CN111032330A - 高温物品防护垫 - Google Patents

高温物品防护垫 Download PDF

Info

Publication number
CN111032330A
CN111032330A CN201880054200.1A CN201880054200A CN111032330A CN 111032330 A CN111032330 A CN 111032330A CN 201880054200 A CN201880054200 A CN 201880054200A CN 111032330 A CN111032330 A CN 111032330A
Authority
CN
China
Prior art keywords
mat
pad
intermediate layer
layer
mat according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201880054200.1A
Other languages
English (en)
Inventor
D·皮卡斯基
S·伯德
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Power Box AG
Original Assignee
Power Box AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Power Box AG filed Critical Power Box AG
Publication of CN111032330A publication Critical patent/CN111032330A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种垫，该垫在热源(例如燃烧器火焰)或者被加热物品(例如在邻近垫的管道系统上进行工作时形成的)与要保护免受热的表面(例如地板或者墙壁)或者另一物品之间定位并用作热屏障。该垫由第一和第二外层形成，所述第一和第二外层围绕它们的周边被结合在一起以形成至少一个材料的中间隔热层设置于其中的腔，在一个实施例中，该材料是充气玻璃纤维。外层和中间层的组合防止热量在正常作业过程中达到的温度下通过垫。

Description

高温物品防护垫
技术领域
本申请涉及的发明是一种垫，该垫被设置用于保护物品、工作表面、地板、墙壁和/或人员，使其免受可能有意或无意地置于所述垫上的高温物品和/或热源。
背景技术
在某些活动中，例如焊接、珠宝制作、敷设管道等，需要使用通常通过燃烧器、喷灯或焊接设备产生的相对高的温度，以允许特定活动进行，例如，使用焊料将管道或金属物品结合在一起，使用燃烧器或焊接设备来熔融物品的一部分，以允许在其上进行工作。这样的结果是，需要能够保护周围的环境和/或进行这项工作的人员。发现，这个问题已经变得更大，因为使用较高温度的设备变得更加普遍，因此需要保护的温度已经升高。
虽然已知能够通过使用片状材料来保护物品，但是发现该片状材料仅在有限的时间段内提供保护，直到其被燃烧尽，因此随着时间的流逝，热源到达被保护的表面，以使其燃烧。在有些形式中，大量的片状材料是使得购买昂贵和/或可能难以在某些区域中使用，例如在限制区域中，可能难以将片状材料以提供所需保护的方式展开。另一个问题是，通常片状材料由石棉形成或包括石棉，石棉尽管有效，但当其寿命到期时，会引起在安全处置产品方面的问题，和/或，如果外部保护层被切割或刺穿，那么石棉的暴露会对在使用该垫的环境中的使用者和/或其它人员造成危险。
发明内容
因此，本发明的目的是提供一种形式的保护垫或片状材料，该保护垫或片状材料在对位于垫的第一侧的表面提供保护方面特别有效，使其免受在垫的相反表面上或者临近其放置、或被应用到其上的高温物品或热源的伤害，并以允许垫有效且相对容易地重复使用的方式提供该保护垫或片状材料。
在本发明的第一方面，提供了一种热防护垫，所述垫由相反的第一和第二外层和至少一个中间层形成，其中所述第一外层具有的外表面设置成形成所述垫的在使用中暴露于热源的面，并且所述第二外层具有的外表面设置成形成所述垫的接触被保护免受热的表面或物品或者临近其定位的面，并且所述至少一个中间层由纤维材料形成以用作绝缘层。
在一个实施例中，在纤维材料置于第一和第二外层之间之前进行预处理。
在一个实施例中，纤维材料包括毡、岩石、玻璃和/或矿物纤维中的任一种或其任一组合。
在一个实施例中，中间层的纤维被固定且保持为相对柔软的材料块。
在一个实施例中，所述中间层包括一系列子层，所述一系列子层由纤维保持在一起以形成中间层。
在一个实施例中，中间层的外面基本上平行于垫的所述外层。
在一个实施例中，中间层基本上由玻璃纤维形成，所述玻璃纤维通过施加空气被处理，以形成充气的玻璃纤维中间层。
在一个实施例中，用于中间层的预处理步骤包括拉伸和/或充气和/或吹气和/或拉开形成该层的纤维中的任一或任一组合，以形成相对疏松地结合的中间层。发现中间层的预处理允许在减轻和减小施加到垫的外表面上的高温的作用方面改善中间层的有效性。
在一个实施例中，提供了预处理步骤，以增加中间层的体积，使得中间层具有的深度在0.75cm至2.0cm的范围内。在一个实施例中，所述中间层以压缩形式被保持在外层之间形成的腔中。
