法 - Google Patents

牙种植体的表面氧化改性方法 Download PDF

Info

Publication number
CN1110546A
CN1110546A CN 94104248 CN94104248A CN1110546A CN 1110546 A CN1110546 A CN 1110546A CN 94104248 CN94104248 CN 94104248 CN 94104248 A CN94104248 A CN 94104248A CN 1110546 A CN1110546 A CN 1110546A
Authority
CN
China
Prior art keywords
minutes
titanium
modifying
organic solvent
artificial tooth
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 94104248
Other languages
English (en)
Other versions
CN1087925C (zh
Inventor
张美康
曹征旺
赵士芳
倪其军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
XIHU BIOLOGICAL MATERIAL INST HANGZHOU
Original Assignee
XIHU BIOLOGICAL MATERIAL INST HANGZHOU
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by XIHU BIOLOGICAL MATERIAL INST HANGZHOU filed Critical XIHU BIOLOGICAL MATERIAL INST HANGZHOU
Priority to CN 94104248 priority Critical patent/CN1087925C/zh
Publication of CN1110546A publication Critical patent/CN1110546A/zh
Application granted granted Critical
Publication of CN1087925C publication Critical patent/CN1087925C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明公开了一种牙种植体的表面氧化改性方 法。它首先将金属钛或钛合金基体进行酸蚀或机械 方法去除基体自然氧化膜，立即采用有机溶剂清洗和 保护，接着用氧化性溶液预处理5～25分钟后，放入 300～600℃的加热炉内加热氧化80～300分钟，并 让其自然冷却，再经过热蒸汽封孔50～100分钟，经 本发明处理的牙种植体氧化层具有高的生物安全性， 生物电位的相近性和体液中高的耐蚀性。经六项生 物学检测，动物试验，临床试验各项试验指标都超过 现有种植材料指标。

Description

本发明涉及牙种植体的表面氧化改性方法。
近10多年来国内外种植牙飞速发展，在种植材料、种植体结构设计、种植医学诸方面都获得了突破性进展，尤其是种植材料。原来曾用Co-Cr合金，刚玉氧化铝其力学性能不能满足要求，易脆断。从80年代开始欧美种植界用钛合金近行试验。材料的弹性模量与牙槽骨的差距减小，改善了种植体的功能。为了改善钛和牙槽骨之间的生物相溶性，在钛材表面喷涂人造骨粉，使钛种植体基本上取代了其它材料，但随着临床应用时间的延长，人们发现在人的长期作用下，喷涂的骨粉和钛材的界面会出现分离，危害种植体的存活寿命，同时钛材表面喷涂骨粉工艺困难，设备投资大，质量难保证，种植体形态设计又受到限制。
本发明的目的提供一种牙种植体的表面氧化改性方法。
牙种植体的表面氧化改性方法为：首先将金属钛、钛合金基体进行酸蚀或机械方法去除自然氧化膜，立即采用丙酮、乙醇有机溶剂清洗和保护，接着用铬酸盐溶液、铬酸溶液、硝酸溶液、铬酸硝酸混合液，NaOH溶液，双氧水等氧化性溶液预处理5～25分钟（10～20分钟较佳）后，放入300～600℃（350～450℃较佳）的电加热炉，氧化性气氛加热炉内加热氧化80～300分钟（120～200分钟较佳），并让其自然冷却，再经过热蒸汽封孔50～100分钟（20～60分钟较佳），即可。
本发明根据钛材的活性氧化势，热力学和动力学特性，结晶学等规律，成功地进行钛材表面的氧化改性，晶态和非晶态氧化层和基体的一定的共格联系，与基体结合牢固，在整个表面为连续的均匀层，其颜色由淡黄褐色到深黄色，灰黑色。氧化层具有高的生物安全性，生物电位的相近性和体液中高的而蚀性，经六项生物学检测，动物试验，临床试验，各项试验指标都超过现有种植材料指标，临床数百例患者无一例因材料而失败。

Claims (2)

1、一种牙种植体的表面氧化改性方法，其特征在于：首先将金属钛或钛合金基体进行酸蚀或机械方法去除基体自然氧化膜，立即采用有机溶剂清洗和保护，接着用氧化性溶液预处理5～25分钟，放入300～600℃的加热炉内加热氧化80～300分钟，并让其自然冷却，再经过热蒸汽封孔50～100分钟。
2、根据权利要求1所述的一种牙种植体的表面氧化改性方法，其特征在于：首先将金属钛或钛合金基体进行酸蚀或机械方法去除自然氧化膜，立即采用丙酮或乙醇有机溶剂清洗和保护，接着用铬酸盐溶液或铬酸溶液预处理10～20分钟后，放入350～450℃的电加热炉或氧化性气氛的加热炉内加热120～200分钟，并让其自然冷却，再经过热蒸汽封孔20～60分钟。
CN 94104248 1994-04-26 1994-04-26 牙种植体的表面氧化 Expired - Fee Related CN1087925C (zh)