CN110965664A - 一种保温墙体的制备工艺 - Google Patents
一种保温墙体的制备工艺 Download PDFInfo
- Publication number
- CN110965664A CN110965664A CN201811151242.5A CN201811151242A CN110965664A CN 110965664 A CN110965664 A CN 110965664A CN 201811151242 A CN201811151242 A CN 201811151242A CN 110965664 A CN110965664 A CN 110965664A
- Authority
- CN
- China
- Prior art keywords
- wall body
- heat
- parts
- cement
- thermal insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种保温墙体的制备工艺，具有如下步骤：根据墙体的形状，通过多个轻质钢条间的焊接构成所述墙体的骨架，在所述骨架的外表面固定上轻质铝合金外板，在所述轻质铝合金外板内浇注水泥形成基层墙体，在所述基层墙体上抹上保温砂浆后烘干，得到保温墙体。本发明提高了轻质钢条结构墙体的承重效果及抗震性能，扩展了轻质钢条结构墙体的使用范围，同时，本发明的保温砂浆导热系数低，能适应各种复杂的建筑节点形状，安全，绿色。通过本发明得到的保温墙体，在常压常温养护下的抗压强度达到为270MPa，抗折强度达到83MPa，还能起到优异的保温效果。
Description
技术领域
本发明涉及一种保温墙体的制备工艺，属于建筑领域。
背景技术
目前，轻质钢条结构建筑由于其自身的特点如安装速度快、易产业化生产而在建筑领域中得到了广泛的应用。但是现有的轻质钢条结构建筑在建造过程中是由多个轻质钢条墙体拼接而成的，其受力体系为多块分别受力，降低了建筑体系的承重效果及抗震性能；并且由于轻质钢条的强度限制，无法通过常规水泥进行整体浇铸，限制了轻质钢条结构建筑的发展和使用范围。
随着各国工业化进程的发展，建筑能耗在人类整个能源消耗中所占的比例甚高，故建筑节能是解决我国能源问题的根本途径，而建筑节能最直接有效的方法是使用保温隔热材料。在建筑上合理采用保温隔热材料，可以减少建筑材料的用量，提高建筑施工的工业化程度，大幅度节能降耗。因此，使用建筑保温隔热材料对缓解能源危机以及提高人们的居住水平具有重要意义。保温隔热墙体材料不仅仅有利于提高建筑面的保温隔热性，改善室内居住环境，同时可以节约能源，降低建筑的使用成本。尤其是建筑外墙保温对于减轻室内热负荷、防止外围结构龟裂和内部结露都是有利的，同时可保护主体结构，减少热应力，避免热冷桥的产生，具有积极意义。在现有技术中，外墙保温系统主要有保温板材和保温砂浆两者类型，其中保温板材施工难度大，技术要求高，成本高，强度低。
发明内容
针对现有技术中的上述技术问题，本发明提供一种保温墙体的制备工艺，提高墙体的承重效果及抗震性能，同时，使用的保温砂浆解决现有技术中的保温砂浆在施工过程中容易破碎、施工复杂、保温砂浆层容易出现空鼓及松动，很大程度降低其热工性能和耐久性的技术问题。
基于以上技术方案，本发明提供了一种保温墙体的制备工艺，具体包括如下步骤：
(1)根据墙体的形状，通过多个轻质钢条间的焊接构成所述墙体的骨架，在所述骨架的外表面固定上轻质铝合金外板，在所述轻质铝合金外板内浇注水泥a形成基层墙体，所述基层墙体应坚实平整、完全干燥，不得有开裂、松动或泛碱，墙表面凸起物高度大于10mm时应剔除。保证施工表面平整，找平层与墙体之间的粘结强度不小于0.2MPa，找平层无空鼓、裂缝；
(2)在所述基层墙体外抹保温砂浆，然后、压入一层耐碱网格布，压实刮平，然后在外表面涂抹装饰材料，之后，烘干，得到保温墙体；具体的，在抹保温砂浆的步骤中，保温砂浆施工宜在找平层未固化干燥前分遍施工，根据该工程设计厚度，保温砂浆分两遍施工，最后一遍保温砂浆抹灰厚度应达到设计厚度，涂抹整个墙面后，用杠尺刮平，用大杠在墙面上搓平，去高补低。最后再用铁抹子压一遍，使表面平整，厚度一致。
基于以上技术方案，优选的，所述保温砂浆含有以下重量份的物质：