在一个实施例中，中间层用作隔热层。
在一个实施例中，所述第一和第二外层至少围绕它们的外周被结合在一起，以在它们之间形成所述中间层位于其中的腔。
在一个实施例中，所述第一和第二外层包括相同的材料，在一个实施例中，所述材料是玻璃纤维。在一个实施例中，所述外层是编织的。
在一个实施例中，各个外层的结构是不同的。在一个实施例中，外层之一具有被涂覆和密封的外面。在一个实施例中，所述密封的面是被定位成与要保护其免受热的表面或物品接触或相邻的面。
在一个实施例中，一个外层或两个外层都被设置成具有膨胀作用。
在一个实施例中，第一和/或第二外层中的一个或两个都设置有相对较硬外皮的外表面，以防止放置在其上的任何物品被刺穿，和/或，可以设置具有一个或多个涂层，以使其防水，以防止掉落到垫上的任何液体进入中间层，并可能影响或改变中间层的结构。
通常，垫可以设置成具有合适的形状和尺寸，以适合于特定的用途和/或用在特定的环境中，并且在一个实施例中，一系列的所述垫被设置成具有不同的尺寸，以允许其被用于一系列的用途。通常，在垫的不同侧之间实现的温度上的降低是例如允许施加到垫的一侧的高温的影响被减小到高温的应用不影响垫所要保护的表面或者物品的程度。
在一个实施例中，可以选择中间层的厚度以适合垫的特定预期用途，从而由此允许针对特定用途确定垫的性能。例如，较厚的中间层可被设置用于被设计用于提供保护免受可能具有较高温度范围的物品的垫，而不是用于不被设计用于具有较低预期温度范围的物品的垫。
在一个实施例中，所述外层中的至少一层被形成为基本上是耐液体的，以防止液体从该外层进入中间层。
在一个实施例中，垫能够承受并保护表面免受直接冲击在第一外层上的火焰的伤害。
在一个实施例中，垫能够承受高达750摄氏度的温度的热量。
附图说明
现在参考附图描述本发明的特定实施例；其中
图1示出了根据本发明的一个实施例的垫的透视图；和
图2a和2b示出了图1的垫沿线AA的横截面端视图，其中图2a示出了使用中的垫，并且图2b以示意性形式示出了垫的层。
具体实施方式
根据本发明的该实施例的垫通常设置用于需要提供抵抗所施加的热的冲击的屏障的任何合适的工业或家庭用途。垫的形式的本发明特别适用于这样的工业或服务中，其中需要在现场进行热的应用，因此在正使用高温进行作业时，需要对正在安装或维修的设备周围的位置进行临时保护。作业的形式可以变化，但是例如可以是通过敷设管道/加热和/或维修生意进行的作业，例如，在家庭环境中使用焊料和热量将管道结合在一起的作业，在该家庭环境中，存在潜在价值的物品可能会被损坏和/或表面可能被烧毁和/或外观损坏的风险。根据本发明的垫被设置用于在高温作业时防止烧伤，高温作业例如为正在进行焊接或钎焊，以及在此期间所使用的设备和/或部件和/或碎屑处于高温下。垫可用于保护装饰表面，例如家具、木材、电线的表面的物品，也可用于掩盖潜在的易燃物品，例如地面覆盖物等。
现在参考图1-2b，示出了根据本发明的一个实施例形成的垫2。垫可以形成有预定尺寸以覆盖指定区域，并且可以设想，不同尺寸的垫会被制造，并且由用户可以购买以适合他们的特定要求。
根据该实施例的垫包括第一外层4，该第一外层具有外表面6，该外表面6形成了垫的在使用时朝向热源的面。用于形成该外层的材料对裸露的火焰具有足够的抵抗力，因此它将抵抗暴露于例如喷灯8火焰的冲击，该火焰可以直接或间接地施加到外层4上，同时其被用于在所述外层4垫附近对例如管接头进行加热操作。
设置了第二外层12，该第二外层12具有外表面14，其形成垫的被放置在被保护免受热的表面或物品16上或与其相邻的面，所述表面或者物品例如为地板或墙壁，或者家具或器具的物品表面。典型地，至少该层被形成或处理为抵抗液体从中通过。
图2a示出了垫2相对于管接头19的一种可能的布置，热源8被施加在垫的一侧21上，并且地板16的表面形式的物品设置在垫的相反侧23上并且被保护免受热，该热不会以任何足以破坏的程度通过垫。
如图中所示，第一和第二外层的外围18、18'通常通过边缘带25的凯夫拉(Kevlar)缝合20被结合在一起，以相应地在第一和第二外层4、12的内表面24、26之间限定基本上密封的腔22。在图2b所示的实施例中，第一和第二外层4、12由玻璃纤维形成，该玻璃纤维通常是编织的，并且两层或者其中一层可以具有在其上施加的密封剂，例如以使其防水。
在腔22内，保持有包括玻璃纤维的纤维材料的中间层28。根据本发明，纤维材料在被密封在腔中以形成中间层之前被预处理，并且该预处理包括对其进行充气，并且还可以包括将纤维拉开，同时确保中间层仍以足够的接触被保持，以便共同作用以形成中间层。在一个实施例中，中间层由一系列子层32形成，所有这些子层与外层一起平行于同一轴线30延伸。子层32通过各个子层的纤维结合在一起，使得它们用作一个充气的中间层。
凹陷和突起可以设置在表面34上，其可以在材料的预处理以形成中间层期间形成，从而增加中间层的有效表面积和/或增加中间层28的有效深度。在一个实施例中，中间层的至少一个表面34设有凹陷和突起，并且在设置时，凹陷和突起可以被设置为重复图案。
发现，对中间层的纤维进行预处理的作用显著地提高了垫的整体承受更高热温度的能力。
如图1所示，可以形成一个或多个定位装置，例如孔30，以辅助将垫存储在例如钩上，和/或，例如通过将钉子、螺钉或针插入孔中在使用位置上允许垫的定位。也可以使用其它定位装置，例如钩环紧固装置。

