CN111020927A - Production method of reticulate pattern powder point color matching adhesive lining cloth - Google Patents
Production method of reticulate pattern powder point color matching adhesive lining cloth Download PDFInfo
- Publication number
- CN111020927A CN111020927A CN201911195666.6A CN201911195666A CN111020927A CN 111020927 A CN111020927 A CN 111020927A CN 201911195666 A CN201911195666 A CN 201911195666A CN 111020927 A CN111020927 A CN 111020927A
- Authority
- CN
- China
- Prior art keywords
- cloth
- singeing
- desizing
- dyeing
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production method of reticulate pattern powder point color matching adhesive lining cloth, relating to the technical field of lining cloth production; the problem that cloth is easily damaged by overburning in the singeing process is solved; the method specifically comprises the following steps: the method comprises the following steps of raw cloth treatment, namely selecting raw cloth, turning over the cloth and sewing, wherein the raw cloth can be selected from pure cotton, washing cotton, polyester cotton, pure polyester or viscose fiber processed fabrics; the pretreatment comprises the steps of singeing, desizing, refining, bleaching, scutching, rolling, drying and mercerizing the base fabric. According to the invention, the cold water cooling roller is arranged above the singeing fire hole for cooling, so that cloth can be prevented from being damaged by overburning; the air blowing device is additionally arranged at the outlet of the singeing cloth for air blowing cooling, so that the phenomenon of excessive thermal shrinkage after singeing can be prevented; the alkali liquor desizing method can realize the purposes of low cost, utilization of boiling or mercerizing waste alkali for caustic soda and no damage to cotton fibers.
Description
Technical Field
The invention relates to the technical field of lining cloth production, in particular to a production method of reticulate pattern powder point color matching bonding lining cloth.
Background
The lining cloth is widely used in the life of people, along with the improvement of the aesthetic appearance of people, the lining cloth has new requirements on the aesthetic degree of the daily lining cloth, and people often beautify the lining cloth by processing and dyeing methods.
In the production process of the lining cloth, the raw cloth is often required to be pretreated, wherein the production process comprises a singeing process link, however, in the singeing link, if the temperature control is not good, the cloth is easily damaged seriously, and the production benefit is influenced.
Through retrieval, the Chinese patent with the application number of CN201010218075.9 discloses a production method of single-sided reticulate powder point adhesive interlining cloth, which comprises the steps of base cloth selection, pretreatment, resin shrink-proof treatment, compounding, preshrinking and the like.
Disclosure of Invention
The invention aims to solve the defects in the prior art and provides a production method of a reticulate pattern powder point color matching adhesive lining cloth.
In order to achieve the purpose, the invention adopts the following technical scheme:
a production method of a reticulate pattern powder point color matching adhesive lining cloth comprises the following steps:
s1: the method comprises the following steps of raw cloth treatment, namely selecting raw cloth, turning over the cloth and sewing, wherein the raw cloth can be selected from pure cotton, washing cotton, polyester cotton, pure polyester or viscose fiber processed fabrics;
s2: pre-treating, including singeing, desizing, refining, bleaching, scutching, rolling, stoving and mercerizing;
s3: preparing a cloth coloring agent according to the ingredients, respectively adding 0.2-1.0 g/L of a high-temperature leveling agent, 0.5-1.0 g/L of a dispersing agent, 0.5-1.0 g/L of acetic acid (98%), and X% of a disperse dye, fully stirring for 3-4 hours, standing for 2-5 hours, and taking to dye the cloth; the dyeing condition is that the dyeing is started at 60-70 ℃, the temperature is gradually increased to 125-135 ℃ after 50-70 minutes, and the dyeing is continued for 50-70 minutes.
S4: and (4) carrying out reduction cleaning when the cloth is dyed with medium dark color, and finally carrying out dehydration, spreading and shaping.
Preferably: the singeing process sequentially comprises the following steps: drying, brushing, singeing and extinguishing fire; the process conditions are as follows: the gasification temperature is 70-80 ℃, the steam pressure is 0.25-0.28 Mpa, the vehicle speed is 100m/min, the number of fire holes is 2 plus or minus 2 minus, a cold water cooling roller is arranged above the singeing fire holes for cooling, and a blowing device is additionally arranged at the outlet of the singeing cloth for blowing and cooling.
