CN110982961A - Automobile leather flame retardant - Google Patents
Automobile leather flame retardant Download PDFInfo
- Publication number
- CN110982961A CN110982961A CN201911163050.0A CN201911163050A CN110982961A CN 110982961 A CN110982961 A CN 110982961A CN 201911163050 A CN201911163050 A CN 201911163050A CN 110982961 A CN110982961 A CN 110982961A
- Authority
- CN
- China
- Prior art keywords
- parts
- flame retardant
- automobile leather
- leather according
- automobile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a formula of an automobile leather flame retardant, which is characterized by comprising the following components in parts by weight: 5-15 parts of 4-diphenyl oxyphosphate, 10-15 parts of an active agent, 1-5 parts of an emulsifier, 1-5 parts of a solvent, 1-5 parts of a penetrating agent, 0.1-1 part of a stabilizer, 2-3 parts of a reinforcing agent, 2-3 parts of an antioxidant, 3-5 parts of a silicon-based synergist and 20-100 parts of water. The invention has the beneficial effects that: the novel environment-friendly phosphorus flame retardant additive is added to the automobile leather flame retardant, so that the flame retardant effect is improved by 30%, the ultra-high-speed constant-temperature emulsification technology is adopted, the stability of the liquid medicine is improved to one year from half a year, and the liquid medicine is more delicate to be nano-scale emulsion and is more softly combined with leather.
Description
Technical Field
The invention relates to the technical field of flame retardants, in particular to an automobile leather flame retardant.
Background
Leather products are increasingly used as special living goods, and are gradually expanded from initial wearing to high-grade consumption, such as office furniture, indoor decoration, vehicles, decoration of aircrafts, trains, automobiles, seat cushions and the like, leather used in the fields is required to have certain flame retardance so as to meet the requirements of government regulations and customers, and the flame retardance of clothes, particularly clothes of flight personnel, is strictly regulated in the United states. Boeing company requires that leatherware used in airplanes have self-extinguishing performance, leather used for high-grade automobile seat cushions also needs to have flame retardant performance, and currently, along with the improvement of the living standard of people in China, the fire prevention degree of leather products is valued.
Disclosure of Invention
The invention aims to provide a flame retardant for automobile leather, which solves the problems in the background technology.
In order to achieve the purpose, the invention provides the following technical scheme: the automobile leather flame retardant comprises the following components in parts by weight:
preferably, the active agent is any one of 10 to 15 parts of fatty alcohol-polyoxyethylene ether sodium sulfate, lauryl alcohol-polyoxyethylene ether sodium sulfate, sodium lauryl alcohol-polyoxyethylene ether sulfate and sodium laureth-5 sulfate.
Preferably, the emulsifier is any one of 1 to 5 parts of EL-30, EL40, EL60 and EL 80.
Preferably, the solvent is 1 to 5 parts of isopropanol.
Preferably, the penetrating agent is any one of sodium dodecyl sulfate, sodium dodecyl benzene sulfonate and sodium dodecyl benzene sulfonate in 1-5 parts.
Preferably, the stabilizer is any one of 0.1 to 1 part of lead salt, metal soap, organic tin, organic antimony, organic rare earth and pure organic compound.
Preferably, the reinforcing agent is 2-3 parts of one or a mixture of barium sulfate and talcum powder.
Preferably, the antioxidant is any one of 2-3 parts of antioxidant 1010 and antioxidant 1076.
Preferably, the silicon-based synergist is any one of silane, dimethyl siloxane, methyl phenyl siloxane, silicone resin and polysilsesquioxane in 3-5 parts.
Advantageous effects
The novel environment-friendly phosphorus flame retardant additive is added to the automobile leather flame retardant, so that the flame retardant effect is improved by 30%, the ultra-high-speed constant-temperature emulsification technology is adopted, the stability of the liquid medicine is improved to one year from half a year, and the liquid medicine is more delicate to be nano-scale emulsion and is more softly combined with leather.
Detailed Description
The following are specific examples of the present invention and further describe the technical solutions of the present invention, but the present invention is not limited to these examples.
Example 1
The automobile leather flame retardant comprises the following components in parts by weight:
example 2
The automobile leather flame retardant comprises the following components in parts by weight:
example 3
The automobile leather flame retardant comprises the following components in parts by weight:
example 4
The automobile leather flame retardant comprises the following components in parts by weight:
example 5
The automobile leather flame retardant comprises the following components in parts by weight:
finally, it should be noted that: although the present invention has been described in detail with reference to the foregoing embodiments, it will be apparent to those skilled in the art that changes may be made in the embodiments and/or equivalents thereof without departing from the spirit and scope of the invention. Any modification, equivalent replacement, or improvement made within the spirit and principle of the present invention should be included in the content of the present invention within the scope of the protection of the present invention.
Claims (9)
2. the flame retardant for automobile leather according to claim 1, wherein: the active agent is any one of 10 to 15 parts of fatty alcohol-polyoxyethylene ether sodium sulfate, lauryl alcohol-polyoxyethylene ether sodium sulfate and lauryl alcohol polyether-5 sodium sulfate.
3. The flame retardant for automobile leather according to claim 1, wherein: the emulsifier is any one of 1 to 5 parts of EL-30, EL40, EL60 and EL 80.
4. The flame retardant for automobile leather according to claim 1, wherein: the solvent is from 1 part to 5 parts of isopropanol.
5. The flame retardant for automobile leather according to claim 1, wherein: the penetrating agent is any one of sodium dodecyl sulfate, sodium dodecyl benzene sulfonate and sodium dodecyl benzene sulfonate in 1-5 weight portions.
6. The flame retardant for automobile leather according to claim 1, wherein: the stabilizer is any one of 0.1 to 1 part of lead salt, metal soap, organic tin, organic antimony, organic rare earth and pure organic compounds.
7. The flame retardant for automobile leather according to claim 1, wherein: the reinforcing agent is 2-3 parts of one or a mixture of barium sulfate and talcum powder.
8. The flame retardant for automobile leather according to claim 1, wherein: the antioxidant is 2-3 parts of any one of antioxidant 1010 and antioxidant 1076.
9. The flame retardant for automobile leather according to claim 1, wherein: the silicon synergist is any one of 3-5 parts of silane, dimethyl siloxane, methyl phenyl siloxane, silicon resin and polysilsesquioxane.