Claims (15)

1.一种热防护垫，所述垫由相对的第一外层和第二外层以及至少一个中间层形成，其中所述第一外层具有设置用于形成垫的在使用中暴露到热源的面的外表面，并且，所述第二外层具有设置用于形成垫的与要保护免受热的表面或物品接触或与其相邻定位的面的外表面，并且所述至少一个中间层由纤维材料形成，以用作绝缘层。
2.根据权利要求1所述的垫，其特征在于，纤维材料在放置在所述第一外层和第二外层之间之前被预处理。
3.根据权利要求1所述的垫，其特征在于，纤维材料包括毡、岩石、玻璃和/或矿物纤维中的任一种或任一组合。
4.根据前述权利要求中的任一项所述的垫，其特征在于，所述中间层由玻璃纤维形成。
5.根据权利要求2所述的垫，其特征在于，所述预处理是拉伸和/或充气和/或吹气和/或拉开纤维，以提供准备用作中间层的形式的材料。
6.根据权利要求5所述的垫，其特征在于，预处理的步骤增加了所述中间层的体积。
7.根据前述权利要求中的任一项所述的垫，其特征在于，所述中间层由一系列子层形成，所述一系列子层通过各个相邻层的纤维的缠结而结合在一起。
8.根据前述权利要求中的任一项所述的垫，其特征在于，所述中间层的至少一个表面设置有凹陷和突起。
9.根据权利要求8所述的垫，其特征在于，所述凹陷和突起以重复图案设置。
10.根据权利要求1所述的垫，其特征在于，所述第一外层和第二外层至少围绕它们的外周被结合在一起，以在它们之间形成所述中间层要位于其中的腔。
11.根据权利要求1所述的垫，其特征在于，所述第一外层和第二外层由玻璃纤维形成。
12.根据权利要求5所述的垫，其特征在于，玻璃纤维被编织以形成所述外层。
13.根据前述权利要求中的任一项所述的垫，其特征在于，至少一个所述外层被处理或密封，以使其防水。
14.根据前述权利要求所述的垫，其特征在于，所述垫被设置为防止高温从垫的一个外层朝向垫的相反外层传递。
15.根据权利要求14所述的垫，其特征在于，所述垫能够在高达750℃的温度下防止从一个外层到所述另一外层的热传递。
CN201880054200.1A 2017-08-22 2018-08-22 高温物品防护垫 Pending CN111032330A (zh)