Preferably: the desizing process is an alkali liquor desizing method, and sequentially comprises the following steps: rolling alkali, steaming (stacking), washing with hot water and washing with cold water; wherein the desizing liquid comprises the following components: 5-10 g/l of caustic soda, 2-5 g/1 of wetting agent and 3-5 g/1 of oxidation desizing agent.
Preferably: the mercerization is to treat the base fabric by using a sodium hydroxide solution, specifically, a cotton product is soaked in the sodium hydroxide solution for 25-40 seconds at 15-25 ℃, and the concentration of the sodium hydroxide solution is 20-24%.
Preferably: the cloth coloring agent is prepared by adding 0.3-0.8 g/L of high-temperature leveling agent, 0.6-0.9 g/L of dispersing agent, 0.6-0.9 g/L of acetic acid (98%) and X% of disperse dye, fully stirring for 3-4 hours, and standing for 2-4 hours for use; the dyeing condition is that the dyeing is started at 62-68 ℃, the temperature is gradually increased to 128-132 ℃ after 55-65 minutes, and the dyeing is continued for 55-65 minutes.
Preferably: the singeing process comprises the following technological conditions: the gasification temperature is 73-77 ℃, the steam pressure is 0.25-0.27 Mpa, and the desizing liquid comprises 6-9 g/l of caustic soda, 3-5 g/1 of wetting agent and 3.5-4.5 g/1 of oxidation desizing agent.
Preferably: the mercerizing treatment specifically comprises the step of soaking the cotton product in a sodium hydroxide solution at 18-22 ℃ for 28-38 seconds, wherein the concentration of the sodium hydroxide solution is 21-23%.
Preferably: the cloth dyeing agent is prepared by respectively adding 0.5 g/L of high-temperature leveling agent, 0.7g/L of dispersing agent, 0.7g/L of acetic acid (98%) and X% of disperse dye, fully stirring for 3-4 hours, standing for 2-3 hours, and then dyeing the cloth. The dyeing condition is that dyeing is started at 65 ℃, the temperature is gradually increased to 130 ℃ after 60 minutes, and dyeing is continued for 60 minutes.
Preferably: the singeing process comprises the following technological conditions: the gasification temperature is 75 ℃, and the steam pressure is 0.26 Mpa; the desizing liquid comprises the following components: 7g/l of caustic soda, 4g/1 of wetting agent and 4g/1 of oxidation desizing agent.
Preferably: the mercerization is specifically to be implemented by soaking cotton products in sodium hydroxide solution at 20 ℃ for 32-35 seconds, wherein the concentration of the sodium hydroxide solution is 22%.
The invention has the beneficial effects that:
1. the cold water cooling roller is arranged above the singeing fire hole for cooling, so that the cloth can be prevented from being damaged by overburning; the air blowing device is additionally arranged at the outlet of the singeing cloth for air blowing cooling, so that the phenomenon of excessive thermal shrinkage after singeing can be prevented.
2. The alkali liquor desizing method can realize the purposes of low cost, utilization of boiling or mercerizing waste alkali for caustic soda and no damage to cotton fibers.
3. Through the whole base fabric treatment process, natural impurities, sizing agent, oil stains and the like on the fibers can be removed, the fabric is white and soft, the dye can be well permeated and processed, and the appearance and the internal quality of the fabric are improved; the color fastness of the dyed finished product can be kept by carrying out reduction cleaning when the cloth is dyed with medium and deep colors.
Detailed Description
The technical solutions in the embodiments of the present invention will be described clearly and completely below, and it should be apparent that the described embodiments are only a part of the embodiments of the present invention, and not all embodiments.
Example 1:
a production method of a reticulate pattern powder point color matching adhesive lining cloth sequentially comprises the following steps:
s1: the method comprises the following steps of raw cloth treatment, namely selecting raw cloth, turning over the cloth and sewing, wherein the raw cloth can be selected from pure cotton, washing cotton, polyester cotton, pure polyester or viscose fiber processed fabrics;
s2: pre-treating, including singeing, desizing, refining, bleaching, scutching, rolling, stoving and mercerizing;
s3: preparing a cloth coloring agent according to the ingredients, respectively adding 0.2-1.0 g/L of a high-temperature leveling agent, 0.5-1.0 g/L of a dispersing agent, 0.5-1.0 g/L of acetic acid (98%), and X% of a disperse dye, fully stirring for 3-4 hours, standing for 2-5 hours, and taking to dye the cloth; the dyeing condition is that the dyeing is started at 60-70 ℃, the temperature is gradually increased to 125-135 ℃ after 50-70 minutes, and the dyeing is continued for 50-70 minutes;
s4: and (3) carrying out reduction cleaning when the cloth is dyed with medium-dark color, keeping the color fastness of a dyed finished product, and finally carrying out dehydration, spreading and shaping.