水泥b 100份；
氧化石墨烯 0.05-5份；
玻璃微珠 0-10；
重质碳酸钙 15-25；
乳胶粉 1-5；
羟丙基甲基纤维素 0.1-2；
木质纤维 0.1-2；
聚丙烯纤维 0.1-2。
基于以上技术方案，优选地，所述步骤(2)中抹保温砂浆时，可采用喷涂或涂抹的方式。
基于以上技术方案，优选的，所述步骤(2)中，涂抹保温砂浆时，外墙外侧保温砂浆层厚度为20-30mm，外墙内侧保温砂浆层厚度为10-20mm。
基于以上技术方案，优选打得，所述步骤(1)中的水泥a和水泥b独自选自于为快硬硅酸盐水泥、石膏矿渣水泥和普通硅酸盐水泥中的一种或多种混合。
基于以上技术方案，进一步优选的，所述玻璃微珠微为粉煤灰空心玻璃微珠，粉煤灰空心玻璃微珠质轻，隔热保温，耐磨，耐碱，化学性能稳定。
具体的，在涂料饰面施工的步骤中，涂料墙面采用保温系统配套的水性外墙底涂料和水性弹性外墙涂料或采用其他与保温系统相容的外墙涂料；外墙腻子均采用专用柔性外墙批嵌腻子。
有益效果：
本发明的保温墙体，保温砂浆以水泥为主，因此与墙面的粘结力强，不需要涂抹界面砂浆层，施工操作更加方便，且长时间后保温层不易开裂和松动，其施工后的墙体的导热系数可达0.055W/(mK)，而其防火性和抗风性等指标均优于现有的有机保温墙体。
本发明的保温墙体，提高了轻质钢条结构墙体的承重效果及抗震性能；浇注水泥后增加了轻质钢条结构墙体的整体强度，扩展了轻质钢条结构墙体的使用范围。通过本发明得到的墙体，在常压常温养护下的抗压强度达到270MPa，抗折强度达到83MPa。基于上述理由本发明可在建筑材料等领域广泛推广。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚，下面对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
根据墙体的形状，通过多个轻质钢条间的焊接构成所述墙体的骨架，在所述骨架的外表面固定上轻质铝合金外板，在所述轻质铝合金外板内浇注石膏矿渣水泥形成基层墙体，：基层墙体应坚实平整、完全干燥，不得有开裂、松动或泛碱，墙表面凸起物高度大于10mm时应剔除。保证施工表面平整，找平层与墙体之间的粘结强度不小于0.2MPa，找平层无空鼓、裂缝。
在所述基层墙体外抹保温砂浆，保温砂浆保温层的厚度为20mm，采用涂抹的方式一遍抹完，抹灰时顺序按照从上至下，从左至右抹灰。涂抹整个墙面后，用杠尺刮平，用大杠在墙面上搓平，去高补低。最后再用铁抹子压一遍，使表面平整，厚度一致。保温砂浆刷完后应养护5d左右(视具体气温而定)。然后、压入一层耐碱网格布，压实刮平，然后在外表面涂抹装饰材料，之后，烘干，得到保温墙体。
保温砂浆包括：
石膏矿渣水泥 100份；
氧化石墨烯 4份；
玻璃微珠 10；
重质碳酸钙 15；
乳胶粉 3；
羟丙基甲基纤维素 1；
木质纤维 0.5；
聚丙烯纤维 0.5。
Claims (6)
1.一种保温墙体的制备工艺，其特征在于具有如下步骤：
(1)根据墙体的形状，通过多个轻质钢条间的焊接构成所述墙体的骨架，在所述骨架的外表面固定上轻质铝合金外板，在所述轻质铝合金外板内浇注水泥a形成基层墙体；
(2)在所述基层墙体外抹保温砂浆，然后、压入一层耐碱网格布，压实刮平，然后在外表面涂抹装饰材料，之后，烘干，得到保温墙体。
2.根据权利要求1所述的制备工艺，其特征在于：所述保温砂浆含有以下重量份的物质：
水泥b100份；
氧化石墨烯0.05-5份；
玻璃微珠0-10；
重质碳酸钙15-25；
乳胶粉1-5；
羟丙基甲基纤维素0.1-2；
木质纤维0.1-2；
聚丙烯纤维0.1-2。
3.根据权利要求1所述的制备工艺，其特征在于：所述步骤(2)中抹保温砂浆时，可采用喷涂或涂抹的方式。
4.根据权利要求1所述的制备工艺，其特征在于：所述步骤(2)中，涂抹保温砂浆时，外墙外侧保温砂浆层厚度为20-30mm，外墙内侧保温砂浆层厚度为10-20mm。
5.根据权利要求1所述的制备工艺，其特征在于：所述步骤(1)中的水泥a和水泥b独立选自于为快硬硅酸盐水泥、石膏矿渣水泥和普通硅酸盐水泥中的一种或多种混合。
6.根据权利要求2所述的制备工艺，其特征在于：所述玻璃微珠微粉煤灰空心玻璃微珠。