Wherein the singeing process sequentially comprises the following steps: drying, brushing, singeing and extinguishing fire. The process conditions are as follows: the gasification temperature is 70-80 ℃, the steam pressure is 0.25-0.28 Mpa, the vehicle speed is 100m/min, the number of fire holes is 2 plus or minus 2 minus, a cold water cooling roller is arranged above the singeing fire hole for cooling, the cloth is prevented from being damaged by overburning, a blowing device is additionally arranged at the outlet of the singeing cloth for blowing and cooling, and the phenomenon of excessive thermal shrinkage after singeing is prevented.
Wherein the desizing process is an alkali liquor desizing method, which sequentially comprises the following steps: rolling alkali, steaming (stacking), washing with hot water and washing with cold water; wherein the desizing liquid comprises the following components: 5-10 g/l of caustic soda, 2-5 g/1 of wetting agent and 3-5 g/1 of oxidation desizing agent; the alkali liquor desizing method can realize the purposes of low cost, utilization of boiling or mercerizing waste alkali for caustic soda and no damage to cotton fibers.
The mercerization is a process for treating the base fabric by using a sodium hydroxide solution to increase the surface gloss of the base fabric, and specifically, a cotton product is soaked in the sodium hydroxide solution for 25-40 seconds at 15-25 ℃, and the concentration of the sodium hydroxide solution is 20-24%.
Through the base fabric treatment process, natural impurities, sizing agent, oil stains and the like on the fibers can be removed, the fabric is white and soft, the dye can be well permeated, and the appearance and the internal quality of the fabric are improved.
Example 2:
a production method of a reticulate pattern powder point color matching adhesive lining cloth sequentially comprises the following steps:
s1: selecting raw cloth, turning the cloth and sewing, wherein the raw cloth can be selected from pure cotton, washing cotton, polyester cotton, pure polyester or viscose fiber processed fabrics;
s2: carrying out singeing, desizing, refining, bleaching, scutching, squeezing, drying and mercerizing on the base fabric;
s3: preparing a cloth coloring agent according to the ingredients, respectively adding 0.3-0.8 g/L of a high-temperature leveling agent, 0.6-0.9 g/L of a dispersing agent, 0.6-0.9 g/L of acetic acid (98%), and X% of a disperse dye, fully stirring for 3-4 hours, standing for 2-4 hours, and taking for cloth dyeing. The dyeing condition is that the dyeing is started at 62-68 ℃, the temperature is gradually increased to 128-132 ℃ after 55-65 minutes, and the dyeing is continued for 55-65 minutes;
s4: and (3) carrying out reduction cleaning when the cloth is dyed with medium-dark color, keeping the color fastness of a dyed finished product, and finally carrying out dehydration, spreading and shaping.
Wherein the singeing process sequentially comprises the following steps: drying, brushing, singeing and extinguishing fire. The process conditions are as follows: the gasification temperature is 73-77 ℃, the steam pressure is 0.25-0.27 Mpa, the vehicle speed is 100m/min, the number of fire holes is 2 plus or minus 2 minus, a cold water cooling roller is arranged above the singeing fire hole for cooling, the cloth is prevented from being damaged by overburning, a blowing device is additionally arranged at the outlet of the singeing cloth for blowing and cooling, and the phenomenon of excessive thermal shrinkage after singeing is prevented.
Wherein the desizing process is an alkali liquor desizing method, which sequentially comprises the following steps: rolling alkali, steaming (stacking), washing with hot water and washing with cold water; wherein the desizing liquid comprises the following components: 6-9 g/l of caustic soda, 3-5 g/1 of wetting agent and 3.5-4.5 g/1 of oxidation desizing agent; the alkali liquor desizing method can realize the purposes of low cost, utilization of boiling or mercerizing waste alkali for caustic soda and no damage to cotton fibers.
The mercerization process comprises the step of treating base fabric by using a sodium hydroxide solution to increase the surface gloss of the base fabric, specifically, soaking a cotton product in the sodium hydroxide solution for 28-38 seconds at 18-22 ℃, wherein the concentration of the sodium hydroxide solution is 21-23%.
Through the base fabric treatment process, natural impurities, sizing agent, oil stains and the like on the fibers can be removed, the fabric is white and soft, the dye can be well permeated, and the appearance and the internal quality of the fabric are improved.
Example 3:
a production method of a reticulate pattern powder point color matching adhesive lining cloth sequentially comprises the following steps:
s1: selecting raw cloth, turning the cloth and sewing, wherein the raw cloth can be selected from pure cotton, washing cotton, polyester cotton, pure polyester or viscose fiber processed fabrics;
s2: carrying out singeing, desizing, refining, bleaching, scutching, squeezing, drying and mercerizing on the base fabric;
s3: preparing a cloth coloring agent according to the ingredients, respectively adding 0.5 g/L of a high-temperature leveling agent, 0.7g/L of a dispersing agent, 0.7g/L of acetic acid (98%) and X% of a disperse dye, fully stirring for 3-4 hours, standing for 2-3 hours, and then, dyeing the cloth. The dyeing condition is that dyeing is started at 65 ℃, the temperature is gradually increased to 130 ℃ after 60 minutes, and the dyeing is continued for 60 minutes;
s4: and (3) carrying out reduction cleaning when the cloth is dyed with medium-dark color, keeping the color fastness of a dyed finished product, and finally carrying out dehydration, spreading and shaping.
Wherein the singeing process sequentially comprises the following steps: drying, brushing, singeing and extinguishing fire. The process conditions are as follows: the gasification temperature is 75 ℃, the steam pressure is 0.26Mpa, the vehicle speed is 100m/min, the number of fire holes is 2 plus 2 minus, and a cold water cooling roller is arranged above the singeing fire hole for cooling, so that the cloth is prevented from being damaged by overburning, and a blowing device is additionally arranged at the outlet of the singeing cloth for blowing and cooling, so that the phenomenon of excessive thermal shrinkage after singeing is prevented.
Wherein the desizing process is an alkali liquor desizing method, which sequentially comprises the following steps: rolling alkali, steaming (stacking), washing with hot water and washing with cold water; wherein the desizing liquid comprises the following components: 7g/l of caustic soda, 4g/1 of wetting agent and 4g/1 of oxidation desizing agent; the alkali liquor desizing method can realize the purposes of low cost, utilization of boiling or mercerizing waste alkali for caustic soda and no damage to cotton fibers.
The mercerization process is a process for treating the base fabric by using a sodium hydroxide solution to increase the surface gloss of the base fabric, and specifically comprises the step of soaking a cotton product in the sodium hydroxide solution at the temperature of 20 ℃ for 32-35 seconds, wherein the concentration of the sodium hydroxide solution is 22%.
Through the base fabric treatment process, natural impurities, sizing agent, oil stains and the like on the fibers can be removed, the fabric is white and soft, the dye can be well permeated, and the appearance and the internal quality of the fabric are improved.
The above description is only for the preferred embodiment of the present invention, but the scope of the present invention is not limited thereto, and any person skilled in the art should be considered to be within the technical scope of the present invention, and the technical solutions and the inventive concepts thereof according to the present invention should be equivalent or changed within the scope of the present invention.
Claims (10)
1. A production method of a reticulate pattern powder point color matching adhesive lining cloth is characterized by comprising the following steps:
s1: the method comprises the following steps of raw cloth treatment, namely selecting raw cloth, turning over the cloth and sewing, wherein the raw cloth can be selected from pure cotton, washing cotton, polyester cotton, pure polyester or viscose fiber processed fabrics;
s2: pre-treating, including singeing, desizing, refining, bleaching, scutching, rolling, stoving and mercerizing;
s3: preparing a cloth coloring agent according to the ingredients, respectively adding 0.2-1.0 g/L of a high-temperature leveling agent, 0.5-1.0 g/L of a dispersing agent, 0.5-1.0 g/L of acetic acid (98%), and X% of a disperse dye, fully stirring for 3-4 hours, standing for 2-5 hours, and taking to dye the cloth; the dyeing condition is that the dyeing is started at 60-70 ℃, the temperature is gradually increased to 125-135 ℃ after 50-70 minutes, and the dyeing is continued for 50-70 minutes;
s4: and (4) carrying out reduction cleaning when the cloth is dyed with medium dark color, and finally carrying out dehydration, spreading and shaping.
2. The production method of the textured powder point color matching adhesive lining cloth as claimed in claim 1, wherein the singeing process sequentially comprises the following steps: drying, brushing, singeing and extinguishing fire; the process conditions are as follows: the gasification temperature is 70-80 ℃, the steam pressure is 0.25-0.28 Mpa, the vehicle speed is 100m/min, the number of fire holes is 2 plus or minus 2 minus, a cold water cooling roller is arranged above the singeing fire holes for cooling, and a blowing device is additionally arranged at the outlet of the singeing cloth for blowing and cooling.
3. The method for producing the textured powder point color-matching adhesive lining cloth as claimed in claim 2, wherein the desizing process is an alkali liquor desizing method which sequentially comprises the following steps: rolling alkali, steaming (stacking), washing with hot water and washing with cold water; wherein the desizing liquid comprises the following components: 5-10 g/l of caustic soda, 2-5 g/1 of wetting agent and 3-5 g/1 of oxidation desizing agent.
4. The production method of the anilox powder point color matching adhesive lining cloth as claimed in claim 3, wherein the mercerization is to treat the base cloth by using a sodium hydroxide solution, specifically, the cotton product is soaked in the sodium hydroxide solution for 25-40 seconds at 15-25 ℃, and the concentration of the sodium hydroxide solution is 20-24%.
5. The production method of the anilox powder point color matching adhesive lining cloth as claimed in claim 1, wherein the cloth coloring agent is prepared by adding 0.3-0.8 g/L of high-temperature leveling agent, 0.6-0.9 g/L of dispersing agent, 0.6-0.9 g/L of acetic acid (98%), and X% of disperse dye, fully stirring for 3-4 hours, standing for 2-4 hours, and taking for use; the dyeing condition is that the dyeing is started at 62-68 ℃, the temperature is gradually increased to 128-132 ℃ after 55-65 minutes, and the dyeing is continued for 55-65 minutes.
6. The production method of the anilox powder point color matching adhesive lining cloth as claimed in claim 2, wherein the singeing process conditions are as follows: the gasification temperature is 73-77 ℃, the steam pressure is 0.25-0.27 Mpa, and the desizing liquid comprises 6-9 g/l of caustic soda, 3-5 g/1 of wetting agent and 3.5-4.5 g/1 of oxidation desizing agent.
7. The production method of the anilox powder point color matching adhesive lining cloth as claimed in claim 4, wherein the mercerization is to immerse a cotton product in a sodium hydroxide solution at 18-22 ℃ for 28-38 seconds, and the concentration of the sodium hydroxide solution is 21-23%.
8. A production method of a textured powder point color matching adhesive lining cloth as claimed in claim 5, wherein the cloth coloring agent is prepared by respectively adding 0.5 g/L of high temperature leveling agent, 0.7g/L of dispersing agent, 0.7g/L of acetic acid (98%) and X% of disperse dye, fully stirring for 3-4 hours, standing for 2-3 hours, and then dyeing the cloth. The dyeing condition is that dyeing is started at 65 ℃, the temperature is gradually increased to 130 ℃ after 60 minutes, and dyeing is continued for 60 minutes.
9. The production method of the anilox powder point color matching adhesive lining cloth as claimed in claim 6, wherein the singeing process conditions are as follows: the gasification temperature is 75 ℃, and the steam pressure is 0.26 Mpa; the desizing liquid comprises the following components: 7g/l of caustic soda, 4g/1 of wetting agent and 4g/1 of oxidation desizing agent.
10. The production method of the anilox powder point color matching adhesive lining cloth as claimed in claim 7, wherein the mercerization is to immerse the cotton product in a sodium hydroxide solution at 20 ℃ for 32-35 seconds, and the concentration of the sodium hydroxide solution is 22%.